Bio-hydrogen production based on catalytic reforming of volatiles generated by cellulose pyrolysis: an integrated process for ZnO reduction and zinc nanostructures fabrication

The paper presents a process of cellulose thermal degradation with bio-hydrogen generation and zinc nanostructures synthesis. Production of zinc nanowires and zinc nanoflowers was performed by a novel processes based on cellulose pyrolysis, volatiles reforming and direct reduction of ZnO. The bio-hydrogen generated in situ promoted the ZnO reduction with Zn nanostructures formation by vapor–solid (VS) route. The cellulose and cellulose/ZnO samples were characterized by thermal analyses (TG/DTG/DTA) and the gases evolved were analyzed by FTIR spectroscopy (TG/FTIR). The hydrogen was detected by TPR (Temperature Programmed Reaction) tests. The results showed that in the presence of ZnO the cellulose thermal degradation produced larger amounts of H2 when compared to pure cellulose. The process was also carried out in a tubular furnace with N2 atmosphere, at temperatures up to 900 °C, and different heating rates. The nanostructures growth was catalyst-free, without pressure reduction, at temperatures lower than those required in the carbothermal reduction of ZnO with fossil carbon. The nanostructures were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and transmission electron microscopy (TEM). The optical properties were investigated by photoluminescence (PL). One mechanism was presented in an attempt to explain the synthesis of zinc nanostructures that are crystalline, were obtained without significant re-oxidation and whose morphologies are dependent on the heating rates of the process. This route presents a potential use as an industrial process taking into account the simple operational conditions, the low costs of cellulose and the importance of bio-hydrogen and nanostructured zinc.

Morphology and properties of (Ba, Sr, Ca) titanates synthesized by microwave-assisted hydrothermal method

Ba1-xCaxTiO3, Ba1-xSrxTiO3 and Sr1-xCaxTiO3 (x = 0, 0.25, 0.50, 0.75 and 1) nanoparticles were synthesized using the microwave-assisted hydrothermal method. Samples were prepared for 40 minutes at 140°C under a pressure of 3 MPa using an adapted domestic microwave oven. The samples were characterized by X-Ray diffraction (XRD), scanning electron microscopy (FE-SEM), and Raman, photoluminescence (PL) and ultraviolet-visible (UV-Vis) spectroscopies. XRD data show that ceramic powders have crystalline phases associated with a short-range structural disorder. This structural disorder is confirmed by Raman spectral bands indicating multi-phonon processes and the presence of defects or impurities. Such defects account for a broad band in the photoluminescence spectrum in the green light (460 nm) region for all samples. Gap energy variation, obtained from UV-Vis spectra, suggest a non-uniform band structure of these titanates in accordance with the PL results. The morphology of each sample is changed with doping and varies from a spherical to cubic appearance for energy minimization.

Effect of Zn Sputtering Rate on the Morphological and Optical Properties of ZnO Films

Zinc oxide (ZnO) and aluminum-doped zinc oxide (ZnO:Al) thin films were deposited onto glass and silicon substrates by RF magnetron sputtering using a zinc-aluminum target. Both films were deposited at a growth rate of 12.5 nm/min to a thickness of around 750 nm. In the visible region, the films exhibit optical transmittances which are greater than 80%. The optical energy gap of ZnO films increased from 3.28 eV to 3.36 eV upon doping with Al. This increase is related to the increase in carrier density from 5.9 × 1018 cm-3 to 2.6 × 1019 cm-3. The RMS surface roughness of ZnO films grown on glass increased from 14 to 28 nm even with only 0.9% at Al content. XRD analysis revealed that the ZnO films are polycrystalline with preferential growth parallel to the (002) plane, which corresponds to the wurtzite structure of ZnO.