Microhardness of dual-polymerized resin cement around a translucent fiber post in the intraradicular environment

Aim: In this study, we evaluated the effect of photopolymerization on Vickers microhardness of dual-polymerized resin cement at three locations when a translucent quartz fiber post was used. Materials and Methods: Single-rooted bovine teeth received quartz fiber post systems (length: 12 mm) using a dual-polymerized resin cement. In Group 1, the posts were cemented but not photopolymerized, and in Group 2, the posts were both cemented and photopolymerized. After cementation, approximately 1.5-mm thick sections were obtained (two cervical, two middle, and two apical) for regional microhardness evaluations. Statistical Analysis: Statistical analyses were performed using the SPSS software (ver. 11.0 for Windows; SPSS, Inc., Chicago, IL, USA). Microhardness (kg/mm 2 ) data were submitted to two-way analysis of variance (two-way ANOVA) and repeated measures with microhardness values as the dependent variable and polymerization status (two levels: with and without) and root region (three levels: cervical, middle, and apical) as independent variables. Multiple comparisons were made using Dunnett's T3 post-hoc test. P values of <0.05 were considered to indicate statistical significance in all tests. Results: Photopolymerization did not significantly change the microhardness values when compared with no photopolymerization. Microhardness values also showed no significant difference between the three regions in the root canals in both groups. Conclusions: The mode of polymerization of the cement tested in combination with the translucent quartz fiber post system did not affect the microhardness of the cement at the cervical, middle, or apical regions of the root.

Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA

Newly available materials for retrograde obturation should have their sealing properties evaluated. The goal of this study was to evaluate the sealing ability of Endo CPM sealer, an MTA-based endodontic cement. Single-rooted extracted human teeth were endodontically treated. After apical sectioning, retrograde cavities were prepared. Teeth were divided into five experimental groups (n=12), in which the following materials were used: Sealer 26 (S26), white Mineral Trioxide Aggregate (MTA), Endo CPM Sealer (CPM1), Endo CPM Sealer in thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE), and two control groups (n=3). After retrograde obturation, the teeth were immersed in 0.2% rhodamine B dye for 48 hours in a vacuum chamber Marginal leakage data were subjected to ANOVA and Tukey tests at 5% significance level. S26 presented greater sealing ability (p<0.05) than ZOE, MTA, CPM1, and CPM2, all of which had similar results (p>0.05). We concluded that Sealer 26 has the greatest sealing ability. Endo CPM Sealer, with sealing ability similar to MTA, could be used as a retrograde obturation material.