Resumo:
In the second half of the last century the automobile industries suffered from the petroleum crisis caused mainly by the wars in the Middle East. These crises led the automakers rethink their vehicles. One of the most important events after that was the adoption of new steels by the industry. One example is the TRIP steels (Transformationinduced plasticity). It is known that the macroscopic behavior of a material is strongly dependent on its microstructure and therefore the quantitative metallography is important to understand and relate the material properties to its microstructure. In this work, different specimens of TRIP steels were etched using LePera reagent. The obtained images were analyzed using digital processing. Using the ImageJ software the methods threshold and watershed were studied as well as a comparison with the ASTM E562 standard. The methods were compared and finally the morphological characteristics and volumetric fraction of the retained austenite and martensite phases were analyzed. The results showed that the threshold led to a higher number of identified grains with lower mean area and total area fraction than the watershed method and ASTM standard
Resumo:
This work examines the possible effects of successive repair procedures on the microstructure of welded steel SAE 4130 by TIG welding process. Discussions and results were made about the metallographic analysis , non-metallic inclusions and microhardness tests , which were conducted on samples taken from the cradle engine component after the end of its life , a model airplane T-27 Tucano , made by EMBRAER and belonging were performed FAB . The choice of such component is due to the fact that this is critical to flight safety since it provides support for the aircraft engine . Thus regions of the weld metal , base metal and heat affected , with samples of the original weld bead , free of weld bead and also with four rework procedures for TIG welding zone were analyzed . It was found that after the fourth rework there is an increase in the amount of martensite , which may weaken the material with respect to resistance to fatigue. It was also found that the regions of the heat affected zone and weld metal have higher microhardness values when compared to those found in the base metal due to favoring the formation of ferritic and tempered martensite microstructures . Moreover, a welding process promotes a region with less non-metallic inclusions than metal base , which also explains the difference in the results obtained
Resumo:
Fracture surfaces express sequences of events of energy release with crack propagation in metal alloys, the evolution of topographic features can indicate the lines of load action, failures during the use or processing. The quantitative fractography is an important tool in the study of fracture surfaces, because it allows their interpretation and characterization. In order to evaluate the effectiveness of the characterization of fracture surfaces grounded on concepts such as selfsimilarity and self-affinity, it used the 15-5PH steel that was characterized by metallographic and tensile tests. The metallography allows the microstructural characterization of this steel and proved the presence of the martensite phase in the slats form and a fine-grained, both in the radial and in the axial direction of the dowel. The tensile test (ASTM E8) of this material allowed the determination of the mechanical properties, so based on the obtained results it was possible to affirm that the 15-5PH steel has high mechanical properties and a good stretch. Besides, the specimens also underwent testing of crack propagation, standardized by ASTM E647-00, thus it was obtained the fracture surfaces for characterization under monofractal and multifractal approaches. In front of all the exposed it was possible to conclude that in all measurements the correlation between the crack tip position and the fractal dimension was established in accordance with changes in the thickness and in the fracture micromechanisms presents. Furthermore, the multifractal approach was more sensitive to these variations allowing a more detailed characterization of the morphology
Resumo:
Seeking to meet the requirements: relatively low cost of materials and wide applicability in the automotive industry. The best option was the steel Dual Phase (DP), because that is lighter, have high formability, meet the cost requirements and applicability, steel Dual Phase (DP) came to meet these requirements with its two-phase microstructure, ferrite and martensite microstructure who claim to respect and mechanical properties. In this context, the aim of this study was to correlate the microstructure revealed in metallography to the mechanical properties observed in hardness and tensile tests. The microstructure is revealed by etching in 2% nital and then captured images of the sample were processed in ImageJ software to aid in determining the volume fraction of the phases present. Therefore, the mechanical properties were evaluated with respect to volume fraction of the steel layers and analyzed DP 600 together with the mechanical properties obtained by Rockwell hardness test and tensile test. With the values of the mechanical properties calculated and tested, it was possible to describe the method of metallography, as the attack phase and counts, so that it can use this relationship tested/calculated property as a qualitative analytical tool. The method used for the correlation between the microstructure and mechanical properties confirmed the importance of the phases present in the Dual Phase steel to obtain the desired mechanical properties in the application of the steel
Resumo:
Several alloys present the shape memory effect and among them, the equiatomic NiTi alloy, nitinol, is the most important one. It is usually used in several engineering applications and also in biomedical devices, in the fabrication of orthodontic wire, stents and Judet staples. Although a considerable amount of these biomedical devices is utilized in Brazil and a fraction of it is already made here, all nitinol used is bought abroad. Thus, it is important to develop the necessary know-how to fabricate NiTi wire and sheet. It would mean less importation with job creation and wealth generation for the country. In this work nitinol was obtained powder metallurgy from elemental powders of Ti and Ni using uniaxial compression and uniaxial compression followed by isostatic compression. The final densities achieved were determined by the Archimedes method. The precipitation of intermetallic secondary phases was studied and the samples were characterized by metallographic analysis, optical microscopy and X-ray diffraction. Results indicated that 50 hours sintering route showed a low amount of intermetallics, and no trace of unreacted powder. XRD and metallography at room temperature indicated B19’ as the predominant phase, which corresponds to martensite. Although density results showed little dispersion, the most dense sample was compacted under uniaxial compression and presented 4.8 g/cm3, corresponding to 20.84% porosity. Density variation was considered normal to the measurement process and independent of the compaction mode
Resumo:
This work aims to study the Dual-Phase 600 and 780 steels, which are part of technology development project materials for the automotive industry. It is worth underscoring the antagonistic properties as the Dual-Phase steel assemble, high mechanical strength and elongation due its microstructure, ferrite and martensite. These properties are obtained by a intercritical heat treatment which facilitates the formation of a hardness metastable microstructure shaped plates of low carbon steels. The applicability of Dual Phase steel in the structure of vehicles is huge and its production is already on a commercial scale, so the study and development of this material implies lower cost in automobile manufacturing processes. The dual phase steels DP600 and DP780 underwent tensile, hardness and metallographic analysis to evaluate and comparing its properties. The results indicate that the DP780 steel has higher strength and hardness than the DP600 steel and its microstructure consists of martensite higher fraction which accounts for the higher resistance and hardness. However, the DP600 has higher conformability to DP780 steel
Resumo:
Pós-graduação em Engenharia Mecânica - FEG
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
Resumo:
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)