Microtensile bond strength of a resin cement to silica-coated and silanized in-ceram zirconia before and after aging

Purpose: This study compared the microtensile bond strength of resin-based cement (Panavia F) to silica-coated, silanized, glass-infiltrated high-alumina zirconia (In-Ceram Zirconia) ceramic in dry conditions and after various aging regimens. Materials and Methods: The specimens were placed in 1 of 4 groups: group 1: dry conditions (immediate testing without aging); group 2: water storage at 37°C for 150 days; group 3: 150 days of water storage followed by thermocycling (× 12,000, 5°C to 55°C); group 4: water storage for 300 days; group 5: water storage for 300 days followed by thermocycling. Results: Group 1 showed a significantly higher microtensile bond strength value (26.2 ± 1 MPa) than the other aging regimens (6.5 ± 1, 6.2 ± 2, 4.5 ± 1, 4.3 ± 1 MPa for groups 2, 3, 4, and 5, respectively) (P < .01). Conclusion: Satisfactory results were seen in dry conditions, but water storage and thermocycling resulted in significantly weaker bonds between the resin cement and the zirconia.

Biocompatibility of resin-based dental materials applied as liners in deep cavities prepared in human teeth

Background: Since only a few data have been published concerning the effects of resinous dental materials on the pulp-dentin complex, the aim of this study was to evaluate the biocompatibility of resin-based materials applied as liners in deep cavities prepared in duman teeth. Methods: After preparing class V cavities, the following dental materials were applied on the axial walls: group 1, Vitrebond™ (VIT; 3M ESPE); group 2, Ultra-Blend® Plus™ (UBP; Untradent); and group 3, Clearfil™ SE Bond (CSEB; Kuraray). In group 4 (control), the hard-setting calcium hydroxide cement Dycal (CH; Caulk/Dentsply) was used. The teeth extracted at 7 days or between 30 and 85 days after the clinical procedures were processed for histological evaluation. Results: For all the experimental and control groups, most of specimens exhibited no pulpal response or slight inflammatory reaction associated with slight tissue disorganization at 7-day period. Moderate inflammatory pulpal response occurred only in one tooth (RDT = 262 μm) of group 3 in which transdentinal diffusion of resin components was observed. Conclusion: The resin-based dental cements VIT and UBP as well as the bonding agent CSEB presented acceptable biocompatibility when applied in deep cavities prepared in sound human teeth. © 2006 Wiley Periodicals, Inc.

Evaluation of the thermoplasticity of different gutta-percha cones and Resilon®

The goal of this study was to evaluate the thermoplasticity of conventional and thermoplastic gutta-percha and Resilon®, a polyester polymer-based material. Specimens with standardised dimensions were made from the following materials: conventional and thermoplastic gutta-percha (Dentsply), conventional and thermoplastic gutta-percha (Endopoints) and Resilon®. After 24 h, the specimens were placed in water at 70°C for 60 s, and thereafter positioned between two glass slabs. Each set was compressed by a 5-kg weight. Digital images of the specimens before and after compression were obtained and analysed. The thermoplasticity of each material was confirmed by the difference between final and initial areas of each sample. The data were analysed statistically by ANOVA and Tukey's test at a 5% significance level. Resilon® had the highest thermoplasticity means (P < 0.05). Among the gutta-percha cones, Endopoints TP (thermoplastic) presented the highest thermoplasticity means and differed significantly from the other commercial brands (P < 0.05). Resilon® had good thermoplasticity, endorsing its use as a thermoplastic root canal filling material. © 2007 The Authors. Journal compilation © 2007 Australian Society of Endodontology.

Effect of resin luting film thickness on fracture resistance of a ceramic cemented to dentin

Purpose: The aim of this study was to evaluate the fracture resistance of ceramic plates cemented to dentin as a function of the resin cement film thickness. Materials and Methods: Ceramic plates (1 and 2 mm thicknesses) were cemented to bovine dentin using resin composite cement. The film thicknesses used were approximately 100, 200, and 300 μm. Noncemented ceramic plates were used as control. Fracture loads (N) were obtained by compressing a steel indenter in the center of the ceramic plates. ANOVA and Tukey tests (α = 0.05) were used for each ceramic thickness to compare fracture loads among resin cement films used. Results: Mean fracture load (N) for 1-mm ceramic plates were: control - 26 (7); 100 μm - 743 (150); 200 μm - 865 (105); 300 μm - 982 (226). Test groups were significantly different from the control group; there was a statistical difference in fracture load between groups with 100 and 300 μm film thicknesses (p < 0.01). Mean fracture load for 2-mm ceramic plates were: control - 214 (111); 100 μm - 1096 (341); 200 μm - 1067 (226); 300 μm - 1351 (269). Tested groups were also significantly different from the control group (p < 0.01). No statistical difference was shown among different film thicknesses. Conclusions: Unluted specimens presented significantly lower fracture resistance than luted specimens. Higher cement film thickness resulted in increased fracture resistance for the 1-mm ceramic plates. Film thickness did not influence the fracture resistance of 2-mm porcelain plates. Copyright © 2007 by The American College of Prosthodontists.

Shear bond strength fatigue limit of rest seats made with dental restoratives

Purpose: This study compared the shear bond strength (SBS) to enamel of rest seats made with a glass-ionomer cement (Fuji IX GP Fast), a resin-modified glass-ionomer cement (Fuji II LC), and a composite resin (Z100 MP) under monotonic and cyclic loading. Materials and Methods: Rest seats were built up onto the lingual surfaces of 80 intact human mandibular incisors. Specimens (n=10) were stored in distilled water at 37°C for 30 days and subjected to shear forces in a universal testing machine (0.5 mm/min) until fracture. The SBS values were calculated (MPa) using the bonding area (9.62 mm2) delimited by adhesive tags. A staircase approach was used to determine the SBS fatigue limit of each material. Specimens were submitted to either 10,000 cycles (5 Hz) or until specimen fracture. A minimum of 15 specimens was tested for each material. Scanning electron microscopy was used to examine the mode of failure. Data were statistically analyzed with one-way ANOVA and Tukey HSD tests (α = 0.05). Results: Z100 MP yielded higher (p < 0.05) SBS (12.25 MPa) than Fuji IX GP Fast (7.21 MPa). No differences were found between Fuji II LC (10.29 MPa) and the other two materials (p > 0.05). Fuji II LC (6.54 MPa) and Z100 MP (6.26 MPa) had a similar SBS limit. Fuji IX GP Fast promoted the lowest (p < 0.05) SBS fatigue limit (2.33 MPa). All samples showed cohesive failure patterns. Conclusion: Fatigue testing can provide a better means of estimating the performance of rest seats made with dental restoratives.

In vitro evaluation of marginal leakage in bonded restorations, with mechanical or chemical-mechanical (Carisolv) removal of carious tissue

This study carried out an in vitro evaluation and comparison of the occurrence of marginal leakage in bonded restorations using mechanical or chemical-mechanical (Carisolv) removal of carious tissue. For that purpose, 40 extracted decayed human molars were divided into 4 groups: GI (burs + Prime & Bond NT + TPH), GII (Carisolv + Prime & Bond NT + TPH), GIII (burs + SBMP + Z100) and GIV (Carisolv + SBMP + Z100). After accomplishment of the restorations and thermal cycling, the teeth were exposed to dye, sectioned and qualitatively evaluated. The results demonstrated that the system of removal of carious tissue did not influence the results of microleakage at any of the cavity margins. At dentinal margins, use of the Prime & Bond NT + TPH restorative system allowed the occurrence of less microleakage than the SBMP + Z100 system.

Resin microtensile bond strength to feldspathic ceramic: Hydrofluoric acid etching vs tribochemical silica coating

This study aimed to compare the microtensile bond strength of resin cement to alumina-reinforced feldspathic ceramic submitted to acid etching or chairside tribochemical silica coating. Ten blocks of Vitadur-α were randomly divided into 2 groups according to conditioning method: (1) etching with 9.6% hydrofluoric acid or (2) chairside tribochemical silica coating. Each ceramic block was luted to the corresponding resin composite block with the resin cement (Panavia F). Next, bar specimens were produced for microtensile testing. No significant difference was observed between the 2 experimental groups (Student t test, P> .05). Both surface treatments showed similar microtensile bond strength values.

Homogenous demineralized dentin matrix for application in cranioplasty of rabbits with alloxan-induced diabetes: Histomorphometric analysis

Purpose: The aim of this work was to evaluate the bone-repair process after implantation of homogenous demineralized dentin matrix (HDDM) slices in surgical defects created in the parietal bones of rabbits with alloxan-induced diabetes. Materials and Methods: Forty-eight rabbits were selected and divided into 4 groups of 12 rabbits: the control group, diabetic rabbits (D), diabetic rabbits with a PTFE barrier (D-PTFE), and diabetic rabbits with a PTFE barrier and with slices of homogenous demineralized dentin matrix (D-PTFE+HDDM). The diabetic animals received a single dose of alloxan monohydrate (90 mg/kg) intravenously on the marginal ear vein, and their blood glucose was verified daily. The rabbits were sacrificed after 15, 30, 60, and 90 days. The histologic findings show both better bone structure and significantly greater bone density, as determined by histomorphometric analysis, for the D-PTFE + HDDM group than for the other 3 groups (P < .01). It was also observed that the mean bone density increased gradually from 15 to 90 days (except in the D-PTFE group). Conclusion: It was concluded that the HDDM was biocompatible with the bone repair of diabetic rabbits and that HDDM slices stimulated bone tissue formation. Facilitation of bone repair with HDDM could be useful in diabetic patients.

Influence of resin composite insertion technique in preparations with a high C-factor

Objective: To evaluate the marginal microleakage in enamel and dentin/cementum walls in preparations with a high C-factor, using 3 resin composite insertion techniques. The null hypothesis was that there is no difference among the 3 resin composite insertion techniques. Method and Materials: Standardized Class 5 cavities were prepared in the lingual and buccal aspects of 30 caries-free, extracted third molars. The prepared teeth were randomly assigned to 3 groups: (1) oblique incremental placement technique, (2) horizontal incremental placement technique, and (3) bulk insertion (single increment). The preparations were restored with a 1-bottle adhesive (Single Bond, 3M ESPE) and microhybrid resin composite (Z100, 3M ESPE). Specimens were isolated with nail varnish except for a 2-mm-wide rim around the restoration and thermocycled (1,000 thermal cycles, 5°C/55°C; 30-second dwell time). The specimens were immersed in an aqueous solution of 50 wt% silver nitrate for 24 hours, followed by 8 hours in a photo-developing solution and evaluated for microleakage using an ordinal scale of 0 to 4. The microleakage scores obtained from occlusal and gingival walls were analyzed with Wilcoxon and Kruskal-Wallis nonparametric tests. Results: The null hypothesis was accepted. The horizontal incremental placement technique, the oblique incremental technique, and bulk insertion resulted in statistically similar enamel and dentin microleakage scores. Conclusion: Neither the incremental techniques nor the bulk placement technique were capable of eliminating the marginal microleakage in preparations with a high C-factor.

Effects of hemostatic agents on the histomorphologic response of human dental pulp capped with calcium hydroxide

Objective: To evaluate the response of human pulps capped with a calcium hydroxide [Ca(OH)2] cement after bleeding control with 2 hemostatic agents. Method and Materials: Pulps were exposed on the occlusal floor, and the bleeding was controlled either with saline solution (SS) or 2.5% sodium hypochlorite (NaOCI) (SH). After that, the pulp was capped with Ca(OH) 2 cement and restored with resin composite. After 30 (groups SS30 and SH30) and 60 (groups SS60 and SH60) days, the teeth were extracted and processed with hematoxylin-eosin and categorized in a histologic score system. The data were subjected to Kruskal-Wallis and Mann-Whitney tests (α = .05). Results: Regarding dentin bridge formation, an inferior response of SH60 group was observed when compared to SS60 (P < .05). The response of the SH30 group generally was similar to that of the groups treated with saline solution. However, after 60 days, 2.5% NaOCl showed a trend toward having an inferior response. Conclusion: Using saline solution as a hemostatic agent before pulp capping with Ca(OH)2 resulted in a significantly better histomorphologic response than using 2.5% NaOCl as a hemostatic agent before capping with Ca(OH)2.

Conservative treatment of patients with periapical lesions associated with extraoral sinus tracts

This paper describes the clinical courses of three cases with extra-oral sinus tract formation, from diagnosis and treatment to short-term follow-up and evaluation. All teeth involved had periradicular radiolucent areas noted on radiographic examination and extra-oral sinus tracts appearing on the chin with exudation and unpleasant aesthetic appearance. The adopted treatment protocol included treating the sinus tract surface simultaneously with the root canal therapy. After root canal shaping using 5.25% sodium hypochlorite solution, calcium hydroxide-based pastes associated with different vehicles were inserted into the root canal for 4 months, and were changed monthly. All the sinus tracts healed in 7 to 10 days. The apical lesions were completely repaired in a maximum period of 24 months. The treatment adopted provided a complete healing of the periapical lesions in a short follow-up period. Surgical repair of the cutaneous sinus tract was therefore unnecessary. © 2007 The Authors. Journal compilation © 2007 Australian Society of Endodontology.

Microhardness and fluoride release of restorative materials in different storage media

This study evaluated the surface microhardness and fluoride release of 5 restorative materials - Ketac-Fil Plus, Vitremer, Fuji II LC, Freedom and Fluorofil - in two storage media: distilled/deionized water and a pH-cycling (pH 4.6). Twelve specimens of each material, were fabricated and the initial surface microhardness (ISM) was determined in a Shimadzu HMV-2000 microhardness tester (static load Knoop). The specimens were submitted to 6- or 18-h cycles in the tested media. The solutions were refreshed at the end of each cycle. All solutions were stored for further analysis. After 15-day storage, the final surface microhardness (FSM) and fluoride release were measured. Fluoride dose was measured with a fluoride-specific electrode (Orion 9609-BN) and digital ion analyzer (Orion 720 A). The variables ISM, FSM and fluoride release were analyzed statistically by analysis of variance and Tukey's test (p<0.05). There was significant difference in FSM between the storage media for Vitremer (pH 4.6 = 40.2 ± 1.5; water = 42.6 ± 1.4), Ketac-Fil Plus (pH 4.6 = 73.4 ± 2.7; water = 58.2 ± 1.3) and Fluorofil (pH 4.6 = 44.3 ± 1.8; water = 38.4 ± 1.0). Ketac-Fil Plus (9.9 ± 18.0) and Fluorofil (4.4 ± 1.3) presented higher fluoride release in water, whereas Vitremer (7.4 ± 7.1), Fuji II LC (5.7 ± 4.7) and Freedom (2.1 ± 1.7) had higher fluoride release at pH 4.6. Microhardness and fluoride release of the tested restorative materials varied according to the storage medium.

Microtensile bond strength of a repair composite to leucite-reinforced feldspathic ceramic

The purpose of this study was to evaluate the microtensile bond strength of a repair composite resin to a leucite-reinforced feldspathic ceramic (Omega 900, VITA) submitted to two surface conditionings methods: 1) etching with hydrofluoric acid + silane application or 2) tribochemical silica coating. The null hypothesis is that both surface treatments can generate similar bond strengths. Ten ceramic blocks (6x6x6 mm) were fabricated and randomly assigned to 2 groups (n=5), according to the conditioning method: G1- 10% hydrofluoric acid application for 2 min plus rinsing and drying, followed by silane application for 30 s; G2- airborne particle abrasion with 30 μm silica oxide particles (CoJet-Sand) for 20 s using a chairside air-abrasion device (CoJet System), followed by silane application for 5 min. Single Bond adhesive system was applied to the surfaces and light cured (40 s). Z-250 composite resin was placed incrementally on the treated ceramic surface to build a 6x6x6 mm block. Bar specimens with an adhesive area of approximately 1 ± 0.1 mm2 were obtained from the composite-ceramic blocks (6 per block and 30 per group) for microtensile testing. No statistically significant difference was observed between G1 (10.19 ± 3.1 MPa) and G2 (10.17 ± 3.1 MPa) (p=0.982) (Student's t test; á = 0.05). The null hypothesis was, therefore, accepted. In conclusion, both surface conditioning methods provided similar microtensile bond strengths between the repair composite resin and the ceramic. Further studies using long-term aging procedures should be conducted.

Surface conditioning of a composite used for inlay/onlay restorations: Effect on μTBS to resin cement

Purpose: To assess the effect of the composite surface conditioning on the microtensile bond strength of a resin cement to a composite used for inlay/onlay restorations. Materials and Methods: Forty-two blocks (6 × 6 × 4 mm) of a microfilled composite (Vita VMLC) were produced and divided into 3 groups (N = 14) by composite surface conditioning methods: Gr1 - etching with 37% phosphoric acid, washing, drying, silanization; Gr2 - air abrasion with 50-l̀m Al2O3 particles, silanization; Gr3 - chairside tribochemical silica coating (CoJet System), silanization. Single-Bond (one-step adhesive) was applied on the conditioned surfaces and the two resin blocks treated with the same method were cemented using RelyX ARC (dual-curing resin cement). The specimens were stored for 7 days in water at 37°C and then sectioned to produce nontrimmed beam samples, which were submitted to microtensile bond strength testing (μTBS). For statistical analysis (one-way ANOVA and Tukey's test, · = 0.05), the means of the beam samples from each luted specimen were calculated (n = 7). Results: μTBS values (MPa) of Gr2 (62.0 ± 3.9a) and Gr3 (60.5 ± 7.9a) were statistically similar to each other and higher than Gr1 (38.2 ± 8.9b). The analysis of the fractured surfaces revealed that all failures occurred at the adhesive zone. Conclusion: Conditioning methods with 50-l̀m Al2O3 or tribochemical silica coating allowed bonding between resin and composite that was statistically similar and stronger than conditioning with acid etching.

Influence of brush type as a carrier of adhesive solutions and paper points as an adhesive-excess remover on the resin bond to root dentin

Purpose: To evaluate the influence of the brush type as a earner of priming adhesive solutions and the use of paper points as a remover of the excess of these solutions on the push-out bond strength of resin cement to bovine root dentin. The null hypotheses were that brush type and the use of paper points do not affect the bond strength. Materials and Methods: The canals of 80 single-root bovine roots (16 mm in length) were prepared at 12 mm using the preparation drill (FRC Postec Plus, Ivoclar). Half of each root was embedded in acrylic resin and the specimens were divided into 8 groups, considering the factors brush type (4 levels) and paper point (2 levels) (n = 10): Gr 1: small microbrush (Cavi-Tip, SDI); Gr 2: Microbrush (Dentsply); Gr 3: Endobrush (Bisco); Gr 4: conventional brush (Bisco); Gr 5: Cavi-Tip (SDI) + paper points; Gr 6: Microbrush (Dentsply) + paper points; Gr 7: Endobrush (Bisco) + paper points; Gr 8: conventional brush (Bisco) + paper points. The root dentin was treated with a multistep total-etch adhesive system (All Bond 2). The adhesive system was applied using each microbrush, with and without using paper points. One fiber post was molded with addition silicon and 80 posts were made of resin cement (Duolink), The resin posts were luted (Duolink resin cement), and the specimens were stored for 24 h in water at 37°C. Each specimen was cut into 4 disk-shaped samples (1.8 mm in thickness), which were submitted to the push-out test. Results: The brush type (p < 0.0001) (small microbrush > microbrush = endobrush = conventional brush) and the use of paper points (p = 0.0001) (with > without) influenced the bond strength significantly (two-way ANOVA). The null hypotheses were rejected. Conclusion: The smallest brush (Cavi-Tip) and the use of paper points significantly improved the resin bond to bovine root dentin.