Obtenção e caracterização óptica e elétrica de 'La''Ta'O IND.4' e LiTaO Ind.3 puros e dopados com Eu POT.3+

Eletronicalceramics are used in many applications such as: multilayer capacitor, transducer, pyroelectric sensors and electrooptic devices. In recent years there has been a growing demand for eletronicalceramics with better performance and functionality. This demand has accelerated the development of synthesis techniques to produce powders with well-defined particle size, shape and crystallinity. The eletronicalceramics in the form of bulk are determined by their performance characteristics of the powders used and the preparation process. So, physical and chemical properties of powders, such as chemical control of stoichiometry, purity, homogeneity, particle size and shape should be observed when choosing the methods of synthesis. Among the techniques used so far, the polymeric precursor method, also known as Pechini, has been considered ideal for the preparation of nanosized powders. Thus, this research project aims to use the polymeric precursor method to prepare powders of lithium tantalate and lanthanum tantalate, with good chemical stability. In this aspect is proposed to investigate the effects of variation of the concentration of europium about the properties of tantalate because doping with Eu3 + indicates that they may occupy different sites in the crystal structure, as in the case of LiTaO3. Effects of things like occupation sites, stability of phases and formation temperature have been previously investigated by the group, which motivated the formulation of this project. Our proposal aims to introduce the Eu3 + LaTaO4 and LiTaO3 and study the structural and optical properties of the powders obtained by Pechini method, as well as correlate these studies with the electrical properties of the material, mainly the Ironelectricty Hysteresis.

Modeling the crystallographic structure of Ho(Ni,Co,Mn)O3±δ perovskite-type manganite

Crystallographic and microstructural properties of Ho(Ni,Co,Mn)O3± perovskite-type multiferroic material are reported. Samples were synthesized with a modified polymeric precursor method. The synchrotron X-ray powder diffraction (SXRPD) technique associated to Rietveld refinement method was used to perform structural characterization. The crystallographic structures, as well as microstructural properties, were studied to determine unit cell parameters and volume, angles and atomic positions, crystallite size and strain. X-ray energies below the absorption edges of the transition metals helped to determine the mean preferred atomic occupancy for the substituent atoms. Furthermore, analyzing the degree of distortion of the polyhedra centered at the transitions metal atoms led to understanding the structural model of the synthesized phase. X-ray photoelectron spectroscopy (XPS) was performed to evaluate the valence states of the elements, and the tolerance factor and oxygen content. The obtained results indicated a small decrease distortion in structure, close to the HoMnO3 basis compound. In addition, the substituent atoms showed the same distribution and, on average, preferentially occupied the center of the unit cell.

Synthesis, structure and magnetic properties of Y3Fe5-xAlxO12 garnets prepared by the soft chemical method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Photocatalytic decomposition of rhodamine-b using scandium and silver-modified TiO2 powders

Semiconductor-mediated photocatalytic oxidation is an interesting method for water decontamination and a specially modified TiO2 is said to be a promising material. This study verified that the synthesis of 1wt%Ag modified-Sc0.01Ti0.99O1.995 powder samples prepared by Polymeric Precursor Method is capable of forming a mixture of anatase-rutile phase with high photocatalytic performance. This kind of material is found to have a lower bandgap compared to the TiO2-anatase commercial powders, which can be associated to an innovative hybrid modification. The simultaneous insertion of scandium in order to generate a p-type semiconductor and a metallic silver nanophase acting as an electron trapper demonstrated being capable of enhancing the degradation of rhodamine B compared to the commercial TiO2. In spite of the different thermal treatments or phase amounts, the hybrid modified powder samples showed higher photocatalytic activity than the commercial ones.

Structural and magnetic characterization of MnxZn1-xFe2O4 (x=0.2; 0.35; 0.65; 0.8; 1.0) ferrites obtained by the citrate precursor method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Microwave-assisted hydrothermal synthesis of structurally and morphologically controlled sodium niobates by using niobic acid as a precursor

There are many advantages to using a microwave as a source of heat in hydrothermal reactions. Because it is a quick and homogeneous way to crystallize ceramic powders, it was used in this work for the production of antiferroelectric sodium mobate (NaNbO3) in a cubic-like form and its intermediary phase, disodium diniobate hydrate (Na2Nb2O6 center dot H2O), with a fiber morphology. The syntheses were carried out by treating niobic acid (Nb2O5 center dot nH(2)O) with NaOH. By changing the reaction time and the concentration of the reactants, particles with different structures and different morphologies could be obtained. The structural evolution of the products of this reaction was elucidated on the basis of the arrangement of the NbO6 octahedral units. Conclusive results were obtained with morphological and structural characterizations through XRD, TEM, MEV, and NMR and Raman spectroscopy. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2008).

Microwave-hydrothermal synthesis of perovskite bismuth ferrite nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microwave-hydrothermal synthesis of single-crystalline Co3O 4 spinel nanocubes

An efficient microwave-hydrothermal (MAH) method has been developed for the synthesis of highly crystalline Co3O4 spinel nanocubes via β-Co(OH)2 without any surfactant assistance. The structure and surface chemical composition along the growth process are studied. The effects as well as the merits of the MAH method on the processing and characteristics of obtained Co3O4 spinel nanocubes are highlighted. © 2013 The Royal Society of Chemistry.

Structure and Physical Properties of EVA/Starch Precursor Materials for Foaming Applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and characterization of mono and polymeric cyclopalladated compounds: Crystal and molecular structure of [{Pd(dmba)(ONO2)}(2)(mu-pz)] center dot H2O (pz = pyrazine)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

X-ray diffraction and mossbauer spectra of nickel ferrite prepared by combustion reaction

Nickel ferrite powders with a nominal NiFe2O4 composition were synthesized by combustion reaction using urea as fuel. The powder was obtained using a vitreous silica basin heated directly on a hot plate at 480 degrees C until self-ignition occurred. After combustion, the powder was calcined at 700 degrees C for 2 h. The formation of the spinel phase and the distribution of cations in the tetrahedral and octahedral sites of the crystal structure were investigated by the Rietveld method, using synchrotron X-ray diffraction data and Mossbauer spectroscopy. The material presented a crystallite size of 120 nm and magnetic properties. The resulting stoichiometry after the Rietveld refinement was (Fe-0.989(2) Ni-0.011(2)) [Fe-1.012(2) Ni-0.989(2)] O-4.

An efficient microwave-assisted hydrothermal synthesis of BaZrO3 microcrystals: growth mechanism and photoluminescence emissions

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of the heat flux direction on electrical properties of SrBi2Nb2O9 thin films crystallized using a microwave oven

Ferroelectric SrBi2Nb2O9 (SBN) thin films were prepared by the polymeric precursors method and deposited by spin coating onto Pt/Ti/SiO2/Si substrate and crystallized using a domestic microwave oven. It was studied the influence of the heat flux direction and the duration of the thermal treatment on the films crystallization. An element with high dielectric loss, a SiC susceptor, was used to absorb the microwave energy and transfers the heat to the film. Influence of the susceptor position to the sample crystallization was verified, the susceptor was, placed or below the substrate or above the film. The SBN perovskite phase was observed after a thermal treatment at 700 degreesC for 10 min when the susceptor was placed below the substrate and for 30 min when the susceptor was placed above the film. Electrical measurements revealed that the film crystallized at 700 degreesC for 10 min, with the susceptor placed below the film, presented dielectric constant, dielectric loss, remanent polarization and coercive field of, 67, 0.011, 4.2 muC/cm(2) and 27.5 kV/cm, respectively. When the films were crystallized at 700 degreesC for 30 min, with the susceptor placed above the film, the dielectric constant was 115 and the dissipation factor was around of 0.033, remanent polarization and coercive field were 10.8 muC/cm(2) and 170 kV/cm, respectively. (C) 2003 Elsevier B.V. All rights reserved.

Structural and phenomenological characterization of the thermoreversible sol-gel transition of a zirconyl aqueous precursor modified by sulfuric acid

The thermoreversible sol-gel transition is well-known in biological and organic polymeric systems but has not been reported for inorganic systems. In this paper we put in evidence a thermoreversible sol-gel transition for zirconyl chloride aqueous solutions modified by sulfuric acid in the ratio 3:1 Zr:SO4. The synthesis conditions are detailed and a variety of experimental techniques (turbidimetry, dynamic rheology, and EXAFS) have been employed for investigating the thermal reversibility and the chemical structure of this new material. Turbidimetric measurements performed for solutions containing different concentrations of precursor have evidenced that the sol-gel transformation temperature increases from 50 to 80 degrees C as the concentration of zirconyl chloride decreases from 0.22 to 0.018 mol L-1. A more detailed study has been done for the sample with [Zr] = 0.156 mol L-1, in which the sol-gel-sol transformation has been repeated several times by a cyclic variation of the temperature. The mechanical properties of this sample, evaluated by measuring the storage and the loss moduli, show a change from liquid like to viscoelastic to elastic behavior during the sol-gel transition and vice versa during the gel-sol one. In situ EXAFS measurements performed at the Zr K-edge show that no change of the local order around Zr occurs during the sol-gel-sol transition, in agreement with the concept of physical gel formation. We have proposed for the structure of the precursor an inner core made of hydroxyl and oxo groups bridging together zirconium atoms surrounded in surface by complexing sulfate ligands, the sulfate groups act as a protective layer, playing a key role in the linking propagation among primary particles during sol-gel-sol transition.

High-efficient microwave synthesis and characterisation of SrSnO3

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)