Flexural strength of autopolymerizing denture reline resins with microwave postpolymerization treatment

Statement of problem. Microwave postpolymerization has been Suggested as a method to improve the mechanical strength of repaired denture base materials. However, the effect of microwave heating oil the flexural strength of the autopolymerizing denture reline resins has not been investigated.Purpose. This study analyzed the effect of microwave postpolymerization on the flexural strength of 4 autopolymerizing reline resins (Duraliner II, Kooliner, Ufi Gel Hard, and Tokuso Rebase Fast) and 1 heat-polymerized resin (Lucitone 550).Material and methods. For each material, 80 specimens (64 X 10 X 3.3 mm) were polymerized according to the manufacturer's instructions and divided into 10 groups (n = 8). Control group specimens remained as processed. Before testing, the specimens were Subjected to postpolymerization in a microwave oven using different power (500, 5,50, or 650 W) and time (3, 4, or 5 Minutes) settings. Load measurements (newtons) were made at a crosshead speed of 5 mm/min using a 3-point bending device with a span of 50 mill. The flexural strength values were calculated in MPa. Data analyses included 3-way and 2-way analysis of variance and the Tukey Honestly Significant Difference test (alpha=.05).Results. The flexural strengths of resins Duraliner 11 and Kooliner were significantly increased (P=.0015 and P=.0046, respectively) with the application of microwave irradiation using different time/power combinations. The materials Lucitone 550, Tokuso Rebase Fast, and Ufi Gel Hard demonstrated no significant strength improvement compared to the corresponding control. Only after microwave postpolymerization irradiation for 3 minutes at 550 W did Lucitione 550 show significantly higher flexural strength than Tokuso Rebase Fast and Ufi Gel Hard relining resins.Conclusion. Microwave postpolymerization irradiation can be an effective method for increasing the flexural strength of Duraliner II (at 650 W) and Kooliner (at 550 W and 650 W for 5 minutes).

Fibrin adhesive implant in wound healing repair of dental sockets with topical application of epsilon aminocaproic acid: Histological analysis

The aim of the study was to evaluate wound healing repair of dental sockets after topical application of 5% epsilon-aminocaproic acid (EACA) and the use of fibrin adhesive implant in rats under anticoagulant therapy with warfarin. Sixty Albinus wistar rats were used, divided into three groups of 20. In Group I, the animals were given 0.1 mL/100 mg of 0.9% saline solution per day, beginning 6 days before dental extraction and continuing throughout the experimental period. In Group II, the animals received 0.03 mL of sodium warfarin daily, beginning 6 days before the surgery and continuing until the day of sacrifice; after tooth extractions, the sockets were filled with fibrin adhesive material. In Group III the animals were treated as in Group II, and after extractions, the sockets were irrigated with 5 mL of 5% EACA and filled with the same fibrin adhesive material. All groups presented biological phases of wound healing repair, the differences being evident only in the chronology. The results obtained in Group III were very similar to those of Group I in the last period of wound repair, whereas Group II presented a late chronology compared to the other groups. © 2005 Wiley Periodicals, Inc.