Microtensile bond strength of a resin cement to feldpathic ceramic after different etching and silanization regimens in dry and aged conditions

Objectives. This study evaluated the durability of bond strength between resin cement and a feldspathic ceramic submitted to different etching regimens with and without silane coupling agent application.Methods. Thirty-two blocks (6.4 mm x 6.4 mm x 4.8 mm) were fabricated using a microparticulate feldspathic ceramic (Vita VM7), ultrasonically cleaned with water for 5 min and randomly divided into four groups, according to the type of etching agent and silanization method: method 1, etching with 10% hydrofluoric (HF) acid gel for I min + silanization; method 2, HF only; method 3, etching with 1.23% acidulated phosphate fluoride (APF) for 5 min + silanization; method 4, APF only. Conditioned blocks were positioned in their individual silicone molds and resin cement (Panavia F) was applied on the treated surfaces. Specimens were stored in distilled water (37 degrees C) for 24 h prior to sectioning. After sectioning the ceramic-cement blocks in x- and Y-axis with a bonded area of approximately 0.6 mm(2), the microsticks of each block were randomly divided into two storage conditions: Dry, immediate testing; TC, thermal cycling (12,000 times) + water storage for 150 d, yielding to eight experimental groups. Microtensile bond strength tests were performed in universal testing machine (cross-head speed: 1 mm/min) and failure types were noted. Data obtained (MPa) were analyzed with three-way ANOVA and Tukey's test (alpha = 0.05).Results. Significant influence of the use of silane (p < 0.0001), storage conditions (p = 0.0013) and surface treatment were observed (p = 0.0014). The highest bond strengths were achieved in both dry and thermocycled conditions when the ceramics were etched with HF acid gel and silanized (17.4 +/- 5.8 and 17.4 +/- 4.8 MPa, respectively). Silanization after HF acid gel and APT treatment increased the results dramatically (14.5 +/- 4.2-17.4 +/- 4.8 MPa) compared to non-silanized groups (2.6 +/- 0.8-8.9 +/- 3.1 MPa) where the failure type was exclusively (100%) adhesive between the cement and the ceramic.Significance. Silanization of the feldspathic ceramic surface after APF or HF acid etching increased the microtensile bond strength results significantly, with the latter providing higher results. Long-term thermocycling and water storage did not decrease the results in silanized groups. (C) 2006 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of handpiece tip design on the cutting efficiency of an air abrasion system

Purpose : the aim of this study was to evaluate the effect of nozzle angle and tip diameter on the cutting efficiency of an air abrasion system. Materials and Methods: Thirty-six extracted human third molars were air-abraded with the PrepStar microabrasion machine using a handpiece with either 80degrees or 45degrees nozzle angles with 0.38 or 0.48 nun tip orifice diameters. The following parameters were held constant: abrasive particle size (27 mum), air pressure (80 psi), distance (2 mm.) and duration (15 seconds). The cutting efficiency was compared using enamel, dentin and cementum substrates. Width and depth of the cutting patterns were analyzed and measured using scanning electron micrographs. Results: Statistical analysis using three-way ANOVA and Duncan's Multiple Range test revealed that the width of the cuts was significantly greater when the cavities were prepared using the 45degrees nozzle angle. Significantly deeper cavities were produced with the 80degrees nozzle angle. The tip orifice of the nozzle influenced the cutting efficiency in softer substrates, dentin and cementum. Precise removal of hard tissue is best accomplished using the 80degrees angle nozzle tips for all types of tooth surfaces, enamel, dentin and cementum.

Treatment of ligature-induced peri-implantitis by lethal photosensitization and guided bone regeneration: A preliminary histologic study in dogs

Background: the purpose of this pilot study was to evaluate the healing potential and reosseointegration in ligature-induced peri-implantitis defects adjacent to various dental implant surfaces following lethal photosensitization.Methods: A total of 36 dental implants with 4 different surface coatings (9 commercially pure titanium surface [CPTi]; 9 titanium plasma-sprayed [TPS]; 9 hydroxyapatite [HA]; and 9 acid-etched [AE]) were inserted in 6 male mongrel dogs 3 months after extraction of mandibular premolars. After a 2-month period of ligature-induced peri-implantitis and 12 months of natural peri-implantitis progression, only 19 dental implants remained. The dogs underwent surgical debridement of the remaining dental implant sites and lethal photosensitization by combination of toluidine blue O (100 mug/ml) and irradiation with diode laser. All exposed dental implant surfaces and bone craters were meticulously cleaned by mechanical means, submitted to photodynamic therapy, and guided bone regeneration (GBR) using expanded polytetrafluoroethylene (ePTFE) membranes. Five months later, biopsies of the implant sites were dissected and prepared for ground sectioning and analysis.Results: the percentage of bone fill was HA: 48.28 +/- 15.00; TPS: 39.54 +/- 12.34; AE: 26.88 +/- 22.16; and CPTi: 26.70 +/- 16.50. The percentage of reosseointegration was TPS: 25.25 +/- 11.96; CPTi: 24.91 +/- 17.78; AE: 17.30 +/- 15.41; and HA: 15.83 +/- 9.64.Conclusion: These data suggest that lethal photosensitization may have potential in the treatment of peri-implantitis.

Influence of the period after ovariectomy on femoral and mandibular bone density and on induced periodontal disease

Background: This study investigated the influence of the period after ovariectomy on femoral and mandibular bone mineral density (BMD) and on induced periodontal disease.Methods: One hundred and twenty-six female Holtzman rats were divided into nine groups: control, sham surgery (SHAM) with and without induction of periodontal disease for 51 and 150 days, and ovariectomy (OVX) with and without induction of periodontal disease for 51 and 150 days. Periodontal disease was induced by placing ligatures on the first lower molars during the last 30 days of each period. BMD was measured by dual-energy x-ray absorptiometry. Vertical bone loss was determined by measuring the distance from the alveolar bone crest to the cemento-enamel junction on the mesial side of the first lower molar.Results: Statistical analyses (Kruskal-Wallis test) revealed a significant difference between the OVX and SHAM groups' global and femoral proximal epiphysis BMD (P < 0.001) for 150 days and in the global evaluation for 51 days. For mandibular BMD, no difference was found between the groups of each period. Influence of the period on femoral BMD was found only for the SHAM groups, with lower BMD for the 51-day period compared to the 150-day period (P < 0.05). In the global evaluation of the mandible, a lower BMD was found after 51 days. The period was a contributing factor for the vertical bone loss, and it resulted in higher values for the 51-day period (P < 0.05).Conclusion: the period influenced the femoral BMD and the vertical bone loss in induced periodontal disease.

Response of rat bone marrow cells to commercially pure titanium submitted to different surface treatments

Objectives. Alterations in the commercially pure titanium (cpTi) surface may be undertaken to improve its biological properties. The aim of this study is to investigate the biocompatibility of cpTi submitted to different surface treatments.Methods. The cpTi surfaces were prepared so that machined and blasted surfaces, either acid etched or not, were compared using rat bone marrow cells cultured to differentiated into osteoblast. For attachment evaluation, cells were cultured for 4 and 24 h. Cell morphology was evaluated after 3 days. After 7, 14, and 21 days cell proliferation was evaluated. Total protein content and alkaline phosphatase (ALP) activity were evaluated after 14 and 21 days. For bone-like nodule formation, cells were cultured for 21 days. Data were compared by analysis of variance.Results. Cell attachment, cell morphology, cell proliferation, and ALP activity were not affected by surface treatments. Total. protein content was reduced by blasted and acid etched surface. Bone-Like nodule formation was significantly reduced by blasted, acid etched, and a combination of both blasted and acid etched surfaces.Conclusions. Based on these results, it can be suggested that cpTi surfaces that were submitted only to machining treatment favor the final event of osteoblastic differentiation of the rat bone marrow cells, evidenced by increased bone-Like nodule formation. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

Influence of surgical repositioning of mature permanent dog teeth following experimental intrusion: a histologic assessment

The aim of this study was to evaluate, through histologic examination, the effect of surgical repositioning of intruded dog teeth upon the pulpal and surrounding tissues. Thirty teeth in 10 adult dogs, aged 2-3 years, were used. Fifteen teeth were intruded, surgically repositioned and fixed using orthodontics wire, composite resin, and enamel acid conditioning. All these teeth served as the experimental group. The remaining intruded teeth were not treated ( control group). The animals were sacrificed to allow observations at 7,15, and 30 post-operative days. The maxillary and mandibular archs were removed and processed for histologic exam. Based on the methodology and observed results, we concluded that: pulpal necrosis, external root resorption and ankylosis were common sequelae to severe traumatic intrusion; a careful immediate surgical repositioning of severed intruded permanent tooth with complete root formation has many advantages with few disadvantages.

On epidote fission track dating

The use of epidote in fission track dating was abandoned since the beginning of the 1980s due to difficulties like absence of a standard etching procedure, obtainment of different closure temperatures and the percentage of the datable samples. The results become much more reproducible when restricting fission track analysis to a peculiar kind of track. We are also studying confined track length, what makes possible to obtain information about fossil track annealing. Fission tracks in epidote were successfully etched with 48% HF at 35 degrees C for 12.5 min. Dating samples by the external detector method was not possible due to problems in measuring the efficiency factor held between the number of fossil fission tracks and tracks induced in mica. Dating a sample from Brejui, RN, Brazil with the population method gave a corrected age of 510 +/- 69Ma, in agreement with published U/Th-Pb ages. From the fact that the fossil track length histogram was bimodal, we were able to infer that this sample registered a thermal episode during its history.These preliminary results indicate that epidote deserves further studies to establish whether it can be employed as a thermochronological tool. (c) 2005 Elsevier Ltd. All rights reserved.

In Vitro Evaluation of ICDAS and Radiographic Examination of Occlusal Surfaces and Their Association With Treatment Decisions

This in vitro study evaluated the performance of visual (International Caries Detection and Assessment System [ICDAS]) and radiographic (bitewing [BW]) examinations for occlusal caries detection and their associations with treatment decision (TD). Permanent teeth (n=104) with occlusal surfaces varying from sound to cavitated were selected. Sites were identified from 10x occlusal surface photographs. Standardized bitewing (BW) radiographs were taken. Four dentists with at least five years of experience scored all teeth twice (one-week interval) for ICDAS (0-6), BW (0=sound, 1=caries restricted to enamel, 2=caries in outer third dentin, 3=caries in inner third dentin), and TD (0=no treatment, 1=sealant, 2=microabrasion and sealant, 3=round bur sealant, 4a=resin, 4b=amalgam). Histological validation was performed by observation under a light microscope, with lesions classified on a five-point scale. Intraexaminer and inter-examiner repeatability were assessed using two-way tables and intraclass correlation coefficients (ICCs). Comparisons between percentage correct, specificity, sensitivity, and area under the receiver-operating characteristic (ROC) curve were performed using bootstrap analyses. ICCs for intraexaminer and interexaminer repeatability indicated good repeatability for each examiner, ranging from 0.78 to 0.88, and among examiners, ranging from 0.74 to 0.81. Correlation between ICDAS and TD was 0.85 and between BW and TD was 0.78. Correlation between the methods and histological scores was moderate (0.63 for ICDAS and 0.61 for BW). The area under the ROC curve was significantly greater for ICDAS than for BW (p<0.0001). ICDAS had significantly lower specificity than BW did (p=0.0269, 79% vs 94%); however, sensitivity was much higher for ICDAS than for BW (p<0.0001, 83% vs 44%). Data from this investigation suggested that the visual examination (ICDAS) showed better performance than radiographic examination for occlusal caries detection. The ICDAS was strongly associated with TD. Although the correlation between the ICDAS and BW was lower, it is still valuable in the clinical decision-making process.

Morphology of the dental carinae in Mariliasuchus amarali (Crocodylomorpha, Notosuchia) and the pattern of tooth serration among basal Mesoeucrocodylia.

Carinated teeth are common in Mesoeucrocodylia, and the occurrence of denticles over the carinae is related to high predacious species, often referred as ziphodont. This characteristic is broadly recognized as homoplastic. Carinae morphology is cryptic, difficult to be studied under common techniques, and Scanning Electronic Microscopy (SEM) allows the access to detailed information, offering a higher degree of confidence. Previous SEM study allowed the recognition of true/false ziphodont patterns, according to the morphology of the denticles, but such studies on gondwanan mesoeucrocodyles are uncommon. Mariliasuchus amarali is an Upper Cretaceous notosuchian mesoeucrocodyle from South America (Bauru Group, Brazil), with carinated teeth and specialized dentition. Its geological and biochronological distribution are reappraised. SEM study of two teeth shows carinae composed of isolated tuberous anisomorphic true denticles, supporting previous study. Enamel ornamentation does not develop over the carinae, and fabric becomes anastomosed in middle and posterior teeth. Carinae only occur in posterior molariform teeth, related to food processing. Morphological variability of Mariliasuchus is commented, focusing on dentition. Overall characteristics, molariform morphology and wear planes support a non-predacious habit for Matiliasuchus. Matiliasuchus pattern could not be related to true/false ziphodont patterns, either by morphology or function, and is defined as ziphomorph. Ziphomorph pattern is evaluated within the range of mesoeucrocodyles. The detailed study of homoplastic characteristics, such as dental carinae, may provide useful apomorphic information for cladistic analysis.

Concentração de flúor e solubilidade em esmalte de dentes decíduos permanentes jovens após aplicações tópicas de soluções fluoretadas.

The aim of this article was to compare, through the distillation method, the incorporated amount of fluoride and the reduction of solubility in the enamel of both deciduous and young permanent teeth, following topical application of a 2% neutral sodium fluoride solution, according to the Knutson's technique and a 1.23% of acidulated solution, according to the Wellock & Brudevold's technique. The greatest fluoride incorporation was observed in the deciduous teeth after the usage of the 2% neutral solution. The amount of calcium and phosphorus liberation by the acid solution was greatest in the control group, followed by the group of teeth treated in acidulated solution and, finally, by those treated in 2% sodium fluoride solution.

Estudo da penetração de agentes ácidos para o condicionamento do esmalte dental em cimentos à base de hidróxido de cálcio.

It was verified the penetration of phosphoric acid into 3 commercial calcium hydroxide-based cements (Life, Renew and Prisma VLC Dycal). The colorimetric method employed permitted the identidication of phosphorus amount in representative samples of 6 successive layers 0.1 mm thick of each material. The acid etching used were the commercial products Scotchbond Etching Gel--3M at 36.114% by weight and Solução Condicionadora--Johnson & Johnson at 36.054% by weight. The contact time was 60 seconds. The result showed that layers 0.1 mm tick for Life and Prisma VLC Dycal and 0.2 mm thick for Renew were able to block the penetration of phosphoric acid solution whereas layers 0.1 mm thick for the 3 cements were able to block the penetration of phosphoric acid gel.

Estudo da infiltração marginal em restaurações de resinas compostas para dentes posteriores. Efeito do material, preparo cavitário e condicionamento do esmalte a nível cervical.

The purpose of this in vitro study was to investigate the cervical marginal leakage in class II restorations with chemically cured resin (P10) and light-cured resin (P30) in two types of cavities: conventional and adhesive. The effect of acid-etching in this area was also observed. Dentine adhesive Scotchbond was used in all experimental groups. Leakage was evidenced by Rodamina B dye penetration after thermocycling procedure between 10 degrees C and 50 degrees C temperature and analysed by using Zeiss Stereoscopic Magnifying Glass (10 X). According to the results obtained marginal leakage occurred in all experimental groups, with lower percentage for adhesives cavities when enamel acid-etching and light-cured resin P30 was used.

Estudo comaprativo da resistência da união esmalt/resina/metal. Efeito de resinas de fixação, artifícios retentivos e ligas metálicas.

The purpose of this study was to compare the enamel/resin/metal bond tensile strength by using human canines, in which castings were bonded. These castings were obtained by Co-Cr or Ni-Cr alloys and showed four types of mechanisms of retention: 50 micrograms aluminum oxide abrasive, electrochemical etch, acrylic beads metal mesh. The castings were bonded utilizing Comspan Opaque and Panavia Ex. The specimens were subjected to tensile forces after 24 hours in an Instron machine. The castings subjected to 50 micrograms aluminum oxide abrasive and bonded utilizing Panavia EX showed the biggest bond tensile strength.

Natal teeth: Case report

The natal teeth are defined as the presence of teeth at birth and the etiology is rather obscure. Clinically, the teeth show normal size and shape, although they reveal an immature appearance. The histological aspect show enamel with the possibility of presenting normal mineralization or being hypoplastic. The dentin may show alterations. The incidence of natal teeth varies greatly, with a predisposition for the female sex. This paper relates a case report of two partially erupted natal teeth in a female baby 9 days-old. The presence of teeth made the parents anxious. In their mind, that meant the child was abnormal. On the radiograph the erupted teeth showed little radioopacity, without a radicular formation. The therapy utilized was the keeping of the teeth and a periodic monitoring, cleaning and daily topical applications sodium fluoride. The case was monitored by monthly consultations. At 9 months of age the primary central lower did not present mobility. On the radiograph examination incomplete radicular formation was observed.

A 2-year clinical evaluation of fluoride-containing pit and fissure sealants placed with an invasive technique

The aim of this study was to clinically evaluate fluoride-containing sealants in teeth subjected to minimal enamel reduction (preventive resin restorations). Two hundred fourteen sealants (109 Fluro Shield and 105 Delton Fluor) were applied in 153 teeth of 32 subjects. The sealants were evaluated for superficial irregularities, marginal adaptation, retention, and caries after 6, 12, 18, and 24 months. After 6, 12, and 18 months, the attendance at recall was 100.00%. After 24 months, 93.75% of subjects returned for reevaluation. Although total or partial loss of sealant occurred in a few instances, no occlusal caries was found in any tooth at any recall. No statistically significant differences in the results of the clinical evaluation were found between sealant in the maxillary and mandibular dentitions.