Caracterização do fator de intensidade de tensão em corpos trincados através do método dos elementos finitos

The industry generally has sought materials with high mechanical resistance, low density, thermal stability and corrosion resistance. In the aerospace industry, for example, the use of aluminum alloys, such as Al 2024-T351 and Al 7075-T7351, have become essential. However, the use of these materials often do not resulted in a satisfactory performance of the component, since the presence of cracks can cause total rupture of the component, even with a tension below the yield stress of the material, unexpectedly. In this work, these aluminum alloys were analyzed and samples were modeled by the finite element method. Moreover, in the models were applied two different types of cracks, central and edge crack, a vertical force was applied to result in a tension 70% of the yield stress of the material analyzed. Through stress asymptotic distribution in the region near the crack tip were calculated the values of the stress intensity factors for each crack length, after the stress intensity factors characterized were compared graphically with the values of fracture toughness found in the available literature

Estudo da fadiga em liga de alumínio aeronáutico 7475-T761

This work will address the study of fatigue conditions with constant load in an alloy of aluminum analysis 7475 - T761, so we can better understand the conditions of the aircrafts which contain this alloy in their structures. A literature review, which was discussed the concepts of fracture mechanics, fatigue, aeronautical components, chemical analysis of aluminum alloys, fatigue problems that appears in the aircrafts, metallographic analysis, and testing of optical microscopy tensile, fatigue and microhardness, surface analysis (MEV) study of the chemical composition of the alloy in question, the main causes of crashes, was performed, completing the work, analysis of data from tensile test, hardness and fatigue together with the interpretation of images of optical microscopy and scanning electron was taken. The data indicated the high mechanical strength of the alloy, along with its microstructure indicating elongated grains and high surface contour, which shows such resistance by hindering the movement of dislocations. The grooves are clearly shown in the MEV images as well as the classic with increased fatigue loading and subsequent reduction of the number of cycles to rupture behavior shown in the graphs. Therefore we observed the optimal behavior is supported by the league when subjected to fatigue loadings

Filmes de 'CO' obtidos por deslocamento galvânico e suas propriedades magnéticas

Pós-graduação em Química - IQ

Herbst esplinte metálico fundido: novo modelo de confecção com Duralay

A má oclusão de Classe II é originária de vários fatores etiológicos e uma das características mais comum desta má oclusão é a retrusão mandibular3, por esse motivo, os aparelhos de avanço mandibular são eleitos para o tratamento e correção desta má oclusão. Um destes aparelhos é o Herbst, que apresenta várias formas de ancoragens na sua confecção10. Tradicionalmente, as bandas eram o sistema de ancoragem mais usado, no entanto, pela alta frequência de quebras as mesmas foram substituídas por esplinte metálico12. Esse aparelho quando confeccionado de cromo cobalto pelo método da prótese parcial removível, apresenta como desvantagens a quantidade de passos laboratoriais e a possível contração do metal, podendo ocasionar a má adaptação da estrutura metálica à boca do paciente. Dessa forma, este artigo apresenta um novo método de confecção do aparelho de Herbst esplinte metálico fundido com uso da Duralay e liga níquel cromo. Esse método diminui os passos laboratoriais, proporciona maior resistência à tração e minimiza a contração da estrutura metálica, pois a resina química Duralay proporciona menor expansão do que a cera2.

Influência do ciclo de sinterização da porcelana na adaptação marginal de infraestruturas de NiCrTi em função da biomecânica do preparo

A metal coping may undergo changes during porcelain firing, which compromises its marginal adaptation. The use of NiCrTi alloy proposes to minimize this effect through the high melting point of titanium present in its composition. This study evaluated the influence of porcelain firing cycle on the marginal adaptation of NiCrTi copings in different preparation designs. Forty standardized metal dies were fabricated with the following combinations finish line/convergence of the axial walls: 1) shoulder/6°; 2) shoulder/20°; 3) sloping shoulder/6°; 4) sloping shoulder/20°. On each die a metal ceramic restoration coping was made. The die/coping set was stabilized with orthodontic elastics, divided into four equidistant areas with three measurement points each and a cementation pressure was simulated. The measurements were taken under a stereomicroscope (32×). After the first measurement, the copings were submitted to sintering cycles simulating porcelain application. For repeated measurements, the same procedures described above were performed. Data were submitted to Student’s-t test, 1-way ANOVA and Tukey´s test (α = 0.05). Adaptation means (µm) before and after porcelain firing in different preparations were: 1) 111.92 and 127.31; 2) 124.15 and 135.48; 3) 122.19 and 138.77; 4) 166.09 and 186.72; respectively. The porcelain firing impaired adaptation, regardless of the preparation design. The preparation in a 20° sloping shoulder provided a worse adaptation when compared with preparations that had 6° and 20° shoulder, which were statistically equal. The 6° sloping shoulder was statistically equal to the other three preparation designs.

Prótese metalocerâmica associada à prótese metaloplástica implantossuportada em paciente desdentado total

The use of different methods and materials should be considered during the planning of implant-supported prostheses. Complications such as fractures of the acrylic resin base, wear and fracture of teeth can occur frequently, creating the need for careful planning for each patient, which can make the selection of the type of treatment more complex. Thus, this article describes the oral rehabilitation of a completely edentulous patient with bimaxillary fixed implant-supported prosthesis, with complaints on aesthetics, loss of vertical dimension and fracture of acrylic resin teeth of the upper arch. After the restoration of vertical dimension, his dentures were replaced with new bimaxillary implant-supported fixed prostheses, ceramic and acrylic resin were used as veneering material for maxilla and mandible, respectively. At the end of the treatment, the patient received bimaxillary flat occlusal splints to protect the teeth and implants of possible parafunctional habits. The approach for the treatment allowed a quick and effective resolution, with aesthetic and functional outcomes very favorable for the patient.

Análise metalográfica do titânio puro submetido à soldagem laser Nd: YAG e TIG

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Análise comparativa dos métodos MQL, MQL/Água e convencional na retificação cilíndrica do aço ABNT 52100, com rebolo de óxido de alumínio

Pós-graduação em Engenharia Mecânica - FEB

Reciclagem de cavacos para a formação de carbonetos de titânio no metal de solda produzido por soldagem GTAW em aço-carbono

Pós-graduação em Engenharia Mecânica - FEIS

Desenvolvimento de uma nova liga quaternária Ti25Ta25Nb3Sn para aplicações odontológicas

Pós-graduação em Engenharia Mecânica - FEG

Utilização de metaheurísticas combinada a diferentes métodos de aglutinação para a otimização de um processo de torneamento com múltiplas respostas

Pós-graduação em Engenharia Mecânica - FEG

Influência de tratamentos termo-mecânicos na estrutura e microestrutura da liga Ti-10%pNi obtida por fusão a arco

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation of the shear bond strength of the union between two CoCr-alloys and a dental ceramic

Introduction: Based on the importance of the integrity of the metal/ceramic interface, the purpose of this work was to evaluate the shear bond strength of the metal-ceramic union of two Co-Cr alloys (Wirobond C, Bego; Remanium 2000, Dentaurum) combined with Omega 900 ceramic (Vita Zahnfabrik). Material and Method: Eleven cylindrical matrixes were made for each alloy, and the metallic portion was obtained with the lost wax casting technique with standardized waxing of 4mm of height and of 4mm of diameter. The ceramic was applied according to the manufacturer's recommendations with the aid of a teflon matrix that allowed its dimension to be standardized in the same size as the metallic portion. The specimens were submitted to the shear bond test in an universal testing machine (EMIC), with the aid of a device developed for such intention, and constant speed of 0.5mm/min. Results and Conclusions: The mean resistance was 48.387MPa for Wirobond C alloy, with standard deviation of 17.718, and 55.956MPa for Remanium 2000, with standard deviation of 17.198. No statistically significant difference was observed between the shear strength of the two metal-ceramic alloys.

Estudo comparativo in vitro da resistência à remoção de grampos circunferenciais aplicados sobre dentes íntegros e restaurados com resina composta

An experimental study was undertaken in arder to find out lhe behavior of the required force to yield dislodgement of circumierential clasps of removable partial dentures ou two groups of samples. 1 with retentive terminais engaging and acting ou enamel 2 with retentive terminais engaging on enamel and acting on composite resm With this aim a device was designed based on a sewing machine (brand name Elgin) that could repeatedly simulate lhe introduction-removal movement of circunferencial clasps ou the samples. ln addiction the device had a platform to sustain the samples and permit measurements, a cycle counter and a dynamometer. The samples were constructed by inclusion in dental stone of extracted natural molar teeth whose retentive areas were ou natural enamel or composite resin addictions.The clasps were fabricated from wax ups of resin and wax and were cast with chromium cobalt alloy. The composite resin used was one of the last generation, monomodal type, photopolymerized and binded to the enamel by the acid etching technique. Tests were carried out in aqueous enviroment. Is was established a maximum of 5.000 cycles for each of the samples. Observatins were made from 100 to 100 cycles until 2.000 and from 200 to 200 cycles to 5.000. Results showed that variations in the amount of the required force for dislodgement of the clasps from the samples during the test periods had no significancy eather to those with retentive areas on the enamel or to those with retentive fabricated with addictions of composite resin