About the thermal stability and pore elimination in the ordered hexagonal mesoporous silica SBA-15

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Distribuição do Tamanho de Poros em Cascas de Ovos Determinada pela Porosimetria de Mercúrio

Neste trabalho foi aplicada a porosimetria de mercúrio na caracterização da porosidade de cascas de ovos de poedeiras com 28 semanas de idade. Aplicando-se a técnica de porosimetria de mercúrio, pudemos descrever as características associadas a porosidade de modo mais amplo, determinando uma distribuição do tamanho de poros nas cascas de ovos estudadas. Nossos resultados mostraram que a maioria dos poros nas cascas de ovos tem tamanhos entre 1 a 10 mim. Neste artigo introduzimos a técnica de porosimetria de mercúrio como uma nova ferramenta aplicada no estudo de cascas de ovos.

Structural modifications in silica sonogels prepared with additions of poly(vinyl alcohol)

Silica wet gels were prepared from acid sonohydrolysis of tetraethoxysilane (TEOS) and additions of poly(vinyl alcohol) (PVA)-water solution. Aerogels were obtained from supercritical CO(2) extraction. The samples were studied by thermal gravimetric (TG) analysis, small-angle X-ray scattering (SAXS), and nitrogen adsorption. The structure of wet gels can be described as a mass fractal with dimension D equal to 2.0 on the whole length scale experimentally probed by SAXS, from similar to 0.3 to similar to 15 nm. Pure and low-PVA-addition wet gels exhibit an upper cutoff accounting for a finite characteristic length xi of the mass fractal structure. Additions , of PVA increase without modifying D, which was attributed to a steric effect of the polymer in the structure. The pore volume fraction of the aerogels diminishes typically about 11% with respect to that of the wet gels, although nitrogen adsorption could be underestimating some porosity. The pore size distribution of the aerogels is shifted toward the mesopore region with the additions of PVA, in a straight relationship with the increase of xi in the wet gels. The thermal stability of the pore size distribution of the aerogels was studied up to 1000 degrees C.

Effects of poly(vinyl alcohol) additions on the structure of silica xerogels

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural features of silicas prepared in n-heptane/water/ethanol/sodium dodecylsulfate microemulsions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Mass fractal characteristics of silica sonogels as determined by small-angle x-ray scattering and nitrogen adsorption

A sample series of silica sonogels was prepared using different water-tetraethoxysilane molar ratio (r(w)) in the gelation step of the process in order to obtain aerogels with different bulk densities after the supercritical drying. The samples were analyzed by means of small-angle x-ray-scattering (SAXS) and nitrogen-adsorption techniques. Wet sonogels exhibit mass fractal structure with fractal dimension D increasing from similar to2.1 to similar to2.4 and mass-fractal correlation length xi diminishing from similar to13 nm to similar to2 nm, as r(w) is changed in the nominal range from 66 to 6. The process of obtaining aerogels from sonogels and heat treatment at 500degreesC, in general, increases the mass-fractal dimension D, diminishes the characteristic length xi of the fractal structure, and shortens the fractal range at the micropore side for the formation of a secondary structured particle, apparently evolved from the original wet structure at a high resolution level. The overall mass-fractal dimension D of aerogels was evaluated as similar to2.4 and similar to2.5, as determined from SAXS and from pore-size distribution by nitrogen adsorption, respectively. The fine structure of the secondary particle developed in the obtaining of aerogels could be described as a surface-mass fractal, with the correlated surface and mass-fractal dimensions decreasing from similar to2.4 to similar to2.0 and from similar to2.7 to similar to2.5, respectively, as the aerogel bulk density increases from 0.25 (r(w)=66) up to 0.91 g/cm(3) (r(w)=6).

Formation of zirconia foams using the thermostimulated sol-gel transition

In this paper we describe the production of zirconia-based foams by a novel thermostimulated sol-gel route, that employs the foaming of colloidal suspensions prior to the sol-gel transition promoted by small increase of temperature (congruent to3 degreesC). This method produces gelled bodies having porosity >70% in the wet stage, and can be used to produce complex-shaped components. The effect of a foaming agent (Freon11 or CCl3F) and surfactant content on the formation and stability of the foams was analyzed. The rheologic measurements demonstrate that by increasing the surfactant concentration, the gelation time decreases increasing foam stability. As the surfactant concentration and quantity of foaming agent increase, the density decreases and the porosity increases. Hg porosimetry results show that the dry foam presents a bimodal pore size distribution. The family of sub-micrometer pores was attributed to the formation of a microemulsion between Freon11 and water. Scanning electron microscopy analysis shows that the foam structure consists of a three-dimensional network of spherical pores, which may be open and interconnected or closed, at larger or smaller porosities, respectively. Finally these results show that the thermostimulated sol-gel transition provides a potential route for ceramic foam manufacture. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Formation of SnO2 supported porous membranes

In this work, the effect of the substrate microstructure on the formation of SnO2 membranes and of the sintering conditions on their porosity have been analysed. Samples have been prepared by colloidal suspensions cast on alumina or kaolin substrates. Supported membranes have been characterized by Hg porosimetry, MEV, XRD and N-2 adsorption-desorption isotherms. The results show that the narrower pore size distribution of alumina substrate allowed to prepare membranes more homogeneous and free of cracks than that supported on kaolin. The crystallite and pore sizes of the membranes could be controlled by adjusting the temperature of sintering, allowing materials with adequate microstructure with application for ultrafiltration process.

Nanostructure and properties of ZnO films produced by the pyrosol process

Indium doped ZnO films were deposited by the pyrosol process on glass substrates at different temperatures from solutions containing In/Zn molar ratios up to 10%. The nanostructure of the films was investigated using grazing-incidence small angle X-ray scattering (GISAXS). The mass density was determined by X-ray reflectivity and the composition by X-ray photoelectron spectroscopy. The GISAXS measurements revealed an anisotropic pattern for films deposited at 573 and 623 K and a isotropic one for those deposited at higher temperatures. The anisotropic patterns indicate the presence of elongated nanopores with their long axes perpendicular to the film surface. In contrast, the isotropic nature of GISAXS patterns of films grown at high temperatures (673 and 723 K) suggests the presence of spherical voids. The pore size distribution function determined from the isotropic patterns indicates a multimodal size distribution. on the other hand, the measured mass density of the doped films with isotropic nanotexture is higher than that of the anisotropic films while the electric resistivity is significantly lower. This is in agreement with the detected strong reduction of the void density and specific surface area at approximately constant pore size.

Effects of self-assembly process of latex spheres on the final topology of macroporous silica

This paper surveys the topology of macroporous silica prepared using latex templates covering the submicrometric range (0.1-0.7 mu m). The behavior of latex spheres in aqueous dispersion has been analyzed by dynamic light scattering (DLS) measurement indicating the most appropriate conditions to form well-defined cubic arrays. The optical behavior of latex spheres has been analyzed by transmittance and reflectance measurements in order to determine their diameter and filling factor when they were assembled in bidimensional arrays. Macroscopic templates have been obtained by a centrifugation process and their crystalline ordering has been confirmed by porosimetry and scanning electron microscopy. These self-assembled structures have been used to produce macroporous silica, whose final topology depends on the pore size distribution of the original template. It has been seen that latex spheres are ordered in a predominant fcc arrangement with slipping of tetragonal pores due to the action of attractive electrostatic interactions. The main effect is to change the spherical shape of voids in macroporous silica into a hexagonal configuration with possible applications to fabricate photonic devices with novel optical properties. (c) 2005 Elsevier B.V. All rights reserved.

Evolution of the fractal structure during sintering of SnO2 compacted sol-gel powder

The structural evolution during sintering of compacted SnO2 sol-gel powder was investigated using nitrogen adsorption isotherm analysis. Results show that for sintering temperatures up to 400°C the samples have a fractal pore size distribution. As the sintering temperature increases, a structural rearragement occurs, allowing an increase of the efficiency of particle packing and the reduction of fractality. Above 400°C, the pore size growth associated with grain coalescence is the main structural change observed as the sintering temperature increases. © 1995.

Anisotropy of crystallite growth during sintering of SnO2 xerogels

The crytallite and pore-size evolution during isothermal sintering (400 ≤ T ≤ 700°C) of SnO2 xerogels was studied by X-ray line broadening and nitrogen adsorption-desorption isotherms. The experimental results show a strong anisotropy of crystallite growth between [110] and [101] directions. The preferential growth at [101] is followed by an increase in the mean pore size, reduction of the specific surface area and invariance of total pore volume. This behaviour is typical of grain coalescence sintering. The kinetic analysis of experimental results suggests that the crystallite coalescence at [101] is governed by lattice diffusion. The strong anisotropy of the growth causes pore-size distribution broadening, hindering the macroscopic shrinkage of the compact during sintering. © 1996 Chapman & Hall.

Response surface methodology applied to the evaluation of the SO 2 sorption process in two Brazilian limestones

This paper proposes a response surface methodology to evaluate the influence of the particle size and temperature as variables and their interaction on the sulfation process using two Brazilian limestones, a calcite (ICB) and a dolomite (DP). Experiments were performed according to an experimental design [central composite rotatable design (CCRD)] carried out on a thermogravimetric balance and a nitrogen adsorption porosimeter. In the SO 2 sorption process, DP was shown to be more efficient than ICB. The best results for both limestones in relation to conversion and Brunauer-Emmett-Teller (BET) surface area were obtained under central point conditions (545 μm and 850 C for DP and 274 μm and 815 C for ICB). The optimal values for conversion were 52% for DP and 37% for ICB. For BET surface area, the optimal values were 35 m2 g-1 for DP and 45 m2 g-1 for ICB. A relationship between conversion and pore size distribution has been established. The experiments that showed higher conversions also exhibited more pores in the region between 20 and 150 Å and larger BET surface area, indicating that the amount of smaller pores may be an important factor in the reactivity of limestones. © 2013 American Chemical Society.

Liquid foam templates associated with the sol-gel process for production of zirconia ceramic foams

The unique properties of ceramic foams enable their use in a variety of applications. This work investigated the effects of different parameters on the production of zirconia ceramic foam using the sol-gel process associated with liquid foam templates. Evaluation was made of the influence of the thermal treatment temperature on the porous and crystalline characteristics of foams manufactured using different amounts of sodium dodecylsulfate (SDS) surfactant. A maximum pore volume, with high porosity (94%) and a bimodal pore size distribution, was observed for the ceramic foam produced with 10% SDS. Macropores, with an average size of around 30 μm, were obtained irrespective of the SDS amount, while the average size of the supermesopores increased systematically as the SDS amount was increased up to 10%, after which it decreased. X-ray diffraction analyses showed that the sample treated at 500 °C was amorphous, while crystallization into a tetragonal metastable phase occurred at 600 °C due to the presence of sulfate groups in the zirconia structure. At 800 and 1000 °C the monoclinic phase was observed, which is thermodynamically stable at these temperatures. © 2013 by the authors; licensee MDPI, Basel, Switzerland.

Soft-chemical synthesis, characterization and humidity sensing behavior of WO3/TiO2 nanopowders

Tungsten oxide/titania (WO3/TiO2) nanopowders were synthesized by the polymeric precursor method which varied the WO3 content between 0 and 10 mol%. The powders were thermally treated in a conventional furnace and their structural, microstructural and electric properties were evaluated by X-ray diffraction (XRD), Raman spectrometry, N 2 physisorption, NH3 chemisorption, temperature-programmed reduction (TPR), X-ray absorption near-edge spectroscopy (XANES) in situ XANES and extended X-ray absorption fine structure spectroscopy (EXAFS) and transmission electron microscopy (TEM). XRD and Raman spectrometry confirmed the homogeneous distribution of an amorphous WO3 phase in the TiO 2 matrix which stabilized the anatase phase through the generation of [TiO5·V0] or [TiO5·V 0] complex sites. Conventional TPR-H2 (temperature programmed reduction) along with XANES TPR-H2 and XANES TPR-EtOH showed that WO3/TiO2 sample reduction occurs through the formation of these complex clusters. Moreover, the addition of WO3 promoted an increase in the surface acidity of doped samples as revealed by NH3 chemisorption. The WO3/TiO2 bulk-ceramic samples were further used to estimate their potential application in a humidity sensor in the range of 15-85% relative humidity. Probable reasons that lead to the different humidity sensor responses of samples were given based on the structural and surface characterizations. Correlation between the sensing performance of the sensor and its structural features are also discussed. Although all samples responded as a humidity sensor, the W2T sample (2 mol% added WO3) excelled for sensitivity due to the increase in acid sites, optimum mean pore size and pore size distribution. © 2013 Elsevier B.V.