Photoluminescence properties and synthesis of a PZT mesostructure obtained by the microwave-assisted hydrothermal method

Micro-cube-shaped lead zirconate titanate was synthesized using the microwave-assisted hydrothermal method. Photoluminescence and field emission scanning electron microscopy were used for monitoring the formation of mesocrystals. Based on these results, a growth mechanism was then proposed which involved nanoparticle aggregation, nanoplate self-assembly on specific architecture and the final formation of mesoscopic micro-cube-shaped lead zirconate titanate. (C) 2011 Elsevier B. V. All rights reserved.

Dielectric properties of Ca(Zr0.05Ti0.95)O-3 thin films prepared by chemical solution deposition

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were grown on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates by the soft chemical method. The films were deposited from spin-coating technique and annealed at 928 K for 4 h under oxygen atmosphere. CZT films present orthorhombic structure with a crack free and granular microstructure. Atomic force microscopy and field-emission scanning electron microscopy showed that CZT present grains with about 47 nm and thickness about 450 nm. Dielectric constant and dielectric loss of the films was approximately 210 at 100 kHz and 0.032 at 1 MHz. The Au/CZT/Pt capacitor shows a hysteresis loop with remnant polarization of 2.5 mu C/cm(2), and coercive field of 18 kV/cm, at an applied voltage of 6 V. The leakage current density was about 4.6 x 10(-8) A/cm(2) at 3 V. Dielectric constant-voltage curve is located at zero bias field suggesting the absence of internal electric fields. (c) 2006 Elsevier B.V. All rights reserved.

Dependence of annealing time on structural and morphological properties of Ca(Zr0.05Ti0.95)O-3 thin films

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were prepared by the polymeric precursor method by spin-coating process. The films were deposited on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates and annealed at 650 degrees C for 2,4, and 6 It in oxygen atmosphere. Structure and morphology of the CZT thin films were characterized by the X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), atomic force microscopy (AFM) and field-emission scanning electron microscopy (FEG-SEM). XRD revealed that the film is free of secondary phases and crystallizes in the orthorhombic structure. The annealing time influences the grain size, lattices parameter and in the film thickness. (c) 2006 Elsevier B.V. All rights reserved.

Synthesis and characterization of CuO flower-nanostructure processing by a domestic hydrothermal microwave

The synthesis and characterization of CuO flower-nanostructure processed in domestic hydrothermal microwave oven was presented. Phase analysis was carried out using X-ray diffraction (XRD) and micro-Raman scattering (MRS) and the results confirmed the CuO flower-nanostructure as a single-phase. The field-emission scanning electron microscopy (FEG-SEM) was used to estimate the average spheres diameter while transmission electron microscope (TEM) to observe the thorn of the flower-nanostructures. The mechanism of CuO flower-nanostructures formation is proposed and explained. (c) 2007 Elsevier B.V. All rights reserved.

An efficient microwave-assisted hydrothermal synthesis of BaZrO3 microcrystals: growth mechanism and photoluminescence emissions

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A Joint Experimental and Theoretical Study on the Nanomorphology of CaWO4 Crystals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Growth mechanism of octahedron-like BaMoO4 microcrystals processed in microwave-hydrothermal: Experimental observations and computational modeling

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

CuO urchin-nanostructures synthesized from a domestic hydrothermal microwave method

This letter reports the synthesis of CuO urchin-nanostructures by a simple and novel hydrothermal microwave method. The formation and growth of urchin-nanostructures is mainly affected by the addition of polyethylene glycol (PEG). The hierarchical malachite particles are uniform spheres with a diameter of 0.7-1.9 mu m. CuO urchin-nano structures were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FEG-SEM) and nitrogen adsorption (BET). The specific surface area of the CuO nanostructured microspheres was about 170.5 m(2)/g. A possible mechanism for the formation of such CuO urchin-nanostructures is proposed. (c) 2007 Elsevier Ltd. All rights reserved.

Electronic structure, growth mechanism and photoluminescence of CaWO4 crystals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Joint Experimental and Theoretical Analysis of Order Disorder Effects in Cubic BaZrO3 Assembled Nanoparticles under Decaoctahedral Shape

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Photolumiscent Properties of Nanorods and Nanoplates Y2O3:Eu3+

Nanorods and nanoplates of Y2O3:Eu3+ powders were synthesized through the thermal decomposition of the Y(OH)(3) precursors using a microwave-hydrothermal method in a very short reaction time. These powders were analyzed by X-ray diffraction, field emission scanning electron microscopy, Fourrier transform Raman, as well as photoluminescence measurements. Based on these results, these materials presented nanoplates and nanorods morphologies. The broad emission band between 300 and 440 nm ascribed to the photoluminescence of Y2O3 matrix shifts as the procedure used in the microwave-hydrothermal assisted method changes in the Y2O3:Eu3+ samples. The presence of Eu3+ and the hydrothermal treatment time are responsible for the band shifts in Y2O3:Eu3+ powders, since in the pure Y2O3 matrix this behavior was not observed. Y2O3:Eu3+ powders also show the characteristic Eu3+ emission lines at 580, 591, 610, 651 and 695 nm, when excited at 393 nm. The most intense band at 610 nm is responsible for the Eu3+ red emission in these materials, and the Eu3+ lifetime for this transition presented a slight increase as the time used in the microwave-hydrothermal assisted method increases.

Structural Effects of Nanotubes, Nanowires, and Nanoporous Ti/TiO2 Electrodes on Photoelectrocatalytic Oxidation of 4,4-Oxydianiline

The present work illustrates the effect of electrolyte composition on the self-organized TiO2 nanotube arrays electrode preparation. The influence of structural and surface morphology of the TiO2 nanotube-like anode on their photoactivity and photoelectrocatalytic performance was also investigated. TiO2 nanotubular array electrodes are grown by anodization of Ti foil in 0.25wt % NH4F/glycerol/water, but nanowires can be obtained in 4% HF-DMSO as supporting electrolyte, even when both are subjected to electrochemical anodization at 30V during 50 h. The morphological characteristics are analyzed by X-ray diffraction (XRD) and field emission scanning electron microscope (FEG-SEM). The electrodes were successfully applied in photoelectrocatalytic oxidation of 4,4'-oxydianiline (ODAN) in aqueous solution, as a model of a harmful pollutant. Complete removal of the aromatic amine was obtained after 3 hours of photoelectrocatalytic treatment on nanotubular arrays electrodes.

Bacterial cellulose-laponite clay nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microstructural and transport properties of LaNiO3-delta films grown on Si(111) by chemical solution deposition

Electrically conductive LaNiO3-delta (LNO) thin films with typical thickness of 200 nm were deposited on Si (111) substrates by a chemical solution deposition method and heat-treated in air at 700 degreesC. Structural, morphological, and electrical properties of the LNO thin films were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), field-emission scanning electron microscopy (FEG-SEM), and electrical resistivity rho(T). The thin films have a very flat surface and no droplet was found on their surfaces. The average grain size observed by AFM and FEG-SEM was approximately 100 nm in excellent agreement with XRD data. The rho(T) data showed that these thin films display a good metallic character in a large range of temperature. These results suggest the use of this conductive layer as electrode in the integration of microelectronic devices. (C) 2003 Elsevier B.V. All rights reserved.

beta-ZnMoO4 microcrystals synthesized by the surfactant-assisted hydrothermal method: Growth process and photoluminescence properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)