Técnica híbrida de plasma para a deposição de filmes de alumina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Hydroxyapatite deposition study through polymeric process on commercially pure Ti surfaces modified by laser beam irradiation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Deposition and photo-induced electrical resistivity of dip-coated NiO thin films from a precipitation process

Thin films of the semiconductor NiO are deposited using a straightforward combination of simple and versatile techniques: the co-precipitation in aqueous media along with the dip- coating process. The obtained material is characterized by gravimetric/differential thermal analysis (TG-DTA) and X-ray diffraction technique. TG curve shows 30 % of total mass loss, whereas DTA indicates the formation of the NiO phase about 578 K (305 C). X-ray diffraction (XRD) data confirms the FCC crystalline phase of NiO, whose crystallinity increases with thermal annealing temperature. UV-Vis optical absorption measurements are carried out for films deposited on quartz substrate in order to avoid the masking of bandgap evaluation by substrate spectra overlapping. The evaluated bandgap is about 3.0 eV. Current-voltage (I-V) curves measured for different temperatures as well as the temperature-dependent resistivity data show typical semiconductor behavior with the resistivity increasing with the decreasing of temperature. The Arrhenius plot reveals a level 233 meV above the conduction band top, which was attributed to Ni2+ vacancy level, responsible for the p-type electrical nature of NiO, even in undoped samples. Light irradiation on the films leads to a remarkable behavior, because above bandgap light induced a resistivity increase, despite the electron-hole generation. This performance was associated with excitation of the Ni 2+ vacancy level, due to the proximity between energy levels. © 2012 Springer Science+Business Media New York.

Molecular architecture of thin films fabricated via physical vapor deposition and containing a poly(azo)urethane

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Numerical simulation of the liquid phase in SnO2 thin film deposition by sol-gel-dip-coating

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Deposition and characterization of BiVO4 thin films and evaluation as photoanodes for methylene blue degradation

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Ultrastructural detection of proteins, lipids and carbohydrates in oocytes of Amblyomma triste (Koch, 1844) (Acari; Ixodidae) during the vitellogenesis process

The ovary of the tick Ainblyomma triste is classified as panoistic, which is characterized by the presence of oogonia without nurse and follicular cells. The present study has demonstrated that the oocytes in all developmental stages (I-IV) are attached to the ovary through a pedicel, a cellular structure that synthesizes and provides carbohydrate, lipids and proteins supplies for the oocytes during the vitellogenesis process. The lipids are deposited during all oocyte stages; they are freely distributed as observed in stages II, III and IV or they form complexes with other elements. The proteins are also deposited in all stages of the oocytes, however, in lower concentration in the stage IV. There is carbohydrate deposition from oocytes in the stage II as well as in stages III and IV. In addition, the present work has demonstrated that the oocyte yolk of A. triste has a glycolipoprotein nature and the elements are deposited in the following sequence: firstly the lipids and proteins, and finally the carbohydrates. (c) 2007 Elsevier Ltd. All rights reserved.

Seed deposition patterns and the survival of seeds and seedlings of the palm Euterpe edulis

The seed deposition pattern created by a seed disperser is one of the components of the efficiency of a species as seed disperser, and ultimately may influence the recruitment of a plant species. In this study, we used the seeds of a bird-dispersed forest palm, Euterpe edulis, to investigate the effects of two distinct seed deposition patterns created by birds that defecate (clumped pattern) and regurgitate seeds (loose-clumped pattern) on the survival of seeds experimentally set in an E. edulis-rich site, and of seedlings grown under shade-house conditions. The study was conducted in the lowland forest of Parque Estadual Intervales, SE Brazil. Clumped and loose-clumped seeds were equally preyed upon by rodents and insects. Although clumped and isolated seedlings had the same root weight after 1 year, the isolated seedlings survived better and presented more developed shoots, suggesting intraspecific competition among clumped seedlings. Our results indicate that animals that deposit E. edulis seeds in faecal clumps (e.g. cracids, tapirs) are less efficient seed dispersers than those that regurgitate seeds individually (e.g. trogons, toucans). Intraspecific competition among seedlings growing from faecal clumps is a likely process preventing the occurrence of clumps of adult palms. (C) 2001 Editions scientifiques et medicales Elsevier SAS.

Study of the growth process of in situ polyaniline deposited films

Polyaniline (PAni) thin films were deposited onto BK7 glass substrates using the in situ deposition technique. The control of the time and the aniline concentration in the PAni polymerization reaction on the film deposition allowed us to prepare films with different thickness, down to similar to 25 nm. The film growth process was monitored by measuring the UV-vis spectra and the AFM height profiles of the film surface. The curves of adsorption kinetics were analyzed with the Avrami's model, yielding an exponent it n = 3, thus indicating nucleation of spheroids at the initial stages of polymerization that grow through a diffusion process. AFM images of the surface height profiles corroborate this hypothesis, with spheroids growing with no preferred orientation during the in situ deposition. (C) 2007 Elsevier B.V. All rights reserved.

Chemical vapor deposition of multi-walled carbon nanotubes from nickel/yttria-stabilized zirconia catalysts

Multi-walled carbon nanotubes (MWNT) were produced by chemical vapor deposition using yttria-stabilized zirconia/nickel (YSZ/Ni) catalysts. The catalysts were obtained by a liquid mixture technique that resulted in fine dispersed nanoparticles of NiO supported in the YSZ matrix. High quality MWNT having smooth walls, few defects, and low amounts of by-products such as amorphous carbon were obtained, even from catalysts with large Ni concentrations (> 50 wt.%). By adjusting the experimental parameters, such as flux of the carbon precursor (ethylene) and Ni concentration, both the MWNT morphology and the process yield could be controlled. The resulting YSZ/Ni/MWNT composites can be interesting due to their mixed ionic-electronic transport properties, which could be useful in electrochemical applications.

Influence of ambient gas on the growth and properties of porous tin-doped indium oxide thin films made by pulsed laser deposition

The laser ablation method was used for depositing porous nanocrystalline indium-tin oxide thin films for gas sensing applications. Samples were prepared at different pressures using three gases (O-2, 0.8N(2):0.2O(2), N-2) and heat-treated in the same atmosphere used for the ablation process. X-ray diffraction results show that the films are not oriented and the grain sizes are in the range between 15 and 40 nm. The grains are round shaped for all samples and the porosity of the films increases with the deposition pressure. The degree of sintering after heat treatment increases for lower oxygen concentrations, generating fractures on the surface of the samples. Film thicknesses are in the range of I pm for all gases as determined from scanning electron microscopy cross-sections. Electrical resistance varies between 36.3 ohm for the film made at 10 Pa pressure in N-2 until 9.35 x 10(7) ohm for the film made at 100 Pa in O-2. (C) 2007 Elsevier B.V. All rights reserved.

Very large dielectric constant of highly oriented Pb1-xBaxTiO3 thin films prepared by chemical deposition

Highly (100) oriented Pb0.8Ba0.2TiO3/LaNiO3 structures were grown on LaAlO3(100) substrates by using a wet, soft chemical method and crystallized by the microwave oven technique. The Au/PBT/LaNiO3/LaAlO3 capacitor shows a hysteresis loop with remnant polarization, P-r, of 15 muC/cm(2), and coercive field, E-c, of 47 kV/cm at an applied voltage of 3 V, along with a dielectric constant over 1800. Atomic force microscopy showed that Pb0.8Ba0.2TiO3 is composed of large grains about 300 nm. The experimental results demonstrated that the microwave preparation is rapid, clean, and energy efficient. Therefore, we demonstrated that the combination of the soft chemical method with the microwave process is a promising technique to grow highly oriented thin films with excellent dielectric and ferroelectric properties, which can be used in various integrated device applications. (C) 2004 American Institute of Physics.

Preparation of 9/65/35 PLZT thin films deposited by a dip-coating process

Crack-free polycrystalline PLZT (Pb,a)(Zr,Ti)O-3 thin films with the perovskite structure were prepared by dir-coating using the Pechinis process. Lead acetate, hydrated lanthanum carbonate, zirconium n-propoxide and titanium isopropoxide were used as raw materials. The viscosity of the solution was adjusted in the range of 20 to 56 cP and the films were deposited by a dip-coating process on silicon (100) as substrate. Solutions with ionic concentration of 0.1 and 0.2 M were used. Thin film deposition was accomplished by dipping the substrates in the solution with control of withdrawal speed from 5 to 20 mm/min. The thin films were thermally treated in two steps: at 300 degreesC amid 650 degreesC. The influence of withdrawal speed. viscosity, heating rate and ionic concentration on the morphology of PLZT thin film was discussed. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Structural and electrical properties of strontium barium niobate thin films crystallized by conventional furnace and rapid-thermal annealing process

Strontium barium niobate (SBN) thin films were crystallized by conventional electric furnace annealing and by rapid-thermal annealing (RTA) at different temperatures. The average grain size of films was 70 nm and thickness around 500 nm. Using x-ray diffraction, we identified the presence of polycrystalline SBN phase for films annealed from 500 to 700 °C in both cases. Phases such as SrNb2O6 and BaNb2O6 were predominantly crystallized in films annealed at 500 °C, disappearing at higher temperatures. Dielectric and ferroelectric parameters obtained from films crystallized by conventional furnace and RTA presented essentially the same values.

Influence of oxygen atmosphere on LiNbO3 thin films prepared by Pechini process

Thin films of lithium niobate were deposited on the Pt/Ti/SiO2 (111) substrates by the polymeric precursor method (Pechini process). Annealing in static air and oxygen atmosphere was performed at 500°C for 3 hours. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The dielectric constant, dissipation factor and resistance were measured in frequency region from 10 Hz to 10 MHz. Electrical characterizations of the films pointed to ferroelectricity via hysteresis loop. The influence of oxygen atmosphere on crystallization and properties of LiNbO3 thin films is discussed.