Sintering and crystallite growth of nanocrystalline copper doped tin oxide

The effect of Cu2+ contents and of firing temperature on sintering and crystallite growth of nanocrystalline SnO2 xerogels was analyzed by thermoanalysis (mass loss (TG), linear shrinkage, and differential thermal analysis (DTA)), X-ray powder diffraction (XRPD), and EXAFS (extended X-ray absorption fine structures) measurements. Samples were prepared by two methods: (a) coprecipitation of a colloidal suspension from aqueous solution containing both Sn(IV) and Cu(II) ions and (b) grafting copper(II) species on the surface of tin pride gel. The thermoanalysis has shown that the shrinkage associated with the mass loss decreases by increasing the amount of copper. The EXAFS measurements carried out at the Cu K edge have evidenced the presence of copper in substitutional solid solution for the dried xerogel prepared with 0.7 mol % of copper, while for higher concentration of doping, copper has been observed also at the external surface of crystallites. The solid solution is metastable and copper migrates toward the surface during firing. The XRPD and DTA results have shown a recrystallization process near 320 degrees C, which leads to crystallite growth. The presence of copper segregated near the crystallite surface controls its growth.

Dynamical study of ZnO nanocrystal and Zn-HDS layered basic zinc acetate formation from sol-gel route

We have pointed out that zinc based particles obtained from ethanolic solution of a zinc acetate derivative (zinc oxy-acetate, Zn4O(Ac)(6)) are a mixture of nanometer sized ZnO, zinc oxy-acetate, and zinc hydroxide double salt (Zn-HDS). The knowledge of the mechanisms involved in the formation of ZnO and Zn-HDS phases, and the evolution of Zn species in reaction medium was monitored in situ during 14 h by simultaneous measurements of UV-vis absorption and extended X-ray absorption fine structures (EXAFS) spectra. This spectroscopic monitoring was initialized just after the addition of an ethanolic lithium hydroxide solution ([LiOH]/[Zn] = 0. 1) to the reaction medium kept under controlled temperature (40 degrees C). This study points out the first direct evidence of the reaction between ZnO nanoparticles and unreacted zinc oxy-acetate to form a Zn-HDS phase. The dissolution of ZnO and the reprecipitation of Zn-HDS are induced by the gradual release of water mainly produced by ethanol esterification well evidenced by gas chromatography coupled to mass spectroscopy and FT-IR measurements.

In situ and simultaneous nanostructural and spectroscopic studies of ZnO nanoparticle and Zn-HDS formations from hydrolysis of ethanolic zinc acetate solutions induced by water

The simultaneous formation of nanometer sized zinc oxide (ZnO), and acetate zinc hydroxide double salt (Zn-HDS) is described. These phases, obtained using the sol-gel synthesis route based on zinc acetate salt in alcoholic media, were identified by direct characterization of the reaction products in solution using complementary techniques: nephelometry, in situ Small-Angle X-ray Scattering (SAXS), UV-Vis spectroscopy and Extended X-ray Absorption Fine Structures (EXAFS). In particular, the hydrolytic pathway of ethanolic zinc acetate precursor solutions promoted by addition of water with the molar ratio N = [H2O]/[Zn2+] = 0.05 was investigated in this paper. The aim was to understand the formation mechanism of ZnO colloidal suspension and to reveal the factors responsible for the formation of Zn-HDS in the final precipitates. The growth mechanism of ZnO nanoparticles is based on primary particle (radius approximate to 1.5 nm) rotation inside the primary aggregate (radius < 3.5 nm) giving rise to an epitaxial attachment of particles and then subsequent coalescence. The growth of second ZnO aggregates is not associated with the Otswald ripening, and could be associated with changes in equilibrium between solute species induced by the superficial etching of Zn-HDS particles at the advanced stage of kinetic.

Short Range Order Evolution in the Preparation of SnO2 Based Materials

The evolution of Eu3+ doped SnO2 xerogels to the cassiterite structure observed during sintering was studied by means of Eu3+ spectroscopy, XRD and EXAFS at the Sn K-edge. Eu3+ ions adsorbed at the surface of colloidal particles present a broad distribution of sites, typical of oxide glasses. With sintering at 300°C, this distribution is still broadened. Crystallization is clearly observed by the three techniques with increasing sintering temperature. It is found that the addition of Eu3+ limits the crystallite growth.

EXAFS and XRD Study of the Structural Evolution during Isothermal Sintering of SnO2 Xerogels

The formation of an ordered (crystalline) phase during isothermal sintering of SnO2 monolithic xerogels, at 200, 250, 300, 400, 500, 600 and 700°C, has been analyzed by the combined use of EXAFS and XRD techniques. For the desiccated gel (110°C), EXAFS results show the formation of small microcrystallites with the incipient cassiterite structure. Between 110 and 250°C, the dehydratation reaction leads to an amorphization evidenced by a decrease of the long and short range crystallographic order. It is due to fissure formation in the xerogel network. For higher temperatures, a continuous coagulation of the crystallites occurs, leading to grain growth. Grain and pore growth obeys the same kinetic relation, so that the microstructure grows by simple enlargement while its morphology is static.

Effect of in concentration in the starting solution on the structural and electrical properties of ZnO films prepared by the pyrosol process at 450°C

Undoped and indium-doped Zinc oxide (ZnO) solid films were deposited by the pyrosol process at 450°C on glass substrates from solutions where In/Zn ratio was 2, 5, and 10 at.%. Electrical measurements performed at room temperature show that the addition of indium changes the resistance of the films. The resistivities of doped films are less than non-doped ZnO films by one to two orders of magnitude depending on the dopant concentration in the solution. Preferential orientation of the films with the c-axis perpendicular to the substrate was detected by X-ray diffraction and polarized extended X-ray absorption fine structures measurements at the Zn K edge. This orientation depends on the indium concentration in the starting solution. The most textured films were obtained for solutions where In/Zn ratio was 2 and 5 at.%. When In/Zn = 10 at.%, the films had a nearly random orientation of crystallites. Evidence of the incorporation of indium in the ZnO lattice was obtained from extended X-ray absorption fine structures at the In and Zn K edges. The structural analysis of the least resistive film (Zn/In = 5 at.%) shows that In substitutes Zn in the wurtzite structure. © 2000 Elsevier Science B.V. All rights reserved.

TiO2-Cu photocatalysts: A study on the long- and short-range chemical environment of the dopant

In this study, the short- and long-range chemical environments of Cu dopant in TiO2 photocatalyst have been investigated. The Cu-doped and undoped TiO2 specimens were prepared by the sol-gel approach employing CuSO4·5H2O and Ti(O-iPr)4 precursors and subjecting the dried gels to thermal treatment at 400 and 500 C. The photocatalytic activity, investigated by methylene blue degradation under sunlight irradiation, showed a significantly higher efficiency of Cu-doped samples than that of pure TiO2. The X-ray diffraction results showed the presence of anatase phase for samples prepared at 400 and 500 C. No crystalline CuSO4 phase was detected below 500 C. It was also found that doping decreases the crystallite size in the (004) and (101) directions. Infrared spectroscopy results indicated that the chemical environment of sulfate changes as a function of thermal treatment, and UV-vis spectra showed that the band gap decreases with thermal treatment and Cu doping, showing the lowest value for the 400 C sample. X-ray absorption fine structure measurements and analysis refinements revealed that even after thermal treatment and photocatalytic assays, the Cu2+ local order is similar to that of CuSO4, containing, however, oxygen vacancies. X-ray photoelectron spectroscopy data, limited to the near surface region of the catalyst, evidenced, besides CuSO4, the presence of Cu1+ and CuO phases, indicating the active role of Cu in the TiO2 lattice. © 2013 Springer Science+Business Media New York.

Local electronic structure, optical bandgap and photoluminescence (PL) properties of Ba(Zr0.75Ti0.25)O3 powders

Ba(Zr0.75Ti0.25)O3 (BZT-75/25) powders were synthesized by the polymeric precursor method. Samples were structurally characterized by X-ray diffraction (XRD), Rietveld refinement, X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) techniques. Their electronic structures were evaluated by first-principle quantum mechanical calculations based on density functional theory at the B3LYP level. Their optical properties were investigated by ultraviolet-visible (UV-Vis) spectroscopy and photoluminescence (PL) measurements at room temperature. XRD patterns and Rietveld refinement data indicate that the samples have a cubic structure. XANES spectra confirm the presence of pyramidal [TiO5] clusters and octahedral [TiO6] clusters in the disordered BZT-75/25 powders. EXAFS spectra indicate distortion of Ti-O and Ti-O-Ti bonds the first and second coordination shells, respectively. UV-Vis absorption spectra confirm the presence of different optical bandgap values and the band structure indicates an indirect bandgap for this material. The density of states demonstrates that intermediate energy levels occur between the valence band (VB) and the conduction band (CB). These electronic levels are due to the predominance of 4d orbitals of Zr atoms in relation to 3d orbitals of Ti atoms in the CB, while the VB is dominated by 2p orbitals related to O atoms. There was good correlation between the experimental and theoretical optical bandgap values. When excited at 482 nm at room temperature, BZT-75/25 powder treated at 500 C for 2 h exhibited broad and intense PL emission with a maximum at 578 nm in the yellow region. © 2013 Elsevier Ltd. All rights reserved.

In Situ and Simultaneous UV-vis/SAXS and UV-vis/XAFS Time-Resolved Monitoring of ZnO Quantum Dots Formation and Growth

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of K beta X-ray emission spectroscopy applied to Mn((2-x))V((1+x))O4 (x=0 and 1/3) oxyspinel and comparison with XANES

Oxidation state and coordination of transition metal cations seems to be hard to assess when considering multiple cations, each one with different possible oxidation states. In fact, this is the case of the spineltype double oxides family. High resolution K beta X-ray fluorescence spectra were measured in Mn(2-x)V(1+4)O4 (x=0 and 1/3) spinels-type double oxides in order to determine the oxidation state and coordination of V and Mn cations. The relative intensity of radiative Auger effect KM2,3M4,5 to the total intensity and the integral absolute difference value were used as reference parameters for the characterization of Mn oxidation states. The coordination of Mn ions was inferred by the intensity of the K beta(5) line. In the case of V compounds, it was used as the intensity of the line K beta' relative to the total area of K beta region. The obtained results were further compared with X-ray absorption spectra analysis, showing good agreements regarding the oxidation state characterization. However, there were found some discrepancies in coordination, due to customary oversimplifications in the K beta(5) line origin. The obtained results might represent valuable and useful data for chemical scopes of characterizing spineltype oxides family. (C) 2013 Elsevier Ltd. All rights reserved.

Fingerprints of short-range and long-range structure in BaZr1-xHfxO3 solid solutions: an experimental and theoretical study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Síntese e caracterização de materiais semicondutores nanoestruturados luminescentes à base de ZnS

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

SAXS and UV-Vis combined to Quick-XAFS monitoring of ZnO nanoparticles formation and growth

Time-resolved X-ray absorption-fine structure (Quick-XAFS) and UV-Vis absorption spectroscopies were combined for monitoring simultaneously the time evolution of Zn-based species and ZnO quantum dot (Qdot) formation and growth during the sol-gel synthesis from zinc oxy-acetate precursor solution. The time evolution of the nanostructural features of colloidal suspension was independently monitored in situ by small angle X-ray scattering (SAXS). In both cases, the monitoring was initialized just after the addition of NaOH solution (B = [OH]/[Zn] = 0.5) to the precursor solution at 40 degrees C. Combined time-resolved Quick-XAFS and UV-Vis data showed that the formation of ZnO colloids from the zinc oxy-acetate consumption achieves a quasi-steady-state chemical equilibrium in less than 200s. Afterwards, the comparison of the ZnO Qdots size and Guinier gyration radius evidences a limited aggregation process coupled to the Qdots growth. The analysis of the experimental results demonstrates that the nanocrystal coalescence and Ostwald ripening control the kinetics of the Qdot growth.

Local order around rare earth ions during the devitrification of oxyfluoride glasses

Erbium L-3-edge extended x-ray absorption fine structure (EXAFS) measurements were performed on rare earth doped fluorosilicate and fluoroborate glasses and glass ceramics. The well known nucleating effects of erbium ions for the crystallization of cubic lead fluoride (based on x-ray diffraction measurements) and the fact that the rare earth ions are present in the crystalline phase (as indicated by Er3+ emission spectra) seem in contradiction with the present EXAFS analysis, which indicates a lack of medium range structural ordering around the Er3+ ions and suggests that the lead fluoride crystallization does not occur in the nearest neighbor distance of the rare earth ion. Molecular dynamics simulations of the devitrification process of a lead fluoride glass doped with Er3+ ions were performed, and results indicate that Er3+ ions lower the devitrification temperature of PbF2, in good agreement with the experimental results. The genuine role of Er3+ ions in the devitrification process of PbF2 has been investigated. Although Er3+ ions could indeed act as seeds for crystallization, as experiments suggest, molecular dynamics simulation results corroborate the experimental EXAFS observation that the devitrification does not occur at its nearest neighbor distance. (c) 2008 American Institute of Physics.

Coordenação local do Eu(III) em híbridos orgânicos/inorgânicos emissores de luz branca

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)