Synthesis and electrical characterization of CaBi2Nb2O9 thin films deposited on Pt/Ti/SiO2/Si substrates by polymeric precursor method

We report the successful deposition of CaBi2Nb2O9 (CBN) thin films on platinum coated silicon substrates by polymeric precursor method. The CBN thin films exhibited good structural, dielectric and CBN/Pt interface characteristics. The leakage current of the capacitor structure was around 0.15 A cm(-2) at an applied electric field of 30 kV cm(-1). The capacitance-voltage measurements indicated good ferroelectric polarization switching characteristics. The typical measured small signal dielectric constant and the dissipation factor at a frequency of 100 kHz were 90 and 0.053, respectively. The remanent polarization and the drive voltage values were 4.2 C cm(-2) and 1.7 V at an applied voltage of 10 V. No significant fatigue was observed at least up to 10(8) switching cycles. (c) 2005 Elsevier B.V. All rights reserved.

Preparation and characterization of erbium and ytterbium co-doped sol-gel SiO2 : HfO2 films for planar waveguides

This work reports on the preparation of erbium and ytterbium co-doped SiO2:HfO2 single mode planar waveguides using the sol-gel method. Silica nanoparticles were prepared from tetraethylorthosilicate in basic media and the films were characterized by transmission electron microscopy, scanning electron microscopy, mechanical profilometry, M-lines spectroscopy based on prism coupling technique, X-ray diffractometry, infrared spectroscopy and photoluminescence spectroscopy. The film thicknesses and the refractive indexes were adjusted in order to satisfy a future efficient coupling to single mode optical fiber. Films suitable for both weak and strong light confinement were prepared varying hafnia concentration into the silica matrix. The lifetime values of erbium I-4(13/2) state were measured in order to investigate the influence of clustering and hydroxyl groups on the fluorescence quantum efficiency of the I-4(13/2) level, responsible for the emission at 1.55 mu m attributed to the I-4(13/2) -> I-4(15/2) transition. The high lifetime values suggest the absence of erbium clusters and the elimination of hydroxyl groups by rapid thermal process. (c) 2007 Elsevier B.V. All rights reserved.

Preparation of CuO/SiO2 and photocatalytic activity by degradation of methylene blue

A photocatalyst based on CuO/SiO2 was prepared, and evaluated for the degradation of methylene blue in aqueous medium. The photocatalyst was obtained by calcination method of copper salt, in the presence of silica. The characterization by XRD, FTIR, and TPR techniques confirmed the formation of CuO as active phase. SEM studies showed CuO deposited on the surface of SiO2. By ESI-MS, it was demonstrated that the degradation of methylene blue occurs through successive hydroxylations. Photodegradation assays showed that CuO/SiO2 was efficient for degradation, and that the material worked better in the presence of UV light.

Active planar waveguides based on sol-gel Er3+-doped SiO2-ZrO2 for photonic applications: Morphological, structural and optical properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Photothermal Study of Two Different Nanofluids Containing SiO2 and TiO2 Semiconductor Nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Superparamagnetic Ni:SiO2-C nanocomposites films synthesized by a polymeric precursor method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Non-leachable highly luminescent ordered mesoporous SiO2 spherical particles

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SiO2-GeO2 soot preform as a core for Eu2O3 nanocoating: Synthesis and photophysical study

Nowadays solid state chemists have the possibility of work with low temperature strategies to obtain solid state materials with appropriate physical and chemical properties for useful technological applications. Photonic core shell materials having a core and shell domains composed by a variety of compounds have been synthesized by different methods. In this work we used silica-germania soot prepared by vapor-phase axial deposition as a core where a nanoshell of Eu2O3 was deposited. A new sol-gel like method was used to obtain the Eu2O3 nanoshell coating the SiO2-GeO2 particles, which was prepared by the polymeric precursor method. The photophysical properties of Eu3+ were used to obtain information about the rare earth surrounding in the SiO2-GeO2@Eu2O3 material during the sintering process. The sintering process was followed by the luminescence spectra of Eu3+ and all the samples present the characteristic emission related to the D-5(0) -> F-7(J) (J=0, 1, 2, 3 and 4). The ratios of the D-5(0) -> F-7(2)/D-5(0) -> F-7(1) emission intensity for the SiO2-GeO2@Eu2O3 systems were calculated and it was observed an increase in its values, indicating a low symmetry around the Eu3+ as the temperature increases.

Structural and Spectroscopic Properties of Luminescent Er3+-Doped SiO2-Ta2O5 Nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation and characterization of glass-ceramic materials in the BaO-Li2O-ZrO2-SiO2 system and their dependence on treatment temperatures

The preparation and characterization of transparent glass-ceramics in the composition of 30Li2O:5ZrO2:xBaO:(100-x) SiO2 with x = 0, 5, 10, 15, and 20 mol% are described. Glasses were melted in a platinum crucible at 1100°C for 2 h and then heat-treated at 900°C for 3 h. The characterizations were performed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman and infrared spectroscopy, and scanning electron microscopy (SEM). The experimental results indicate that there was a structural change in the glass-ceramics as the BaO concentration in the mixture increased. In the XRD patterns of samples without heat treatment, only the halo was observed. After heat treatment, the appearance of the materials was verified by X-ray diffraction peaks. The reorganization of the amorphous solid was confirmed by Raman and IR spectroscopy along with XPS and SEM, with a more homogeneous phase formation being observed.

Rare earth doped HfO2 nanoparticles embedded in SiO2-HfO2 planar waveguides. Preparation, optical, structural and spectroscopic characterization

In this work we present results on the preparation of planar waveguides based on HfO2 and HfO2-SiO2. Stable sols containing europium and erbium doped HfO2 nanoparticles have been prepared and characterized. The nanosized sol was either deposited (spin-coating) on quartz substrates or embedded in (3-glycidoxipropil)trimethoxisilane (GPTS) used as a hybrid host for posterior deposition. The refractive index dispersion and luminescence characteristics were determined for the resulting HfO2 films. The optical parameters of the waveguides such as refractive index, thickness and propagation losses were measured for the hybrid composite. The planar waveguides present thickness of a few micra and support well confined propagating modes.

Alkali activated materials based on fluid catalytic cracking catalyst residue (FCC): Influence of SiO2/Na2O and H 2O/FCC ratio on mechanical strength and microstructure

Reuse of industrial and agricultural wastes as supplementary cementitious materials (SCMs) in concrete and mortar productions contribute to sustainable development. In this context, fluid catalytic cracking catalyst residue (spent FCC), a byproduct from the petroleum industry and petrol refineries, have been studied as SCM in blended Portland cement in the last years. Nevertheless, another environmental friendly alternative has been conducted in order to produce alternative binders with low CO2 emissions. The use of aluminosilicate materials in the production of alkali-activated materials (AAMs) is an ongoing research topic which can present low CO2 emissions associated. Hence, this paper studies some variables that can influence the production of AAM based on spent FCC. Specifically, the influence of SiO 2/Na2O molar ratio and the H2O/spent FCC mass ratio on the mechanical strength and microstructure are assessed. Some instrumental techniques, such as SEM, XRD, pH and electrical conductivity measurements, and MIP are performed in order to assess the microstructure of formed alkali-activated binder. Alkali activated mortars with compressive strength up to 80 MPa can be formed after curing for 3 days at 65°C. The research demonstrates the potential of spent FCC to produce alkali-activated cements and the importance of SiO2/Na2O molar ratio and the H2O/spent FCC mass ratio in optimising properties and microstructure. © 2013 Elsevier Ltd. All rights reserved.

Vitrocerâmicas de alta resistência mecânica obtidas a partir da cristalização do sistema SiO2-Al2O3-MgO-Li2O com adição de ZrO2 e B2O3

Pós-graduação em Engenharia Mecânica - FEG

Structural, microstructural, optical and electrical properties of (Pb,Ba,Sr)TiO3 films growth on conductive LaNiO3-coated LaAO(3)(100) and Pt/Ti/SiO2/Si substrates

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Simultaneous determination of epinephrine and dopamine by electrochemical reduction on the hybrid material SiO2/graphene oxide decorated with Ag nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)