pH changes at the surface of root dentin when using root canal sealers containing calcium hydroxide

The purpose of this study was to investigate long-term pH changes in cavities prepared in root surface dentin of extracted teeth after obturation of the root canal with gutta-percha and a variety of sealers containing calcium hydroxide. After cleaning and shaping, root canals in 50 recently extracted, human single-rooted teeth were divided into five groups. Each of four groups was obturated with gutta-percha and either Sealapex, Sealer 26, Apexit, or CRCS, all of which contain calcium hydroxide. The remaining group served as the control and was not obturated with gutta-percha or sealer. Cavities were prepared in the facial surface of the roots in the cervical and middle regions. The pH was measured in these dentinal cavities at the initiation of the experiment, and 3, 7, 14, 21, 28, 45, 60, 90, and 120 days after obturation. Results indicate that the pH at the surface of the root does not become alkaline when calcium hydroxide cements are used as root canal sealers. Regardless of the sealer used, the observed pattern of pH change was not different from that seen in the control group of roots that were not treated with sealer. It is concluded that calcium hydroxide-containing cements, although suitable for use as root canal sealants, do not produce an alkaline pH at the root surface. If such a pH change is related to treatment of root resorption, these sealants do not contribute to this treatment. Copyright © 1996 by The American Association of Endodontists.

Calcium hydroxide root canal sealers: Evaluation of pH, calcium ion concentration and conductivity

The calcium hydroxide ionization of four root canal sealers (Sealapex, CRCS, Sealer 26, and Apexit) was studied by measuring conductivity and pH and by conducting atomic absorption spectrophotometry. Samples 6 mm in diameter and 15 mm long were prepared from these sealers. After setting and 48 h storage in a desiccator, five samples of each material were placed in 50 mL distilled water and analysed after 0,1,2,4, 6 and 24 h and 5, 15 and 30 days. The results showed that Sealapex was the root canal sealer showing the highest pH, ionic calcium and total calcium values (P<0.05) throughout the experimental period, followed by CRCS, Apexit and Sealer 26.

Effect of different root canal sealers on periapical repair of teeth with chronic periradicular periodontitis

Teeth with induced chronic periradicular periodontitis in dogs were root canal treated. After the biomechanical preparation, using K files and 5.25% sodium hypochlorite as the irrigant solution, all root canals were dressed with an antibacterial dressing based on calcium hydroxide, which was left in place for 7 days. After this time, the root canals were obturated with lateral condensation of cold gutta-percha with either a calcium hydroxide root canal filling material (Sealapex) or a zinc oxide-eugenol sealer (Fill Canal). After 270 days, histopathological analysis showed better apical and periapical repair in the teeth obturated with Sealapex (P < 0.05).

Release of formaldehyde by 4 endodontic sealers

Objective. The purpose of this study was to evaluate the release of formaldehyde by some root canal filling materials. Study design. Two older endodontic sealers, AH 26 and Endomethasone, and 2 recently available sealers, AH Plus and Top Seal, were analyzed. Infrared and electronic spectroscopy were used to determine formaldehyde content after set of the materials. Results. Analysis showed that the AH 26 and Endomethasone sealers released formaldehyde. Although the AH Plus and Top Seal sealers have similar chemical composition, they released formaldehyde in a minimal concentration. Conclusions. The AH 26 and Endomethasone sealers released formaldehyde after setting; however, a minimum release was observed for the AH Plus and Top Seal sealers. Copyright © 1999 by Mosby, Inc.

Evaluation of apical sealing of three endodontic sealers

Aim: The apical sealing ability of three different endodontic sealers was evaluated in extracted teeth using dye penetration. Methodology: The root canals of 99 extracted human maxillary central incisors were prepared sequentially 2 mm beyond the apical foramen with a size 55 Nitiflex file. The teeth were divided into three experimental groups and obturated by lateral condensation of cold gutta-percha and one of the following sealers: group 1, zinc oxide and eugenol sealer (Fill Canal); group 2, glass ionomer sealer (Ketac-Endo) and group 3, epoxy resin sealer (AH Plus). The teeth were covered with nail varnish to within 1 mm of the apical foramen and immersed in 2% methylene blue in a reduced pressure environment for 24h. After this period, the teeth were washed and cut longitudinally for apical leakage analysis. The values were obtained from the maximum depth of leakage as well as the average between the maximum and minimum values observed for each group. Results: Statistical evaluation of the results showed no significant difference in the leakage between Fill Canal and Ketac-Endo (P > 0.05). Leakage with AH Plus was significantly less (P < 0.01) than with the other sealers. Conclusions: All three sealers allowed some leakage to occur. Leakage with AH Plus was significantly different than with Fill Canal or Ketac-Endo.

Evaluation of cell culture cytotoxicity of five root canal sealers

The cytotoxicity of four calcium hydroxide-based root canal sealers (Sealapex, CRCS, Apexit, and Sealer 26) and one zinc oxide-eugenol-based sealer (Fill Canal) was evaluated microscopically for morphological changes in rat peritoneal macrophages. The least cytotoxic sealer was Fill Canal, followed in increasing order of cytotoxicity by CRCS, Sealer 26, Apexit, and Sealapex. Copyright © 2000 by The American Association of Endodontists.

In vitro evaluation of antimicrobial activity of sealers and pastes used in endodontics

The antimicrobial activity of four root canal sealers (AH Plus, Sealapex, Ketac Endo, and Fill Canal), two calcium hydroxide pastes (Calen and Calasept), and a zinc oxide paste was evaluated. Seven bacterial strains were used, six of them standard; Micrococcus luteus ATCC 9341, Staphylococcus aureus ATCC 25923, Pseudomonas aeruginosa ATCC 27853, Staphylococcus epidermidis ATCC 12228, Escherichia coli ATCC 25922, and Enterococcus faecalis ATCC 10541. There was a wild strain of Streptococcus mutans isolated from saliva obtained in an adult dental clinic. Activity was evaluated using the agar diffusion method with Brain Heart Infusion agar and Müller Hinton medium seeded by pour plate. Calcium hydroxide-based sealers and pastes were either placed directly into 4.0 × 4.0 mm wells or by using absorbent paper points. The plates were kept at room temperature for 2 hr for diffusion. After incubation at 37°C for 24 hr, the medium was optimized with 0.05 g% TTC gel and inhibition haloes were measured. All bacterial strains were inhibited by all materials using the well method. However, when the materials were applied with absorbent paper points, Enterococcus faecalis was not inhibited by zinc oxide, and Pseudomonas aeruginosa was not inhibited by AH Plus, Fill Canal, and the zinc oxide-based paste. We conclude that sealers and pastes presented antimicrobial activity in vitro and culture medium optimization with 0.05 g% TTC gel facilitated observation of the inhibition haloes. Copyright © 2000 by The American Association of Endodontists.

Calcium salts deposition in rat connective tissue after the implantation of calcium hydroxide-containing sealers

This study was conducted to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes that were filled with mineral trioxide aggregate, Sealapex, Calciobiotic Root Canal Sealer (CRCS), Sealer 26, and the experimental material, Sealer Plus. The animals were sacrificed after 7 and 30 days, and the specimens were prepared for histological analysis after serial sections with a hard-tissue microtome. The undecalcified sections were examined with polarized light after staining according to the Von Kossa technique for calcium. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was irregular tissue, like a bridge, that was Von Kossa-positive. The dentin walls of the tubes exhibited a structure highly birefringent to polarized light, usually like a layer, in the tubules. These results were observed with all the studied materials, except the CRCS, which didn't exhibit any kind of mineralized structure. The results suggest that among the materials studied, the CRCS could have the least possibility of encouraging hard tissue deposition.

Apical and periapical repair of dogs' teeth with periapical lesions after endodontic treatment with different root canal sealers.

The aim of this study was to evaluate the apical and periapical repair after root canal treatment of dogs' teeth with pulp necrosis and chronic periapical lesion using different root canal sealers. After periapical lesion induction, forty-four root canals of 3 dogs were submitted to biomechanical preparation using 5.25% sodium hypochlorite as an irrigating solution. A calcium hydroxide dressing (Calen PMCC) was applied for 15 days and the root canals were filled using the lateral condensation technique with gutta-percha points and Sealapex, AH Plus or Sealer Plus for sealing. After 180 days, the animals were sacrificed by anesthetic overdose and the obtained histological sections were stained with hematoxylin-eosin for optical microscopic analysis of the apical and periapical repair. The groups filled with Sealapex and AH Plus had better histological repair (p < 0.05) than the group filled with Sealer Plus, that had unsatisfactory results.

Secretion of tumor necrosis factor-alpha by mouse peritoneal macrophages in the presence of dental sealers, sealapex and endomethasone

After filling root canals, the healing process depends on the chemical composition or physical-chemical properties of the material used, among other factors. All root canal sealers, whether solid or plastic, are foreign matter for the body if they remain in permanent contact with apical and periapical tissues. As a result, the first organic reaction that occurs is an attempt to phagocytize the material. During phagocytosis, macrophages release a large number of cell mediators into the area, among which are cytokines that are essential in intercellular communication and in many physiological and pathophysiological processes. One of these cytokines is tumor necrosis factor-alfa (TNF-α), which acts through links to specific receptors on the cell membrane initiating a cascade of events leading to induction, activation, or inhibition of numerous cytokine-regulated genes in the cell nucleus. The release of TNF-α in a cell culture of mouse peritoneal macrophages incubated with three concentrations (25, 50, and 100 mg/ml) of two endodontic sealers was measured. The solutions containing the calcium hydroxide-based root canal sealer (Sealapex) released fewer units of TNF-α than solutions containing the zinc oxide and eugenol-based sealer (Endomethasone).

In vitro antimicrobial activity of endodontic sealers, MTA-based cements and Portland cement.

The aim of this study was to evaluate the antimicrobial activity of different root-end filling materials - Sealer 26, Sealapex with zinc oxide, zinc oxide and eugenol, white and gray Portland cement, white and gray MTA-Angelus, and gray Pro Root MTA - against six different microorganism strains. The agar diffusion method was used. A base layer was made using Müller-Hinton agar (MH) and wells were formed by removing the agar. The materials were placed in the wells immediately after manipulation. The microorganisms used were: Micrococcus luteus (ATCC9341), Staphylococcus aureus (ATCC6538), Escherichia coli (ATCC10538), Pseudomonas aeruginosa (ATCC27853), Candida albicans (ATCC 10231), and Enterococcus faecalis (ATCC 10541). The plates were kept at room temperature for 2 h for prediffusion and then incubated at 37 degrees C for 24 h. Triphenyltetrazolium chloride 0.05% gel was added for optimization, and the zones of inhibition were measured. Data were subjected to the Kruskal-Wallis and Dunn tests at a 5% significance level. The results showed that all materials had antimicrobial activity against all the tested strains. Analysis of the efficacy of the materials against the microbial strains showed that Sealapex with zinc oxide, zinc oxide and eugenol and Sealer 26 created larger inhibition halos than the MTA-based and Portland cements (P < 0.05). On the basis of the methodology used, it may be concluded that all endodontic sealers, MTA-based and Portland cements evaluated in this study possess antimicrobial activity, particularly the endodontic sealers.

Evaluation of the biocompatibility of root canal sealers using subcutaneous implants

The purpose of this study was to evaluate in vivo the biocompatibility of Endométhasone, Pulp Canal Sealer EWT and AHPlus root canal sealers after implantation in rat connective tissue. Twenty-four Wistar-Furth rats were used. Polyethylene tubes were filled with the sealers and implanted into specific dorsal subdermal tissue sites of the rats. Implants were removed after 3, 7 and 30 days, fixed and processed for glycol methacrylate-embedding technique to be examined microscopically. On the 3rd day, there was a mild inflammatory reaction to Pulp Canal Sealer EWT implants, but a severe response to the other sealers with presence of acute inflammatory cells. On the 7th day, tissue organization was more evident with attenuation of the inflammatory reaction, especially for the AH-Plus implants. On the 30th day, connective tissue with few inflammatory cells was observed in contact with all sealer implants. In this time interval, the tissue in contact with Pulp Canal Sealer EWT implants was more organized, while the tissue close to Endométhasone and AH-Plus implants showed a mild persistent inflammatory reaction and had similar results to each other. In conclusion, the sealers had a similar pattern of irritation, which was more severe in the beginning and milder with time, in such a way that all sealers showed a persistent mild reaction. Pulp Canal Sealer EWT yielded better tissue organization than Endométhasone and AH-Plus, which, in turn, showed similar results to each other.

Antimicrobial activity of endodontic sealers based on calcium hydroxide and MTA.

The aim of this study was to evaluate the antimicrobial activity of a new root canal sealer containing calcium hydroxide (Acroseal) and the root canal sealer based on MTA (Endo CPM Sealer), in comparison with traditional sealers (Sealapex, Sealer 26 and Intrafill) and white MTA-Angelus, against five different microorganism strains. The materials and their components were evaluated after manipulation, employing the agar diffusion method. A base layer was made using Müller-Hinton agar (MH) and wells were made by removing agar. The materials were placed into the wells immediately after manipulation. The microorganisms used were: Micrococcus luteus (ATCC9341), Staphylococcus aureus (ATCC6538), Pseudomonas aeruginosa (ATCC27853), Candida albicans (ATCC 10231), and Enterococcus faecalis (ATCC 10541). The plates were kept at room temperature for 2 h for prediffusion and then incubated at 37 degrees C for 24 h. The results showed that Sealapex and its base paste, Sealer 26 and its powder, Endo CPM Sealer and its powder, white MTA and its powder all presented antimicrobial activity against all strains. Intrafill and its liquid presented antimicrobial activity against all strains except P. aeruginosa and Acroseal was effective only against M. luteus and S. aureus.

Periapical repair after root canal filling with different root canal sealers

The aim of this study was to evaluate periapical repair after root canal filling with different endodontic sealers. Sixty four root canals from dog ́s teeth were filled, divided into 4 groups (n=16). Root canals were instrumented with K-type files and irrigated with 1% sodium hypochlorite solution. Root canals were filled in the same session by active lateral condensation of the cones and sealers: Intrafill, AH Plus, Roeko Seal and Resilon/Epiphany System. After 90 days, the animals were euthanized and the tissues to be evaluated were processed and stained with hematoxylin and eosin. For histopathological analysis, the following parameters were evaluated: inflammatory process, mineralized tissue resorption, and apical mineralized tissue deposition. Histopathological analysis demonstrated that Intrafill had less favorable results in terms of apical and periapical repair, compared to the other sealers (p<0.05). AH Plus, Roeko Seal, and Epiphany sealers had similar and satisfactory results (p>0.05). In conclusion, AH Plus and the materials Roeko Seal and Epiphany are good options for clinical use in Endodontics.

Radiopacity evaluation of root canal sealers containing calcium hydroxide and MTA

The purpose of this study was to evaluate the radiopacity of root canal sealers containing calcium hydroxide and MTA (Acroseal, Sealer 26, Sealapex, Endo CPM Sealer, Epiphany and Intrafill). Five disc-shaped specimens (10 x 1 mm) were fabricated from each material, according to the ISO 6876/2001 standard. After setting of the materials, radiographs were taken using occlusal film and a graduated aluminum stepwedge varying from 2 to 16 mm in thickness. The dental X-ray unit (GE1000) was set at 50 kVp, 10 mA, 18 pulses/s and distance of 33.5 cm. The radiographs were digitized and the radiopacity compared to that of the aluminum stepwedge using VIXWIN-2000 software (Gendex). The data (mmAl) were analyzed statistically by ANOVA and Tukey's test at the 5% significance level. Epiphany and Intrafill presented the highest radiopacity values (8.3 mmAl and 7.5 mmAl respectively, p < 0.05) followed by Sealer 26 (6.3 mmAl), Sealapex (6.1 mmAl) and Endo CPM Sealer (6 mmAl). Acroseal was the least radiopaque material (4 mmAl, p < 0.05). In conclusion, the calcium hydroxide- and MTA-containing root canal sealers had different radiopacities. However, all materials presented radiopacity values above the minimum recommended by the ISO standard. © 2009 Sociedade Brasileira de Pesquisa Odontológica.