Marginal adaptation of Class 2 adhesive restorations

Objective: Control of microleakage represents a challenge for posterior composite restorations. The technique for composite placement may reduce microleakage. The null hypothesis of this in vitro study was that centripetal incremental insertion of composite resin would result in less microleakage than that obtained with the oblique incremental technique or bulk technique. Method and Materials: Standardized Class 2 preparations were made in 60 caries-free extracted third molars and randomly assigned to 3 groups ( n = 20): ( 1) oblique incremental insertion technique ( control), ( 2) centripetal incremental insertion technique, and ( 3) bulk insertion. The teeth were restored with a total-etch adhesive and micro-hybrid composite resin. The specimens were isolated with nail varnish except for a 2-mm-wide area around the restoration and then thermocycled ( 1,000 thermal cycles, 5 degrees C/ 55 degrees C; 30-second dwell time). The specimens were immersed in an aqueous solution of 50% silver nitrate for 24 hours, followed by 8 hours of immersion in a photo-developing solution and subsequently evaluated for leakage. The microleakage scores ( 0 to 4) obtained from the occlusal and cervical walls were analyzed with median nonparametric tests ( P <.05). Results: The null hypothesis was rejected. All techniques attained statistically similar dentin microleakage scores ( P =.15). The centripetal insertion technique displayed significantly less microleakage than the oblique technique at the enamel margins ( P =.04). Conclusion: None of the techniques eliminated marginal microleakage in Class 2 preparations. However, in occlusal areas, the centripetal technique performed significantly better than the other techniques.

Effect of Static and Cyclic Loading on Ceramic Laminate Veneers Adhered to Teeth with and Without Aged Composite Restorations

Purpose: Existing composite restorations on teeth are often remade prior to the cementation of fixed dental prostheses. The aim of this study was to evaluate the effect of static and cyclic loading on ceramic laminate veneers adhered to aged resin composite restorations.Materials and Methods: Eighty sound maxillary incisors were collected and randomly divided into four groups: group 1: control group, no restorations; group 2: two Class III restorations; group 3: two Class IV restorations; group 4: complete composite substrate. Standard composite restorations were made using a microhybrid resin composite (Anterior Shine). Restored teeth were subjected to thermocycling (6000 cycles). Window preparations were made on the labial surface of the teeth for ceramic laminate fabrication (Empress II). Teeth were conditioned using an etch-and-rinse system. Existing composite restorations representing the aged composites were silica coated (CoJet) and silanized (ESPE-Sil). Ceramic laminates were cemented using a bis-GMA-based cement (Variolink Veneer). The specimens were randomly divided into two groups and were subjected to either static (groups 1a, 2a, 3a, 4a) or cyclic loading (groups 1b, 2b, 3b, 4b). Failure type and location after loading were classified. Data were analyzed using one-way ANOVA and Tukey's test.Results: Significantly higher fracture strength was obtained in group 4 (330 +/- 81 N) compared to the controls in group 1 (179 +/- 120 N) (one-way ANOVA, p < 0.05). Group lb survived a lower mean number of cyclic loads (672,820 cycles) than teeth of groups 2b to 4b (846x10(3) to 873x10(3) cycles). Failure type evaluation after the fracture test showed predominantly adhesive failures between dentin and cement, but after cyclic loading, more cohesive fractures in the ceramic were seen.Conclusion: Ceramic laminate veneers bonded to conditioned aged composite restorations provided favorable results. Surface conditioning of existing restorations may eliminate the necessity of removing aged composite restorations.

Bond strengths, degree of conversion of the cement and molecular structure of the adhesive-dentine joint in fibre post restorations

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

A retrospective look at esthetic resin composite and glass-ionomer Class III restorations: A 2-year clinical evaluation

Objective: A restorative material for Class III cavities must, besides being functional, be esthetically satisfactory, providing good working conditions and several shade and color options. A clinical evaluation was initiated to compare the suitability of resin composite and glass-ionomer cement materials for such restorations.Method and materials: Forty-two Class III conservative cavities, esthetically important because of facial extensions, were selected. Resin composite restorations were placed in 21 cavities, and the remaining 21 were restored with glass-ionomer cement. The following characteristics were studied: color or-esthetics, anatomic shape, surface texture, staining, marginal infiltration, dental plaque retention, and occurrence of fracture. After 24 months, the restorations were evaluated.Results: the only statistically significant difference between the resin composite and glass-ionomer cement restorations in the experimental period involved color or esthetics.Conclusion: Resin composites and glass-ionomer materials provide excellent functional and esthetic results in Class III cavities when properly indicated.