Structural resistance in immature teeth using root reinforcements in vitro

The purpose of this study was to evaluate in vitro the efficacy of root reinforcements by light-cured composite resin or zirconium fiber post in simulated immature non-vital teeth. Fifty-six bovine incisors teeth were used for this study. The crown of each tooth was removed in the medium third to obtain a standard length of 30 mm. The specimens were divided into four groups (n = 14): G1) the root canals were instrumented and enlarged to simulate immature non-vital teeth and were reinforced with a light-cured composite resin using a translucent curing post (Luminex system); (G2) the specimens were instrumented, enlarged and they received root reinforcement with zirconium fiber post; G3 (positive control): they received similar treatment to the G1 and G2 groups, but did not receive root reinforcement; G4 (negative control): the roots were not weakened and did not receive reinforcement. Every tooth was submitted to compressive force using an Instron testing machine with an angle of 45&DEG; at a speed of 1 mm min(-1) until the fracture. The results showed a markedly increased resistance to fracture in the G1 and G2 (122.38 and 122.08 kgf, respectively). Among the results of G1 and G2 there was not any significant difference (P > 0.05) but they were significantly different from the control groups (P < 0.05). The conclusion is that the use of root reinforcements with zirconiun fiber post or composite resin can increase significantly the structural resistance of the weakened teeth, decreasing the risk of the fracture.

Fracture resistance of endodontically treated teeth with different heights of crown ferrule restored with prefabricated carbon fiber post and composite resin core by intermittent loading

This study evaluated the fracture resistance of endodontically treated teeth restored with prefabricated carbon fiber posts and varying quantities of coronal dentin. Sixty freshly extracted upper canines were randomly divided into groups of 10 teeth each. The specimens were exposed to 250,000 cycles in a controlled chewing simulator. All intact specimens were subjected to a static load (N) in a universal testing machine at 45 degrees to the long axis. Data were analyzed by 1-way analysis of variance and Tukey test (alpha = .05). Significant differences (P < .001) were found among the mean fracture forces of the test groups (positive control, 0 mm, 1 mm, 2 mm, 3 mm, and negative control groups: 1022.82 N, 1008.22 N, 1292.52 N, 1289.19 N, 1255.38 N, and 1582.11, respectively). These results suggested that the amount of coronal dentin did not significantly increase the fracture resistance of endodontically treated teeth restored with prefabricated carbon fiber post and composite resin core. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2008;106:e52-e57)

Effect of post length on the fatigue resistance of bovine teeth restored with bonded fiber posts: A pilot study

This study evaluated the influence of the cementation length of glass fiber-reinforced composite (FRC) on the fatigue resistance of bovine teeth restored with an adhesively cemented FRC. Thirty roots of single-rooted bovine teeth were allocated to 3 groups (n = 10), according to the ratio of crown length/root length (post cementation length): group 1 = 2/3, group 2 = 1/2, and group 3 = 1/1. The roots were prepared, the fiber posts (FRC Postec Plus) were cemented, and the specimens were submitted to 2 million mechanical cycles. After fatigue testing, a score was given based on the number of fatigue cycles until fracture, and data were submitted to statistical analysis. All specimens were resistant to fatigue. Taking into account the methodology and results of this study, the evaluated fiber posts can be cemented based on the ratio of crown/root at 1/1. Further clinical studies must be conducted to verify this ratio.

Evaluation of the microscopic observation drug susceptibility assay for detection of Mycobacterium tuberculosis resistance to pyrazinamide

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fatigue resistance of the bond of a glass-infiltrated alumina ceramic to human dentin

Purpose: To evaluate the fatigue resistance of the bond between dentin and glass-infiltrated alumina ceramic, using different luting protocols. Materials and Methods: The null hypothesis is that the fatigue resistance varies with the luting strategy. Forty blocks of In-Ceram Alumina were prepared, and one surface of each block was abraded with 110-μm aluminum oxide particles. Then, the blocks were luted to flat dentin surfaces of 40 human third molars, using 4 different luting strategies (luting system [LS]/ceramic surface conditioning [CSC]) (n=10): (G1) [LS] RelyX-Unicem/[CSC] airborne abrasion with 110-μm Al2O3 particles; (G2) [LS] One-Step + Duo-Link (bis-GMA-based resin)/[CSC] etching with 4% hydrofluoric acid + silane agent; (G3) [LS] ED-Primer + Panavia F (MDP-based resin)/[CSC] Al2O 3; (G4) [LS] Scotchbond1+RelyX-ARC (bis-GMA-based resin)/[CSC] chairside tribochemical silica coating (air abrasion with 30-μm SiO x particles + silane). After 24 h of water storage at 37°C, the specimens were subjected to 106 fatigue cycles in shear with a sinusoidal load (0 to 21 N, 8 Hz frequency, 37°C water). A fatigue survivor score was given, considering the number of the fatigue cycles until fracture. The failure modes of failed specimens were observed in a SEM. Results: G3 (score = 5.9, 1 failure) and G4 (score = 6, no failures) were statistically similar (p = 0.33) and had significantly higher fatigue resistance than G1 (score = 3.9, 5 failures) and G2 (score = 3.7, 6 failures) (p < 0.03). SEM analysis of fractured specimens of G1 and G2 showed that almost all the failures were between ceramic and cement. Conclusion: The MDP-based resin cement + sandblasting with Al2O3 particles (G3) and bis-GMA-based resin cement + tribochemical silica coating (G4), both using the respective dentin bonding systems, were the best luting protocols for the alumina ceramic. The null hypothesis was confirmed.

Fatigue resistance of bovine teeth restored with resin-bonded fiber posts: Effect of post surface conditioning

This study evaluated the effect of post surface conditioning on the fatigue resistance of bovine teeth restored with resin-bonded fiber-reinforced composite (FRC). Root canals of 20 single-rooted bovine teeth (16 mm long) were prepared to 12 mm using a preparation drill of a double-tapered fiber post system. Using acrylic resin, each specimen was embedded (up to 3.0 mm from the cervical part of the specimen) in a PVC cylinder and allocated into one of two groups (n = 10) based on the post surface conditioning method: acid etching plus silanization or tribochemical silica coating (30 μm SiOx + silanization). The root canal dentin was etched (H2PO3 for 30 seconds), rinsed, and dried. A multi-step adhesive system was applied to the root dentin and the fiber posts were cemented with resin cement. The specimens were submitted to one million fatigue cycles. After fatigue testing, a score was given based on the number of fatigue cycles until fracture. All of the specimens were resistant to fatigue. No fracture of the root or the post and no loss of retention of the post were observed. The methodology and the results of this study indicate that tribochemical silica coating and acid etching performed equally well when dynamic mechanical loading was used.

Influence of bleaching treatment on flexural resistance of hybrid materials.

The aim of this study is to evaluate the flexural resistance of three types of restorative materials: compomer (Freedom), resin-modified glass-ionomer (Vitremer) and composite resin (Esthet-X), observing whether the application of bleaching agent can cause alterations of their flexural properties. Sixty samples were made using a 10 x 1 x 1 mm brass mold, and divided into three groups: G1- Freedom (SDI); G2- Vitremer (3M ESPE); G3- Esthet-X (Dentsply). On half of the samples of each group (10 samples) the bleaching treatment was applied and the other half used as control, was stored in distilled water at a temperature of 37 degrees C. Whiteness HP Maxx bleaching system was applied on the sample surface following the manufacturer's recommendations, simulating the bleaching treatment at the clinic. After this period, a flexural strength (three-point bending) test was conducted using (EMIC DL 1000) machine until the samples fractured. The data were submitted to ANOVA and Tukey tests. Of the restorative materials studied, G3-(87.24 +/- 31.40 MPa) presented the highest flexural strength, followed by G1-(61.67 +/- 21.32 MPa) and G2-(61.67 +/- 21.32 MPa). There was a statistical difference in flexural strength after the bleaching treatment. It was concluded that the use of a beaching agent can promote significant alteration of the flexural strength of these restorative materials.

Fracture resistance of bovine incisors restored with different glass fiber posts: Effect of the diameter of fiber post

Aim: Compare the effect of three post designs on the fracture resistance and failure modes of composite core-fiber post-crownless tooth sets. Materials and Methods: Ninety bovine incisors were selected and divided into nine groups of 10 specimens. The teeth were assigned to three groups based on the post design: Cylindrical, tapered, and double-tapered. Each group was subdivided into three subgroups in accordance with the diameter of the post: Small (No.1), medium (No.2), and large (No.3). The Panavia F system was used for post cementation. The specimens were mounted in acrylic resin blocks with a layer of silicone rubber covering the roots. A universal testing machine compressively loaded the specimens from the palatal side at a crosshead speed of 1 mm/min and at an angle of 135I to the long axis of the teeth, until failure occurred. The failure mode was determined by a stereomicroscope inspection of all the specimens. Data were analyzed by one-way ANOVA and the Tukey test (P < 0.05). Results: The fracture resistance was affected by the type of post (P < 0.0001). A narrower diameter for all of the post systems allowed for higher resistance. The main failure mode in the large cylindrical group was catastrophic fractures, while the main failures in the other eight groups were favorable. Conclusion: Narrower diameter posts showed higher fracture resistance. The dominant failure pattern was repairable fracture, except for those with large cylindrical groups.

Influence of convergence angle of tooth preparation on the fracture resistance of Y-TZP-based all-ceramic restorations

Objective: To investigate the influence of the convergence angle of tooth preparation on the fracture load of Y-TZP-based ceramic (YZ-Vita YZ) substructure (SB) veneered with a feldspathic porcelain (VM9-Vita VM9). Methods: Finite element stress analysis (FEA) was performed to examine the stress distribution of the system. Eighty YZ SB were fabricated using a CAD-CAM system and divided into four groups (n = 20), according to the total occlusal convergence (TOC) angle: G6-6° TOC; G12-12° TOC; G20-20° TOC; and G20MOD-20° TOC with modified SB. All SB were veneered with VM9, cemented in a fiber reinforced epoxy resin die, and loaded to failure. Half of the specimens from each group (n = 10) were cyclic fatigued (106 cycles) before testing. Failure analysis was performed to determine the fracture origin. Data were statistically analyzed using Anova and Tukey's tests (α = 0.05). Results: The greatest mean load to fracture value was found for the G20MOD, which was predicted by the FEA. Cyclic fatigue did not significantly affect the load of fracture. Catastrophic failure originating from the internal occlusal surface of the SB was the predominant failure mode, except for G20MOD. Significance: The YZ-VM9 restorations resisted greater compression load than the usual physiological occlusal load, regardless of the TOC angle of preparations. Yet, the G20MOD design produced the best performance among the experimental conditions evaluated. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of the Layering Technique on Bond Strength and Cohesive Resistance of a Porcelain-Zirconia System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Genetic variability in progenies of Eucalyptus dunnii Maiden for resistance to Puccinia psidii

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The fracture resistance of a CAD/CAM Resin Nano Ceramic (RNC) and a CAD ceramic at different thicknesses

Objective. This study aimed to investigate the influence of restoration thickness to the fracture resistance of adhesively bonded Lava (TM) Ultimate CAD/CAM, a Resin Nano Ceramic(RNC), and IPS e. max CAD ceramic.Methods. Polished Lava (TM) Ultimate CAD/CAM (Group L), sandblasted Lava (TM) Ultimate CAD/CAM (Group LS), and sandblasted IPS e.max CAD (Group ES) discs (n=8, phi=10 mm) with a thickness of respectively 0.5 mm, 1.0 mm, 1.5 mm, 2.0 mm, and 3.0 mm were cemented to corresponding epoxy supporting discs, achieving a final thickness of 3.5 mm. All the 120 specimens were loaded with a universal testing machine at a crosshead speed of 1 mm/min. The load (N) at failure was recorded as fracture resistance. The stress distribution for 0.5 mm restorative discs of each group was analyzed by Finite Element Analysis (FEA). The results of facture resistances were analyzed by one-way ANOVA and regression.Results. For the same thickness of testing discs, the fracture resistance of Group L was always significantly lower than the other two groups. The 0.5 mm discs in Group L resulted in the lowest value of 1028 (112) N. There was no significant difference between Group LS and Group ES when the restoration thickness ranged between 1.0 mm and 2.0 mm. There was a linear relation between fracture resistance and restoration thickness in Group L (R = 0.621, P < 0.001) and in Group ES (R = 0.854, P < 0.001). FEA showed a compressive permanent damage in all groups.Significance. The materials tested in this in vitro study with the thickness above 0.5 mm could afford the normal bite force. When Lava Ultimate CAD/CAM is used, sandblasting is suggested to get a better bonding. (C) 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Comparison of cyclic fatigue and torsional resistance in reciprocating single-file systems and continuous rotary instrumentation systems

As compared with continuous rotary systems, reciprocating motion is believed to increase the fatigue resistance of NiTi instruments. We compared the cyclic fatigue and torsional resistance of reciprocating single-file systems and continuous rotary instrumentation systems in simulated root canals. Eighty instruments from the ProTaper Universal, WaveOne, MTwo, and Reciproc systems (n = 20) were submitted to dynamic bending testing in stainless-steel simulated curved canals. Axial displacement of the simulated canals was performed with half of the instruments (n = 10), with back-and-forth movements in a range of 1.5 mm. Time until fracture was recorded, and the number of cycles until instrument fracture was calculated. Cyclic fatigue resistance was greater for reciprocating systems than for rotary systems (P < 0.05). Instruments from the Reciproc and WaveOne systems significantly differed only when axial displacement occurred (P < 0.05). Instruments of the ProTaper Universal and MTwo systems did not significantly differ (P > 0.05). Cyclic fatigue and torsional resistance were greater for reciprocating systems than for continuous rotary systems, irrespective of axial displacement.

Fracture resistance of teeth submitted to several internal bleaching protocols

Aim: The aim of this study was to evaluate the fracture resistance of teeth submitted to several internal bleaching protocols using 35% hydrogen peroxide (35HP), 37% carbamide peroxide (37CP), 15% hydrogen peroxide with titanium dioxide nanoparticles (15HPTiO2) photoactivated by LED-laser or sodium perborate (SP). Materials and methods: After endodontic treatment, fifty bovine extracted teeth were divided into five groups (n = 10): G1-unbleached; G2-35HP; G3-37CP; G4-15HPTiO2 photoactivated by LED-laser and G5-SP. In the G2 and G4, the bleaching protocol was applied in 4 sessions, with 7 days intervals between each session. In the G3 and G5, the materials were kept in the pulp teeth for 21 days, but replaced every 7 days. After 21 days, the teeth were subjected to compressive load at a cross head speed of 0.5 mm/min, applied at 135° to the long axis of the root using an eletromechanical testing machine, until teeth fracture. The data were submitted to ANOVA and Tukey tests (α = 5%). Results: The 35HP, 37CP, 15HPTiO2 and SP showed similar fracture resistance teeth reduction (p > 0.05). All bleaching treatments reduced the fracture resistance compared to unbleached teeth (p < 0.05). Conclusion: All bleaching protocols reduced the fracture resistance of endodontically-treated teeth, but there were no differences between each other. Clinical significance: There are several internal bleaching protocols using hydrogen peroxide in different concentrations and activation methods. This study evaluated its effects on fracture resistance in endodontically-treated teeth.

Fracture resistance of endodontically-treated teeth submitted to bleaching treatment with hydrogen peroxide and titanium dioxide nanoparticles photoactivated by LED-laser

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)