Upconversion luminescence in transparent glass ceramics containing beta-PbF2 nanocrystals doped with erbium

Frequency upconversion luminescence in erbium-doped PbGeO3-PbF2-CdF2-based transparent glass ceramics (TGC) under 980 nm infrared excitation is investigated. Upconversion emission signals around 410, 525, 550, 660, and 850 nm were generated and identified as due to the H-2(9/2) H-2(11/2), S-4(3/2), and F-4(9/2) transitions to the I-4(15/2) ground-state, and S-4(3/2)-I-4(13/2), respectively. The erbium ions excited-state emitting levels were populated via a combination of stepwise ground-state absorption (GSA), excited-state absorption (ESA), and cross-relaxation processes. The results also disclosed that both blue (410 nm) and red (660 nm) upconversion emission signals in the transparent glass ceramic sample presented twice as much intensity as compared to its vitreous counterpart. (C) 2003 Elsevier B.V. All rights reserved.

Exciton formation in dye doped OLEDs using electrically detected magnetic resonance

Electrically Detected Magnetic Resonance (EDMR) was used to investigate the influence of dye doping molecules on spin-dependent exciton formation in Aluminum (III) 8-hydroxyquinoline (Alq(3)) based OLEDs with different device structures and temperature ranges. 4-(dicyanomethylene)-2-methyl-6-{2-[(4-diphenylamino-phenyl]ethyl}-4H-pyran (DCM-TPA) and 5,6,11,12-tetraphenylnaphthacene (Rubrene) were used as dopants. A strong temperature dependence have been observed for doped OLEDs, with a decrease of two orders of magnitude in EDMR signal for temperatures above similar to 200 K. The signal temperature dependence were fitted supposing different spin-lattice relaxation processes. The results suggest that thermally activated vibrations of dopants molecules induce spin pair dissociation, reducing the signal.

Thermally activated dynamics of the tilts of the CuO6 octahedra, hopping of interstitial O, and possible instability towards the LTT phase in La2CuO4+δ

The anelastic spectrum (dynamic Young's modulus and elastic energy absorption) of La2CuO4+δ has been measured between 1 and 700 K with 0<δ<0.02. The spectrum of stoichiometric La2CuO4 in the low-temperature orthorhombic (LTO) phase is dominated by two intense relaxation processes which cause softenings of 16% around 150 K and 9% below 30 K at f∼1 kHz. The relaxation at 150 K is attributed to the presence of a fraction of the CuO6 octahedra which are able to change their tilted configuration by thermal activation between orientations which are nearly energetically equivalent, possibly within the twin boundaries. The relaxation below 30 K is governed by tunneling, and involves a considerable fraction of the lattice atoms. It is proposed that the double-well potentials for the low-temperature relaxation are created by the tendency of the LTO phase to form low-temperature tetragonal (LTT) domains, which however are not stabilized like when La is partially substituted with Ba. On doping with excess O, the relaxation rates of these processes are initially enhanced by hole doping, while their intensities are depressed by lattice disorder; an explanation of this behavior is provided. Excess O also causes two additional relaxation processes. The one appearing at lower values of δ is attributed to the hopping of single interstitial O2- ions, with a hopping rate equal to τ-1=2×10-14exp(-5600/T) s. The second process is slower and can be due to O pairs or other complexes containing excess O.

Electric and magnetic properties of polymer electrolyte/carbon black composites

Measurements of 1H Nuclear Magnetic Resonance (NMR) relaxation times, Electron Paramagnetic Resonance (EPR) and AC Impedance Spectroscopy (IS) are reported for composites based on PEO8:LiClO4 and carbon black (CB), prepared by two methods: solvent and fusion processing. Three nuclear relaxation processes were identified for 1H nuclei: (i) belonging to the polymer chains in the amorphous phase, loosely bound to the CB particles, whose dynamics is almost the same as for unfilled polymer, (ii) belonging to the polymer chains which are tightly attached to the CB particles, and (iii) belonging to the crystalline phase in the loose polymer chain. The paramagnetic electronic susceptibility of the composite samples, measured by EPR, was interpreted by assuming a contribution of localized spin states that follow a Curie law, and a Pauli-like contribution of delocalized spins. A significant change of the EPR linewidth was observed at 40 K, which is the temperature where the Curie and Pauli susceptibilities equally contribute to the paramagnetic electronic susceptibility. The electrical properties are very sensitive to the preparation methods of the composites, which conditions the interaction between carbon particle-carbon particle and carbon particle-polymer chain. Classical statistic models to describe the conductivity in these media were not satisfactory. © 1998 Published by Elsevier Science B.V. All rights reserved.

Fractal approach to ac impedance spectroscopy studies of ceramic materials

A novel fractal model for grain boundary regions of ceramic materials was developed. The model considers laterally inhomogeneous distribution of charge carriers in the vicinity of grain boundaries as the main cause of the non-Debye behaviour and distribution of relaxation times in ceramic materials. Considering the equivalent circuit the impedance of the grain boundary region was expressed. It was shown that the impedance of the grain boundary region has the form of the Davidson-Cole equation. The fractal dimension of the inhomogeneous distribution of charge carriers in the region close to the grain boundaries could be calculated based on the relation ds = 1 + β, where β is the constant from the Davidson-Cole equation.

Enhanced frequency upconversion in Er3+ doped fluoroindate glass due to energy transfer from Tm3+

Energy transfer processes between Er3+ and Tm3+ were investigated examining the frequency upconversion emissions in a fluoroindate glass pumped at 790 nm. A 60-fold enhancement in the emission at ≈670 nm originating from Er3+ was observed when Tm3+ at concentration of 2% was introduced in a sample containing 2% of Er3+. The results are explained considering the influence of cross-relaxation processes between the active ions. © 2002 Elsevier Science B.V. All rights reserved.

Transparent Er3+-activated lead fluorogermanate glass ceramics

Transparent glass ceramics containing β-PbF2:Er 3+ nanocrystals were obtained through appropriate thermal treatments of a glass of molar composition 60PbGeO3-10PbF2-30CdF 2 doped with 0.5 mol% Er3+. Their optical properties, as well as upconversion processes among erbium ions in the glass and glass ceramic matrix were studied. From absorption spectra, Judd-Ofelt parameters and radiative transition rates for several excited levels were calculated. Emission spectra in the visible and NIR regions were collected, and stimulated emission cross sections were obtained by McCumber theory for the 4F 13/2→4I15/2 transition at 1.5 μm. Red and green upconversion emissions were measured in glass and glass ceramics upon excitation at 980 nm; lifetimes were measured in order to assess the upconversion mechanisms.

Anelastic spectroscopy in TiO2

Titanium dioxide (rutile) has a lot of interesting and useful features and hence is widely utilized for application. It has been used as white pigment, photocatalyst, biocompatible material and semiconductor material used in solar battery. In semiconducting TiO2 oxygen vacancies are said to play an important role in the electrical conduction. Measurements of the elastic energy loss and modulus (anelastic spectroscopy) as a function of temperature can distinguish among the different atomic jumps, which occur in the various phases or at different local ordering. In this paper, it is reported anelastic relaxation measurements in TiO2 samples using a torsion pendulum operating in frequencies around 40Hz, in the temperature range between -173°C to 330°C with heating rate of 1°C/min. The results shown a reduction in the elasticity modulus with the increase in the corn starch content used for this consolidation.

Anelastic spectroscopy in superconducting oxides

Since the discovery of the high Tc superconductors, several works have been made about the different properties of these materials. Anelastic spectroscopy experiments are sensitive tools to the study of defects in solids and phase transitions. By this technique, we can distinguish the different types of atomic jumps that happen to different temperatures. The intensity of the peaks in the anelastic spectrum and the step in the torsional modulus are related with the concentration of the relaxing entities, and the position of the peaks is determined by its mobility. In this paper, the study on Bi and Sm based superconducting oxides was made by anelastic relaxation measurements using a torsion pendulum. The samples were submitted to successive thermal treatments in high vacuum, in the temperature range between 100 K and 650 K, heating rate about 1 K/min. For Bi based superconducting oxides the results shown two peaks, that were associated to interstitial oxygen mobility and to orthorhombic to monoclinic phase transition. For Sm based superconducting oxides the results shown a relaxation peak that was attributed to the jumps of the oxygen atoms in the inter-chains O1 and 05 of the lattice.

Lead-cadmium fluorogermanate glasses and transparent glassceramics. Spectroscopy and structure

In Lead-cadmium fluorogermanate glasses (PbF2-CdF 2-PbGeO3) the addition of metal fluorides to the base PbGeO3 glass leads to a decrease of the glass transition temperature (Tg) and to an enhancement of the ionic conductivity properties. Based on different spectroscopic techniques (19F NMR, Ge K-edge X-ryas absorption and Raman scattering) an heterogeneous glass structure is proposed at the molecular scale, which can be described by fluoride rich regions permeating the metagermanate chains. The temperature dependence of the 19F NMR lineshapes and relaxation times exhibits the qualitative and quantitative features associated with the high fluoride mobility in these systems. Eu 3+ emission and vibronic spectra are used to follow the crystallization process leading to transparent glass ceramics.

Mechanical damping of the snoek peak in tantalum - Oxygen system

Interstitial solutes in body-centered cubic metals, such as oxygen in tantalum, produce ideally Snoek effects when they are in solutions enough diluted. However, for higher concentration of these solutes, more complex relaxation process can occur, as interaction between interstitial solutes and dislocations. Anelastic relaxation measurements were carried out in polycrystalline tantalum samples, using torsion pendulum inverted, operating between 300 K and 680 K and oscillation frequencies in the hertz bandwidth, for three different experimental sample conditions: as received sample, annealed and annealed followed by a treatment in an oxygen atmosphere. These measurements have revealed the following behavior: the intensity of the internal friction peak associated to matrix-interstitial interaction Ta-O decreased between the first run and the next runs, and this phenomenon did not occur for the others conditions. The variation of relaxation strength of Ta-O peak, with number of runs is due to a decrease of an amount of oxygen in solid solution, which can be associated with the precipitation of new phases in Ta sample and with the trapping of oxygen atoms by dislocations.

Diffusion phenomena of the oxygen and nitrogen in niobium by mechanical spectroscopy

The short-range diffusion phenomenon (Snoek Effect) was investigated by mechanical spectroscopy measurements between 300 K and 650 K, in a polycrystalline niobium sample, containing oxygen and nitrogen, using a torsion pendulum. Experimental spectra of anelastic relaxation were obtained under three conditions: as-received sample; annealed sample and subsequently annealed in an oxygen atmosphere for three hours at 1170 K in partial pressure of 5°10 -5mbar. The experimental spectra obtained were decomposed in elementary Debye peaks and the anelastic relaxation processes were identified. With anelastic relaxation parameters and the lattice parameters, the interstitial diffusion coefficients of the oxygen and nitrogen in niobium were calculated for each kind of preferential occupation (octahedral and tetrahedral). The results were compared with the literature data, and confirmed that the best adjustment is for the preferential occupation octahedral model for low concentrations of interstitial solutes, but at higher concentration of oxygen were observed deviations of experimental data for the interstitial diffusion coefficients of oxygen in niobium when compared with the literature data, this could be related to the possible occurrence of a double occupation of interstitial sites in the niobium lattice by oxygen interstitials. © (2010) Trans Tech Publications.

Upconversion luminescence in Er3+ doped Ga10Ge 25S65 glass and glass-ceramic excited in the near-infrared

The infrared-to-visible frequency upconversion was investigated in Er 3+-doped Ga10Ge25S65 glass and in the transparent glass-ceramic obtained by heat-treatment of the glass above its glass-transition temperature. Continuous-wave and pulsed lasers operating at 980 nm and 1480 nm were used as excitation sources. The green (2H 11/2 → 4I15/2; 4S3/2 → 4I15/2) and red (4F9/2 → 4I15/2) photoluminescence (PL) signals due to the Er3+ ions were characterized. The PL decay times were influenced by energy transfer among Er3+ ions, by cross-relaxation processes and by energy transfer from the Er3+ ions to the host material. The PL from the Er3+ ions hosted in the crystalline phase was distinguished only when the glass-ceramic was excited by the 1480 nm pulsed laser. The excitation pathways responsible for the green and red PL bands are discussed to explain the differences between the spectra observed under continuous-wave and pulsed excitation. © 2013 American Institute of Physics.

Estudo de propriedades anelásticas de MgB2

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efeito de elementos intersticiais nas propriedades anelásticas do aço 316L usado como biomaterial

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)