Production and characterization of Tm3+/Yb3+ codoped waveguides based on PbO-GeO2 thin films

Fabrication and optical characterization of Tm3+/Yb3+ codoped PbO-GeO2 (PGO) pedestal-type waveguides are investigated in this work. It is important to mention that, to the best of authors' knowledge, the use of PGO pedestal-type waveguide has not been studied before. PGO thin films codoped with Tm3+ and Yb3+ were obtained through RF magnetron sputtering technique. The pedestal profile was obtained using conventional optical lithography procedures, followed by plasma etching and sputtering deposition. The profile of Tm3+/Yb3+ codoped PGO waveguides was observed by means of Scanning Electron Microscopy (SEM) measurements. Also the infrared and infrared-to-visible frequency upconversion luminescences of Tm3+ ions were measured exciting the samples with a cw 980 nm diode laser. Propagation losses around 11 dB/cm and 9 dB/cm were obtained at 630 and 1050 nm, respectively, for waveguides in the 20-100 μm width range. Single-mode propagation was observed for waveguides width up to 12 μm and 7 μm, at 1050 nm and 630 nm, respectively; larger waveguides width provided multi-mode propagation. The present results corroborate the possibility of using Tm3+/Yb3+ codoped PGO thin films as active waveguide for photonic applications. © 2013 Elsevier B.V. All rights reserved.

Nonlinear optical properties of Bi2O3-GeO2 glass at 800 and 532 nm

The nonlinear (NL) optical properties of glassy xBi2O 3-(1-x) GeO2 with x = 0.72 and 0.82 were investigated. The experiments were performed with lasers at 800 nm (pulses of 150 fs) and 532 nm (pulses of 80 ps and 250 ns). Using the Kerr gate technique, we observed that the NL response of the samples at 800 nm is faster than 150 fs. NL refraction indices, | n 2 | ≈ 5 × 10-16 cm2/W, and two-photon absorption coefficients, α 2, smaller than 0.03 cm/GW, were measured at 800 nm. At 532 nm, we measured the NL transmittance of the samples. From the results obtained, we determined α 2 ≈1 cm/GW and excited-state absorption cross-sections of ≈10-22 cm2 due to free-carriers. © 2013 AIP Publishing LLC.

Um estudo da dependência do índice de refração linear com a composição dos vidros teluretos dos sistemas TeO2-Li2O-TiO2 e TeO2-Li2O-WO3

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Vidros óxidos contendo átomos pesados para aplicações em óptica não linear e fotônica na região do infravermelho

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Non-centrosymmetric crystals of new N-benzylideneaniline derivatives as potential materials for non-linear optics

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparação e caracterização óptica de filmes de ORMOSIL obtidos via processo sol-gel dopados com azocorantes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Parameterization of bio-optical models for estimating chlorophyll-a concentration in a tropical eutrophic reservoir

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural and Electronic Effects of Incorporating Mn in TiO2 Films Grown by Sputtering: Anatase versus Rutile

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Erbium and ytterbium co-doped SiO2 : GeO2 planar waveguide prepared by the sol-gel route using an alternative precursor

The sol-gel method combined with a spin-coating technique has been successfully applied for the preparation of rare-earth doped silica:germania films used for the fabrication of erbium-doped waveguide amplifiers (EDWA), presenting several advantages over other methods for the preparation of thin films. As with other methods, the sol-gel route also shows some drawbacks, such as cracks related to the thickness of silica films and high hydrolysis rate of certain precursors such as germanium alkoxides. This article describes the preparation and optical characterization of erbium and ytterbium co-doped SiO2:GeO2 crack-free thick films prepared by the sol-gel route combined with a spin-coating technique using a chemically stable non-aqueous germanium oxide solution as an alternative precursor. The non-crystalline films obtained are planar waveguides exhibiting a single mode at 1,550 nm with an average thickness of 3.9 mu m presenting low percentages of porosity evaluated by the Lorentz-Lorenz Effective Medium Approximation, and low stress, according to the refractive index values measured in both transversal electric and magnetic polarizations. Weakly confining core layers (0.3% < Delta n < 0.75%) were obtained according to the refractive index difference between the core and buffer layers, suggesting that low-loss coupling EDWA may be obtained. The life time of the erbium I-4(13/2) metastable state was measured as a function of erbium concentration in different systems and based on these values it is possible to infer that the hydroxyl group was reduced and the formation of rare-earth clusters was avoided.

Photoluminescence in ZrO2 doped with Y and La

O objetivo deste trabalho é descrever a síntese e a caracterização óptica de uma solução sólida de óxido de zircônio contendo ítrio e lantânio. Foram misturados citrato de zircônio, nitrato de ítrio e nitrato de lantânio nas proporções 94 mol% ZrO2-6 mol% Y2O3 e 92 mol% ZrO2-6 mol % Y2O3-2 mol % La2O3. A análise de espectroscopia de absorção no infravermelho com tranformada de Fourier mostra material orgânico em decomposição e a análise térmica mostra a transformação de fases da zircônia tetragonal para monoclínica, a perda de água e a desidroxilação do zircônio. A análise por difração de raios X mostra formação de fases homogênea de ZrO2-Y2O3-La2O3 demonstrando que a adição de lantânio não provoca formação de fases, promovendo uma solução sólida baseada em zircônia cúbica. Os espectros de fotoluminescência mostram bandas de absorção em 562 nm e 572 nm (350 ºC) e bandas de absorção específicas em 543 nm, 561 nm, 614 nm e 641 nm (900 ºC). O efeito fotoluminescente a baixas temperaturas é causado por defeitos como (Y Zr,Y O)', (2Y Zr,V O)'' e V O. As emissões em 614 nm e 641 nm são causadas pela transição O-2p -> Zr-4d. Uma emissão em 543 nm pode ser atribuída a centros LaO8 com transição O-2p -> La-5d.

Fabrication and analysis of self-assembled photonic crystals structures

This paper presents the fabrication and analysis of a three-dimensional FCC photonic crystal (PhC) based on a self-assembly synthesis of monodispersive latex spheres. Experimental optical characterization, achieved by measurements of the specular reflectance under variable angles, indicated the clear presence of a Bragg diffraction pattern. Results are further explored by theoretical calculations based on the Finite Difference Time Domain (FDTD) method to determine the full PhC band structure.

Organic-inorganic hybrids prepared by carboxylic acid solvolysis: Planar waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In(PO3)3 stabilised fluoroindate glasses

Results on thermal and optical characterization of new lanthanide containing fluoroindate glasses in the system InF3-BaF2-In(PO3)3 are presented. Good optical quality and very stable glasses presenting up to 5 mm in thickness could be prepared in this system. Thermal analysis, Raman scattering and Eu3+ luminescence were the techniques utilized. A novel method for In(PO3)3 synthesis is proposed and the dependence of physical properties and structural features on the polyphosphate content is stressed. © 1998 Elsevier Science S.A.

Broadband NIR emission in novel sol-gel Er3+-doped SiO 2-Nb2O5 glass ceramic planar waveguides for photonic applications

This paper reports on the sol-gel preparation and structural and optical characterization of new Er3+-doped SiO2-Nb 2O5 nanocomposite planar waveguides. Erbium-doped (100-x)SiO2-xNb2O5 waveguides were deposited on silica-on-silicon substrates and Si(1 0 0) by the dip-coating technique. The waveguides exhibited uniform refractive index distribution across the thickness, efficient light injection at 1538 nm, and low losses at 632 and 1538 nm. The band-gap values lied between 4.12 eV and 3.55 eV for W1-W5, respectively, showing an excellent transparency in the visible and near infrared region for the waveguides. Fourier Transform Infrared (FTIR) Spectroscopy analysis evidenced SiO2-Nb2O5 nanocomposite formation with controlled phase separation in the films. The HRTEM and XRD analyses revealed Nb2O5 orthorhombic T-phase nanocrystals dispersed in a silica-based host. Photoluminescence (PL) analysis showed a broad band emission at 1531 nm, assigned to the 4I13/2 → 4I15/2 transition of the Er3+ ions present in the nanocomposite, with a full-width at half medium of 48-68 nm, depending on the niobium content and annealing. Hence, these waveguides are excellent candidates for application in integrated optics, especially in EDWA and WDM devices. © 2012 Elsevier B.V. All rights reserved.

Lead-germanate glasses and fibers: A practical alternative to tellurite for nonlinear fiber applications

We report on the fabrication of novel lead-germanate glasses and fibers. We have characterized these glasses in terms of their thermal properties, Raman spectra and refractive indices (both linear and nonlinear) and present them as viable alternatives to tellurite glasses for applications requiring highly nonlinear optical fibers. © 2013 Optical Society of America.