Diffusion and interface controlled reactions in alpha-(Cu-Al-Ag) alloys

The isothermal kinetics of Ag precipitation was studied in Cu-Al-Ag alloys with concentrations ranging from 2 to 8 wt.%Al and 2 to 12 wt.%Ag, using scanning electron microscopy (SEM), X-ray energy dispersive spectroscopy (EDX) and microhardness measurements. The results indicated a change in the precipitates growing mechanism from diffusion to interface controlled process, probably due to a change in the nature of the interface with the Ag and Al enrichment of the precipitates. (C) 2006 Elsevier B.V. All rights reserved.

Vehicle influence on calcium hydroxide pastes diffusion in human and bovine teeth

The purpose of this study was to compare the pH and calcium ion liberation after use of calcium hydroxide pastes with different paste vehicles in human or bovine teeth. Ninety-two single-rooted human and bovine roots were used. The roots were instrumented and an external cavity preparation was performed. The roots were divided in to human and bovine groups. Each group was subdivided into four subgroups (SB) according to the vehicle:SB1, detergent; SB2, saline; SB3, polyethylenoglycol + camphorated paramonochlorophenol (Calen PMCC) and SB4, polyethylenoglycol + furacyn paramonochlorophenol (FPMC). Specimens were immersed into saline solution at 37 degrees C and after 7 and 14 days pH and calcium ion measurements were made. The results were analyzed by ANOVA and Tukey tests (P < 0.05). There was no statistical difference between bovine and human teeth in the pH analysis (P < 0.05), but bovine teeth provided larger calcium ion liberation than human teeth. Calen PMCC was statistically more effective for pH increase and calcium ion liberation in all analyses, followed by FPMC and saline. Detergent showed the lowest pH alterations and calcium ion liberation. The period of 14 days showed more calcium ionic liberation than the 7-day period.

The effects of ice-water storage on blood gas and acid-base measurements

Objective: To determine the effects of storage of arterial and venous blood samples in ice water on blood gas and acid-base measurements.Design: Prospective, in vitro, laboratory study.Setting: School of veterinary medicine.Subjects: Six healthy dogs.Measurements and main results: Baseline measurements of partial pressure of oxygen (PO2), partial pressure of carbon dioxide (PCO2), pH, hemoglobin concentration (tHb), oxyhemoglobin saturation, and oxygen content (ContO(2)) were made. Bicarbonate (HCO3) and standard base excess (SBE) were calculated. Arterial and venous blood samples were separated into 1 and 3 mL samples, anaerobically transferred into 3 mL plastic syringes, and stored in ice water for 6 hours. Measurements were repeated at 15, 30 minutes, and 1, 2, 4, and 6 hours after baseline measurements. Arterial (a) PO2 increased significantly from baseline after 30 minutes of storage in the 1 mL samples and after 2 hours in the 3 mL samples. Venous (v) PO2 was significantly increased from baseline after 4 hours in the 1 mL samples and after 6 hours in the 3 mL samples. The pHa significantly decreased after 2 hours of storage in the 1 mL samples and after 4 hours in the 3 mL samples. In both the 1 and 3 mL samples, pHv decreased significantly only after 6 hours. Neither the arterial nor the venous PCO2 values changed significantly in the 1 mL samples and increased only after 6 hours in the 3 mL samples. No significant changes in tHb, ContO(2), SBE, or HCO3 were detected.Conclusions: the PO2 of arterial and venous blood increased significantly when samples were stored in plastic syringes in ice water. These increases are attributable to the diffusion of oxygen from and through the plastic of the syringe into the blood, which occurred at a rate that exceeded metabolic consumption of oxygen by the nucleated cells.

Stepped light-induced transient measurements of photocurrent and voltage in dye-sensitized solar cells based on ZnO and ZnO:Ga

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SAXS measurements of the porosity in Cu(II)-doped SnO2 xerogels during crystallization

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

CH and C2 radicals characterization in natural gas turbulent diffusion flames

This paper reports the construction of an axisymmetric nonpremixed piloted jet burner, with well-defined initial and boundary conditions, known as the Delft burner, to assess turbulence-chemistry interaction in non-premixed turbulent flames. Detailed experimental information is described, involving hot-wire anemometry, thin-wire thermocouples and chemiluminescence visualization measurements. Radial profile of the axial mean velocity indicates excellent agreement between flow patterns developed within Delft installation and the one described herein. Chemiluminescence emissions from CH and C2 free-radicals were acquired with a CCD camera. Tomography reconstruction analysis was utilised to compare radical emissions and temperature spatial distributions. There was a strong dependence between temperature and CH/C 2 emissions. This is an indication that these radicals can be used in flame front studies.

Anelastic relaxation due to interstitial solutes diffusion in Nb and Nb-1 wt% Zr

Metals and alloys containing solute atoms dissolved interstitially often show anelastic behavior due to a process know as stress-induced ordering. The application of mechanical spectroscopy measurements to diffusion studies in body-centered cubic metals has been extensively used in the last decades. However the kind of preferential occupation of interstitial solutes in body-centered cubic metals is still controversial. The anelastic properties of the Nb and Nb-1 wt% Zr polycrystalline alloys were determined by internal friction and oscillation frequency measurements using a torsion pendulum inverted performed between 300K and 650K, operating in a frequency oscillation in the hertz bandwidth. The interstitial diffusion coefficients of oxygen and nitrogen in Nb and Nb-1 wt% Zr samples were determined at two distinct conditions: (a) for low concentration of oxygen and (b) for high concentration of oxygen.

Initial concentration profile influence on migration measurements from plastic packaging: A simulation study

Migration of components from plastic packaging into foodstuffs or into medicines is a very important issue, concerning public health. Using experimental techniques, like gas chromatography-mass spectrometry, these essays measure total migration and specific migration of components from plastic packaging. This work presents an explanation and applications of a numerical technique tool for this measurement, allowing the comprehension of the diffusion process and the estimate of component migration in difficult or impractical measurements. As an application example, the non-uniform influence of initial concentration profile on the migration is presented, demonstrating the necessity of this profile determination for high quality considerations on involved metrology.

Diffusion phenomena of the oxygen and nitrogen in niobium by mechanical spectroscopy

The short-range diffusion phenomenon (Snoek Effect) was investigated by mechanical spectroscopy measurements between 300 K and 650 K, in a polycrystalline niobium sample, containing oxygen and nitrogen, using a torsion pendulum. Experimental spectra of anelastic relaxation were obtained under three conditions: as-received sample; annealed sample and subsequently annealed in an oxygen atmosphere for three hours at 1170 K in partial pressure of 5°10 -5mbar. The experimental spectra obtained were decomposed in elementary Debye peaks and the anelastic relaxation processes were identified. With anelastic relaxation parameters and the lattice parameters, the interstitial diffusion coefficients of the oxygen and nitrogen in niobium were calculated for each kind of preferential occupation (octahedral and tetrahedral). The results were compared with the literature data, and confirmed that the best adjustment is for the preferential occupation octahedral model for low concentrations of interstitial solutes, but at higher concentration of oxygen were observed deviations of experimental data for the interstitial diffusion coefficients of oxygen in niobium when compared with the literature data, this could be related to the possible occurrence of a double occupation of interstitial sites in the niobium lattice by oxygen interstitials. © (2010) Trans Tech Publications.

Nitrogen diffusion in niobium under low pressure

The interaction among heavy interstitial atoms present in metals with bcc structure is studied using anelastic spectroscopy. This technique makes it possible to obtain information on interstitial concentration, precipitation, solubility limit, and diffusion. The diffusion coefficients of nitrogen in niobium were obtained using the relaxation parameters obtained from anelastic spectroscopy measurements for different oscillation frequencies of the system. The results showed the interstitial diffusion of nitrogen present in solid solution in niobium when submitted to different charges of nitrogen at a temperature of 1373 K and a partial pressure in the order of 10-4 Torr. The exponential variation of the pressure experimentally in function of the time was thus obtained.

Diffusion of oxygen in Ti-15Mo-xZr alloys studied by anelastic spectroscopy

Because of their low elasticity modulus, titanium alloys have excellent biocompatibility, and are largely used in orthopedic prostheses. Among the properties that are beneficial for use in orthopedic implants is the elasticity modulus, which is closely connected to the crystal structure of the material. Interstitial elements, such as oxygen, change the mechanical properties of the material. Anelastic spectroscopy measurements are a powerful tool for the study of the interaction of these elements with the metallic matrix and substitutional solutes, providing information on the diffusion and concentration of interstitial elements. In this study, the effect of oxygen on the anelastic properties of alloys in the Ti-15Mo-Zr system was analyzed using anelastic spectroscopy measurements. The diffusion coefficients, pre-exponential factors, and activation energies of these alloys were calculated for oxygen.