Influence of artificial aging in marginal adaptation of mixed class V cavities

The aim of this study was to investigate whether the artificial aging by thermal cycling had influenced the marginal adaptation of class V restorations with/without chlorhexidine application in the bond process. Twelve intact human third molars were used. Class V cavity preparations were performed on the buccal surface and the teeth received 35% phosphoric acid-etching procedure (Ultradent Products Inc., South Jordan, Utah, USA). Subsequently, the samples were divided in two groups: Untreated acid-etched dentin and chlorhexidine application as an adjunct in the bond process. The adhesive Single Bond 2 (3M ESPE, St. Paul, MN, USA) was used after 2% chlorhexidine application, and the restorations were performed with FiltekTM Z350 XT (3M ESPE) composite resin. The specimens were submitted to artificial aging by thermal cycling with 3,000 cycles. Analyzes were performed on scanning electron microscopy using replicas of marginal adaptation in percentage of continuous margin before and after the artificial aging. The data were analyzed by paired test and the results showed statistically significant differences in the percentage of continuous margin with/without chlorhexidine treatment before and after thermal cycling. This study concluded that the artificial aging by thermal cycling influenced the marginal adaptation of mixed class V composite restorations.

Análise da penetração de material resinoso ao esmalte dental em função de agente clareador e tempo

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The effect of an Er,Cr:YSGG laser on external adaptation of healthy and decayed cavities

The aim of this study was to evaluate the influence of chlorhexidine and Er, Cr:YSGG laser irradiation on the bond strength and external adaptation in mixed healthy and caries-affected class V cavities before and after thermal cycling. Thirty-six cavity preparations were made in mixed class V buccal human molars, half of them being artificially caries-induced. Any remaining affected dentin was removed from the cavity with a round burr at low speed. The teeth were divided into six groups, according to cleaning agent for both healthy and caries-induced dentin: no treatment, chlorhexidine and erbium, chromium-doped: yttrium, scandium, gallium, garnet (Er,Cr:YSGG) laser irradiation. A Filtek P90 (3M ESPE, St Paul, MN, USA) silorane adhesive restorative system was used. The specimens were subjected to 5000 thermal cycles (5-55 degrees C 60 min). Epoxy replicas were obtained to characterize the external adaptation under scanning electron microscopy. The average percentages of non-continuous margins were 5.41% and 6.49% in enamel dentin before thermal cycling and 25% and 33.7% after thermal cycling, respectively. The caries-affected and laser irradiated cavities showed higher non-continuous margins. Thermal cycling was able to raise the percentage of non-continuous margin for all groups. Chlorhexidine did not affect the marginal adaptation results, and the Er,Cr:YSGG laser irradiation showed significantly worse results compared with the control group.

Marginal adaptation of Class V restorations with current generation dentin-bonding agents: effect of different dentin surface treatments.

This study sought to assess the use of chlorhexidine with several excipients as a dentin surface treatment and its effect on marginal adaptation of class V restorations with current-generation dentin bonding agents. A total of 120 human third molars were selected and allocated into 12 groups, with standardized buccal class V restorations randomly divided into preconditioned dentin rinsed with: water; water + chlorhexidine; ethanol; or ethanol + chlorhexidine. After rinsing of dentin (previously conditioned with 35% phosphoric acid) with the test solutions, the Adper single bond 2, prime and bond 2.1, and Excite bonding systems were applied randomly. Restorations were performed with FiltekTM Z350 XT composite resin. The resulting specimens were subjected to thermal and mechanical load cycling. Quantitative analysis of marginal adaptation was performed on epoxy replicas by means of scanning electron microscopy. Results were assessed by means of the Kruskal-Wallis test (percentages of continuous margins) and Wilcoxon test (differences between percentages of continuous margins before and after thermal cycling and mechanical loading), at a significance level of p < 0.05. Outcomes in the chlorhexidine-treated groups were not superior to those obtained with other treatments.

Evaluation of dental restorations: a comparative study between clinical and digital photographic assessments

The aim of this study was to compare the efficacy of a direct clinical evaluation method with an indirect digital photographic method in assessing the quality of dental restorations. Seven parameters (color, occlusal marginal adaptation, anatomy form, roughness, occlusal marginal stain, luster, and secondary caries) were assessed in 89 Class I and Class II restorations from 36 adults using the modified US Public Health Service/Ryge criteria. Standardized photographs of the same restorations were digitally processed by Adobe Photoshop software, separated into the following four groups and assessed by two calibrated examiners: Group A: The original photograph displayed at 100%, without modifications (IMG100); Group B: Formed by images enlarged at 150% (IMG150); Group C: Formed by digital photographs displayed at 100% (mIMG100), with digital modifications (levels adjustment, shadow and highlight correction, color balance, unsharp Mask); and Group D: Formed by enlarged photographs displayed at 150% with modifications (mIMG150), with the same adjustments made to Group C. Photographs were assessed on a calibrated screen (Macbook) by two calibrated clinicians, and the results were statistically analyzed using Wilcoxon tests (SSPS 11.5) at 95% CI. Results: The photographic method produced higher reliability levels than the direct clinical method in all parameters. The evaluation of digital images is more consistent with clinical assessment when restorations present some moderate defect (Bravo) and less consistent when restorations are clinically classified as either satisfactory (Alpha) or in cases of severe defects (Charlie). Conclusion: The digital photographic method is a useful tool for assessing the quality of dental restorations, providing information that goes unnoticed with the visual-tactile clinical examination method. Additionally, when analyzing restorations using the Ryge modified criteria, the digital photographic method reveals a significant increase of defects compared to those clinically observed with the naked eye. Photography by itself, without the need for enlargement or correction, provides more information than clinical examination and can lead to unnecessary overtreatment.