Estudo da segregação de dopantes no contorno de grão e sua influência nas propriedades elétricas de cerâmicas à base de 'SN''O IND.2'

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC

A series of four different powders ceria doped Ce1-xErxO2-delta (0.05 <= x <= 0.20) were synthesized by applying self-propagating reaction at room temperature (SPRT method). SPRT procedure is based on the self-propagating room temperature reaction between metal nitrates and sodium hydroxide, wherein the reaction is spontaneous and terminates extremely fast. The method is known to assure very precise stoichiometry of the final product in comparison with a tailored composition. XRPD, Raman spectroscopy, TEM and BET measurements were used to characterize the nanopowders at room temperature. It was shown that all obtained powders were single phase solid solutions with a fluorite-type crystal structure and all powder particles have nanometric size (about 3-4 nm). Densification was performed at 1550 degrees C, in an air atmosphere for 2 h. XRPD, SEM and complex impedance method measurements were carried out on sintered samples. Single phase form was evidenced for each sintered materials. The best value of conductivity at 700 degrees C amounted to 1.10 x 10(-2) Omega(-1) cm(-1) for Ce0.85Er0.O-3(2-delta) sample. Corresponding activation energies of conductivity amounted to 0.28 eV in the temperature range 500-700 degrees C. (C) 2015 Elsevier B.V. All rights reserved.

Toward the Optimization of an e-Tongue System Using Information Visualization: A Case Study with Perylene Tetracarboxylic Derivative Films in the Sensing Units

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estimativa da composição corporal e análise de concordância entre analisadores de impedância bioelétrica bipolar e tetrapolar

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Espectroscopia de impedância no laboratório de ensino

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of thickness coating on the electrochemical behaviour of thermal spray Cr3C2-NiCr coatings

Thermally sprayed HVOF coatings are increasingly being used in industrial applications where high wear and corrosion resistance are needed [1,2]. In this paper, electrochemical ac and de experiments were used in order to obtain the corrosion resistance of coated steel with different numbers of Cr3C2-NiCr layers. This work has been performed in order to determine the role of coating thickness in the corrosion behaviour of a steel protected with cermet thermally sprayed coatings. It is known that a thicker layer protects better against corrosion when a metallic coating is evaluated. But cermet coatings, such as Cr3C2-NiCr, contain higher levels of porosity and residual stresses than metallic coatings, which really could influence the corrosion resistance of the deposited layer. Electrochemical measurements, such as Open-Circuit Potential (E-Osubset of), Polarisation Resistance (RP) and Cyclic Voltammetry (CV), were performed in an aerated 3.4 NaCI media (%wt.). Electrochemical Impedance Measurements (EIS) were also done in order to obtain a mechanism that explains the corrosion process. Structural Characterisation was carried out by means of Optical and Scanning Electron Microscopes (OM, SEM) with an Energy Dispersive Spectrometry analyser (EDS). Results show that the corrosion resistance of the complete system is mainly influenced by the substrate behaviour. The application of a higher number of deposited layers did not substantially increase their anticorrosive properties. Stress generation during the spraying deposition process plays an important role in the behaviour of the coated steel against corrosion phenomena. (C) 2002 Elsevier B.V. B.V All rights reserved.

Effect of cerium on structure modifications of a hybrid sol-gel coating, its mechanical properties and anti-corrosion behavior

An organic-inorganic hybrid coating was developed to improve the corrosion resistance of the aluminum alloy AA 2024-T3. Organic and inorganic coatings derived from glycidoxypropyltrimethoxysilane (GPTMS) and aluminum tri-sec-butoxide Al((OBu)-Bu-s)(3), with different cerium contents, were deposited onto aluminum by dip-coating process. Corrosion resistance and mechanical properties were investigated by electrochemical impedance measurements and nano-indentation respectively. An optimal cerium concentration of 0.01 M was evidenced. To correlate and explain the hybrid coating performances in relation to the cerium content, NMR experiments were performed. It has been shown that when the cerium concentration in the hybrid is higher than 0.01 M there are important modifications in the hybrid structure that account for the mechanical properties and anti-corrosion behavior of the sol-gel coating. (C) 2012 Elsevier Ltd. All rights reserved.

Effect of cerium (IV) ions on the anticorrosion properties of siloxane-poly(methyl methacrylate) based film applied on tin coated steel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Relationship between grain-boundary capacitance and bulk shallow donors in SnO2 polycrystalline semiconductor

The relationship between grain-boundary capacitance and extrinsic shallow donors caused by Nb addition to SnO2 center dot COO binary polycrystalline system has been investigated by means of combined techniques such as I-V characteristic response, complex impedance and capacitance analysis and electrostatic force microscopy. The estimated role of the Nb doping is to increase the concentration of shallow donors that are capable of enhancing the electronic donation to grain-boundary acceptors. This effect leads to the formation of potential barriers at grain boundaries with a simultaneous increase of grain-boundary capacitance and non-Ohmic features of the polycrystalline device doped with Nb atoms.

Eletrodo de pasta de carbono em minicavidade de contato sólido

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The use of Langmuir-Blodgett films of a perylene derivative and polypyrrole in the detection of trace levels of Cu2+ ions

Langmuir films of a tetracarboxylic perylene derivative and polypyrrole display condensed surface pressure isotherms that are shifted when Cu2+ ions are added to the ultrapure water subphase. These films were transferred onto interdigitated gold electrodes leading to Y-type Langmuir-Blodgett (LB) films. The electrodes modified with 5-layer LB films were immersed into a flask with ultrapure water and water containing Cu2+ ions at concentrations ranging from mM to muM. Impedance measurements indicated a distinct electrical response for the two types of films. Although the materials chosen have no specificity for ionic metals, they can be combined for detecting trace levels of Cu2+, which may be exploited in water quality monitoring. (C) 2004 Elsevier B.V. All rights reserved.

Metal-insulator transitions and magnetic ordered states in oxygen-depleted manganites

The use of AC/DC magnetic susceptibility and impedance measurements to detect oxygen depletion effects in La0.7Ca0.3MnO3 +/-delta and NiMn2O4+delta spinel-type compounds is reported. For the NiMn2O4, for which no Mn4+ was found, three superposed Debye relaxations were observed in the range 260-180 K. Otherwise, in La0.7Ca0.3MnO3, the argon annealed has contributed to a decrease in T-C, but the amount of Mn4+ is still too high to allow the observation of a relaxation in this frequency window. (c) 2006 Elsevier B.V. All rights reserved.

Siloxane-polypropyleneoxide hybrid ormolytes: structure-ionic conductivity relationships

Siloxane-polypropyleneoxide (PPO) hybrids doped with sodium perchlorate (NaClO4) obtained by the sol-gel process were prepared with two PPO molecular weights (2000 and 4000 g/mol) and two sodium concentrations such as [O]/[Na] = 4 and 15 (O being the ether-type oxygen of PPO chains). The structure of these hybrids was investigated by Na-23 nuclear magnetic resonance (NMR) and X-ray absorption spectroscopy at the sodium K-edge (1071.8 eV) whereas complex impedance spectroscopy was used to determine their ionic conductivity. Three sodium sites were determined by NMR. The conjunction of NMR and X-ray absorption results allows us to identify one site in which Na is in a NaCl structure, a second one in which Na is in contact with perchlorate anions. The third site is attributed to mobile sodium species in interaction with the polymeric chain. The relative proportion of the different sites in the materials determines the ionic conductivity of the materials at room temperature: the largest ionic conductivity is 8.9 x 10(-6) Omega(-1) cm(-1) and is observed on the material with the larger amount (at least 85%) of sites in which sodium interacts with the polymer. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Effect of salt nature on structure and ionic conductivity of sodium-doped siloxane-PPO ormolytes

Siloxane-polyoxypropylene (PPO) hybrids obtained by the sol-gel process and containing short polymer chain have been doped with different sodium salts NaX (X = ClO4, BF4 or I). The effect of the counter-ion (X) on the chemical environment of the sodium ions and on the ionic conductivity of these hybrids was investigated by Na-23 NMR, small angle X-ray scattering (SAXS), complex impedance, Raman spectroscopy and differential scanning calorimetry (DSC). Results reveal that the different sodium salts have essentially the same effect on the nanoscopic structure of the hybrids. The formation of immobile Na+ cations involved in NaCl-like species could be minimized by using a low amount of HCl as hydrolytic catalyst. The differences in the ionic conductivity of hybrids doped with different sodium salts were correlated with the proportion of Na ions solvated by ether-type oxygen of the polymeric chains and by the carboxyl oxygen located in the urea groups of the PPO chain extremities. (c) 2005 Elsevier Ltd. All rights reserved.

Dielectric thermal analysis as a tool for quantitative-evaluation of the viscosity and the kinetics of epoxy resin cure

Dielectric thermal analysis has been proved as a valuable tool for monitoring the epoxy curing process and the related rheological properties in the fabrication of polymer-matrix composite materials. This technique also has the potential to be applied in the monitoring of magnet impregnation processes as well as in quality control. In this work we present the quantitative evaluation of the viscosity changing and the curing kinetics for a commercial Stycast epoxy resin system at different temperatures through the impedance analysis. The results showed correlation between the real component of the complex impedance and the isothermal reaction extent. Comparing the dielectric analysis result with the viscosity measured by rotational rheometer we observed a similar behavior reported for dynamic mechanic analysis. The results comparison have shown that the kinetics parameters obtained from DSC and DETA analysis showed different sensitivities related to the characteristics of curing stages. We concluded that the dielectric thermal analysis should be applied in quantitative evaluation of cure kinetics.