Inhibition of demineralization in vitro around amalgam restorations

Objective: The purpose of this in vitro study was to evaluate some forms of preventing or avoiding demineralization within enamel cavity walls adjacent to amalgam restorations. Method and materials: Third molar teeth were sectioned to obtain 72 specimens, divided into one control and five experimental groups: amalgam only; varnish plus amalgam; acidulated phosphate fluoride plus amalgam; adhesive amalgam; glass-ionomer cement plus amalgam; control (amalgam only, not subjected to a demineralization challenge). The experimental groups were subjected to pH and thermal cycling and then submitted to enamel hardness determinations. Results: Significant differences between the treatment groups revealed that the bonded amalgam technique offered the best resistance to demineralization. The use of cavity varnish resulted in greater mineral loss than amalgam placed alone. Conclusion: The use of an adhesive system, glass-ionomer cement, or acidulated phosphate fluoride under amalgam restorations may interfere with development of secondary caries.

Microleakage in primary teeth restored by conventional or bonded amalgam technique.

The aim of this in vitro study was to evaluate marginal leakage in class V restorations in primary teeth restored with amalgam, using three different techniques. Thirty maxillary anterior primary teeth, clinically sound and naturally exfoliated, were used. In group 1 (n = 10), two thin layers of a copal varnish (Cavitine) were applied. In group 2 (n = 10), Scotchbond Multi-Purpose Plus, a dual adhesive system, was used according to manufacturer instructions. In group 3 (n = 10), One-Step adhesive system in combination with a low-viscosity resin (Resinomer) were used according to manufacturer instructions. All samples were restored with a high-copper dental amalgam alloy (GS 80, SDI). After restoration, the samples were stored in normal saline at 37 degrees C for 72 h. The specimens were polished, thermocycled (500 cycles, 5 degrees and 55 degrees C, 30-s dwell time) and impermeabilized with fingernail polish to within 1.0 mm of the restoration margins. The teeth were then placed in 0.5% methylene blue for 4 h. Finally, the samples were sectioned and evaluated for marginal leakage. The Kruskal-Wallis test showed that the filled adhesive resin (group 3) had the least microleakage. There was no significant difference between groups 1 and 2.

Indicators of the risk mechanics for Class-I and Class-II amalgam and composite resin restorations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Longitudinal results of a 10-year clinical trial of repair of amalgam restorations

The aim of this prospective, blind, and randomized clinical trial was to assess the effectiveness of repair of localized clinical defects in amalgam restorations that were initially scheduled for replacement. A cohort of 20 patients with 40 (Class I and Class II) amalgam restorations that presented one or more clinical features that deviated from the ideal (Bravo or Charlie) according to US Public Health Service criteria, were randomly assigned to either the repair or the replacement group—A: repair, n = 19; and B: replacement, n = 21. Two examiners who had calibration expertise evaluated the restorations at baseline and 10 years after according to seven parameters: marginal occlusal adaptation, anatomic form, surface roughness, marginal staining, contact, secondary caries, and luster. After 10 years, 30 restorations (75%) were evaluated (Group A: n = 17; Group B: n = 13). Repaired and replaced amalgam restorations showed similar survival outcomes regarding marginal defects and secondary caries in patients with low and medium caries risk, and most of the restorations were considered clinically acceptable after 10 years. Repair treatment increased the potential for tooth longevity, using a minimally interventional procedure. All restorations trend to downgrade over time.

Is there difference of Streptococcus mutans count and adherence on amalgam and resin occlusal restorations? A blind clinical study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Seal, replacement or monitoring amalgam restorations with occlusal marginal defects? Results of a 10-year clinical trial

The aim of this prospective and blind clinical trial was to assess the effectiveness of sealing localized marginal defects of amalgam restoration that were initially scheduled to be replaced. A cohort of twenty six patients with 60 amalgam restorations (n=44Class I and n=16Class II), that presented marginal defects deviating from ideal (Bravo) according to USPHS criteria, were assigned to either sealing or replacement groups: A: sealing n=20, Replacement n=20, and no treatment (n=20). Two blind examiners evaluated the restorations at baseline (K=0.74) and after ten years (K=0.84) according with USPHS criteria, in four parameters: marginal adaptation (MA), secondary caries (SC), marginal staining (MS) and teeth sensitivity (TS). Multiple comparison of restorations degradation/upgrade was analyzed by Friedman test and the comparisons within groups were performed by Wilcoxon test. After 10 years, 44 restorations were assessed (73.3%), Group A: n=14 and Group B: n=16; and Group C: n=14 sealing and replacement amalgam restorations presented similar level of quality in MA (p=0.76), SC (p=0.25) and TS (p=0.52), while in MS (p=0.007) presented better performance in replacement group after 10-years. Most of the occlusal amalgam restorations with marginal gaps showed similar long term outcomes than the restorations were sealed, replaced, or not treated over a 10-year period. Most of the restorations of the three groups were clinically acceptable, under the studied parameters. All restorations had the tendency to present downgrade/deterioration over time.

Surface Roughness Analysis of Four Restorative Materials Exposed to 10% and 15% Carbamide Peroxide

The aim of this study was to evaluate the effects of carbamide peroxide (CP) on surfaces of different restorative materials. Porcelain, composite resin, glass ionomer, and amalgam were analyzed in this study. Surface roughness (Ra) was measured before and after treatment with 10% and 15% CP. Fifteen percent CP increased Ra values in both the glass ionomer and amalgam subgroups, while 10% CP increased Ra values in the glass ionomer subgroup only. Changes in restorative material surfaces can be more severe when bleaching is completed without a clinician's supervision. Hence, thorough patient examinations must be done before, during, and after bleaching treatment. Int J Prosthodont 2011;24:155-157

Effect of prolonged erosive pH cycling on different restorative materials

This in vitro study evaluated the effect of a prolonged erosive pH cycling on the superficial microhardness change (SMHC) and the erosive wear of different restorative materials. Eighty enamel specimens with prepared cavities of 1.5 x 1.5 mm were randomly divided into eight groups according to the restorative materials used for the fillings (RMGI - resin-modified glass-ionomer, CGI - conventional glass-ionomer, CR- composite resin, A - amalgam) and immersion media used (ERO - erosive medium or SAL - artificial saliva). During 35 days, half of the specimens were immersed in a cola drink (ERO), for 5 min, three times a day, and they remained in SAL between the erosive cycles. The other half of the specimens was immersed in SAL only, for the entire experimental period (control). Data were tested for significant differences by anova and Tukey's tests (P < 0.05). Scanning electron microscopy images were made to illustrate the enamel erosive wear and restorative materials alterations. The mean SMHC (%) and mean erosive wear (mu m) of the materials were: RMGI-ERO (30/0.5); CGI-ERO (37/0.5); CR-ERO (-0.3/0.3); A-ERO (-4/0.3); RMGI-SAL (4/0.4); CGI-SAL (-6/0.4); CR-SAL (-3/0.2) and A-SAL (2/0.4). Scanning electron microscopy images showed pronounced enamel erosive wear on groups submitted to erosive pH cycling when compared with groups maintained in saliva. In conclusion, the prolonged pH cycling promoted significantly higher alterations (SMHC and erosive wear) on the glass-ionomer cements than the CR and amalgam.

In situ effect of an erosive challenge on different restorative materials and on enamel adjacent to these materials

Objectives: This in situ study evaluated the effect of an erosive challenge on different restorative materials and on enamel restored with these materials, as well as the ability of these materials to protect the adjacent enamel against erosion.Methods: Ten volunteers wore palatal devices with eight bovine enamel blocks, randomly selected and distributed into two vertical rows, corresponding to the following groups: GI/GV, resin-modified glass ionomer; GII/GVI, conventional glass ionomer; GIII/GVII, composite resin; GIV/GVIII, amalgam. one row (corresponding to groups I-IV) was immersed in a cola drink and the other row (corresponding to groups V-VIII) was subjected to saliva only. The palatal device was continuously worn for 7 days and only half of the appliance (groups I-IV) was immersed in the soft drink (Coca-Cola (R), 150 mL) for 5 min, three times a day. The study variables comprised the wear (profilometry, mu m) and the percentage of surface microhardness change (%SMHC). Data were tested for significant differences by two-way ANOVA and Tukey's tests (p < 0.05).Results: Considering the restorative materials, for %SMHC and wear, there were no differences among the materials and between the saliva and the erosive challenge. For enamel analyses, the erosive challenge promoted a higher wear and %SMHC of the enamel than did the saliva. There were no significant differences in wear and %SMHC of the enamel adjacent to the different restorative materials.Conclusion: This research data suggest that there is little %SMHC and wear of the studied restorative materials and none of them had a preventive effect against erosion on adjacent enamel, which showed a pronounced wear. (c) 2007 Elsevier Ltd. All rights reserved.

Effect of erosive pH cycling on different restorative materials and on enamel restored with these materials

This in vitro study evaluated the effect of erosive pH cycling on the percentage of surface micro-hardness change (%SMHC) and wear of different restorative materials and bovine enamel restored with these materials. Eighty enamel specimens were randomly divided into eight groups according to the restorative materials and immersion media used: GI/GV-resin-modifled glass-ionomer, GII/GVI-conventional glass-ionomer, GIII/GVII-resin composite and GIV/GVIII-amalgam. Over a period of seven days, groups GI to GIV were immersed in a cola drink (ERO) for 5 minutes, 3x/day and kept in artificial saliva between erosive cycles. Groups GV to GVIII were immersed in artificial saliva (SAL) throughout the entire experimental period (control). Data were tested for significant differences using ANOVA and Tukey's tests (p < 0.05). For %SMHC, considering the restorative materials, no significant differences were detected among the materials and immersion media. Mean wear was higher for the resin modified glass ionomer cement when compared to conventional cement, but those materials did not significantly differ from the others. For enamel analyses, erosive pH cycling promoted higher wear and %SMHC compared to saliva. There were no significant differences in wear and %SMHC of enamel around the different restorative materials, regardless of the distance from the restorative material (50, 150 or 300 mu m). In conclusion, there were only subtle differences among the materials, and these differences were not able to protect the surrounding enamel from erosion.