Investigation about the copper adsorption on the chloropropylsilica gel surface modified with a nanostructured dendrimer DAB-Am-16: an analytical application for determination of copper in different samples

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Fracture resistance of bleached teeth restored with different procedures

This study evaluated the fracture resistance of teeth submitted to internal bleaching and restored with different non-metallic post. Eighty mandibular incisors were endodontically treated and randomly divided in 10 groups (n = 8): G1- restored with composite resin (CR), G2- CR + fiber-reinforced composite post (FRC, Everstick post, Sticktech) cemented with resin cement self-etch adhesive (RCS, Panavia F 2.0, Kuraray), G3- CR + FRC + self-adhesive resin cement (SRC, Breeze, Pentral Clinical), G4- CR+ glass fiber post (GF, Exacto Post, Angelus) + RCS, G5- CR + GF + SRC. The G6 to G10 were bleached with hydrogen peroxide (HP) and restored with the same restorative procedures used for G1 to G5, respectively. After 7 days storage in artificial saliva, the specimens were submitted to the compressive strength test (N) at 0.5 mm/min cross-head speed and the failure pattern was identified as either reparable (failure showed until 2 mm below the cement-enamel junction) or irreparable (the failure showed <2 mm or more below the cement-enamel). Data were analyzed by ANOVA and Tukey test (α = 0.05). No significant difference (p < 0.05) was found among G1 to G10. The results suggest that intracoronal bleaching did not significantly weaken the teeth and the failure patterns were predominately reparable for all groups. The non-metallic posts in these teeth did not improve fracture resistance.

Influence of surface sealant on the translucency of composite resin: effect of immersion time and immersion media

This study evaluated the effect of surface sealant on the translucency of composite resin immersed in different solutions. The study involved the following materials: Charisma, Fortify and coffee, Coca-Cola®, tea and artificial saliva as solutions. Sixty-four specimens (n = 8) were manufactured and immersed in artificial saliva at 37 ± 1 °C. Samples were immersed in the solutions for three times a day and re-immersed in artificial saliva until the translucency readings. The measurements were carried out at nine times: T1 - 24 hours after specimen preparation, T2 - 24 hours after immersion in the solutions, T3 - 48 hours and T4 to T9 - 7, 14, 21, 30, 60 and 90 days, respectively, after immersion. The translucency values were measured using a JOUAN device. The results were subjected to ANOVA and Tukey's test at 5%. The surface sealant was not able to protect the composite resin against staining, the coffee showed the strongest staining action, followed by tea and regarding immersion time, a significant alteration was noted in the translucency of composite resin after 21 days.

Effect of antioxidant agents on bond strength of composite to bleached enamel with 38% hydrogen peroxide

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

WC-CoCr coatings sprayed by high velocity oxygen-fuel (HVOF) flame on AA7050 aluminum alloy: electrochemical behavior in 3.5% NaCl solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparison of crystallinity between natural hydroxyapatite and synthetic cp-Ti /HA coatings

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of shot peening on the fatigue strength of anodized Ti-6Al-4V alloy

The increasingly design requirements for modern engineering applications resulted in the development of new materials with improved mechanical properties. Low density, combined with excellent weight/strength ratio as well as corrosion resistance, make the titanium attractive for application in landing gears. Fatigue control is a fundamental parameter to be considered in the development of mechanical components. The aim of this research is to analyze the fatigue behavior of anodized Ti-6Al-4V alloy and the influence of shot peening pre treatment on the experimental data. Axial fatigue tests (R = 0.1) were performed, and a significant reduction in the fatigue strength of anodized Ti-6Al-4V was observed. The shot peening superficial treatment, which objective is to create a compressive residual stress field in the surface layers, showed efficiency to increase the fatigue life of anodized material. Experimental data were represented by S-N curves. Scanning electron microscopy technique (SEM) was used to observe crack origin sites.

Electronic ceramics based on polycrystalline SnO2, TiO2 and (Sn xTi1-x)O2 solid solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of rare earth oxides doping SnO2.(Co1/4,Mn3/4)O-based varistor system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of ceramic powders used in the inCeram systems to fixed dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of PVDF/HAP composites for medical applications

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Grain size effect on the electrical response of SnO2 thin and thick film gas sensors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Processing of high performance composites based on peek by aqueous suspension prepregging

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and mechanical properties of PVDF/PANI blends

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)