Effect of light energy density on conversion degree and hardness of dual-cured resin cement

This study evaluated the effect of different light energy densities on conversion degree (CD) and Knoop hardness number (KHN) of RelyX ARC (RLX) resin cement. After manipulation according to the manufacturer's instructions, RLX was inserted into a rubber mold (0.8 mm X 5 mm) and covered with a Mylar strip. The tip of the lightcuring unit (LCU) was positioned in contact with the Mylar surface. Quartz-tungsten-halogen (QTH) and light-emitting diode (LED) LCUs with light densities of 10, 20 and 30 J/cm2 were used to light-cure the specimens. After light curing, the specimens were stored dry in lightproof containers at 37°C. After 24 hours, the CD was analyzed by FT-Raman and, after an additional 24-hours, samples were submitted to Knoop hardness testing. The data of the CD (%) and KHN were submitted to two-way ANOVA and the Tukey's test (α=0.05). QTH and LED were effective light curing units. For QTH, there were no differences among the light energy densities for CD or KHN. For LED, there was a significant reduction in CD with the light energy density set at 10 J/cm2. KHN was not influenced by the lightcuring unit and by its light energy density. © Operative Dentistry.

Effect of weathering and thickness on roughness of acrylic resin and ocular button

Purpose: The aim of this study was to evaluate the roughness of colorless ocular button and four brands of colorless acrylic resins designed to fabricate ocular prosthesis as a function of weathering (1008 h) and different thickness (1 and 3.5 mm). Materials and methods: One-hundred-and-twenty specimens were fabricated and distributed in 12 groups. The analysis was carried out by means of digital roughness meter. Results: Data were analyzed statistically by ANOVA and Tukey test at 1% significance. The results showed that there was no statistically significant difference after the weathering period. Both the Vipi Cril acrylic resin with 3.5 mm in thickness and ocular button with 1 mm in thickness presented the lowest roughness values (0.12. Ra). Conclusion: The roughness of the acrylic resins and the ocular button was not affect by the weathering of 1008 h. However, the thickness of the specimens proved to have a major influence on roughness property. © 2010.

Effect of storage in artificial saliva and thermal cycling on Knoop hardness of resin denture teeth

Purpose: This study aimed to evaluate the effect of different storage periods in artificial saliva and thermal cycling on Knoop hardness of 8 commercial brands of resin denture teeth. Methods: Eigth different brands of resin denture teeth were evaluated (Artplus group, Biolux group, Biotone IPN group, Myerson group, SR Orthosit group, Trilux group, Trubyte Biotone group, and Vipi Dent Plus group). Twenty-four teeth of each brand had their occlusal surfaces ground flat and were embedded in autopolymerized acrylic resin. After polishing, the teeth were submitted to different conditions: (1) immersion in distilled water at 37 ± 2 °C for 48 ± 2. h (control); (2) storage in artificial saliva at 37 ± 2 °C for 15, 30 and 60 days, and (3) thermal cycling between 5 and 55 °C with 30-s dwell times for 5000 cycles. Knoop hardness test was performed after each condition. Data were analyzed with two-way ANOVA and Tukey's test (α= .05). Results: In general, SR Orthosit group presented the highest statistically significant Knoop hardness value while Myerson group exhibited the smallest statistically significant mean (P< .05) in the control period, after thermal cycling, and after all storage periods. The Knoop hardness means obtained before thermal cycling procedure (20.34 ± 4.45 KHN) were statistically higher than those reached after thermal cycling (19.77 ± 4.13 KHN). All brands of resin denture teeth were significantly softened after storage period in artificial saliva. Conclusion: Storage in saliva and thermal cycling significantly reduced the Knoop hardness of the resin denture teeth. SR Orthosit denture teeth showed the highest Knoop hardness values regardless the condition tested. © 2010 Japan Prosthodontic Society.

Clinical evaluation of two packable resin-based composite restorations: A three-year report

This randomized clinical trial sought to evaluate the performance of two packable composites over a period of 36 months. A total of 39 Class I and II restorations were placed in the permanent teeth of 20 patients. Using United States Public Health Services criteria, two investigators evaluated the restorations immediately after placement and again after 12 and 36 months, examining color match, marginal discoloration, marginal integrity, recurrent caries, proximal contact, anatomical shape, surface texture, and postoperative sensitivity. It was concluded that the packable composites evaluated showed satisfactory clinical performance after three years.

Effect of thickness of indirect restoration and distance from the light-curing unit tip on the hardness of a dual-cured resin cement

This study evaluated the Knoop hardness and polymerization depth of a dual-cured resin cement, light-activated at different distances through different thicknesses of composite resin. One bovine incisor was embedded in resin and its buccal surface was flattened. Dentin was covered with PVC film where a mold (0.8-mm-thick and 5 mm diameter) was filled with cement and covered with another PVC film. Light curing (40 s) was carried out through resin discs (2, 3, 4 or 5 mm) with a halogen light positioned 0, 1, 2 or 3 mm from the resin surface. After storage, specimens were sectioned for hardness measurements (top, center, and bottom). Data were subjected to split-plot ANOVA and Tukey's test (α=0.05). The increase in resin disc thickness decreased cement hardness. The increase in the distance of the light curing tip decreased hardness at the top region. Specimens showed the lowest hardness values at the bottom, and the highest at the center. Resin cement hardness was influenced by the thickness of the indirect restoration and by the distance between the light-curing unit tip and the resin cement surface.

Effect of surface treatments on the bond strength of a resin cement to commercially pure titanium

Investigation of the effectiveness of surface treatments that promote a strong bond strength of resin cements to metals can contribute significantly to the longevity of metal-ceramic restorations. This study evaluated the effect of surface treatments on the shear bond strength (SBS) of a resin cement to commercially pure titanium (CP Ti). Ninety cast CP Ti discs were divided into 3 groups (n=30), which received one of the following airborne-particle abrasion conditions: (1) 50 μm Al2O3 particles; (2) 30 μm silica-modified Al2O3 particles (Cojet Sand); (3) 110 μm silica-modified Al2O3 particles (Rocatec). For each airborne-particle abrasion condition, the following post-airborne-particle abrasion treatments were used (n=10): (1) none; (2) adhesive Adper Single Bond 2; (3) silane RelyX Ceramic Primer. RelyX ARC resin cement was bonded to CP Ti surfaces. All specimens were thermally cycled before being tested in shear mode. Failure mode was determined. The best association was Rocatec plus silane. All groups showed 100% adhesive failure. There were combinations that promote higher SBS than the protocol recommended by the manufacturer of RelyX ARC.

Effects of five carbamide peroxide bleaching gels on composite resin microhardness.

The purpose of this study was to evaluate the effects of five home bleaching products containing 15-16% carbamide peroxide on the microhardness of microhybrid composite resin Z-250 (3M/Espe). A total of 72 specimens were fabricated in cylindrical acrylic matrices (4 x 2 mm), filled with composite resin and photo-activated for 40 seconds. They were divided in 6 study groups (n = 12), according to the bleaching product: Review (SS White), Magic Bleaching (Vigodent), Opalescence (Ultradent), Whiteness Perfect (FGM), Claridex (Biodinâmica), and a control group (not bleached). Specimens were exposed to 1 cc of bleaching gel for 6 hours daily for 2 weeks. The control group specimens were kept in artificial saliva throughout this time. All the specimens were then analyzed in a microhardness tester. Knoop hardness measurements were performed, and the results were submitted to parametric statistical analysis (analysis of variance and Tukey's test). Mean Knoop values and standard deviation were: baseline, 68.52a (4.28); control, 63.42b (7.16); Whiteness Perfect, 57.57c (1.81); Magic Bleaching, 57.22c (3.84); Opalescence, 57.03cd (4.00); Claridex, 53.64de (3.33); Review 51.45e (2.82). Identical letters mean statistical equality according to Tukey's test at the 5% significance level. The products significantly decreased Z-250 (3M/Espe) microhardness.

Bond strength of a composite resin to an adhesive luting cement

This study evaluated the influence of surface treatment on the shear bond strength of a composite resin (CR), previously submitted to the application of a temporary cement (TC), to an adhesive luting cement. Eight-four CR cylinders (5 mm diameter and 3 mm high) were fabricated and embedded in acrylic resin. The sets were divided into 6 groups (G1 to G6) (n=12). Groups 2 to 6 received a coat of TC. After 24 h, TC was removed and the CR surfaces received the following treatments: G2: ethanol; G3: rotary brush and pumice; G4: air-abrasion; G5: air-abrasion and adhesive system; G6: air-abrasion, acid etching and adhesive system. G1 (control) did not receive TC or any surface treatment. The sets were adapted to a matrix and received an increment of an adhesive luting cement. The specimens were subjected to the shear bond strength test. ANOVA and Tukey's tests showed that G3 (8.53 MPa) and G4 (8.63 MPa) differed significantly (p=0.001) from G1 (13.34 MPa). The highest mean shear bond strength values were found in G5 (14.78 MPa) and G6 (15.86 MPa). Air-abrasion of CR surface associated with an adhesive system provided an effective bond of the CR to the adhesive luting cement, regardless the pre-treatment with the phosphoric acid.

Effect of maintenance therapy with or without the use of chlorhexidine in teeth restored with composite resin in patients with diabetes mellitus

The objective of this study was to evaluate the effects of maintenance therapy with or without the use of 0.12% chlorhexidine in the periodontal tissues of patients with diabetes mellitus who had carious lesions restored with composed resin. Twenty patients were selected, all of whom had diabetes mellitus in addition to carious cervical lesions in previously treated teeth. After 90 days, improvement in plaque and gingival indices and probing depth were noticed among patients in the group that received 0.12% chlorhexidine.

Effects evaluation of remaining resin removal (three modes) on enamel surface after bracket debonding

Introduction: An appropriate selection of instruments is essential to perform a correct debonding technique, by properly removing orthodontic brackets and the remaining resin. Objective: The aim of this study was to evaluate three methods of remaining resin removal on enamel surface after bracket debonding, by means of Scanning Electron Microscopy (SEM). Methods: Eighteen bovine incisors were selected and divided into three groups (A, B and C) of six teeth each. Before bracket bonding, epoxy resin casts were obtained by impression of the teeth with addition silicon, in order to register baseline enamel characteristics and representing the control group. The methods for remaining resin removal were: Group A - gross and medium granulation Soflex discs; Group B - carbide bur in low-speed; Group C - carbide bur in high-speed. Soflex polishing system fine and ultrafine granulation discs were used for Group A, rubber tips for Groups B and C, and polishing paste for all groups. After polishing, impression of teeth were taken and casts were analyzed by means of SEM. The baseline enamel characteristics (Control Group) were compared to the final aspect of enamel to determine the method that generated less enamel abrasion. Results and Conclusion: The remaining resin removal by carbide bur in low-rotation, and enamel polished with rubber tips followed by polishing paste produced the smaller damage to the enamel.

The effects of exposure time on the surface microhardness of three dual-cured dental resin cements

This study evaluated the exposure time of light-curing of the polymers used for cementation on microhardness test in different storage times. The polymers (specifically called resin cements) were RelyX ARC, RelyX U100, and SET. Five specimens of each group were prepared and photo-polymerized with exposure times of 20 s and 180 s, using a LED polymerization unit with wavelength of 440 ~ 480 nm and light output was consistently 1,500 mW/cm2. The Vickers hardness test was performed in a MMT-3 Microhardness Tester. Data were submitted to ANOVA and Tukey's test (α = 0.05). The values of RelyX ARC showed statistically significant difference to groups with light exposure when considering only chemical cure (p < 0.05). The groups with light exposure (20 s and 180 s) showed no significant difference between them (p > 0.05). The RelyX U100 cured only chemically showed statistically significant difference between 48 h and 7 days (p < 0.05). The SET resin cement showed no significant difference to groups without light exposure for all storage times (p > 0.05). The values of hardening of the dual-cured resin cements improved after setting by light and chemical activation demonstrating the importance of light curing. © 2011 by the authors.

Fracture resistance of composite resin cores with or without prefabricated posts over different substrates

The fracture resistance of endodontically treated teeth has been an obstacle to the durability of the remaining teeth and restorations. The aim of this study was to evaluate the fracture resistance of endodontically treated bovine and human teeth that were restored with either prefabricated metal posts, glass fiber posts, or composite resin cores. Statistical analysis revealed significant difference between different substrates, but there was no statistically significant difference between different types of intraradicular posts or in the interaction between substrate and post types. The intraradicular posts do not increase the fracture resistance of endodontically treated teeth. The metal posts presented more unfavorable fracture modes when compared to glass fiber posts and composite resin cores.

Shear bond strength of resin cement bonded to alumina ceramic after treatment by aluminum oxide sandblasting or silica coating

Purpose: To evaluate the shear bond strength and bond durability between a dual-cured resin cement (RC) and a high alumina ceramic (In-Ceram Alumina), subjected to two surface treatments. Materials and Methods: Forty disc-shaped specimens (sp) (4-mm diameter, 5-mm thick) were fabricated from In-Ceram Alumina and divided into two groups (n = 20) in accordance with surface treatment: (1) sandblasting by aluminum oxide particles (50 μm Al 2O 3) (SB) and (2) silica coating (30 μm SiO x) using the CoJet system (SC). After the 40 sp were bonded to the dual-cured RC, they were stored in distilled water at 37°C for 24 hours. After this period, the sp from each group were divided into two conditions of storage (n = 10): (a) 24 h-shear bond test 24 hours after cementation; (b) Aging-thermocycling (TC) (12,000 times, 5 to 55°C) and water storage (150 days). The shear test was performed in a universal test machine (1 mm/min). Results: ANOVA and Tukey (5%) tests noted no statistically significant difference in the bond strength values between the two surface treatments (p= 0.7897). The bond strengths (MPa) for both surface treatments reduced significantly after aging (SB-24: 8.2 ± 4.6; SB-Aging: 3.7 ± 2.5; SC-24: 8.6 ± 2.2; SC-Aging: 3.5 ± 3.1). Conclusion: Surface conditioning using airborne particle abrasion with either 50 μm alumina or 30 μm silica particles exhibited similar bond strength values and decreased after long-term TC and water storage for both methods. © 2011 by The American College of Prosthodontists.

Microhardness of dual-polymerized resin cement around a translucent fiber post in the intraradicular environment

Aim: In this study, we evaluated the effect of photopolymerization on Vickers microhardness of dual-polymerized resin cement at three locations when a translucent quartz fiber post was used. Materials and Methods: Single-rooted bovine teeth received quartz fiber post systems (length: 12 mm) using a dual-polymerized resin cement. In Group 1, the posts were cemented but not photopolymerized, and in Group 2, the posts were both cemented and photopolymerized. After cementation, approximately 1.5-mm thick sections were obtained (two cervical, two middle, and two apical) for regional microhardness evaluations. Statistical Analysis: Statistical analyses were performed using the SPSS software (ver. 11.0 for Windows; SPSS, Inc., Chicago, IL, USA). Microhardness (kg/mm 2 ) data were submitted to two-way analysis of variance (two-way ANOVA) and repeated measures with microhardness values as the dependent variable and polymerization status (two levels: with and without) and root region (three levels: cervical, middle, and apical) as independent variables. Multiple comparisons were made using Dunnett's T3 post-hoc test. P values of <0.05 were considered to indicate statistical significance in all tests. Results: Photopolymerization did not significantly change the microhardness values when compared with no photopolymerization. Microhardness values also showed no significant difference between the three regions in the root canals in both groups. Conclusions: The mode of polymerization of the cement tested in combination with the translucent quartz fiber post system did not affect the microhardness of the cement at the cervical, middle, or apical regions of the root.

Dispersing carbon nanotubes in phenolic resin using an aqueous solution

The ability to control the carbon nanotube (CNT) dispersion in polymers is considered the key to most applications of nanotube/polymer composites. The carbon nanotube dispersion into water with different surfactants, as well as its incorporation into phenolic resins, was investigated. Ultrasonication of liquid suspensions was used to prepare stable dispersions. In order to evaluate the best surfactant to be used, light scattering and UV-Visible spectroscopy were employed. The structure of CNT reinforced of phenolic resin was analyzed in function of the concentration and type of surfactant, sonication power and time. It was also evaluated the influence in the dispersion by using the glass temperature transition properties being obtained by dynamic mechanical analyses and impact energy. © 2011 Sociedade Brasileira de Química.