Electrical properties of highly conducting Sno2:Sb nanocrystals synthesized using a nonaqueous sol gel method

This work describes the synthesis of highly conducting antimony-doped tin oxide (ATO) nanocrystals prepared via a nonaqueous sol–gel route in the size range of 4–6 nm and provides insights into its electrical properties. The antimony composition was varied from 1 to 18 mol% and the lowest resistivity (4.0 × 10−4Ω·cm) was observed at room temperature in the SnO2:8.8 mol% Sb composition. The samples were evaluated by X-ray diffraction, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, and scanning electron microscope, and resistivity measurements were taken in the four-probe mode in the temperature range of 13–300 K. The results show highly crystalline nanoparticles in a monodisperse colloidal system, dependence on the shape of ATO nanoparticles as a function of Sb distribution, low resistivity, and semiconductor–metal transition.

Construction of a chamber for in situ monitoring of the drying process of gels and porous solids

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Irmão Sol, Irmã Lua: gênero, poder e clausura em um mosteiro da Ordem de Santa Clara de Assis - São Paulo

Pós-graduação em Ciências Sociais - FFC

Structural and optical properties of Er3+ doped SiO2-Al2O3-GeO2 compounds prepared by a simple route

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of cryoprotectants on the reconstitution of silica nanoparticles produced by sol-gel technology

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Improved electrical transport in lightly Er-doped sol-gel spin-coating SnO2 thin films, processed by photolithography

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Poloxamer-based binary hydrogels for delivering tramadol hydrochloride: sol-gel transition studies, dissolution-release kinetics, in vitro toxicity, and pharmacological evaluation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rietveld refinement and optical properties of SrWO4:Eu3+ powders prepared by the non-hydrolytic sol-gel method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of the quantity of coloring agent in bleaching gels activated with LED/laser appliances on bleaching efficiency

The aim of this study was to assess the influence of the quantity of coloring agent on the bleaching efficiency of gels containing 35% H2O2. Sixty human third molars were sectioned mesiodistally, darkened in a coffee solution and sectioned in the occlusal-cervical direction, resulting in mesial (not bleached) and distal halves (bleached). They were distributed into three groups: Whiteness HP, Total Bleach, and Whiteform Perox Red Gel; and subdivided into four sub-groups: no coloring agent, manufacturer's standard, double the standard, and triple the standard. The gels were activated with light-ermitting diode/laser appliances. The images were analyzed with the Adobe Photoshop program (deltaEL*a*b*). The variation was submitted to the ANOVA test (two factors: type of gel and quantity of coloring agent) and Tukey test. Differences were observed for the quantity of coloring agent. The mean (+/-SD) was determined for each quantity of coloring used: no coloring agent -6.85 (+/-2.26)a, manufacturer's standard -794 (+/-2.55)ab, double the standard -8.65 (+/-2.47)b, triple the standard -9.05 (+/-2.72)b. In conclusion, the standard quantity of coloring agent did not provide significantly more intense bleaching than when it was completely absent. The use of double and triple the amount provided greater bleaching than that observed for the gel without coloring agent. No significant differences were observed between the tested gels.

Effect of incorporation of remineralizing agents into bleaching gels on the microhardness of bovine enamel in situ

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of simulated pulpal pressure on efficacy of bleaching gels

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of home-bleaching gels modified by calcium and/or fluoride and the application of nano-hydroxyapatite paste on in vitro enamel erosion susceptibility

This in vitro study compared the effect of bleaching agents modified by the addition of calcium and/or fluoride and the application of a nano-hydroxyapatite paste after bleaching, on the susceptibility of enamel to erosion. Bovine enamel cylindrical samples (3 mm diameter) were assigned to six groups (n = 20 specimens/group) according to the bleaching agent: no bleaching (C-control), 7.5% hydrogen peroxide gel (HP), HP with 0.5% calcium gluconate (HP+Ca), HP with 0.2% sodium fluoride (HP+F), HP with calcium and fluoride (HP+Ca+F) and HP followed by the application of a nano-hydroxyapatite agent (HP+NanoP). The gels were applied on the enamel surface (1 h) followed by cyclic erosive challenges (Sprite Zero®-2 min), for 14 days. The paste was applied after bleaching for 5 min (HP+NanoP). The enamel surface alteration was measured by contact profilometry (µm) (after 7 and 14 days). C-control (mean ± SD: 2.29 ± 0.37 at 7 days/4.86 ± 0.72 at 14 days) showed significantly lower loss compared to the experimental groups. HP+Ca (3.34 ± 0.37/6.75 ± 1.09) and HP+F (4.49 ± 0.92/7.61 ± 0.90) presented significantly lower enamel loss than HP (4.18 ± 0.50/10.30 ± 1.58) only for 14 days and HP+Ca+F (4.92 ± 1.03/8.12 ± 1.52) showed values similar to the HP+F group. The HP+NanoP (5.51 ± 1.04/9.61 ± 1.21) resulted in enamel loss similar to the HP after 14 days. It was found that 7.5% hydrogen peroxide increased the susceptibility of enamel to erosion. The addition of calcium or fluoride to the bleaching gel reduced the erosion effect, while the nano-hydroxyapatite agent did not provide any protective effect.

Análise estrutural de aerogéis via espalhamento de luz a baixo ângulo

The sol-gel process is a method for obtaining vitreous or vitro-ceramic materials which, are prepared a sol and by drying the liquid phase. This technique has been used extensively for the preparation of glassy gels, films, fibers and particles from the hydrolysis and polycondensation reactions of metal alkoxides. The usual methods for drying are: evaporation drying (xerogels), freeze drying (criogéis) and via supercritical CO2 extraction (aerogels). In the present work, we studied the preparation of silica gels by the sol-gel process from the hydrolysis of alkoxides tetraethylorthosilicate (TEOS) and 3-glycidoxypropyltrimethoxysilane (GPTS). The hydrolysis was promoted from GPTS and TEOS in proportion (4: 1) under acidic conditions. The hydrolysis reaction was promoted inside a Becker at room temperature. After hydrolyses the prepared sol had pH 2, and kept under mechanical agitation for a period of 1 hour. In order to accelerate the polycondensation reaction, the pH was corrected to a value near 5 by slowly adding NH4OH. Then the sols were leaked in sealed polycarbonate containers and maintained for 20 days at 40°C for gelation. Silica aerogels were prepared via supercritical CO2 extraction of the wet gel at temperature and pressure higher than 31°C and 74 atm, in an autoclave specially developed for the process. The structural characteristics were studied in the dry gel (aerogel). Aerogels were then characterized by nitrogen adsorption and small angle light scattering. The nitrogen adsorption data were analyzed for the determination of the BET specific surface (SBET), the total pore volume Vp, the pore mean size (lP=4Vp/SBET), the particle mean size (lS) and the pore size distribution (PSD). And the data from small angle light scattering were analyzed to determine the correlation function (γ'), the area per unit volume (S/V), average pore size (l ) and the average particle size...

Materiais híbridos de sílica/orgânico dopados com rodamina-B: estudo da luminescência e preparação de filmes finos para aplicações em fotônica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Propriedades ópticas e elétricas de materiais híbridos de sílica/orgânico à base de GPTS:TEOS preparados pelo método sol-gel

Fabrication of optoelectronic devices requires the employment of at least one transparent electrode. Usually, commercially transparent electrodes have been made by deposition of indium tin oxide (ITO) films by RF-Sputtering technique. These commercial electrodes have sheet resistance of about 100 Ω/sq and optical transmittance of 77% at the wavelength of 550 nm. The poly(3,4-ethylenedioxythiophene):polystyrene-sulfonate (PEDOT:PSS) is an alternative material to fabricate transparent electrodes due to its high conductivity (about 600 S/cm) and solubility in water. Soluble conductive materials exhibits advantages for processing of electrode layers, however there is a disadvantage during devices fabrication once materials with the same solvent of the electrode material cannot be coated one over the other. Alternatively, organic/Silica hybrid materials prepared by sol-gel process allow producing bulks and films with high chemical durability. In order to obtain transparent electrodes with high chemical durability, we introduced a blended material comprising the high UV-VIS transparency of organic/Silica sol-gel material and a high conductivity polymer PEDOT:PSS. The organic/Silica sol was obtained using two different molar concentrations (1:1 and 4:1), of tetraethylorthosilicate (TEOS) and 3-glycidoxypropyltrimethoxysilane (GPTS). Amounts of PEDOT:PSS solutions were added to the sol material, resulting in different weight fractions of sol and polymer. G:T/P:P were deposit onto glass substrates by spray-coating. In order to perform electrical characterization of the blended material, gold electrodes were thermally evaporated onto the films. The electrical characterization was performed using a Keithley 2410 source/meter unity and the optical characterization, using a Cary50 UV-Vis spectrophotometer. The absorption coefficient and electric conductivity of the different compositions blends, as function of the PEDOT:PSS concentration, were...