Estudo da influência da aplicação do fluido de corte no torneamento da liga de alumínio AA7075

One of the ways to minimize the effects of unproductive time caused by tool wear can be achieved by introducing an efficient system of lubrication and cooling in the process. However, in the last decade the research had the goal to restrict the maximum use of refrigerants and / or lubricants in metal-mechanical production. The important factors that justify this procedure include the operational costs of production, ecological issues, and the legal requirements of environmental conservation and preservation of human health. The purpose of the proposed work is the study of machining by turning with the focus on the influence caused by the application of cutting fluid in several ways of application (abundant and MQF) and also by comparing the results obtained by machining without the presence of fluid . For this purpose, the turning tests are conducted using an aluminum alloy (AA 7075). The response variables to be analyzed were obtained from the roughness (Ra and Ry), the stresses presented (VB) and their progression in relation to the cutting length achieved, the type of chip formed, in addition to changes in the degree of finish (roughness) presented by the turned parts. The results of this study should provide more detailed information about the actual influence of cutting fluids in turning this alloy, which are characterized by high rates of deformation when the formation of damaging your chip machining and also the quality of surface generated. Therefore, it is expected to provide subsidies to promote the optimization of machining this alloy making the most of the role of cutting fluid

Estudo das propriedades mecânicas do aço SAE 1312 modificado ao nióbio

The study of mechanical properties of high-alloy special steels is of great interest of the steel industry due to the great demand by companies that manufacture automotive components of high criticality, and also because of its high commercial value. However, the development of this type of alloy metals demand highly technical knowledge. Among these extremely important kinds of steel, the subject which is the interest of this study is the special steel modified by niobium. The manganese and niobium are the main alloying elements in the composition of these steels, both of them increase the stability of the austenite region, however, manganese increases the hardenability and tensile yield strength, and niobium increases the mechanical strength and promotes refining the grain. The mechanical characterization of steel SAE 1312 modified the niobium was made in order to gain a better understanding of the influence on the mechanical properties caused by aging at different temperatures and for different reductions in the drawing of gauge material. This characterization was made by means of tensile test and hardness. This material showed an increase in yield strength and hardness when gauge with large reductions during the wiredrawing, but when subjected to aging temperatures higher than 300 ° C had a slight loss of these properties

Avaliação da influência da taxa de resfriamento posterior ao tratamento térmico nas propriedades mecânicas do aço API 5L X70

In this work a study about the mechanical properties of the API 5L X70 steel, with or without heat treating, has been made, with the intetion of assess the influence of cooling after the austenitization heat treating by air cooling (normalizing) and a rapid cooling with oil (tempering). This steel is known by high strength and ductility values and it is commonly used in the manufacture of oil pipes. The growing energy demand encouraged the study and manufacture of this material. Although this microalloyed dispense subsequent heat treatings, it was proven that its implementation is very advantageous for this type of application, improving hardness and plastic stability. It was also assessed that the faster the cooling rate is, the better will be these properties

Mapeamento geológico e petrologia dos complexos máfico-ultramáficos de Mangabal Sul e Mangabal Norte, região de Sanclerlândia, Goiás

The Mangabal Sul and Mangabal Norte mafic-ultramafic complexes are interpreted as intrusive stratiform bodies in the Goiás Magmatic Arc during the Brazilian cycle, being economically important for harboring significant amounts of nickel and copper sulfides. The main lithotypes of the complexes are gabbronorites, olivine gabbronorites, pyroxenites and peridotites, with variated degrees of deformation, recrystallization and metamorphism superimposed, with metamorphic peak of amphibolite to granulite facies evidenced mainly by the occurrence of coronitic olivine in metamafic rocks and the occurrence of syn-kinematic retrometamorphism associated with the development of the main foliation Sn. The Sn foliation planes show NE-SW preferential direction, consistent with the foliation direction of VIII the enclosing gneisses and schists, also concordant with the general elongation of mafic and ultramafic bodies displayed on map. The sulfide phase presents textures that indicate remobilization, associated with the occurrence of significant amounts of rutile within the ore which reinforces this idea. Along with the sulfides, the occurrence of expressive quantities of titanium oxides such as ilmenite and rutile, make the area more economically attractive. It can be suggested that the Mangabal Norte and Mangabal Sul complexes are contemporary, have the same genetic affinity and suffered the same deformational and metamorphic processes, evidenced by their structural and petrological similarities

Análise macro e micrográfica da liga AA-356 conforme a taxa de resfriamento

The present work aims to study the characteristics of the alloy Al - 7 % Si - 0 , 3Mg ( AA356 ) , more specifically characterize the macrostructure and microstructure and mechanical properties of the alloy ingots AA356 obtained in metal molds and sand molds for power studying the structures through the difference of cooling rates . This alloy is explained by the fact of referring league has excellent combination of properties such as low solidification shrinkage and good fluidity, good weldability , high wear resistance , high strength to weight ratio, has wide application in general engineering , and particularly in the automotive and aerospace engineering . In this work we will verify this difference in properties through two different cooling rates . We monitor the solid solidification temperatures by thermocouples building with them the cooling curve as a tool that will aid us to evaluate the effectiveness of the grain refining because it achieved with some important properties of the alloy as the latent heat of solidification fraction the liquid and solid temperatures, the total solidification time, and identify the presence of inoculants for grain refinement. Thermal analysis will be supported by the study of graphic software “Origin “will be achieved where the cooling curve and its first derivative that is the cooling rate. Made thermal analysis, analysis will be made in macrographs ingots obtained for observation of macrostructures obtained in both types of ingots and also analysis of micrographs where sampling will occur in strategic positions ingots to correlate with the microstructure. Finally will be collecting data from Brinell hardness of ingots and so then correlating the properties of their respective ingots with cooling rate. We found that obtained with cast metal ingots showed superior properties to the ingots obtained with sand mold

Crescimeno de apatita na superfície da liga Ti-7, 5Mo empregando tratamento higrotérmico

The objective of the present work was to evaluate surface of experimental alloy Ti-7.5Mo after hydrothermal treatment. Ingots were obtained in arc melting furnace under an argon atmosphere and then homogenized under vacuum at 1100ºC for 86.4 ks to eliminate chemical segregation and after cold worked discs were cutting and grinding. For surface treatment, samples were immersed in a container with NaOH aqueous solution 5M, autoclaved, washed with distilled water. Followed, samples were heat treated and they were soaking in 5xSBF to form an apatite layer on the surface. Surfaces were investigated by, scanning electron microscopy, X-Rays powder diffraction, atomic force microscopy and contact angle, in order to evaluate the wettability of the alloy surface. The results were compared with our previous studies using the group of chemical surface treatments and results shows better condition is 120 minutes in the autoclave

Caracterização da liga do sistema binário Ti-15Mo para aplicações biomedicas

As they have excellent mechanical properties, corrosion resistance and biocompatibility, much research has been conducted with respect to biomedical applications of titanium alloys. This work aims to study the experimental system binary alloy Ti-15Mo, in the raw state of fusion and heat treatment after homogenization, solubilization and calcination (simulating conditions employed for nanotube growth) targeting biomedical applications. Samples were obtained by casting the components in an electric arc furnace with inert atmosphere of argon. After obtaining the alloy, it was heat treated at three different heat treatments, namely homogenizing, calcining and simulation solubilization. The phases present were analyzed by X-ray diffraction, optical microscopy and microhardness testing

Caracterização estrutural da Liga Al-1% Si

The aim of this study is to characterize the macrostructure and microstructure of Al - 1%Si alloy obtained in sand and metallic molds. Aluminium has good mechanical properties, but adding silicon, even in small quantities, can change the microstructure and improves mechanical behavior. Workpieces were castings in metallic and sand molds and one can see a difference in their cooling curve, macroscopic and microscopic structures. The sand mold casting has lower cooling rate and so its grains are larger. Due to the lower concentration of grain boundary, the hardness is lower compared to that found in metallic molds, which has smaller grains and a higher hardness. Therefore, it can be concluded that the cooling rate and alloying elements affect the final microstructure of the workpiece

Análise da curva de resfriamento da liga de alumínio AA 356

It is very important to study the macrostructure of a material in the crude state of solidification due to influence the mechanical properties, as well as the study of their cooling curve. In the present work was to study the alloy AA 356, its macrostructure and its cooling curve. The material was cast in two different molds, a sand and other metallic. In this paper we study the differences in its macrostructure and its cooling curves. In macrostructure can observe the absence of the three zones of solidification and the presence of large pores because of moisture in the sand. In the sample taken from the metal mold can observe the three zones of solidification: a coquilhada, columnar and equiaxed

Cádmio, chumbo, cromo, mercúrio e níquel nos rios do estado de São Paulo e em peixes do Rio Sorocaba (São Paulo, Brasil)

To verify the levels of concentration of some heavy metals in fishes from Sorocaba river (São Paulo, Brazil) and evaluate if this contamination offers health risks to the fishermen, 63 samples of fishes collected from four points along the river were studied for cadmium, lead, chromium, nickel and mercury, with emphasis in this last, since it is the most toxic and most probable as a fish contaminant. Analyzing muscle samples by cold vapor atomic absorption spectrometry it was shown that the fishes are not contaminated. None of the five metals studied were present in prohibitive level and the fishes could be judged secure for human consume. It was also analyzed data from four years of cadmium, lead, chromium, nickel and mercury monitoring made by CETESB, from 1997 to 2000, in water from the main rivers of the State of São Paulo. The study pointed out that the majority of the monitored rivers still present contamination by those metals in a level that requires an improvement of the pollution control actions.

Crescimento de apatita na superfície da liga Ti-25Ta empregando dois tipos de tratamento de superfície: biomimético e deposição de polímero por eletrofiação

Titanium and its alloys has been widely used as materials for metallic biomaterials implants are usually employed to restore the hard tissue function, being used for artificial joints and bones, synthetic plates, crowns, dental implants and screws . Objective of this work was the surface modification of Ti-alloy 25Ta from biomimetic surface treatment of employment and deposition of polymer by electrospinning. The league was obtained from the fusion of the pure elements in the arc furnace with controlled atmosphere. The ingots were subjected to heat treatment, cold forged and sectioned discs with 13 mm diameter and 3 mm thick. Two surface treatments was evaluated, biomimetic and electrospinning with PCL fiber. The biomimetic treatment was performed involving alkaline treatment for three molarities 1.5M, 3M and 5M with immersion in SBF. The electrospinning was performed using PCL polymer alloy surface after the alkali treatment Ti25Ta 1M. For this group the polymer coated surfaces were immersed in calcium phosphate containing solution for immobilization of apatite. The results were compared with previous studies using surface treatment group to verify hydroxyapatite formation on the sample surface and it is concluded that the best condition is biomimetic treatment with 5M alkali treatment and heat treatment at 80 ° C for 72 hours

Estudo da influência do agente nucleante )ALTi5%B1%) na microestrutura de chapas AA8011 obtidas por lingotamento contínuo

The aluminum includes several properties with excellent relation between weight and mechanical resistance. With technological advances, increasingly demand the development of new alloys and other production processes in order to reduce the cost of production and insert these new alloys in broader applications. The process of continuous caster (TRC promoted the unite of the aluminum smelting process with the first stage of rolling, making it most economical through the merger these two phases besides transform the continuous casting process. The AA8xxx series is one of the most versatile aluminum alloys and the most often used in continuous caster process provided a great potential application in the market. In order to further, optimize the process it is necessary to increase awareness of the aluminum solidification phenomena associated with the addition of grain refiner, and control of some aluminum production parameters in the process (production rate, metal temperature, etc.). In this study, AA8011 alloy samples were taken in the raw state obtained by the continuous casting process. The samples were laminated to a thickness of 7mm during the process itself and analyzed at three points along its width by microstructural analysis throughout its thickness, the variation rate of addition of the grain refiner in order to assess the influence of this addition with crystallographic formation and some formation of intermetallic precipitates during the solidification. Through this work, it was possible to improve the knowledge related to the addition of refiner with the monitoring of these production processes

Analise comparativa do desempenho de ferramentas no torneamento do aluminio 2024

The aluminium alloys are used in many fields because of their versatility combined with the excellent aluminium’s properties, mentioned in the study. This study aims to compare the performance of polished Hard Metal, Hard Metal covered with TiB2 and High Speed Steel (HSS) tools, at the aluminium 2024 alloy’s turning, as a function of variation of some turning parameters such as: feed, depth of cut and cutting speed; and study the surface finish and the required power during turning by processing the output data, like analyze the chip’s features for each used tool. The results provide information of the tool’s material effects, when submitted to different turning conditions, about the output variable in question. In this way, it was possible to notice that although the Hard Metal covered with TiB2 tool has provided the better surface finish, the chip’s features were better when the turning was accomplished by the Polished Hard Metal tool. In relation to the required turning’s power, the lowest consumption occurred with the High Speed Steel tool

Usinabilidade e integridade superficial de implantes dentários

Pós-graduação em Engenharia Mecânica - FEIS

Estudo do efeito do processo de shot peening na taxa de propagação de trinca por fadiga na liga aeronáutica 2024 - T3

Pós-graduação em Engenharia Mecânica - FEG