Photoelastic Analysis of Implant-Retained and Conventional Obturator Prostheses With Different Attachment Systems and Soft Relining

Complete and partial loss of maxillary bone may jeopardize oral physiology and generate complications as oral-sinus-nasal communication. Palatal obturator prostheses are a treatment alternative for rehabilitation of these patients. The aim of this study was to assess stress distribution, through photoelasticity, on palatal obturator prostheses associated with different attachment systems (o'ring, bar clip, and o'ring/bar clip) of implants and submitted to relining. Two photoelastic models were fabricated according to an experimental maxillary model with oral-sinus-nasal communication. One model did not present implants, whereas the other included 2 implants with 13.0 mm in length in the left ridge. Four colorless maxillary obturator prostheses were fabricated and relined with soft silicone. One of these prostheses presented no attachment system, whereas the remaining prostheses included attachment systems adapted to the implants. The assembly (model/attachment system/prosthesis) was positioned in a circular polariscope during loading with 100 N at 10 mm/s. The results were based on observation during the experiment and photographic records of stress on the photoelastic model. The bar clip system exhibited the highest stress concentration followed by o'ring/bar clip and o'ring systems. The attachment systems presented different stress distribution with greater concentration surrounding the implants and homogenous stress distribution on the photoelastic model without implants. The highest concentration of fringes occurred, in ascending order, with o'ring, o'ring/bar clip, and bar clip systems.

Effect of thermocycling on hardness, absorption, solubility and colour change of soft liners

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

TMJ Vibrations in Asymptomatic Patients Using Old and New Complete Dentures

Purpose: The aim of this study was to assess the presence of temporomandibular joint (TMJ) noises in subjects with severe bone resorption, who have worn the same complete dentures for over 10 years, and 5 months after treatment with increments of acrylic resin on the occlusal surface after having new dentures in place.Methods: After applying the research diagnostic criteria (RDC)/temporomandibular disorder (TMD) questionnaire, 20 asymptomatic subjects were assessed before and 5 months after the new dentures were put in place. Joint vibrations were assessed by the Sono Pak program by selecting the vibrations that occurred during the opening and closing cycle.Results: The means of the results revealed a nonnormal distribution and were submitted to Kruskal-Wallis statistical analysis (p < 0.05). The vibration means were of low intensity (<= 9.96 Hz). After rehabilitation, there was a reduction in the vibrations (<= 5.2 Hz) statistically significant only at the end of mouth opening with the old dentures when compared with the other cycles.Conclusion: The intensity and number of occurrences of joint vibrations were reduced after 5 months of wearing new dentures.

Mobility, Aesthetic, Implants, and Satisfaction of the Ocular Prostheses Wearers

During the process of facial rehabilitation, the mobility of ocular prostheses must be considered. Whereas some factors depend exclusively on the dentist, such as molding techniques and selection of material for denture construction, regarding ocular rehabilitation, factors, such as type of surgery, whether to adopt implants, and the use of lubricants, deserve special attention owing to their integration and their association with other factors pertaining exclusively to the patient. To establish harmony, and with the intention of aiding the dentist, after a discerning evaluation, the authors of this study report the factors that provide greater or less mobility to ocular prostheses and conceal the prosthesis in a more natural way, thereby contributing toward achieving a favorable aesthetic result in rehabilitations.

Photoelastic analysis to compare implant-retained and conventional obturator dentures

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Antimicrobial Properties and Cytotoxicity of an Antimicrobial Monomer for Application in Prosthodontics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microscopical analysis of Candida albicans biofilms on heat-polymerised acrylic resin after chlorhexidine gluconate and sodium hypochlorite treatments

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of metal conditioners on the adhesive bonding of resin cements to cast titanium

Objective: To assess the effect of metal conditioners on the bond strength between resin cements and cast titanium. Method and Materials: Commercially pure titanium (99.56%) was cast using an arc casting machine. Surfaces were finished with 400-grit silicon carbide paper followed by air abrasion with 50-mu m aluminum oxide. A piece of double-coated tape with a 4-mm circular hole was then positioned on the metal surface to control the area of the bond. The prepared surfaces were then divided into 4 groups (n=10): G1, unprimed Panavia F; G2, Alloy Primer-Panavia F; G3, unprimed Bistite DC; G4, Metaltite-Bistite DC. Forty minutes after insertion of the resin cements, the specimens were detached from the mold and stored in water at 37 C for 24 hours. Shear bond strength was performed in a testing machine (MTS 810) at a crosshead speed of 0.5 mm/min. Data were analyzed using ANOVA and Tukey's test with a .05 significance level. The fractured surfaces were observed through an optical microscope at 10x magnification. Results: the G1 group demonstrated significantly higher shear bond strength (17.95 MPa) than the other groups. G3 (13.79 MPa) and G4 (12.98 MPa) showed similar mean values to each other and were statistically superior to G2 (9.31 MPa). Debonded surfaces generally presented adhesive failure between metal surfaces and resin cements. Conclusion: While the Metaltite conditioner did not influence the bond strength of the Bistite DC cement, the Alloy Primer conditioner significantly decreased the mean bond strength of the Panavia F cement.

Effect of microwave disinfection on the hardness and adhesion of two resilient liners

Statement of problem. Microwave irradiation has been suggested for denture disinfection. However, the effect of this procedure on the hardness and bond strength between resilient liners and denture base acrylic resin is not known.Purpose. This study evaluated the effect of water storage time and microwave disinfection on the hardness and peel bond strength of 2 silicone resilient lining materials to a heat-polymerized acrylic resin.Material and methods. Acrylic resin (Lucitone 199) specimens (75 X 10 X 3 mm) were stored in water at 37 degrees C (2 or 30 days) before bonding (n = 160). The resilient lining materials (GC Reline Extra Soft and Dentusil) were bonded to the denture base and divided into the following 4 groups (n = 10): Tests performed immediately after bonding (control); specimens immersed in water (200 mL) and irradiated twice, with 650 W for 6 minutes; specimens irradiated daily for 7 total cycles of disinfection; specimens immersed in water (37 degrees C) for 7 days. Specimens were submitted to a 180-degree peel test (at a crosshead speed of 10 mm/min) and the failure values (MPa) and mode of failure were recorded. Pretreatment and posttreatment hardness measurements (Shore A) of the resilient materials were also performed. Three-way analysis of variance, followed by the Tukey HSD test, was performed (alpha=.05).Results. The analysis revealed that, for all conditions, the mean failure strengths of GC Reline Extra Soft (0.95-1.19 MPa) were significantly higher (P<.001) than those of Dentusil (0.45-0.50 MPa). The adhesion of the liners was not adversely affected by water storage time of Lucitone 199 or microwave disinfection. All peel test failures were cohesive. There was a small but significant difference (P<.001) between the pretreatment (34.33 Shore A) and posttreatment (38.69 Shore A) hardness measurements.Conclusion. Microwave disinfection did not compromise the hardness of either resilient liners or their adhesion to the denture base resin Lucitone 199.

Effect of disinfection on adhesion of reline polymers

Cylinders (3.5 x 5.0 mm) of the reline resins Kooliner (K), New Truliner (N), Tokuso Rebase Fast (T), and Ufi Gel Hard (U) were bonded to cylinders (20 x 20 mm) of the denture base resin Lucitone 550 (L), and samples were divided into two controls and four test groups (n = 8). Shear tests (0.5 mm/min) were performed after polymerization or immersion in water (37 degrees C) for 7 days (controls); two or seven cycles of disinfection by immersion in sodium perborate (50 degrees C/10 min) or microwave irradiation (650 W/6 min). Statistical analyses (alpha = 0.05) revealed that two cycles of microwave and chemical disinfection increased the mean bond strengths of materials T (9.08 to 12.93 MPa) and L (18.89 to 23.02 MPa). For resin L, seven cycles of chemical (15.72 MPa) and microwave (17.82 MPa) disinfection decreased the shear bond strength compared with the respective control (21.74 MPa). Resins U (13.12 MPa), K (8.44 MPa), and N (7.98 MPa) remained unaffected.

Hardness of heat-polymerized acrylic resins after disinfection and long-term water immersion

Statement of the problem. In selecting a disinfectant for dental prostheses, compatibility between the disinfectant and the type of denture base material must be considered to avoid adverse effects on the hardness of the acrylic resin.Purpose. This study investigated the hardness of 2 denture base resins after disinfection and long-term water immersion.Material and methods. Thirty-two disk-shaped specimens (13 mm in diameter and 8 mm thick) were fabricated from each resin (Lucitone 550 and QC-20), polished, stored in water at 37degreesC for 48 hours, and submitted to hardness tests (Vickers hardness number [VHN]) before disinfection. Disinfection methods included scrubbing with 4% chlorhexidine gluconate for 1 minute, immersion for 10 minutes in I of the tested disinfectant Solutions (n=8) (3.78% sodium perborate, 4% chlorhexidine gluconate, or 1% sodium hypochorite), and immersion in water for 3 minutes. The disinfection procedures were repeated 4 times, and 12 hardness measurements were made on each specimen. Control specimens (not disinfected) were stored in water for 56 minutes. Hardness tests (VHN) were also performed after 15, 30, 60, 90, and 120 days of storage in water. Statistical analyses of data were conducted with a repeated measures 3-way analysis of variance (ANOVA) and Tukey post-hoc test (alpha=.05).Results. Mean values +/- SD for Lucitone 550 (16.52 +/- 0.94 VHN) and QC-20 (9.61 +/- 0.62 VHN) demonstrated a significant (P<.05) decrease in hardness after disinfection, regardless of material and disinfectant solutions used (Lucitone 550: 15.25 +/- 0.74; QC-20: 8.09 +/- 0.39). However, this effect was reversed after 15 days of storage in water. Both materials exhibited a continuous increase (P<.05) in hardness values for up to 60 days of water storage, after which no significant change was observed.Conclusion. Within the limitations of this in vitro study, QC-20 and Lucitone 550 specimens exhibited significantly lower hardness values after disinfection regardless of the disinfectant solution used.

Effect of microwave disinfection on the flexural strength of hard chairside reline resins

Objectives: This study investigated the effect of microwave disinfection (650 W/6 min) on the flexural strength of five hard chairside reline resins (Kooliner, Duraliner II, Tokuso Rebase Fast, Ufi Get Hard, New Truliner) and one denture base resin (Lucitone 550).Methods: Thirty-two specimens (3.1x10x64 mm) from each acrylic resin were produced and divided into four groups of eight specimens each. The flexural test was performed after polymerization (G1), after two cycles of microwave disinfection (G2), after 7 days storage in water at 37 degrees C (G3) and after seven cycles of microwave disinfection (G4). Specimens from group G4 were microwaved daily being stored in water at 37 degrees C between exposures. The specimens were placed in three-point bend fixture in a MTS machine and loaded until failure. The flexural values (MPa) were submitted to ANOVA and Tukey's test (p=0.05).Results: Two cycles of microwave disinfection promoted a significant increase in flexural strength for materials Kooliner and Lucitone 550. After seven cycles of microwave disinfection, materials Kooliner and New Truliner showed a significant increase (p<0.05) in flexural values. The flexural strength of the material Tokuso Rebase was not significantly affected by microwave irradiation. Seven cycles of microwave disinfection resulted in a significant decrease in the flexural strength of material Duraliner II. Material Ufi Get Hard was the only resin detrimentally affected by microwave disinfection after two and seven cycles.Conclusions: Microwave disinfection did not adversely affect the flexural strength of all tested materials with the exception of material Ufi Get Hard. (c) 2005 Elsevier Ltd. All rights reserved.

Resistência de união entre dentes artificiais e resinas acrílicas para base protética

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of partially dentate patients' knowledge about caries and periodontal disease

Objective: This investigation evaluated the knowledge of dental caries and periodontal disease among removable partial denture (RPD) wearers.Method: A total of 127 partially dentate patients participated in this observational study. A structured questionnaire, which included eight questions referring to knowledge about aetiology and prevention of dental caries and periodontal disease, was developed in the local language (Portuguese) and used to collect the data of all the partial denture wearers. A descriptive analysis of data was performed by means of drafting tables.Results: The results demonstrated that 68.5% of patients interviewed had previously received information about oral health care. With regard to bacterial plaque, it was observed that only 34.6% reported having knowledge of this. Whereas, in relation to caries, 76.4% of the interviewees replied that they knew the meaning of this. Nevertheless, 28.3% referred to caries as a whole in the teeth, 16.5% as bad teeth and 9.4% bacteria/creatures on the teeth. Only 17.3% of the partially edentulous patients evaluated were shown to know what disease of the gingiva was.Conclusion: By means of the methodology applied, it could be concluded that the patients who wore RPDs presented deficient knowledge with regard to the prevention, aetiology and development of dental caries and periodontal disease.

Validation of the Brazilian versions of two inventories for measuring oral health-related quality of life of edentulous subjects

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)