Retention and processing methods of nasal prosthesis

Patients with congenital malformations, traumatic or pathological mutilation and maxillofacial developmental disorders can be restored aesthetically and emotionally by the production and use of facial prostheses. The aim of this study was to review the literature about the retention and processing methods of facial prostheses, and discuss their characteristics. A literature review on Medline (PubMed) database was performed by using the keywords maxillofacial prosthesis, silicone, resin, pigment, cosmetic, prosthetic nose, based on articles published from 1956 to 2010. Several methods of retention, from adhesives to the placement of implants, and different processing methods such as laser, CAD/CAM and rapid prototyping technologies have been reported. There are advantages and disadvantages of each procedure, and none can be classified as better compared to others.

Shellac and hydroxyapatitte coatings on titanium niobium and AISI 316L steel surfaces produced by dip-coating

Shellac is a natural resin used for the preservation of fruits, bones and as a coating on drugs. The hydroxyapatite (HA), which is naturally found in human bones, is used as filler to substitute amputated bone or as a coating for prosthetics, promoting bone growth in implants of prostheses. The objective of this work is to immobilize HA from an alcoholic solution of shellac on plates of titanium, niobium and AISI 316L steel using the simple dip-coating method. The corrosion resistance of the uncoated films is compared with ones coated with shellac and shellac plus HA. The deterioration of the film composed of shellac with hydroxyapatite in saline solution follows the ascending order: AISI 316L steel, titanium, niobium. The elemental analysis of the shellac showed that it mainly consists of the elements C, H, N and O. We used the FT-IR spectrum to characterize the shellac and HA. ©The Electrochemical Society.

Correlation between hybrid layer thickness, resin tag length and microtensile bond strength of a self-etching adhesive system

The purpose of this study was to evaluate the correlation between the hybrid layer thickness, resin tag length and resin bond strength of a self-etching adhesive system to sound dentin tissue in vivo. After performing restorative procedures and tooth extractions, ten specimens were sectioned in a mesiodistal direction. One dental section was used for light microscope analysis, in which both the resin tag length and hybrid layer thickness were measured, while the other section was analyzed using a microtensile test (0.5 mm/min). The fractured surface of the latter section was characterized using a stereoscopic magnifying glass (40x magnifcation). The results were subject to statistical analysis using the Pearson Correlation Test (a = 0.05). The hybrid layer thickness, resin tag length and resin bond strength mean values were 2.19 microm (0.34), 4.34 microm (0.28) and 9.73 MPa (5,55), respectively. In addition, correlation tests between the resin tag length and the resin bond strength (r=0.014) and also between the hybrid layer thickness and bond strength (r=0.43), showed no statistically significant correlation. The microtensile bond strength of Adper Prompt L Pop self-etching adhesive system does not depend on hybrid layer thickness or resin tag length.

Antimicrobial activity and surface properties of an acrylic resin containing a biocide polymer

Objective: To evaluate the antimicrobial activity and surface properties of an acrylic resin containing the biocide polymer poly (2-tert-butylaminoethyl) methacrylate (PTBAEMA). Background: Several approaches have been proposed to prevent oral infections, including the incorporation of antimicrobial agents to acrylic resins. Materials and methods: Specimens of an acrylic resin (Lucitone 550) were divided into two groups: 0% (control) and 10% PTBAEMA. Antimicrobial activity was assessed by adherence assay of one of the microorganisms, Staphylococcus aureus, Streptococcus mutans and Candida albicans. Surface topography was characterised by atomic force microscopy and wettability properties determined by contact angle measurements. Results: Data of viable cells (log (CFU + 1)/ml) for S. aureus (control: 7.9 ± 0.8; 10%: 3.8 ± 3.3) and S. mutans (control: 7.5 ± 0.7; 10%: 5.1 ± 2.7) showed a significant decrease with 10% of PTBAEMA (Mann-Whitney, p < 0.05). For C. albicans (control: 6.6 ± 0.2; 10%: 6.6 ± 0.4), there was no significant difference between control and 10% of PTBAEMA (Kruskal-Wallis, p > 0.05). Incorporating 10% PTBAEMA increased surface roughness and decreased contact angles. Conclusion: Incorporating 10% PTBAEMA into acrylic resins increases wettability and roughness of acrylic resin surface; and decreases the adhesion of S. mutans and S. aureus on acrylic surface, but did not exhibit antimicrobial effect against C. albicans. © 2012 The Gerodontology Society and John Wiley & Sons A/S.

Viscosity, pH, and moisture effect in the porosity of poly(furfuryl alcohol)

The poly(furfuryl alcohol) is highly indicated to obtain advanced carbonaceous materials due mainly to its good carbon yield (around 50%) and a controllable cure reaction. In the processing of some carbonaceous materials, such as monolithic vitreous carbon, it is necessary to make sure that the material has the smallest porosity to be used in nobler applications such as heart valves and aerospace integrated systems. In this manuscript, a design of experiments was used to study the influence of viscosity, pH, and moisture in the porosity of the cured material. This study shows that the moisture exerts a significant influence on the porosity and the trend of the results lead to conclude that lower viscosity and moisture, and the use of non-neutralized poly(furfuryl alcohol) resins lead to obtain materials with better quality. © 2012 Wiley Periodicals, Inc.

Effect of experimental photopolymerized coatings on the hydrophobicity of a denture base acrylic resin and on Candida albicans adhesion

Objective: This study investigated the effect of experimental photopolymerized coatings, containing zwitterionic or hydrophilic monomers, on the hydrophobicity of a denture base acrylic resin and on Candida albicans adhesion. Methods: Acrylic specimens were prepared with rough and smooth surfaces and were either left untreated (control) or coated with one of the following experimental coatings: 2-hydroxyethyl methacrylate (HE); 3-hydroxypropyl methacrylate (HP); and 2-trimethylammonium ethyl methacrylate chloride (T); and sulfobetaine methacrylate (S). The concentrations of these constituent monomers were 25%, 30% or 35%. Half of the specimens in each group (control and experimentals) were coated with saliva and the other half remained uncoated. The surface free energy of all specimens was measured, regardless of the experimental condition. C. albicans adhesion was evaluated for all specimens, both saliva conditioned and unconditioned. The adhesion test was performed by incubating specimens in C. albicans suspensions (1 × 10 7 cell/mL) at 37 °C for 90 min. The number of adhered yeasts were evaluated by XTT (2,3-bis[2-methoxy-4-nitro-5-sulfophenyl]-5-[{phenylamino} carbonyl]-2H-tetrazolium-hydroxide) method. Results: For rough surfaces, coatings S (30 or 35%) and HP (30%) resulted in lower absorbance values compared to control. These coatings exhibited more hydrophilic surfaces than the control group. Roughness increased the adhesion only in the control group, and saliva did not influence the adhesion. The photoelectron spectroscopy analysis (XPS) confirmed the chemical changes of the experimental specimens, particularly for HP and S coatings. Conclusions: S and HP coatings reduced significantly the adhesion of C. albicans to the acrylic resin and could be considered as a potential preventive treatment for denture stomatitis. © 2012 Elsevier Ltd.

Bond strength of adhesive systems with different solvents to dry and wet dentin

Aim: This study evaluates bond strength between dentin and composite using adhesives with different solvents to dry and wet dentin. Materials and methods: Ninety bovine incisors were used; the vestibular surfaces were worn by the exposure of an area with a diameter of 4 mm of dentin. The specimens were divided into 6 groups, according to the type of adhesive used and hydratation stals: Group SB-wet: Single Bond 2 in wet dentin, Group SBdry: Single Bond 2 in dry dentin, Group SL-wet: Solobond M in wet dentin, Group SL-dry: Solobond M in dentin dry. Group XPwet: XP Bond in wet dentin, Group XP-dry: XP Bond in dentin dry. They were cut to obtain specimens in the shape of stick with 1 × 1 mm and subjected to microtensile test in universal testing machine with a cross speed of 1mm/min. The data were analyzed with ANOVA and Tukey's tests (5%). Results: ANOVA showed significant differences for surface treatment and interaction, but no difference was found for adhesive factor. The Tukey's test showed that the samples with wet dentin shown higher values of bond strength. Conclusion: The adhesive did not influence in the bond strength. The groups with wet dentin showed higher values of bond strength than groups with dry dentin.

Influence of CVD diamond tips and Er:YAG laser irradiation on bonding of different adhesive systems to dentin

Aim: The aim of this study was to compare the microtensile bond strength of three adhesive systems, using different methods of dentin preparation. Materials and methods: A hundred and eight bovine teeth were used. The dentin from buccal face was exposed and prepared with three different methods, divided in 3 groups: Group 1 (DT)- diamond tip on a high-speed handpiece; Group 2 (CVD)-CVD tip on a ultrasonic handpiece; Group 3 (LA)-Er: YAG laser. The teeth were divided into 3 subgroups, according adhesive systems used: Subgroup 1-Adper Single Bond Plus/3M ESPE (SB) total-etch adhesive; Subgroup 2-Adper Scotchbond SE/3M ESPE (AS) selfetching adhesive; Subgroup 3-Clearfil SE Bond/Kuraray (CS) selfetching adhesive. Blocks of composite (Filtek Z250-3M ESPE) 4 mm high were built up and specimens were stored in deionized water for 24 hours at 37°C. Serial mesiodistal and buccolingual cuts were made and stick-like specimens were obtained, with transversal section of 1.0 mm2. The samples were submitted to microtensile test at 1 mm/min and load of 10 kg in a universal testing machine. Data (MPa) were subjected to ANOVA and Tukey's tests (p < 0.05). Results and conclusion: Surface treatment with Diamond or CVD tips associated with Clearfil SE Bond adhesive produced significantly lower bond strength values compared to other groups. Surface treatment with Er: YAG laser associated with Single Bond Plus or Clearfil SE Bond adhesives and surface treatment with CVD tip associated with Adper Scotchbond SE adhesive produced significantly lower bond strength values compared to surface treatment with diamond or CVD tips associated with Single Bond Plus or Adper Scotchbond SE adhesives. Clinical significance: Interactions between laser and the CVD tip technologies and the different adhesive systems can produce a satisfactory bonding strength result, so that these associations may be beneficial and enhance the clinical outcomes.

Effects of dentin dry/moist condition on the immediate adhesive performance of different solvent-based etch-and-rinse adhesivesystems

Purpose: The purpose of this research was to analyze and measure, under optical microscopy, the hybrid layer thickness and resin tags length, as well as the microtensile bond strength of two conventional adhesive systems when applied to dry and moist dentinal substrate. Methods: Thirty-two extracted human molars were randomly distributed into four groups according to the adhesive systems (XP Bond and Prime&Bond 2.1) and moisture condition (dry and moist). In Groups I and II, XP adhesive system was applied on dry and moist dentin, respectively; while Groups III and IV received PB adhesive system, in the same way as was done in Groups I and II, respectively. After adhesive and restorative procedures, all specimens were sectioned along their long axes; one hemi-tooth sample was subjected to the microtensile bond strength test while the other was decalcified and serially sectioned into six micron thick slices and sequentially mounted on glass slides. These sections were stained by the Brown and Brenn method for posterior analysis and measurement of the hybrid layer and resin tags under a light microscope with a micrometric ocular 40/075. Results: Data were analyzed using two-way ANOVA and Tukey's test (α=0.05). For the variable hybrid layer thickness, XP showed no significant differences between dry and moist dentin (5.2 μm and 5.5 μm, respectively), but for PB, hybrid layer was significantly thicker for moist (4.0 μm) than for dry dentin (3.0 μm). For the variable resin tags length XP showed 17.9 μm length for dry dentin and 20.8 μm for moist dentin; PB 11.7 μm for dry and 12.69 μm for moist dentin;there was no significant differences between them, independent of the moisture condition. For the variable microtensile bond strength, XP showed 38.0 MPa for dry dentin and 44.5 MPa for moist dentin; and PB showed 22.7 MPa for dry dentin and 20.8 MPa for dry dentin no significant difference was observed between moist and dry dentin for XP (p=0.2) and PB (p=0.7), but XP was presented significantly higher bond strength values than PB in both moisture conditions (p=0.003 for dry and p=0.002 for moist). Conclusion: The two-step butanol-based etch-and-rinse adhesive XP Bond presented a superior behavior with regard to the hybrid layer thickness, length of resin tags and bond strength to dry and moist dentin substrates when compared with two-step acetone-based adhesive system Prime&Bond2.1. © 2013 Elsevier Ltd.

Evaluation of degree of conversion and hardness of dental composites photoactivated with different light guide tips

Objective: The aim of this study was to evaluate the degree of conversion and hardness of different composite resins, photo-activated for 40 s with two different light guide tips, fiber optic and polymer. Methods: Five specimens were made for each group evaluated. The percentage of unreacted carbon double bonds (% C=C) was determined from the ratio of absorbance intensities of aliphatic C=C (peak at 1637 cm-1) against internal standard before and after curing of the specimen: aromatic C-C (peak at 1610 cm-1. The Vickers hardness measurements were performed in a universal testing machine. A 50 gf load was used and the indenter with a dwell time of 30 seconds. The degree of conversion and hardness mean values were analyzed separately by ANOVA and Tukey's test, with a significance level set at 5%. Results: The mean values of degree of conversion for the polymer and fiber optic light guide tip were statistically different (P<.001). The hardness mean values were statistically different among the light guide tips (P<.001), but also there was difference between top and bottom surfaces (P<.001). Conclusions: The results showed that the resins photo-activated with the fiber optic light guide tip promoted higher values for degree of conversion and hardness.

Protective effect of oregano (Origanum vulgar L.) and thyme (Thymus vulgaris L.) oleoresins in stored soybean oil

Purpose: The objective of this study was to evaluate the antioxidant effect of oregano and thyme extracts isolatedly and combinedly applied in soybean oil. Design/methodology/approach: Soybean oil containing 3,000 mg/kg of oregano and thyme oleoresins and the mixture of both, as well as soybean oil containing TBHQ (50 mg/kg) and soybean oil free of antioxidants, were subjected to accelerated oven test (60°C/10 days). Samples were collected every two days and analyzed as to their peroxide and conjugated diene values. Findings: The mixture of oleoresins and consequent increase of concentration were as effective as the antioxidant TBHQ. Practical implications: These studies may prove to be beneficial to the exploitation of natural antioxidant sources for the preservation and/or extension of raw and processed food shelf life. Therefore, they could also be applied in the area of pharmaceuticals for the protection of human life. Originality/value: This study offers information on the use of natural antioxidants as an alternative to the use of synthetic antioxidants, which might be considered toxic. © Emerald Group Publishing Limited.

Durability of Adhesion between Feldspathic Ceramic and Resin Cements: Effect of Adhesive Resin, Polymerization Mode of Resin Cement, and Aging

Purpose: Adhesive cementation is an important step for restorations made of feldspathic ceramic as it increases the strength of such materials. Incorrect selection of the adhesive resin and the resin cement to adhere to the ceramic surface and their durability against aging can affect the adhesion between these materials and the clinical performance. This study evaluated the effect of adhesive resins with different pHs, resin cements with different polymerization modes, and aging on the bond strength to feldspathic ceramic. Materials and Methods: One surface of feldspathic ceramic blocks (VM7) (N = 90) (6.4 × 6.4 × 4.8 mm3) was conditioned with 10% hydrofluoric acid for 20 seconds, washed/dried, and silanized. Three adhesive resins (Scotchbond Multi-Purpose Plus [SBMP], pH: 5.6; Single Bond [SB], pH: 3.4; and Prime&Bond NT [NT], pH: 1.7) were applied on the ceramic surfaces (n = 30 per adhesive). For each adhesive group, three resin cements with different polymerization modes were applied (n = 10 per cement): photo-polymerized (Variolink II base), dual polymerized (Variolink II base + catalyst), and chemically polymerized (C&B). The bonded ceramic blocks were stored in water (37°C) for 24 hours and sectioned to produce beam specimens (cross-sectional bonded area: 1 ± 0.1 mm2). The beams of each block were randomly divided into two conditions: Dry, microtensile test immediately after cutting; TC, test was performed after thermocycling (12,000×, 5°C to 55°C) and water storage at 37°C for 150 days. Considering the three factors of the study (adhesive [3 levels], resin cement [3 levels], aging [2 levels]), 18 groups were studied. The microtensile bond strength data were analyzed using 3-way ANOVA and Tukey's post hoc test (α= 0.05). Results: Adhesive resin type (p < 0.001) and the resin cement affected the mean bond strength (p= 0.0003) (3-way ANOVA). The NT adhesive associated with the chemically polymerized resin cement in both dry (8.8 ± 6.8 MPa) and aged conditions (6.9 ± 5.9 MPa) presented statistically lower bond strength results, while the SBMP adhesive resin, regardless of the resin cement type, presented the highest results (15.4 to 18.5 and 14.3 to 18.9 MPa) in both dry and aged conditions, respectively (Tukey's test). Conclusion: Application of a low-pH adhesive resin onto a hydrofluoric acid etched and silanized feldspathic ceramic surface in combination with chemically polymerized resin cement did not deliver favorable results. The use of adhesive resin with high pH could be clinically advised for the photo-, dual-, and chemically polymerized resin cements tested. © 2012 by the American College of Prosthodontists.

Influence of plaster drying on the amount of residual monomer in heat-cured acrylic resins

Aim: To evaluate the influence of plaster condition, dry or not, on the amount of residual monomer in heat-cured acrylic resin. Methods: Thirty acrylic resin specimens (65×10×3 mm) were fabricated and randomly assigned to 5 groups (n=6). The evaluated resins were heat-cured acrylic resins by conventional or microwave polymerization techniques and the plaster was previously dried in microwave oven in two groups. Each specimen was individually immersed in a test tube containing methanol (7 days) for surface analysis. In the groups for which internal monomer was evaluated, the specimens were fragmented and the small fragments were weighed prior to immersion in methanol. The analysis was made by high performance liquid chromatography (HPLC). Data were analyzed by ANOVA and Tukey test (p<5%) Results: showed statistical differences among the groups. Conclusions: The previous plaster drying influenced the residual monomer amount showing a decrease of these levels.

Effect of thermal cycling and disinfection on microhardness of acrylic resin denture base

The purpose of this study was to investigate the effect of thermal cycling and disinfection on the microhardness of acrylic resins denture base. Four different brands of acrylic resins were evaluated: Onda Cryl, QC 20, Classico and Lucitone. Each brand of acrylic resin was divided into four groups (n = 7) according to the disinfection method (microwave, Efferdent, 4% chlorhexidine and 1% hypochlorite). Samples were disinfected during 60 days. Before and after disinfection, samples were thermal cycled between 5-55 °C with 30-s dwell times for 1000 cycles. The microhardness was measured using a microhardener, at baseline (B), after first thermal cycling (T1), after disinfection (D) and after second thermal cycling (T2). The microhardness values of all groups reduced over time. QC-20 acrylic resin exhibited the lowest microhardness values. At B and T1 periods, the acrylic resins exhibited statistically greater microhardness values when compared to D and T2 periods. It can be concluded that the microhardness values of the acrylic resins denture base were affected by the thermal cycling and disinfection procedures. However, all microhardness values obtained herein are within acceptable clinical limits for the acrylic resins. © 2013 Informa UK Ltd.

Effect of immersion cleansers on the bond strength between a denture base resin and acrylic resin teeth

The aim of the present study was to assess the shear bond strength between a heat-polymerized denture base resin and acrylic resin teeth after immersion in different denture cleansers by simulating a 180-day use. Two acrylic teeth (Biotone, Biotone IPN, Dentsply Ind. e Com., Rio de Janeiro, RJ, Brazil) were chosen for bonding to a heat-polymerized denture base resin (Lucitone 550- Dentsply Ind. e Com., Rio de Janeiro, RJ, Brazil). Eighty specimens were produced and divided into eight groups (n=10) according to their experimental condition (distilled water, 2% chlorhexidine digluconate, 1% sodium hypochlorite and Corega Tabs). Shear bond strength tests (MPa) were performed with a universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed by two-way analysis of variance (ANOVA) and Student-Newman-Keuls' multiple comparisons post hoc analysis (α=.05). The shear bond strength results revealed statistically significant differences between the groups. For the Biotone IPN tooth, significantly lower shear bond strength values were found for the group immersed in sodium-perborate solution (4.48±2.18 MPa) than for the group immersed in distilled water (control group) (10.83±1.84 MPa). For Biotone, significantly higher bond strength values (10.04±3.28 MPa) were found for the group immersed in Corega Tabs than for the control group (5.45±2.93 MPa). The immersion in denture cleanser solutions was more detrimental to the conventional acrylic denture tooth (Biotone) than to the highly cross-linked denture tooth (Biotone IPN). However, this effect was not observed for the groups immersed in Corega Tabs solution, regardless of the type of denture tooth. © 2013 Elsevier Ltd.