Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel

Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental requirements causes one to search for possible alternatives. To improve the fatigue and corrosion resistance of AISI 4340 steel, an experimental study has been made for an intermediate electroless nickel layer deposited on base metal. The objective of this study was to analyze the effect of nickel underplate on the fatigue and corrosion strength of hard-chromium-plated AISI 4340 steel. Deposition of the conventional wear-resistant hard chromium plating leads to a decrease in mechanical properties of the base metal, especially the fatigue strength. Rotating bending fatigue tests results indicate better performance for conventional hard chromium plating. Good corrosion resistance in salt fog exposure was obtained for the accelerated hard chromium plating. Experimental data showed higher fatigue and corrosion resistance for samples prepared with accelerated hard chromium plate over electroless nickel plate, when compared with samples without electroless nickel underplate.

Influence of cross-head speed on resin-dentin shear bond strength

Objective: To evaluate the influence of different cross-head speeds on shear bond strength test on the dentin surface.Methods: One hundred and twenty extracted bovine incisors were embedded in polystyrene resin. The specimens were prepared by wet grinding with 320-, 400- and 600-grit Al2O3 paper exposing dentin. After the application of the adhesive system Single Bond (3M) to etched dentin, the composite resin Z-100 (3M) was applied and light cured. The specimens were randomly assigned to four groups (n = 30). The shear bond strength tests were performed with an EMIC DL 500 universal testing machine at four different cross-head speeds: 0.50 (A); 0.75 (B); 1.00 (C); and 5.00 mm/min (D).Results: the mean values of shear bond strength in MPa (SD) were: A, 11.78 (3.91); B, 11.82 (4.78); C, 16.32 (6.45); D, 15.46 (5.94). The data were analyzed with one-way ANOVA and Tukey's test (alpha = 0.05). The results indicated that A = B < C = D. The fracture pattern was evaluated by visual analysis in a stereomicroscope (25 x). The percentage of fractures that occurred at the adhesive interface were: A, 92.5%; B, 91.6%; C, 70.0%; D, 47.0%. The Student's t-test to percentages ( = 0.05) indicated that there were no significant differences among A, B and C; A and B differed from D, and there was no significant difference between C and D.Significance: Different cross-head speeds may influence the shear bond strength and the fracture pattern in dentin substrate. Shear bond strength using cross-head speeds of 0.50 and 0.75 mm/min should be preferred. (C) 2001 Academy of Dental Materials. published by Elsevier B.V. Ltd. All rights reserved.

Retention force and fatigue strength of overdenture attachment systems

This study evaluated retention force and fatigue resistance of two overdenture attachment systems. Twenty samples (O-ring and Bar-Clip) from two manufacturers (Conexao Sistemas de Protese and Lifecore Biomedical) were prepared and divided into four groups: (i) Conexao/O-ring; (ii) Conexao/Bar-Clip; (iii) Lifecore/O-ring and (iv) Lifecore/Bar-Clip, with five samples in each group. They were submitted to mechanical fatigue test using a servohydraulic machine performing 5500 cycles of insertion and removal (f=0.8 Hz), immersed in artificial saliva. Retention force values were obtained three times (0, 3000 and after 5500 cycles) simulating the clinical service, using a tensile strength at 1 mm min(-1) and load cell of 1 kN. Data were analysed with analysis of variance and Tukey's test at 5% level. Results showed that Conexao/Bar-Clip specimens had significantly higher retention values than Lifecore/Bar-Clip (44.61 and 18.44 N, respectively), Conexao/O-ring specimens had significantly lower values than Lifecore/O-ring (13.91 and 19.75 N, respectively). Conexao/Bar-Clip values were always significantly higher than those of Conexao/O-ring group (44.61 and 13.91 N, respectively). Lifecore (O-ring and Bar-Clip) presented similar values (19.75 and 18.44 N, respectively). The systems evaluated showed satisfactory retention force values, before and after fatigue testing. Conexao/Bar-Clip specimens presented the highest values. A 5-year simulation of insertion and removal did not decrease retention values or fracture components.