New compositions of fluoroindate glasses with higher chemical resistance

In this paper, glasses in the systems In-Ba-Mg and In-Ba-Zn-Sr-Mg were water leachead at 80ºC showing surface degradation after 72 hours of leaching. The extent of such degradation is determined by the solubility and the concentration of the elemental fluorides that constitute the glasses. The formation of a layer of crystallized phases on the surface of the samples was observed. Small weight losses were registered and the absence of water on the glass matrix after the attack suggested that the use of MgF2 in the systems studied can lead to better results against moisture corrosion when compared to other fluoride glasses such as the fluorozirconates.

Thermal and mechanical properties of PVDF/PANI blends

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Glass transitions and state diagram for freeze-dried pineapple

Glass transition temperature of freeze-dried pineapple conditioned by adsorption at various water activities at 25 degreesC was determined by differential scanning calorimetry (DSC). High moisture content samples corresponding to water activities higher than 0.9, obtained by liquid water addition, were also analysed. The DSC traces showed a well-visible shift in baseline at the glass transition temperature (T(g)). Besides, no ice formation was observed until water activity was equal to 0.75. For water activities lower than 0.88, the glass transition curve showed that T(g) decreased with increasing moisture content and the experimental data could be well-correlated by the Gordon-Taylor equation. For higher water activities, this curve exhibited a discontinuity, with suddenly increasing glass transition temperatures approaching a constant value that corresponds to the T(g) of the maximally freeze-concentrated amorphous matrix. The unfreezable water content was determined through melting enthalpy dependence on the sample moisture content.

Structural studies on lead-cadmium fluoride solid solutions

(1-x)PbF2-(x)CdF2 solid solutions (with 0.1 less than or equal to x less than or equal to 0.5) were obtained by hyper-quenching the melt. Structural characteristics have been studied by X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS). A cubic solid solution was obtained in which the lattice parameter decreases with increasing CdF2 content. High anionic disorder was evidenced from EXAFS investigations, whereas cations remain in the FCC arrangement. Pb L-3-edge EXAFS results illustrate clearly the occurrence of CdxPb1-xF2 mixed crystals by the introduction of Cd atoms in the second Pb coordination shell. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Spectroscopic investigation of a new hybrid glass formed by the interaction between croconate ion and calcium polyphosphate

In this work, a new organic-inorganic hybrid material has been synthesized by the incorporation of croconate ion into a calcium polyphosphate coacervate. The hybrid so obtained was characterized by means of electronic and vibrational spectroscopies. The material is a homogeneous mixture described by a structural model, which includes helical chains of polyphosphate ions, where the calcium ion occupies the internal vacancies of the structure. The croconate ion appears to be occupying the regions outside the polymeric structure, surrounded by several water molecules. The electronic spectrum of the incorporated material shows a broad band peaking at the same wavelength region (363 nm) observed for the aqueous solution of croconate ion, and manifesting the Jahn-Teller effect as evidenced by the doublet structure of the band. The infrared spectrum is widely dominated by the absorption bands of the polyphosphate ion and the appearance of the carbonyl stretching band at ca. 1550 cm(-1) indicates the presence of croconate ion incorporated in the structure. The Raman spectrum of the material shows several vibrational bands related to the oxocarbon moiety; most of them are shifted in comparison with the free ion. These shifts can be understood in terms of strong hydrogen bonding interactions between water molecules and the oxocarbon moiety. The low temperature methodology proposed here can be well used in the preparation of new phosphate glasses containing organic moieties opening the route to an entirely new class of hybrid glasses. (c) 2004 Elsevier B.V All rights reserved.

Different particle size silicas from water glass.

Non-crystalline silica was obtained with different particle sizes. Samples were prepared from soluble sodium silicate (water glass) and sulfuric acid solutions. Dialysis was performed for sodium sulfate elimination. Products were dried in a microwave oven, milled and characterized by X-ray powder diffraction, infrared spectrum and sedigraphic analysis. Products milled for more than 120 minutes showed uniform particle size distribution with average silica particle size of 4.5 mu m.

Effects of maturation and scarification on seed germination of Syagrus schizophylla (Mart.) glass. (Arecaceae)

Syagrus schizophylla (Mart.) Glass. belongs to the Arecaccae family. This palm is native of Brazil and presents great potential for use in gardens and cultivation in pot. Palms species, with relatively few exceptions, can only be propagated from seeds; even so, there are no reports in the literature about the germination of this palm seeds. The seed maturity is a factor that interferes in the success of the germination process. For some species, studies showed that palm seeds germinated better when the fruits were completely ripe (showing full color) and for other, when they were with green coloration. Several species of the Arecaccae family presents physical dormancy of seeds in varied degrees, demanding treatments for improve germination. The objective of this work was to study the effects of maturation and of the scarification on seed germination of S. schizophylla. The experimental design used was a factorial 3 x 2 (3 maturation stadiums: green, half-ripe - yellow and completely ripe - red; and mechanical scarification: with and without), entirely casualized, with four replications of 15 seeds per plot. The seeds (with 32,43% of humidity) were placed in plastic boxes with sand (60% of humidity, placing water according to weight in each three days), under controlled conditions of alternated temperature of 25-35 degrees C, photoperiod of 12 hours. The percentage of germination and the speed germination index (SGI) were evaluated until 79 days. It was observed that, so much for germination percentage as for SGI, there was not significant difference for the interaction among the two factors, maturation stadium and scarification, however, there were significant differences among the maturation stadiums and between seeds scarified or not. The seeds from green fruits presented lower germination percentage and slower germination when compared with seeds from yellow or red fruits; the seeds from yellow or red fruits didn't differ statistically to each other. To seeds scarificated, independently of the maturation stadium, presented germination percentage significantly larger and the germination was significantly faster when compared with the seeds without scarification.

Ytterbium-induced energy-transfer upconversion enhancement in Nd3+/Pr3+-codoped PbGeO3-PbF2-CdF2 glass excited at 810nm

The effect of ytterbium ions upon energy transfer (ET) excited upconversion emission in Nd3+/Pr3+ -codoped PbGeO3-PbF2-CdF2 glass under 810 nm diode laser excitation is investigated. The results revealed that the presence of Yb3+ ions in the Nd3+/Pr3+-doped sample yields a fourfold enhancement in the visible and near infrared upconversion luminescence. The dependence of the upconversion process upon the excitation power, Nd3+, and Yb3+ concentrations is examined. The results indicated that ytterbium plays a major role in the ET upconversion process by bridging the 810nm neodymium excitation to praseodymium ions. The population of the Pr3+ ions P-3(0) emitting level was accomplished through a multi-ion interaction involving ground-state and excited-state absorption of pump photons at 810 nm by the Nd3+ followed by successive ET involving the Nd3+-Yb3+ and Yb3+-Pr3+ pairs. There is also direct ET Nd3+-Pr3+. (c) 2005 Elsevier B.V. All rights reserved.

Effect of calcium pre-rinse and fluoride dentifrice on remineralisation of artificially demineralised enamel and on the composition of the dental biofilm formed in situ

Objective: This in situ blind crossover study investigated the effect of calcium (Ca) rinse prior to the use fluoride (F) dentifrice on remineralisation of artificially demineralised enamel and on the composition of biofilm. Design: During four phases of 14 days, 10 volunteers wore appliances containing two artificially demineralised bovine enamel blocks. Three times a day, they rinsed with 10 mL, of Ca (150 mM) or placebo rinse (1 min). A slurry (1:3, w/v) of F (1030 ppm) or placebo dentifrice was dripped onto the blocks. During I min, the volunteers brushed their teeth with the respective dentifrice. The appliance was replaced into the mouth and the volunteers rinsed with water. The biofilm formed on the blocks was analysed for F and Ca. Enamel alterations were evaluated by the percentage of surface microhardness change (%SMHC), cross-sectional microhardness (% mineral volume) and alkali-soluble F analysis. Data were analysed by ANOVA (p < 0.05). Results: the use of the Ca pre-rinse before the F dentifrice produced a six- and four-fold increase in biofilm F and Ca concentrations, respectively. For enamel, the remineralisation was significantly improved by the Ca pre-rinse when compared to the other treatments. There was a significantly higher concentration of alkali-soluble F in enamel when the F dentifrice was used, but the Ca pre-rinse did not have any significant additive effect. Conclusions: According to our protocol, the Ca pre-rinse significantly increased biofilm F concentration and, regardless the use of F dentifrice, significantly enhanced the remineralisation of artificially demineralised enamel. (c) 2007 Elsevier Ltd. All rights reserved.

A viscosity model for fluorochloroindate glasses

Viscosity of fluoride glasses is generally Arrhenian between glass transition temperature and crystallization temperature. This dependence on temperature is not observed in some special compositions which have two regions with different activation energies. The viscosity of glasses 40InF(3)-20ZnF(2)-25BaF(2)-10SrF(2)-5LiCl and 40InF(3)-20ZnF(2)-15SrF(2)-20BaF(2)-5NaCl was obtained by the parallel plate method. A theoretical model has been proposed to explain the viscosity data. (C) 1999 Elsevier B.V. B.V. All rights reserved.