Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0-14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia. © 2013 Elsevier B.V. All rights reserved.

Air-particle abrasion on zirconia ceramic using different protocols: Effects on biaxial flexural strength after cyclic loading, phase transformation and surface topography

This study evaluated the effect of different air-particle abrasion protocols on the biaxial flexural strength and structural stability of zirconia ceramics. Zirconia ceramic specimens (ISO 6872) (Lava, 3M ESPE) were obtained (N=336). The specimens (N=118, n=20 per group) were randomly assigned to one of the air-abrasion protocols: Gr1: Control (as-sintered); Gr2: 50 μm Al2O3 (2.5 bar); Gr3: 50 μm Al2O3 (3.5 bar); Gr4: 110 μm Al2O3(2.5 bar); Gr5: 110 μm Al2O3 (3.5 bar); Gr6: 30 μm SiO2 (2.5 bar) (CoJet); Gr7: 30 μm SiO2(3.5 bar); Gr8: 110 μm SiO2 (2.5 bar) (Rocatec Plus); and Gr9: 110 μm SiO2 (3.5 bar) (duration: 20 s, distance: 10 mm). While half of the specimens were tested immediately, the other half was subjected to cyclic loading in water (100,000 cycles; 50 N, 4 Hz, 37 °°C) prior to biaxial flexural strength test (ISO 6872). Phase transformation (t→m), relative amount of transformed monoclinic zirconia (FM), transformed zone depth (TZD) and surface roughness were measured. Particle type (p=0.2746), pressure (p=0.5084) and cyclic loading (p=0.1610) did not influence the flexural strength. Except for the air-abraded group with 110 μm Al2O3 at 3.5 bar, all air-abrasion protocols increased the biaxial flexural strength (MPa) (Controlnon-aged: 1030±153, Controlaged: 1138±138; Experimentalnon-aged: 1307±184-1554±124; Experimentalaged: 1308±118-1451±135) in both non-aged and aged conditions, respectively. Surface roughness (Ra) was the highest with 110 μm Al2O3(0.84 μm. FM values ranged from 0% to 27.21%, higher value for the Rocatec Plus (110 μm SiO2) and 110 μm Al2O3 groups at 3.5 bar pressure. TZD ranged between 0 and 1.43 μm, with the highest values for Rocatec Plus and 110 μm Al2O3 groups at 3.5 bar pressure. © 2013 Elsevier Ltd.

Deposição de filmes por plasma eletrolítico em ligas de alumínio

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Alteração das propriedades superficiais do alumínio via eletrólise e plasma

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Avaliação de maçã Royal Gala revestida com filme de quitosana durante o período de pós-colheita

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação das condições cromatográficas de análise e efeito da aplicação de coberturas comestíveis nos caratenóides de abóboras desidratadas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo dacriocistográfico e tomográfico da via lacrimal excretora de cães portadores de epífora

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Contribuição da comunicação visual para o design de superfície

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo experimental de ligações entre paredes de alvenaria estrutural de blocos cerâmicos sujeitas a ações verticais

Pós-graduação em Engenharia Civil - FEIS

Efeito da adição de revestimentos comestíveis sobre a qualidade de mamão desidratado após a secagem e durante o armazenamento

Pós-graduação em Engenharia e Ciência de Alimentos - IBILCE

Análise experimental do comportamento de vigas mistas de concreto e alvenaria estrutural sujeitas à flexão simples

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Procedimento numérico para análise de vigas de alvenaria estrutural submetidas à flexão simples

Pós-graduação em Engenharia Civil - FEIS

Diagnósticos dos procedimentos executivos nos canteiros de obras de alvenaria estrutural

Pós-graduação em Engenharia Civil - FEIS

Influência do graute e da taxa de armadura no comportamento da alvenaria de blocos de concreto

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estudo de polímeros comerciais tratados a plasma em pressão atmosférica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)