Amorphous silicon carbonitride films modified by plasma immersion ion implantation

Amorphous silicon carbonitride (a-SiCN:H) films were deposited from hexamethyldisilazane (HMDSN) organic compounds via radio-frequency (RF) glow discharges. Afterwards the films were bombarded, from 15 to 60 min, with nitrogen ions using Plasma Immersion Ion Implantation (PIII) technique. X-ray photoelectron spectroscopy (XPS) showed that O-containing groups increased, while C-C and/or C-H groups decreased with treatment time. This result indicates chemical alterations of the polymeric films with the introduction of polar groups on the surface, which changes the surface wettability. In fact, the hydrophobic nature of a-SiCN:H films (contact angle of 100 degrees) was changed by nitrogen ion implantation and, and after aging in atmosphere air, all samples preserved the hydrophilic character (contact angle <80 degrees) independently of treatment time. The exposure of the films to oxygen plasma was performed to evaluate the etching rate, which dropped from 24% to 6% while the implantation time increased from 15 to 60 min. This data suggests that Pill increased the film structure strength, probably due to crosslinking enhancement of polymeric chains. Therefore, the treatment with nitrogen ions via Pill process was effective to modify the wettability and oxidation resistance of a-SiCN:H films. (C) 2014 Elsevier Ltd. All rights reserved.

Protonation Pattern, Tautomerism, Conformerism, and Physicochemical Analysis in New Crystal Forms of the Antibiotic Doxycycline

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

One-dimensional silicon and germanium nanostructures with no carbon analogues

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Elucidating the crystal structure of the antimalarial drug (+/-)-mefloquine hydrochloride: a tetragonal hydrated species

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SILICON IN ROW AND NITROGEN IN TOPDRESSING FERTILIZATION ON RICE UNDER DRY LAND AND SPRINKLER IRRIGATION CONDITIONS

The objective of this work was to evaluate the effects of silicon application adjusted with nitrogen fertilization via top-dressing on grain productivity, the silicon contents of the soil, in the plant tissue and nitrogen contents in dry and irrigated conditions. The experimental outlining was from designed blocks with subdivided parcels and four repetitions. The treatments consisted of culture system (dry and irrigated) and the under parcels by the combination of silicon (0 and 100 kg ha(-1)), in magnesium and calcium silicate form (with 23% of SiO2), and four doses of N (urea) via top-dressing (0, 30, 60 and 90 kg ha(-1)). Silicon application at sowing furrow was a viable technique because it provided significant increase in the content of this element in the root growth of rice. The application of silicon in the sowing furrow did not change the content of the element nor the nitrogen nutrition in rice plants. The nitrogen application reduced the silicon content and increased nitrogen nutrition in rice plants. Silicon application at sowing furrow provided no increase in rice grain yield. When there was no water limitation to nitrogen fertilization enhanced linearly on rice grain yield, whereas under water stress the effect of nitrogen fertilization was limited.

Oxidation of ethanol and its derivatives on well defined pt single crystal electrodes vicinal to pt(111): a comparative study

The oxidation of ethanol (EtOH) at Pt(111) electrodes is dominated by the 4e path leading to acetic acid. The inclusion of surface defects such as those present on stepped surfaces leads to an increase of the reactivity towards the most desirable 12e path leading to CO2 as final product. This path is also favored when the methyl group is more oxidized, as in the case of ethylene glycol (EG) that spontaneously decomposes to CO on Pt(111) electrodes, thus showing a more effective breaking of the C-C bond. Some trends in reactivity can be envisaged when other derivative molecules are compared at well-ordered electrodes. This strategy was used in the past, but the improvement in the electrode pretreatment and the overall information available on the subject suggest that relevant information is still missing.

Production and Characterization of Composite Material Useful as a Protective Barrier in Electronic Applications

This work describes the production and characterization of a selective membrane useful for electronic devices. The membrane was a composite made by a thin film of plasma-polymerized HFE (methyl nonafluoro(iso)butyl ether) immersed in plasma-polymerized HMDS (hexamethyldisilazane) film, a third phase being 5 µm starch particles included in this matrix. The film was deposited on silicon substrates and its physical, chemical and adsorption characteristics were determined. Infrared and x-ray photoelectron spectroscopy analyses showed fluorine and carboxyl groups on the bulk and the surface, respectively. SEM results indicate the film is conformal even if starch is present. Optical microscopy analysis showed good resistance toward acid and base solutions. Quartz crystal microbalance indicated adsorption of polar organic compounds on ppm range. This thin film is environment-friendly and can be used as a protective layer or in electronic devices due to adsorption of volatile organic compounds.

Effect of different periods of preconditioning with saliva on adhesion of C. albicans to a denture base resin by crystal violet staining and XTT assay.

Aim: The role of saliva on Candida adhesion to biomaterials has not been clearly defined. The present study investigates whether different periods of preconditioning with saliva would influence the adhesion of Candida albicans to a denture base resin. Methods: Ninety samples of acrylic resin with smooth surfaces were made and then divided into five groups: one control without saliva, and four experimental groups conditioned in saliva for periods of 30 min, 1, 3, or 12 h. Candida adhesion was evaluated by crystal violet staining and 2,3-bis(2-methoxy-4-nitro-5-sulfophenyl)-5-([phenylamino] carbonyl)-2H-tetrazolium-hydroxide assay. Results: The one-way analysis of variance revealed that there were no significant differences among the mean number of adherent cells or among the mean absorbance for all groups. No significant correlation was found between the two methods used for assessing Candida albicans adhesion. Conclusion: The different periods of preconditioning with saliva had no significant influence on the adhesion of Candida albicans to the denture base acrylic resin.

Endogenous and exogenous teeth whitening through gel-based bleaching hydrogen peroxide (35%) with the aid of silicon guide

The aim of this study is to demonstrate through a case report, a proposed treatment for discolored teeth, with and without pulp vitality, by the technique of external and internal tooth bleaching with hydrogen peroxide to 35% Lase Peroxide Sensy (DMC) using Whitening Lase II Device (DMC), and a silicone guide (3M ESPE) in the palatine portion of the upper teeth. In this clinical case, the patient had darkened dental elements 11 and 22, and dissatisfaction with the coloring of other elements. It was observed that the techniques used and the materials chosen allowed for an excellent aesthetic result, with technical simplicity and low cost, and minimal occurrence of signs and symptoms

Biomarker evaluation in fish after prolonged exposure to nano-TiO2: influence of illumination conditions and crystal phase

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Multifunction hexagonal liquid-crystal containing modified surface TiO2 nanoparticles and terpinen-4-ol for controlled release

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystal growth and photoluminescence of europium-doped strontium titanate prepared by a microwave hydrothermal method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Surface morphology and structural modification induced by femtosecond pulses in hydrogenated amorphous silicon films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Foliar or soil applications of silicon alleviate water-deficit stress of potato plants

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)