Assessment of the flexural strength of two heat-curing acrylic resins for artificial eyes

Prosthetic eyes are artificial substitutes for the eyeball, made of heat-curing acrylic resin, serving to improve the esthetic appearance of the mutilated patient and his/her inclusion in society. The aim of this study was to assess the flexural strength of two heat-curing acrylic resins used for manufacturing prosthetic eyes. Thirty-six specimens measuring 64 x 10 x 3.3 mm were obtained and divided into four groups: acrylic resin for artificial sclera N1 (Artigos Odontológicos Clássico, São Paulo, SP, Brazil), heat-cure water technique (GI) and microwave-cured (GII); colorless acrylic resin for prosthetic eyes (Artigos Odontológicos Clássico, São Paulo, SP, Brazil), heat-cure water technique (GIII) and microwave-cured (GIV). Mechanical tests using three point loads were performed in a test machine (EMIC, São José dos Pinhais, PR, Brazil). The analysis of variance and the Tukey test were used to identify significant differences (p < 0.01). Groups GII and GIV presented, respectively, the highest (98.70 ± 11.90 MPa) and lowest means (71.07 ± 8.93 MPa), with a statistically significant difference. The cure method used for the prosthetic eye resins did not interfere in their flexural strength. It was concluded that all the resins assessed presented sufficient flexural strength values to be recommended for the manufacture of prosthetic eyes.

Bond strength of a composite resin to an adhesive luting cement

This study evaluated the influence of surface treatment on the shear bond strength of a composite resin (CR), previously submitted to the application of a temporary cement (TC), to an adhesive luting cement. Eight-four CR cylinders (5 mm diameter and 3 mm high) were fabricated and embedded in acrylic resin. The sets were divided into 6 groups (G1 to G6) (n=12). Groups 2 to 6 received a coat of TC. After 24 h, TC was removed and the CR surfaces received the following treatments: G2: ethanol; G3: rotary brush and pumice; G4: air-abrasion; G5: air-abrasion and adhesive system; G6: air-abrasion, acid etching and adhesive system. G1 (control) did not receive TC or any surface treatment. The sets were adapted to a matrix and received an increment of an adhesive luting cement. The specimens were subjected to the shear bond strength test. ANOVA and Tukey's tests showed that G3 (8.53 MPa) and G4 (8.63 MPa) differed significantly (p=0.001) from G1 (13.34 MPa). The highest mean shear bond strength values were found in G5 (14.78 MPa) and G6 (15.86 MPa). Air-abrasion of CR surface associated with an adhesive system provided an effective bond of the CR to the adhesive luting cement, regardless the pre-treatment with the phosphoric acid.

Retention strength of cobalt-chromium vs nickel-chromium titanium vs Cp titanium in a cast framework association of removable partial overdenture

Aim: There is little information considering the framework association between cast clasps and attachments. The aim of this study was to evaluate the retention strength of frameworks match circumferential clasps and extra resilient attachment cast in three different alloys (cobalt-chromium, nickel-chromium titanium and commercially pure titanium), using two undercut (0.25 and 0.75 mm) and considering different period of time (0, 1/2, 1, 2, 3, 4 and 5 years). Methods: Using two metallic matrices, representing a partially edentulous mandibular right hemiarch with the first molar crown, canine root and without premolars, 60 frameworks were fabricated. Three groups (n = 20) of each metal were cast and each group was divided into two subgroups (n = 10), corresponding the molar undercut of 0.25 mm and 0.75 mm. The nylon male was positioned at the matrix and attached to the acrylic resin of the prosthetic base. The samples were subjected to an insertion and removal test under artificial saliva environment. Results: The data were analyzed and compared with ANOVAs and Tukey's test at 95% of probability. The groups cast in cobaltchromium and nickel-chromium-titanium had the highest mean retention strength (5.58 N and 6.36 N respectively) without significant difference between them, but statistically different from the group cast in commercially pure titanium, which had the lowest mean retention strength in all the periods (3.46 N). The association frameworks using nickel-chromium-titanium and cobalt-chromium could be used with 0.25 mm and 0.75 mm of undercut, but the titanium samples seems to decrease the retention strength, mainly in the 0.75 mm undercut. The circumferential clasps cast in commercially pure titanium used in 0.75 mm undercuts have a potential risk of fractures, especially after the 2nd year of use. Conclusion: This in vitro study showed that the framework association between cast clasp and an extra resilient attachment are suitable to the three metals evaluated, but strongly suggest extra care with commercially pure titanium in undercut of 0.75 mm. Clinical significance: Frameworks fabricated in Cp Ti tend to decrease in retentive strength over time and have a potential risk of fracture in less than 0.75 mm of undercut.

Adhesion between fiber post and root dentin: evaluation of post surface conditioning for bond strength improvement.

The aim of this paper was to evaluate two surface conditioning methods associated with the application of adhesive on the post surface for improving the bond to resin cement. Sixty single-rooted bovine teeth were sectioned at 16 mm in length, prepared (9 mm depth), embedded in a PVC cylinder using acrylic resin, and allocated into 3 groups (N.=20) according to post surface treatment: cleaning with ethanol (control group); etching with hydrogen peroxide; etching with hydrofluoric acid. Ten posts for each group were silanized and other 10 posts were silanized and received an adhesive agent. The posts were cemented with self-adhesive resin cement (RelyX U100 resin cement). All teeth were sectioned perpendicularly to the long axis (2 mm thickness per slice), submitted to push out bond strength testing and the type of failure was recorded. The obtained data were submitted to two-way ANOVA and Turkey's test, with the level of significance set at 5%. Neither the hydrofluoric acid or hydrogen peroxide post surface treatment, nor the adhesive application, had an influence on bond strength values. The main type of failure was adhesive between cement and dentin. Etching and the application of an adhesive on the post surface did not presented a significant influence on the bond strength results for the fiber post resin cement-root dentin assembly. The cement appears to adhere very well to the fiber post surface rather than the dentin surface.

Prevalence and microscopic features of enamel pearls from permanent human molars

Enamel pearls are ectopic structures observed mainly on the roots of permanent teeth and could be related to periodontal diseases. Aim: To evaluate the prevalence of enamel pearls in extracted human molars and characterize their structures using light and scanning electron microscopy. Methods: The study comprised 2,201 extracted human permanent molars. The teeth were analyzed and classified according to morphological features. The presence, location and shape of enamel pearls were investigated. Fifteen human molars with enamel pearls were embedded in acrylic resin and observed by light microscopy. Results: Seventy-one enamel pearls were identified on third molar root. Microscopically, most pearls were composed of prismatic irregular enamel and normal dentin. The dentinoenamel junction presented an irregular course. The number of dentinal tubules was normal and they presented curvature to continue within the root dentin of the carrier tooth. Dentinal tubules below the enamel pearls were closer to each other. Conclusions: Scanning electron microscopic analysis revealed that the enamel pearls were similar to coronal enamel.

Fracture resistance of bovine incisors restored with different glass fiber posts: Effect of the diameter of fiber post

Aim: Compare the effect of three post designs on the fracture resistance and failure modes of composite core-fiber post-crownless tooth sets. Materials and Methods: Ninety bovine incisors were selected and divided into nine groups of 10 specimens. The teeth were assigned to three groups based on the post design: Cylindrical, tapered, and double-tapered. Each group was subdivided into three subgroups in accordance with the diameter of the post: Small (No.1), medium (No.2), and large (No.3). The Panavia F system was used for post cementation. The specimens were mounted in acrylic resin blocks with a layer of silicone rubber covering the roots. A universal testing machine compressively loaded the specimens from the palatal side at a crosshead speed of 1 mm/min and at an angle of 135I to the long axis of the teeth, until failure occurred. The failure mode was determined by a stereomicroscope inspection of all the specimens. Data were analyzed by one-way ANOVA and the Tukey test (P < 0.05). Results: The fracture resistance was affected by the type of post (P < 0.0001). A narrower diameter for all of the post systems allowed for higher resistance. The main failure mode in the large cylindrical group was catastrophic fractures, while the main failures in the other eight groups were favorable. Conclusion: Narrower diameter posts showed higher fracture resistance. The dominant failure pattern was repairable fracture, except for those with large cylindrical groups.

Influence of plaster drying on the amount of residual monomer in heat-cured acrylic resins

Aim: To evaluate the influence of plaster condition, dry or not, on the amount of residual monomer in heat-cured acrylic resin. Methods: Thirty acrylic resin specimens (65×10×3 mm) were fabricated and randomly assigned to 5 groups (n=6). The evaluated resins were heat-cured acrylic resins by conventional or microwave polymerization techniques and the plaster was previously dried in microwave oven in two groups. Each specimen was individually immersed in a test tube containing methanol (7 days) for surface analysis. In the groups for which internal monomer was evaluated, the specimens were fragmented and the small fragments were weighed prior to immersion in methanol. The analysis was made by high performance liquid chromatography (HPLC). Data were analyzed by ANOVA and Tukey test (p<5%) Results: showed statistical differences among the groups. Conclusions: The previous plaster drying influenced the residual monomer amount showing a decrease of these levels.

Avaliação da resistência de união entre dentina preparada por laser e um sistema adesivo a base de silorano, variando a técnica de aplicação e umidade do substrato

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência à fratura de raízes fragilizadas reabilitadas por diferentes técnicas de construção de núcleos intra-radiculares

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união ao microcisalhamento de sistemas adesivos distintos em substrato dentinário normal e hipermineralizado artificialmente

Pós-graduação em Ciências Odontológicas - FOAR

Influência do preparo biomecânico na microdureza e selamento marginal do MTA e do polímero derivado da mamona em perfurações radiculares simuladas

Pós-graduação em Odontologia Restauradora - ICT

Avaliação de tratamentos de superfície em diferentes sistemas cerâmicos e seu efeito na resistência de união a um cimento resinoso

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito do armazenamento prolongado em água sobre a resistência de união entre resinas para reembasamento e resina para base de prótese

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito de tratamentos da superfície de união e materiais reembasadores na resistência ao impacto de resina para base de prótese

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito de reembasamento, ciclagem mecânica e armazenagem em água sobre a resistência flexural de uma resina acrílica para base de prótese

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)