Estudo do efeito de cério como sensibilizador e ativador, em matrizes de difenilfosfinatos de lantânio, dopadas com európio e/ou térbio

This paper aims the preparation, characterization and study of luminescence, particularly as for the cerium ion action as activator or sensitizer, in diphenylphosphinate of lanthanum compounds trivalent ions cerium-, europium-, and/or terbium-doped. The following compounds were prepared and studied: i) La1-(x+y)CexEuy(DFF)3; ii) La1-(x+y)CexTby(DFF)3; iii) La1-(x+y+z)CexEuyTbz(DFF)3, with x = 10%, y = 5% e z = 5%. The diphenylphosphinate of lanthanum, Ln[(Ph2)PO2]3, are complexes obtained by the mixture of lanthanides chlorides with diphenylphosphinic acid, ethanol medium. These compounds make white powders, crystalline, insoluble in normal temperature and pressure, and are chemically and thermally stable. When doping with Ce3+, Eu3+ and/or Tb3+, the compounds present characteristic luminescence. Luminescent materials are made of a host matrix incorporated with few amounts of ions called activators, which are able to present luminescence after being excited by UV light or high energy radiation, and sensitizer ions, which have the role of absorbing excitation energy and transfer it to the activator, for it to emit luminescence radiation. The infrared vibrational spectroscopy indicates that the coordination occurs by the oxygens of phosphorile group with ΔνPO of about 40 cm-1 compared to the free ligand. The X Ray difractograms of compounds Eu- and/or Tb-doped are similar, but they present profile of diffraction different observed by Stucchi and col. In previous papers, indicated an influence of Ce in the crystalline phase formation of these matrices. In luminescence spectrums, the excitation that can be made by the levels of ligand in 273 nm, or cerium ion in area between 300 and 400 nm were observed. In the emission spectrum, with excitation in 273 nm, is possible to observe the emission of Ce3+ below 400 nm and the Eu3+ in 592, 611 and 617 nm, and the...as a sensitizer to.

Preparação e caracterização de novos híbridos orgânicos-inorgânicos baseados em carboximetilcelulose/polifosfato de sódio dopados com 'Eu'Cl IND.3

Organic- inorganic hybrid (HOI) are materials prepared with the combination of inorganic and organic components. The properties of a hybrid material are unique, not being the sum of each individual component added. This occurs because there is a synergism that depends of the chemical nature of organic and inorganic components, of the size and morphology of their domains. The sodium carboxymethylcellulose (CMC) it's an anionic polymer obtained of the cellulose, very soluble in water in which forms both solutions themselves and gels. The sodium polyphosphate (NaPO3)n, known commercially as Graham Salt is the only polyphosphate soluble in water, and it's the polyphosphate with the longest chain. At the present work it was prepared and characterized new phosphate organic- inorganic hybrids films of carboxymethylcellulose / sodium phosphate and luminescent films of CMC/NaPO3 doped with europium chloride (EuCl3). The films where prepared in several proportions. At first, it was set the amount of water to be used and the amount of carboxymethylcellulose, changing the concentrations of sodium polyphosphate and europium chloride. After pre-establishing concentrations, for each film, the components were submitted to constant agitation and subsequent drying. The inorganic-organic hybrid films were characterized by, TG, DR-X, DMA, FT-IR, UV-Vis-NIR, RMN 31P e 13C and at last, a study of luminescence was made. The hybrid films obtained are transparent and macroscopically homogeneous, however, the MET measures showed the formation of micro-islands of polyphosphate along the material, this fact indicates a bigger fragmentation of the films and this is verified by DMA analysis which shows a smaller resistance of the film with the increase of the concentration of phosphate. Both spectrum FT-IR and RMN analysis of the films, don't show the formation of new bands of their precursors, CMC e NaPO3,....

Propriedades luminescentes de polioxometalato contendo európio(III) correlacionadas à sua conformação em sólido estendido e em filmes auto-organizados de Langmuir e Langmuir-Blodgett

Pós-graduação em Química - IQ

Propriedades estruturais e espectroscópicas de WO3 e WO3:Eu3+

Used as catalysts even in organic and inorganic molecules, as additives on catalysts, electrochromic films on smart windows the tungsten trioxide have been largely studied on the lasts decades, but there is just a few about it's luminescence. Using as precursors nitric acid and sodium tungstate the tungsten trioxide were been prepared thru wet process then treating on thermic and hydrothermal treatments. Where been evaluated the effects of methodology, nitric acid concentration, duration and temperature of treatments. The samples were characterized by X-ray diffraction (XRD), Raman scattering spectroscopy (RSS), Fourier transformed infrared spectroscopy, photoluminescence spectroscopy (PLS) and X-ray excited optical luminescence (XEOL). Hydrated phases of tungsten trioxide were obtained through hydrothermal treatments and the non-hydrated phases occur with thermic treatments. The acid concentration has the ability to determine the major phase formed as well the temperature determine the hydratation of the product. With lower temperatures dihydrate phase were preferable formed and with the rise of temperature, the water molecules were lost up to the fractionary hydratation and then the non-hydrated phase with higher temperatures depending on the atmosphere used on the thermal treatment. Doping the system with europium ions even substituting tungsten or in the interstices of the matrix were not been successful, as well the XEOL spectroscopy intensity were null and quite low for ultraviolet and visible excitation photoluminescence because of oxygen defect levels localized into the prohibited band.