Synthesis of manganese porphyrinosilica imprinted with templates using the sol-gel process

The optimized conditions for the preparation of a new manganese porphyrinosilica-template material are reported. The manganese porphyrinosilica-template was prepared by the sol-gel process, by the reaction of -SO2Cl groups present in the phenyl rings of MnTDC(SO2Cl)PPCl with 3-aminopropyltriethoxysilane. The reaction produces a precursor porphyrinopropylsilyl species, which were then polymerized with tetraethoxysilane. The presence of manganese porphyrin on xerogel is confirmed by ultraviolet visible absorption spectroscopy and thermogravimetric analysis (TGA). The prepared materials have surface areas between 19 and 674 m2 g-1. Electron spectroscopy imaging of the materials show that manganese distribution in the xerogel is uniform. Both manganese(III) porphyrinosilica-template and a similar iron(III) porphyrinosilica-template can catalyze the epoxidation of cyclooctene using iodozylbenzene as oxygen donor. The metalloporphyrinosilica-template presents catalytic activity similar to that of metaloporphyrin in solution. © 2000 Elsevier Science B.V. All rights reserved.

Effect of in concentration in the starting solution on the structural and electrical properties of ZnO films prepared by the pyrosol process at 450°C

Undoped and indium-doped Zinc oxide (ZnO) solid films were deposited by the pyrosol process at 450°C on glass substrates from solutions where In/Zn ratio was 2, 5, and 10 at.%. Electrical measurements performed at room temperature show that the addition of indium changes the resistance of the films. The resistivities of doped films are less than non-doped ZnO films by one to two orders of magnitude depending on the dopant concentration in the solution. Preferential orientation of the films with the c-axis perpendicular to the substrate was detected by X-ray diffraction and polarized extended X-ray absorption fine structures measurements at the Zn K edge. This orientation depends on the indium concentration in the starting solution. The most textured films were obtained for solutions where In/Zn ratio was 2 and 5 at.%. When In/Zn = 10 at.%, the films had a nearly random orientation of crystallites. Evidence of the incorporation of indium in the ZnO lattice was obtained from extended X-ray absorption fine structures at the In and Zn K edges. The structural analysis of the least resistive film (Zn/In = 5 at.%) shows that In substitutes Zn in the wurtzite structure. © 2000 Elsevier Science B.V. All rights reserved.

Surface amorphization in diamond turning of silicon crystal investigated by transmission electron microscopy

Silicon crystal exhibits a ductile regime during machining prior to the onset of fracture when appropriate cutting conditions are applied. The present study shows that the ductile regime is a result of a phase transformation which is indirectly evidenced by the amorphous phase detected in the machined surface. Transmission electron microscopy (TEM) planar view studies were successfully performed on monocrystalline silicon (1 0 0) single point diamond turned. TEM electron diffraction patterns show that the machined surface presents diffuse rings along with traces of crystalline material. This is attributed to crystalline silicon immersed in an amorphous matrix. Furthermore, only diffuse rings in the diffraction patterns of the ductile chip are detected, indicating that it is totally amorphous. © 2000 Elsevier Science B.V. All rights reserved.

Crystallization of amorphous GaAs films prepared onto different substrates

This work reports changes in structural properties produced by thermal annealing of flash evaporated amorphous GaAs films using the micro-Raman scattering and the X-ray diffraction (XRD) techniques. Films of about 1 μm were grown on c-Si and glass substrates. The crystallization process is less effective for samples deposited on c-Si. This could be due to the ordering in the first layers of the film imposed by the oriented Si substrates. We propose that this ordering makes the growth of crystallites in these films more restrained than the growth occurring in the completely amorphous films on glass substrates. © 2002 Elsevier Science B.V. All rights reserved.

Urbach energy parameter of flash evaporated amorphous gallium arsenide films

The dependence of the optical absorption edge on the deposition crucible temperature is used to investigate the electronic states in As-rich a-GaAs flash evaporated films. The Urbach energy parameter, determined from photothermal deflection spectroscopy (PDS), presents large correlated variations with crucible temperature. The optical and electrical results are consistent with the As under coordinated sites being the more important defect in the material. © 2002 Elsevier Science B.V. All rights reserved.

Enhanced frequency upconversion in Er3+ doped fluoroindate glass due to energy transfer from Tm3+

Energy transfer processes between Er3+ and Tm3+ were investigated examining the frequency upconversion emissions in a fluoroindate glass pumped at 790 nm. A 60-fold enhancement in the emission at ≈670 nm originating from Er3+ was observed when Tm3+ at concentration of 2% was introduced in a sample containing 2% of Er3+. The results are explained considering the influence of cross-relaxation processes between the active ions. © 2002 Elsevier Science B.V. All rights reserved.

Tm3+ and Tm3+-Ho3+ doped fluorogermanate glasses for S-band amplifiers

Two series of glasses with composition (mol%) 70PbGeO3- 15PbF2-15CdF2, the first one with different Tm 3+ contents (0.2, 0.4, 0.6 and 0.8 mol%) and the second one with 0.2 mol% Tm3+ and different Ho3+ contents (0.1, 0.5, 1.0 and 1.5 mol%), have been prepared and some of their spectroscopic properties studied. Absorption in the visible-near infrared and emission in the near infrared region of the electromagnetic spectrum have been obtained. Concerning emission at the 1.4-1.5 μm region, optimization of rare earth ions content leads to 0.2 and 0.5 mol% for Tm3+ and Ho3+, respectively. We discuss potential application of these compositions. © 2005 Elsevier B.V. All rights reserved.

Magnetic resonance study of the crystallization behavior of InF3-based glasses doped with Cu2+, Mn2+ and Gd3+

The crystallization of fluoroindate glasses doped with Gd3+, Mn2+ and Cu2+ heat treated at different temperatures, ranging from the glass transition temperature (Tg) to the crystallization temperature (Tc), are investigated by electron paramagnetic resonance (EPR) and 19F nuclear magnetic resonance (NMR). The EPR spectra indicate that the Cu2+ ions in the glass are located in axially distorted octahedral sites. In the crystallized glass, the g-values agreed with those reported for Ba2ZnF6, which correspond to Cu2+ in a tetragonal compressed F- octahedron and to Cu2+ on interstitial sites with a square-planar F- co-ordination. The EPR spectra of the Mn2+ doped glasses exhibit a sextet structure due to the Mn2+ hyperfine interaction. These spectra suggest a highly ordered environment for the Mn2+ ions (close to octahedral symmetry) in the glass. The EPR spectra of the recrystallized sample exhibit resonances at the same position, suggesting that the Mn2+ ions are located in sites of highly symmetric crystalline field. The increase of the line intensity of the sextet and the decrease of the background line in the thermal treated samples suggest that the Mn2+ ions move to the highly ordered sites which contribute to the sextet structure. The EPR spectra of the Gd3+ doped glasses exhibit the typical U-spectrum of a s-state ion in a low symmetry site in disordered systems. The EPR of the crystallized glasses, in contrast, have shown a strong resonance in g ≈ 2.0, suggesting Gd3+ ions in environment close to cubic symmetry. The 19F NMR spin-lattice relaxation rates were also strongly influenced by the crystallization process that takes over in samples annealed above Tc. For the glass samples (doped or undoped) the 19F magnetization recoveries were found to be adjusted by an exponential function and the spin-lattice relaxation was characterized by a single relaxation time. In contrast, for the samples treated above Tc, the 19F magnetization-recovery becomes non-exponential. A remarkable feature of our results is that the changes in the Cu2+, Mn2+, Gd3+ EPR spectra and NMR relaxation, are always observed for the samples annealed above Tc. © 2006 Elsevier B.V. All rights reserved.

Anelastic spectroscopy in potassium aluminum metaphosphate glasses

Anelastic spectroscopy (internal friction and the dynamic modulus) was measured by means of a torsion pendulum at 3-12 Hz, in the range of 100-300 K, for a KAP metaphosphate glass. Two thermally activated internal friction peaks appeared at ∼190 and ∼250 K. These peaks were attributed to the behavior of potassium ions (high temperature) and to hydrogen (low temperature). Dynamic modulus showed a gradual decrease with increasing temperature in the range studied for all compositions. © 2006 Elsevier B.V. All rights reserved.

Temporal evolution of sulfated zirconia sol-gel during dip coating: Analysis of mass drainage with time-varying refractive index

The formation of sulfated zirconia films from a sol-gel derived aqueous suspension is subjected to double-optical monitoring during batch dip coating. Interpretation of interferometric patterns, previously obscured by a variable refractive index, is now made possible by addition of its direct measurement by a polarimetric technique in real time. Significant sensitivity of the resulting physical thickness and refractive index curves (uncertainties of ±7 nm and ±0.005, respectively) to temporal film evolution is shown under different withdrawal speeds. As a first contribution to quantitative understanding of temporal film formation with varying nanostructure during dip coating, detailed analysis is directed to the stage of the process dominated by mass drainage, whose simple modeling with temporal t-1/2 dependence is verified experimentally. © 2006 Elsevier B.V. All rights reserved.

Laser stimulated light reflection for TeO2-WO 3-Bi2O3 thin films with incorporated Si nanoparticles

A novel method of preparation of the Si nanoparticles (NPs) incorporated in tellurite TeO2-WO3-Bi2O3 (TWB) thin films is proposed. This mew method applies RF magnetron sputtering technique at room temperature. The incorporation of Si NP was confirmed by transmission electron microscopy (TEM); isolated Si NPs with diameters of around 6 nm are observed. Energy dispersive X-ray spectroscopy (EDS) was performed during TEM analysis in order to confirm the presence of Si NP and also the other elements of the thin film. The thin films are explored with respect to the photoinduced changes of the reflectivity within the 400-65 nm spectra range using a 10 ns pulsed Nd:YAG with power densities varying up to 400 MW/cm2 and beam diameter within the 3-5 mm range. The observed processes are analyzed within a framework of trapping level conceptions for the Si NP. The possible application of the discovered materials as optical sensitive sensors is proposed. © 2013 Elsevier B.V.

Structural characteristics of P123-modified supercritical drying and hydrophobic ambient pressure drying aerogels

Supercritical drying (SCD) and hydrophobic ambient pressure drying (APD) aerogels were prepared from hydrolysis of tetraethoxysilane in solutions of poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (P123) in the range of composition below the threshold for the ordered mesoporous silica precipitation. APD was carried out after silylation of wet gels with trimethylchlorosilane (TMCS) or hexamethyldisilazane (HMDZ). The samples were analyzed by small-angle X-ray scattering and nitrogen adsorption. Wet gels are formed by mass-fractal domains, with fractal dimension close to 2, and larger pores superposing the pores belonging to the fractal structure in case of high P123 concentrations. Aerogels exhibit smaller-sized mass-fractal domains with larger mass-fractal dimension accounting for some porosity elimination on drying. The pore volume of the aerogels increases significantly with the P123 amount and it is even larger in the APD aerogels than in the SCD aerogels. © 2013 Elsevier B.V. All rights reserved.

Tunable plasmon resonance modes on gold nanoparticles in Er 3 +-doped germanium-tellurite glass

Relative to the Er3 +:gold-nanoparticle (Er3 +:Au-NP) axis, the polarization of the gold nanoparticle can be longitudinal (electric dipole parallel to the Er3 +:Au-NP axis) or transverse (electric dipole perpendicular to the Er3 +:Au-NP axis). For longitudinal polarization, the plasmon resonance modes of gold nanoparticles embedded in Er3 +-doped germanium-tellurite glass are activated using laser lines at 808 and 488 nm in resonance with radiative transitions of Er3 + ions. The gold nanoparticles were grown within the host glass by thermal annealing over various lengths of time, achieving diameters lower than 1.6 nm. The resonance wavelengths, determined theoretically and experimentally, are 770 and 800 nm. The absorption wavelength of nanoparticles was determined by using the Frohlich condition. Gold nanoparticles provide tunable emission resulting in a large enhancement for the 2H11/2 → 4I13/2 (emission at 805 nm) and 4S 3/2 → 4I13/2 (emission at 840 nm) electronic transitions of Er3 + ions; this is associated with the quantum yield of the energy transfer process. The excitation pathways, up-conversion and luminescence spectra of Er3 + ions are described through simplified energy level diagrams. We observed that up-conversion is favored by the excited-state absorption due to the presence of the gold nanoparticles coupled with the Er3 + ions within the glass matrix. © 2013 Elsevier B.V.

Influence of ethanol and glycerol concentration over functional and structural properties of zein-oleic acid films

This study was performed in order to determine the effect of the addition of different concentrations of glycerol and ethanol over functional and structural properties of zein-oleic acid films. Films were prepared from zein and oleic acid formulations, containing: 0, 10, 20 and 30% (w/w) of glycerol as plasticizer and 75, 80, 85, 90 and 95% (v/v) of ethanol as zein solvent. Water vapor permeability (WVP) at 4 and 24 C, opacity, water solubility and structural behavior of the film were assessed. The film water barrier properties, WVP and water solubility, were increased when higher ethanol concentration and lower glycerol concentration were used. Furthermore, WVP at 4 C was lower than WVP at 24 C due to the crystalline solid state of oleic acid at lower temperatures. Likewise, opacity, homogeneity and structure of the composite film were improved as ethanol increased and glycerol lowered. © 2013 Elsevier B.V. All rights reserved.

Thermal and structural study of glasses in the binary system TeO2-Pb(PO3)(2)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)