The effect of the ocean water immersion and UV ageing on the dynamic mechanical properties of the PPS/glass fiber composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Polymer treatment by plasma immersion ion implantation of nitrogen for formation of diamond-like carbon film

Nitrogen ions were implanted by plasma immersion in Kapton, Mylar and polypropylene, with the objective of forming a diamond-like carbon layer on these polymers. The Raman spectrum of the implanted polypropylene showed typical Diamond-Like Carbon (DLC) graphite (G) and disorder (D) peaks, with an sp 3/sp2 hybridization ratio of approximately 0.4 to 0.6. The XPS analysis of the three implanted polymers also showed peaks of C-C and N-C bonds in the sp3 configuration, with hybridization ratios in the same range as the Raman result. The implanted polymers were exposed to oxygen plasma to test the resistance of the polymers to oxygen degradation. Mass loss rate results, however, showed that the DLC layer formed is not sufficiently robust for this application. Nevertheless, the layer formed can be suitable for other applications such as in gas barriers in beverage containers. Further study of implantation conditions may improve the quality of the DLC layer.

Structural analyzes of the use of residues of tires in reinforced concrete

The search for an adequate destination to the tires without use is a problem for many countries. The use of tire rubber in concrete through the partial substitution of the small aggregate has for objective the withdrawal of this material of the environment besides serving as alternative material in places that present sand scarcity. However, to use this type of concrete in civil construction it's necessary to verify its structural behavior. The behavior of the adherence enters the bar of armor and the concrete surrounding it has decisive importance with relation to the load capacity of the structures of reinforced concrete. In this context, this work presents, argues and evaluates the results of the experimental studies for determination of the adherence tension according to pulling up assays pull-out normalized for CEB RC6 and also related in the ASTM C-234 in concrete with and without rubber residues. Armors of nominal diameter of 10,0; 12,5 and 16 mm had been used and concrete contend 10% of rubber fibres in substitution to the sand in volume.

New developments for lignocellulosics-nanocomposites with low carbon footprint

Cellulose nanofibrils have been evaluated as reinforcement material in polymeric matrixes due to their potential to improve the mechanical, optical, and dielectric properties of these matrixes as well as its environmental positive footprint. This work describes how banana nanocellulose can be used to replace others not so friendly materials in many applications including, biomaterials, automotive industries and packaging by proved with their mechanical properties. The process used is very mild to the environment and consists of a high pressure fibrillation followed by a chemical purification which affects the fiber morphology. Many fibers characterization processes were used including microscopy techniques and X-ray diffraction to study the structure and properties of the prepared nanofibers and composites. Microscopy studies showed that the used individualization processes lead to a unique morphology of interconnected web-like structure of the fibers. © 2012 Materials Research Society.

Atmospheric plasma treatment of carbon fibers for enhancement of their adhesion properties

Plasma processing of carbon fibers (CFs) is aimed to provide better contact and adhesion between individual plies without decrease in the CF mechanical resistance. This paper deals with surface modification of CFs by an atmospheric pressure dielectric barrier discharge (DBD) for enhancing the adhesion between the CF and the polymeric matrix. The scanning electron microscopy of the treated samples revealed many small particles distributed over entire surface of the fiber. These particles are product of the fiber surface etching during the DBD treatment that removes the epoxy layer covering as-received samples. The alteration of the CF surface morphology was also confirmed by the Atomic force microscopy (AFM), which indicated that the CF roughness increased as a result of the plasma treatment. The analysis of the surface chemical composition provided by X-ray photoelectron spectroscopy showed that oxygen and nitrogen atoms are incorporated onto the surface. The polar oxygen groups formed on the surface lead to the increasing of the CF surface energy. The results of interlaminar shear strength test (short beam) of CFs/polypropylene composites demonstrated a greater shear resistance of the composites made with CFs treated by DBD than the one with untreated fibers. Both the increase in surface roughness and the surface oxidation contribute for the enhancement of CF adhesion properties. © 2012 IEEE.

Subcutaneous tissue reaction and cytotoxicity of polyvinylidene fluoride and polyvinylidene fluoride-trifluoroethylene blends associated with natural polymers

Cytotoxicity and subcutaneous tissue reaction of innovative blends composed by polyvinylidene fluoride and polyvinylidene fluoride-trifluoroethylene associated with natural polymers (natural rubber and native starch) forming membranes were evaluated, aiming its applications associated with bone regeneration. Cytotoxicity was evaluated in mouse fibroblasts culture cells (NIH3T3) using trypan blue staining. Tissue response was in vivo evaluated by subcutaneous implantation of materials in rats, taking into account the presence of necrosis and connective tissue capsule around implanted materials after 7, 14, 21, 28, 35, 60, and 100 days of surgery. The pattern of inflammation was evaluated by histomorphometry of the inflammatory cells. Chemical and morphological changes of implanted materials after 60 and 100 days were evaluated by Fourier transform infrared (FTIR) absorption spectroscopy and scanning electron microscopy (SEM) images. Cytotoxicity tests indicated a good tolerance of the cells to the biomaterial. The in vivo tissue response of all studied materials showed normal inflammatory pattern, characterized by a reduction of polymorphonuclear leukocytes and an increase in mononuclear leukocytes over the time (p < 0.05 Kruskal-Wallis). On day 60, microscopic analysis showed regression of the chronic inflammatory process around all materials. FTIR showed no changes in chemical composition of materials due to implantation, whereas SEM demonstrated the delivery of starch in the medium. Therefore, the results of the tests performed in vitro and in vivo show that the innovative blends can further be used as biomaterials. © 2013 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 101B: 1284-1293, 2013. Copyright © 2013 Wiley Periodicals, Inc.

Estudo dos critérios de falhas em compósitos PPS/fibras de carbono utilizando elementos finitos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural and optical properties of brominated plasma polymers

Novel brominated amorphous hydrogenated carbon (a-C:H:Br) films were produced by the plasma polymerization of acetylene-bromoform mixtures. The main parameter of interest was the degree of bromination, which depends on the partial pressure of bromoform in the plasma feed, expressed as a percentage of the total pressure, R-B. When bromoform is present in the feed, deposition rates of up to about 110 nm min(-1) may be obtained. The structure and composition of the films were characterized by Transmission Infrared Reflection Absorption Spectroscopy (IRRAS) and X-ray Photo-electron Spectroscopy (XPS). The latter revealed that films with atomic ratios Br:C of up to 0.58 may be produced. Surface contact angles, measured using goniometry, could be increased from similar to 63 degrees (for an unbrominated film) to similar to 90 degrees for R-B of 60 to 80%. Film surface roughness, measured using a profilometer, does not depend strongly on R-B. Optical properties the refractive index, n, absorption coefficient, alpha(E), where E is the photon energy, and the optical gap, E-g, were determined from film thicknesses and data obtained by Transmission Ultraviolet-Visible Near Infrared Spectroscopy (UVS). Control of n was possible via selection of R-B. The measured optical gap increases with increasing F-BC, the atomic ratio of Br to C in the film, and semi-empirical modeling accounts for this tendency. A typical hardness of the brominated films, determined via nano-indentation, was similar to 0.5 GPa. (C), 2013 Elsevier B.V. All rights reserved.

Viscoelastic Behavior of Multiwalled Carbon Nanotubes into Phenolic Resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Three-dimensional analysis of reinforced concrete members via embedded discontinuity finite elements

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Carbon isotope fractionation for cotton genotype selection

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

An Electrochemical Sensor for Reducing Sugars Based on a Glassy Carbon Electrode Modified with Electropolymerized Molecularly Imprinted Poly-o-phenylenediamine Film

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Potential of bamboo organosolv pulp as a reinforcing element in fiber-cement materials

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A new biomimetic sensor based on molecularly imprinted polymers for highly sensitive and selective determination of hexazinone herbicide

A new selective sensor based on molecularly imprinted polymers (MIPs) was developed for the determination of hexazinone (HXZ) in environmental samples. MIPs were synthesized using a non-covalent approach, and selection of the monomers employed in the polymerization reaction was carried out by molecular modeling. Three functional monomers with high (2-vinylpyridine (MP17)) and intermediate (methacrylic acid (MP12) and acrylamide (MP5)) energies of binding to the template (HXZ) were selected for preparation of the MIPs, in order to conduct comparative studies and validate the theoretical data. For sensor construction, carbon pastes were modified with each MIP or NIP (non-imprinted polymer), and HXZ determination was performed using differential pulse adsorptive cathodic stripping voltammetry (DPAdCSV). All parameters affecting the sensor response were optimized. In HCl at pH 2.5, the sensor prepared with MP17 (5% w/w in the paste) showed a dynamic linear range between 1.9 × 10−11 and 1.1 × 10−10 mol L−1, and a detection limit of 2.6 × 10−12 mol L−1, under the following conditions: accumulation time of 200 s at a potential of −0.5V, scan rate of 50 mVs−1, pulse amplitude of 60 mV, and pulse width of 50 ms. The sensor was selective in the presence of other similar compounds, and was successfully applied to the analysis of HXZ in river water samples.

Effect of random/aligned nylon-6/MWCNT fibers on dental resin composite reinforcement

The aims of this study were (1) to synthesize and characterize random and aligned nanocomposite fibers of multi-walled carbon nanotubes (MWCNT)/nylon-6 and (2) to determine their reinforcing effects on the flexural strength of a dental resin composite.Nylon-6 was dissolved in hexafluoropropanol (10 wt%), followed by the addition of MWCNT (hereafter referred to as nanotubes) at two distinct concentrations (i.e., 0.5 or 1.5 wt%). Neat nylon-6 fibers (without nanotubes) were also prepared. The solutions were electrospun using parameters under low- (120 rpm) or high-speed (6000 rpm) mandrel rotation to collect random and aligned fibers, respectively. The processed fiber mats were characterized by scanning (SEM) and transmission (TEM) electron microscopies, as well as by uni-axial tensile testing. To determine the reinforcing effects on the flexural strength of a dental resin composite, bar-shaped (20 x 2 x 2 mm(3)) resin composite specimens were prepared by first placing one increment of the composite, followed by one strip of the mat, and one last increment of composite. Non-reinforced composite specimens were used as the control. The specimens were then evaluated using flexural strength testing. SEM was done on the fractured surfaces. The data were analyzed using ANOVA and the Tukey's test (alpha=5%).Nanotubes were successfully incorporated into the nylon-6 fibers. Aligned and random fibers were obtained using high- and low-speed electrospinning, respectively, where the former were significantly (p<0.001) stronger than the latter, regardless of the nanotubes'presence. Indeed, the dental resin composite tested was significantly reinforced when combined with nylon-6 fibrous mats composed of aligned fibers (with or without nanotubes) or random fibers incorporated with nanotubes at 0.5 wt%. (C) 2015 Elsevier Ltd. All rights reserved.