Evaluation of the shear bond strength of a composite resin in sound, demineralized and hypermineralized bovine dentin after irradiation with Er:YAG and Nd:YAG lasers, employing a self-etching adhesive system

Background and Objectives. The adhesion of dental materials is important for the success of treatment. The aim of this study is to evaluate the bond strength of a composite resin applied with a self-etching adhesive system in different dentins after irradiation with Er:YAG and Nd:YAG lasers, observing their morphologic pattern using Scanning Electronic Microscopy (SEM). Materials and Methods. The buccal surface of 72 bovine incisors was worn until exposure of medium depth dentin. The specimens were divided into three groups; GI: normal, GII: demineralized and GIII: hypermineralized dentin. These were also divided into two subgroups; A-irradiated for 30 s with Er:YAG laser in noncontact mode at 40 mJ and 6 Hz and B- irradiated for 30 s with Nd:YAG laser in contact mode at 60 mJ and 10 Hz. The adhesive system Clearfil SE. Bond (Kuraray) and composite resin Tetric Ceram (Vivadent) were applied on the irradiated area by the incremental technique. After storage for 24 h in distilled water at 37 degrees C, the specimens were submitted to the shear strength test in a universal testing machine (EMIC) at a crosshead speed of 1.0 mm/min. Other specimens were made to be analyzed by SEM. Results. The results were statistically analyzed by Analysis of Variance and the Tukey test. Regardless of the type of dentin, the bond strength of specimens irradiated with the Nd:YAG laser (8,94 +/- 2,07) was higher compared to specimens irradiated with the Er:YAG laser (7,03 +/- 2,47); the highest bond strength was obtained for the group of hypermineralized dentin irradiated with the Nd:YAG laser. The SEM analysis showed that the Er:YAG laser caused opening of tubules and the Nd:YAG laser produced areas of fusion as well as regions of opening of dentinal tubules. Conclusions. The dentin showed different morphological patterns and the laser promote alterations on their surfaces, influencing the bond strength of the composite resin. (C) 2010 Laser Institute of America.

Synthetic and natural polycations for gene therapy: State of the art and new perspectives

Currently, the major drawback of gene therapy is the gene transfection rate. The two main types of vectors that. are used in gene therapy are based on viral or non-viral gene delivery systems. There are several non-viral systems that can be used to transfer foreign genetic material into the human body. In order to do so, the DNA to be transferred must escape the processes that affect the disposition of macromolecules. These processes include the interaction with blood components, vascular endothelial cells and uptake by the reticuloendothelial system. Furthermore, the degradation of therapeutic DNA by serum nucleases is also a potential obstacle for functional delivery to the target cell. Cationic polymers have a great potential for DNA complexation and may be useful as non-viral vectors for gene therapy applications. The objective of this review was to address the state of the art in gene therapy using synthetic and natural polycations and the latest strategies to improve the efficiency of gene transfer into the cell.

Effect of bleaching on sound enamel and with early artificial caries lesions using confocal laser microscopy

The aim of this study was to evaluate effect of bleaching agents on sound enamel (SE) and enamel with early artificial caries lesions (CL) using confocal laser scanning microscopy (CLSM). Eighty blocks (4 × 5 × 5 mm) of bovine enamel were used and half of them were submitted to a pH cycling model to induce CL. Eight experimental groups were obtained from the treatments and mineralization level of the enamel (SE or CL) (n=10). SE groups: G1 - unbleached (control); G2 - 4% hydrogen peroxide (4 HP); G3 - 4 HP containing 0.05% Ca (Ca); G4 - 7.5% hydrogen peroxide (7.5 HP) containing amorphous calcium phosphate (ACP). CL groups: G5 - unbleached; G6 - 4 HP; G7 - 4 HP containing Ca; G8 - 7.5 HP ACP. G2, G3, G6, G7 were treated with the bleaching agents for 8 h/day during 14 days, while G4 and G8 were exposed to the bleaching agents for 30 min twice a day during 14 days. The enamel blocks were stained with 0.1 mM rhodamine B solution and the demineralization was quantified using fluorescence intensity detected by CLSM. Data were analyzed using ANOVA and Fisher's tests (α=0.05). For the SE groups, the bleaching treatments increased significantly the demineralization area when compared with the unbleached group. In the CL groups, no statistically significant difference was observed (p>0.05). The addition of ACP or Ca in the composition of the whitening products did not overcome the effects caused by bleaching treatments on SE and neither was able to promote remineralization of CL.

Titanium in Dentistry: Historical development, state of the art and future perspectives

Titanium is a metallic element known by several attractive characteristics, such as biocompatibility, excellent corrosion resistance and high mechanical resistance. It is widely used in Dentistry, with high success rates, providing a favorable biological response when in contact with live tissues. Therefore, the objective of this study was to describe the different uses of titanium in Dentistry, reviewing its historical development and discoursing about its state of art and future perspective of its utilization. A search in the MEDLINE/PubMed database was performed using the terms 'titanium', 'dentistry' and 'implants'. The title and abstract of articles were read, and after this first screening 20 articles were selected and their full-texts were downloaded. Additional text books and manual search of reference lists within selected articles were included. Correlated literature showed that titanium is the most used metal in Implantology for manufacturing osseointegrated implants and their systems, with a totally consolidated utilization. Moreover, titanium can be also employed in prosthodontics to obtain frameworks. However, problems related to its machining, casting, welding and ceramic application for dental prosthesis are still limiting its use. In Endodontics, titanium has been used in association to nickel for manufacturing rotatory instruments, providing a higher resistance to deformation. However, although the different possibilities of using titanium in modern Dentistry, its use for prostheses frameworks still needs technological improvements in order to surpass its limitations. © 2012 Indian Prosthodontic Society.

Some deviations of form: a little essay on psychoanalysis, art and aesthetics

This work intends to investigate the use of psychoanalytical theory within the aesthetic and critical contemporary art field. To this purpose, it focuses on two philosophers who have become significant in our time: the art critic Hal Foster and the art historian Georges Didi-Huberman. This study aims to show how far the concepts generated in psychoanalytic praxis allowed interpretations that disrupt the traditional aesthetics field. This type of analysis is possible once we abandon the paradigm of “applied psychoanalysis”, which is still current in non-clinical setting. Finally, the proposal wants to argue that the category of the amorphous may clarify certain aesthetic experiences that range from the modernity of art through postmodernity.

Art in the inclusion of children with special needs in dentistry

A proposta deste estudo é relatar a utilização da arte e seus segmentos, como recurso para inclusão da criança portadora de necessidades especiais ao ambiente odontológico. Foi utilizado como método a aplicação da arte em atividades de socioterapia e oficinas, divididas em módulos: sessão de socialização, oficinas de arte e atividades complementares, visando à elaboração de uma anamnese cultural por meio de questionários e a obtenção das preferências artísticas dos 313 participantes, previamente às suas assistências odontológicas no CAOE (Centro de Assistência Odontológica a Portadores de Necessidades Especiais) FOA/Unesp. de acordo com os questionários respondidos, a música e a pintura, segundo a preferência dos participantes, são os segmentos artísticos que mais auxiliam nas atividades de inclusão e adaptação. Concluímos que a utilização da arte na adaptação e inclusão ambiental do paciente, previamente à assistência odontológica, é favorável e eficaz.

Effect of a 4% titanium tetrafluoride (TiF4) varnish on demineralisation and remineralisation of bovine enamel in vitro

Objectives: This in vitro study assessed the effect of a 4% TiF4 varnish on demineralisation and remineralisation of sound enamel and artificial carious enamel lesions, respectively.Methods: Bovine sound and carious enamel (n = 110) were randomly allocated to each type of varnish: Duraphat (R))-D (NaF, 2.26%F, pH 4.5, Colgate-Brazil, n = 30), Duofluorid (R)-F (NaF, 2.71%F, pH 8.0, FGM-Brazil, n = 30), TiF4-T (2.45%F, pH 1.0, FGM-Brazil, n = 30) and no-fluoride-P (FGM-Brazil, pH 5.0, n = 20). For the formation of artificial enamel caries, half of the blocks were immersed in 32 mL buffer acetate solution (16 h), whereas the other half was maintained sound. The varnishes were applied onto the enamel surfaces. Thus, the samples were subjected to pH cycles (37 degrees C) for 7 days. The response variables tested were surface and cross-sectional hardness. Data were tested using Kruskal-Wallis test (p < 0.05).Results: All F varnishes significantly reduced demineralisation and increased remineralisation in comparison to placebo. The TiF4 did not significantly reduce the surface enamel softening when compared with the other F varnishes, but it decreased the loss of subsurface hardness to the same extent. In enamel blocks with previous artificial carious lesions, the TiF4 significantly improved the rehardening compared to the other varnishes up to 30 mu m depth.Conclusions: The TiF4 varnish was able to decrease the demineralisation and increase the remineralisation of previously sound and carious enamel, respectively. It was equally effective compared to NaF varnishes on reducing the demineralisation at subsurface, but it was more effective on improving the remineralisation at surface and subsurface. (c) 2007 Elsevier Ltd. All rights reserved.

Evaluation of Laser Fluorescence in the Monitoring of the Initial Stage of the De-/Remineralization Process: An in vitro and in situ Study

This study aimed to evaluate laser fluorescence (LF) for monitoring the initial stage of subsurface de- and remineralization (<150 mu m depth). Ninety-six sound blocks of bovine enamel, selected according to surface hardness (SH) and LF were used in two experimental studies, in vitro and in situ. In vitro, blocks were exposed to a demineralizing solution, then remineralized by pH cycling for 6 days. In situ, 10 volunteers wore acrylic palatal appliances, each containing 4 dental enamel blocks that were demineralized for 14 days by exposure to 20% sucrose solution. Following this treatment, blocks were submitted to remineralization for 1 week with fluoride dentifrice (1,100 mu g F/g). In both experiments, SH and LH were measured after demineralization and after remineralization. Further, enamel blocks were selected after the demineralization/remineralization steps for measurement of cross-sectional hardness and integrated loss of subsurface hardness (Delta KHN). SH and Delta KHN showed significant differences among the phases in each study. LF values for sound, demineralized and remineralized enamel were: 5.2 +/- 1.1, 8.1 +/- 1.2 and 5.6 +/- 0.8, respectively, in the in vitro study, and 5.3 +/- 0.3, 16.5 +/- 4.7 and 6.5 +/- 2.5, respectively, in the in situ study, values for demineralized enamel being significantly higher than for sound and remineralized enamel in both studies. However, LF was correlated with Delta KHN only in situ. LF was capable of monitoring de- and remineralization in early lesions in situ, when bacteria are presumably present in the caries lesion body, but is not correlated with mineral changes in bacteria-free systems. Copyright (C) 2009 S. Karger AG, Basel

Disinfection of Bovine Enamel by Microwave Irradiation: Effect on the Surface Microhardness and Demineralization/Remineralization Processes

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caries resistance of lased human enamel with Er : YAG laser - morphological and ratio Ca/P analysis

Objective: In vitro analysis of caries resistance of dental enamel under caries simulation after irradiation with Er:YAG laser. Background Data: More susceptible to caries development spots at adjacent hard tissues from cavity preparations of dental tissues using burrs or lasers are quite common. Methods: Thirteen caries-free third permanent human molars were distributed as follows: G1: sound control and caries control; G2: Er:YAG 100, 200, 300, or 400 mJ/ 10 Hz/ 3 sec.; G3: the same parameters of G2 followed by artificial caries simulation, through dynamic model of demineralization and remineralization (DE/RE). Caries resistance analysis was evaluated through scanning electron microscopy (SEM) and Ca/P rate (X-Rays spectroscopy - EDX). Results: Photomicrographs showed that the Er:YAG laser created craters with rough aspect which became more evident as the energy per pulse was increased, but without change of regular morphology of enamel prisms. Significant statistical changes among the irradiated and control groups was observed considering the Ca/P ratio. Conclusion: Irradiated groups showed higher caries resistance than control groups. However, it is not possible to affirm that the enamel surface accidental irradiation could be a benefit to caries resistance for other situations can be considered, as biofilm deposit, which could increase the caries susceptibility.

Experimental Basis and New Insights for Cell Therapy in Chronic Obstructive Pulmonary Disease

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Secretion of middle ear in infants - Occurrence, recurrence and related factors

Objective: The present study aimed at evaluating the occurrence and recurrence of middle ear effusion and possible associated factors in the first two years of life of 190 newborns and infants, participants in the interdisciplinary prevention, detection, and intervention program at the Clínica de Educação para Saúde of Universidade do Sagrado Coração, Methods: Newborns and infants were monthly submitted to anamneses, otoscopy, behavioral hearing assessment using sound instruments and pure tones (pediatric audiometry) and tympanometry. Results: The results revealed that 68.4% of infants presented one or more episodes of middle ear effusion during their two first years, with more recurrence among males. Peak occurrence was between four and 12 months of age and, the earlier the first episode, the higher the probability of recurrence. Greatest incidence was during May and August. It was found that, of the variables investigated, the period of exclusive breastfeeding actuated as a protector factor. With respect of risk factors, it was observed that passive smoking, gastro-esophageal reflux and respiratory allergy were related with the recurrences of effusion. Conclusion: Findings revealed the importance of periodic auditory follow-up for infants during their first two years of life, considered to be the critical period of auditory system maturation, during which sensory deprivation can be responsible for damage to the development of speech, language and other auditory abilities. Copyright © 2005 by Sociedade Brasileira de Pediatria.

Effect of fluoridated varnish and silver diamine fluoride solution on enamel demineralization: pH-cycling study

Objective: In the present investigation, the anticariogenic effect of fluoride released by two products commonly applied in infants was evaluated. Methods: Bovine sound enamel blocks were randomly allocated to each one of the treatment groups: control (C), varnish (V) and diamine silver fluoride solution (D). The blocks were submitted to pH cycles in an oven at 37°C. Next, surface and cross-sectional microhardness were assessed to calculate the percentage loss of surface microhardness (%SML) and the mineral loss (ΔZ). The fluoride present in enamel was also determined. Results: F/Px10 -3 (ANOVA, p<0.05) in the 1 st layer of enamel before pH-cycling were (C, V and D): 1.61 a; 21.59 b and 3.98 c. The %SMH (Kruskal-Wallis, p<0.05) were: -64.0 a, -45.2 b and -53.1 c. %ΔZ values (ANOVA, p<0.05) were: -18.7 a, -7.7 b and -17.3 a. Conclusion: The data suggested that the fluoride released by varnish showed greater interaction with sound enamel and provided less mineral loss when compared with silver diamine solution.

Remote Sensing Detection of atmospheric pollutants using Lidar, Sodar and correlation with air quality data in an industrial area

Optical remote sensing techniques have obvious advantages for monitoring gas and aerosol emissions, since they enable the operation over large distances, far from hostile environments, and fast processing of the measured signal. In this study two remote sensing devices, namely a Lidar (Light Detection and Ranging) for monitoring the vertical profile of backscattered light intensity, and a Sodar (Acoustic Radar, Sound Detection and Ranging) for monitoring the vertical profile of the wind vector were operated during specific periods. The acquired data were processed and compared with data of air quality obtained from ground level monitoring stations, in order to verify the possibility of using the remote sensing techniques to monitor industrial emissions. The campaigns were carried out in the area of the Environmental Research Center (Cepema) of the University of São Paulo, in the city of Cubatão, Brazil, a large industrial site, where numerous different industries are located, including an oil refinery, a steel plant, as well as fertilizer, cement and chemical/petrochemical plants. The local environmental problems caused by the industrial activities are aggravated by the climate and topography of the site, unfavorable to pollutant dispersion. Results of a campaign are presented for a 24- hour period, showing data of a Lidar, an air quality monitoring station and a Sodar. © 2011 SPIE.

Laser ultrasonics system for measurement of speed of sound in gases

In this work we developed a setup to measure the speed of sound in gases using a laser ultrasonics system. The mentioned setup is an all optical system composed by a Q-switched Nd:YAG laser to generate the sound waves, and a fiber optical microphone to detect them. The Nd:YAG provided a laser pulse of approximately 420 mJ energy and 9 ns of pulse width, at the wavelength of 1064 nm. The pulsed laser beam, focused by a positive lens, was used to generate an electrical breakdown (in the gas) which, in turn, generates an sound wave that traveled through a determined distance and reached the fiber optical microphone. The resulting signal was acquired in an oscilloscope and the time difference between the optical pulse and the arrival of the sound waves was used to calculate the speed of sound, since the distance was known. The system was initially tested to measure the speed of sound in air, at room pressure and temperature and it presented results in agreement with the theory, showing to be suitable to measure the speed of sound in gases. © 2012 American Institute of Physics.