Processing and hygrothermal effects on viscoelastic behavior of glass fiber/epoxy composites

Fiber reinforced epoxy composites are used in a wide variety of applications in the aerospace field. These materials have high specific moduli, high specific strength and their properties can be tailored to application requirements. In order to screening optimum materials behavior, the effects of external environments on the mechanical properties during usage must be clearly understood. The environmental action, such as high moisture concentration, high temperatures, corrosive fluids or ultraviolet radiation (UV), can affect the performance of advanced composites during service. These factors can limit the applications of composites by deteriorating the mechanical properties over a period of time. Properties determination is attributed to the chemical and/or physical damages caused in the polymer matrix, loss of adhesion of fiber/resin interface, and/or reduction of fiber strength and stiffness. The dynamic elastic properties are important characteristics of glass fiber reinforced composites (GRFC). They control the damping behavior of composite structures and are also an ideal tool for monitoring the development of GFRC's mechanical properties during their processing or service. One of the most used tests is the vibration damping. In this work, the measurement consisted of recording the vibration decay of a rectangular plate excited by a controlled mechanism to identify the elastic and damping properties of the material under test. The frequency amplitude were measured by accelerometers and calculated by using a digital method. The present studies have been performed to explore relations between the dynamic mechanical properties, damping test and the influence of high moisture concentration of glass fiber reinforced composites (plain weave). The results show that the E' decreased with the increase in the exposed time for glass fiber/epoxy composites specimens exposed at 80 degrees C and 90% RH. The E' values found were: 26.7, 26.7, 25.4, 24.7 and 24.7 GPa for 0, 15, 30, 45 and 60 days of exposure, respectively. (c) 2005 Springer Science + Business Media, Inc.

Hygrothermal effects on damping behavior of metal/glass fiber/epoxy hybrid composites

Continuous fiber/metal laminates (FML) offer significant improvements over current available materials for aircraft structures due to their excellent fatigue endurance and low density. Glass fibers/epoxy laminae and aluminum foil (Glare) are commonly used to obtain these hybrid composites. The environmental factors can limit the applications of composites by deteriorating the mechanical properties during service. Usually, epoxy resins absorb moisture when exposed to humid environments and metals are prone to surface corrosion. Therefore, the combination of the two materials in Glare (polymeric composite and metal). can lead to differences that often turn out to be beneficial in terms of mechanical properties and resistance to environmental influences. In this work. The viscoelastic properties. such as storage modulus (E') and loss modulus (E'), were obtained for glass fiber/epoxy composite, aluminum 2024-T3 alloy and for a glass fiber/epoxy/aluminum laminate (Glare). It was found that the glass fiber/epoxy (G/E) composites decrease the E' modulus during hygrothermal conditioning up to saturation point (6 weeks). However, for Glare laminates the E' modulus remains unchanged (49GPa) during the cycle of hygrothermal conditioning. The outer aluminum sheets in the Glare laminate shield the G/E composite laminae from moisture absorption. which in turn prevent, in a certain extent, the material from hygrothermal degradation effects. (c) 2005 Elsevier B.V. All rights reserved.

Factors affecting on bond strength of glass fiber post cemented with different resin cements to root canal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Flexural Strength of Four Adhesive Fixed Dental Prostheses of Composite Resin Reinforced with Glass Fiber

Purpose: To evaluate the flexural strength of two fixed dental prosthesis (FDP) designs simulating frameworks of adhesive fixed partial prostheses, reinforced or not by glass fiber.Materials and Methods: Forty specimens, made with composite resin, were divided into 4 groups according to the framework design and the presence of fiber reinforcement: A1 - occlusal support; A2: occlusal support + glass fiber; B1: occlusal and proximal supports; B2: occlusal and proximal supports + glass fiber. The specimens were subjected to the three-point bending test, and the data were submitted to two-way ANOVA and Tukey's test (5%).Results: Group A2 (97.9 +/- 38 N) was statistically significantly different from all other experimental groups, presenting a significantly lower mean flexural strength.Conclusion: The use of glass fibers did not improve the flexural strength of composite resin, and designs with occlusal and proximal supports presented better results than designs simulating only occlusal support.

Influence of Environmental Conditioning on the Shear Behavior of Poly(phenylene sulfide)/Glass Fiber Composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

The effect of the ocean water immersion and UV ageing on the dynamic mechanical properties of the PPS/glass fiber composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

An In Vitro Comparison of Different Cementation Strategies on the Pull-out Strength of a Glass Fiber Post

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of the flexural strength of carbon fiber-, quartz fiber-, and glass fiber-based posts

This study investigated the flexural strength of eight fiber posts (one carbon fiber, one carbon/quartz fiber, one opaque quartz fiber, two translucent quartz fiber, and three glass fiber posts). Eighty fiber posts were used and divided into eight groups (n = 10): G1: C-POST (Bisco); G2: ÆSTHETI-POST (Bisco); G3: ÆSTHETI-PLUS (Bisco); G4: LIGHT-POST (Bisco); G5: D.T. LIGHT-POST (Bisco); G6: PARAPOST WHITE (Coltene); G7: FIBERKOR (Pentron); G8: REFORPOST (Angelus). All of the samples were tested using the three-point bending test. The averages obtained were submitted to the ANOVA and to Tukey's test (p < 0.05). The mean values (MPa) of the groups ÆSTHETI-POST - carbon/ quartz fiber post (Bisco) and ÆSTHETI-PLUS - quartz fiber post (Bisco) were statistically similar and higher than the mean values of the other groups. The mean values of the groups C-POST - carbon fiber post (Bisco), LIGHT-POST - translucent quartz fiber post (Bisco), D.T. LIGHT-POST - double tapered translucent quartz fiber post (Bisco), PARAPOST WHITE - glass fiber post (Coltene) and FIBREKOR - glass fiber post (Pentron) were similar and higher than the group REFORPOST - glass fiber post (Angelus). Copyright © 2005 by the American Association of Endodontists.

Three-year follow up of customized glass fiber esthetic posts

Customized glass fiber posts that is well adjusted into the root canal and have mechanical properties similar to those of dentin may be a suitable treatment for severely compromised endodontically treated teeth. This article reports a 3-year follow up of severely damaged endodontically treated teeth restored with unidirectional fiber glass customized post and core system instead of a conventional fiber post. The fabrication of this glass fiber customized post is a simple technique, providing an increased volume of fibers into the root canal, and an adequate polymerization of the post-core system. Over a three-year period, the treatments demonstrated good clinical and radiographic characteristics, with no fracture or loss of the post and/or crown. This technique can be considered effective, less invasive, and suitable for restore endodontically treated teeth.

Fracture resistance of bovine incisors restored with different glass fiber posts: Effect of the diameter of fiber post

Aim: Compare the effect of three post designs on the fracture resistance and failure modes of composite core-fiber post-crownless tooth sets. Materials and Methods: Ninety bovine incisors were selected and divided into nine groups of 10 specimens. The teeth were assigned to three groups based on the post design: Cylindrical, tapered, and double-tapered. Each group was subdivided into three subgroups in accordance with the diameter of the post: Small (No.1), medium (No.2), and large (No.3). The Panavia F system was used for post cementation. The specimens were mounted in acrylic resin blocks with a layer of silicone rubber covering the roots. A universal testing machine compressively loaded the specimens from the palatal side at a crosshead speed of 1 mm/min and at an angle of 135I to the long axis of the teeth, until failure occurred. The failure mode was determined by a stereomicroscope inspection of all the specimens. Data were analyzed by one-way ANOVA and the Tukey test (P < 0.05). Results: The fracture resistance was affected by the type of post (P < 0.0001). A narrower diameter for all of the post systems allowed for higher resistance. The main failure mode in the large cylindrical group was catastrophic fractures, while the main failures in the other eight groups were favorable. Conclusion: Narrower diameter posts showed higher fracture resistance. The dominant failure pattern was repairable fracture, except for those with large cylindrical groups.

Hybridization effect on the mechanical properties of curaua/glass fiber composites

The aim of this paper was to evaluate the effect of hybridizing glass and curaua fibers on the mechanical properties of their composites. These composites were produced by hot compression molding, with distinct overall fiber volume fraction, being either pure curaua fiber, pure glass fiber or hybrid. The mechanical characterization was performed by tensile, flexural, short beam, Iosipescu and also nondestructive testing. From the obtained results, it was observed that the tensile strength and modulus increased with glass fiber incorporation and for higher overall fiber volume fraction (%Vf). The short beam strength increased up to %Vf of 30 vol.%, evidencing a maximum in terms of overall fiber/matrix interface and composite quality. Hybridization has been successfully applied to vegetable/synthetic fiber reinforced polyester composites in a way that the various properties responded satisfactorily to the incorporation of a third component. © 2013 Published by Elsevier Ltd. All rights reserved.

Stress distribution on dentin-cement-post interface varying root canal and glass fiber post diameters. A three-dimensional finite element analysis based on micro-C data

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of fiber orientation on the shear behavior of glass fiber/epoxy composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparison of Different Dentin Pretreatment Protocols on the Bond Strength of Glass Fiber Post Using Self-etching Adhesive

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fatigue surviving, fracture resistance, shear stress and finite element analysis of glass fiber posts with different diameters

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)