Inorganic Graphenylene: A Porous Two-Dimensional Material With Tunable Band Gap

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Refractive index changes in photochromic SbPO4-WO3 glass by exposure to band-gap radiation

We report photoinduced photo-darkening in SbPO4-WO3 glass by exposure to 532 nm light with a power density of 143 mW/cm(2). The time of exposure was varied between 0 and 256 min following which visible photo-darkening, peaking at 850 nm was observed. Spectrophotometer measurement of absorption was performed for both treated and untreated regions of the sample. Time exposure to below band-gap light results in a single exponent Gaussian absorption function over an exceptionally wide range of wavelengths (500 nm-1600 nm), with a 1/e width of 647.5 nm. Kramers-Kronig transform of the change in the absorption indicates a negative local change in the refractive index. The dispersed refractive index change at 1550 nm, Delta n, is calculated to be similar to -5 x 10(-8). The peak absorption increases with time of exposure and the photo-darkening remains irreversible at room temperature. Crown Copyright (C) 2010 Published by Elsevier B.V. All rights reserved.

Microstructure, dielectric properties and optical band gap control on the photoluminescence behavior of Ba[Zr0.25Ti0.75]O-3 thin films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Strain- and electric field-induced band gap modulation in nitride nanomembranes

The hexagonal nanomembranes of the group III-nitrides are a subject of interest due to their novel technological applications. In this paper, we investigate the strain- and electric field-induced modulation of their band gaps in the framework of density functional theory. For AlN, the field-dependent modulation of the bandgap is found to be significant whereas the strain-induced semiconductor-metal transition is predicted for GaN. A relatively flat conduction band in AlN and GaN nanomembranes leads to an enhancement of their electronic mobility compared to that of their bulk counterparts. © 2013 IOP Publishing Ltd.

Síntese e caracterização de materiais semicondutores nanoestruturados luminescentes à base de ZnS

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

O papel dos modificadores de rede na produção da fotoluminescência no CaWO4

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SUBSTITUTIONAL DONOR RELATED STATES AND AU/GE/NI CONTACTS TO ALXGA1-XAS

Current-voltage measurements performed on bulk AlxGa1-xAs equipped with Au/Ge/Ni contacts reveal surprising deviations from ohmic behaviour when the temperature is lowered to that of liquid nitrogen. Significant differences are observed between samples with x = 0.3 (direct band-gap material) and x = 0.5 (indirect band-gap material). The dominant states of the donor atoms Si (doping) or Ge are found to be responsible for such behaviour. Evidence for the existence of an effective-mass X-valley metastable state is also presented.

The origin of photoluminescence in amorphous lead titanate

We discuss the nature of visible photoluminescence at room temperature in amorphous lead titanate in the light of the results of recent experimental and theoretical calculations. Experimental results obtained by XANES and EXAFS revealed that amorphous lead titanate is composed of a Ti-O network having fivefold Ti coordination and NBO-type (non-bridging oxygen) defects. These defects can modify the electronic structure of amorphous compounds. Our calculation of the electronic structure involved the use of first-principle molecular calculations to simulate the variation of the electronic structure in the lead titanate crystalline phase, which is known to have a direct band gap, and we also made an in-depth examination of amorphous lead titanate. The results of our theoretical calculations of amorphous lead titanate indicate that the formation of fivefold coordination in the amorphous system may introduce delocalized electronic levels in the HOMO ( highest occupied molecular orbital) and the LUMO ( lowest unoccupied molecular orbital). A comparison of the experimental and theoretical results of amorphous compounds suggests the possibility of a radiative recombination (electron-hole pairs), which may be responsible for the emission of photoluminescence. (C) 2003 Kluwer Academic Publishers.

The role of defect states in the creation of photoluminescence in SrTiO3

We discuss the nature of visible photoluminescence at room temperature in amorphous strontium titanate in the light of the results of a recent experimental and quantum mechanical theoretical study. Our calculation of the electronic structure involves the use of first-principles molecular calculations to simulate the variation of the electronic structure in the strontium titanate crystalline phase, which is known to have a direct band gap, and we also make an in-depth examination of amorphous strontium titanate. The results of our simulations of amorphous strontium titanate indicate that the formation of five-fold coordination in the amorphous system may introduce delocalized electronic levels in the highest occupied molecular orbital and the lowest unoccupied molecular orbital. These delocalized electronic levels are ascribed to the formation of a tail in the absorbance-spectrum curve. Optical absorption measurements experimentally showed the presence of a tail. The results are interpreted by the nature of these exponential optical edges and tails associated with defects promoted by the disordered structure of the amorphous material. We associate them with localized states in the band gap.

Ferroelectric and optical properties of Ba0.8Sr0.2TiO3 thin film

Barium strontium titanate (Ba0.8Sr0.2TiO3) thin films have been prepared on Pt/Ti/SiO2/Si substrates using a soft solution processing. X-ray diffraction and also micro-Raman spectroscopy showed that the Ba0.8Sr0.2TiO3 thin films exhibited a tetragonal structure at room temperature. The presence of Raman active modes was clearly shown at the 299 and 725 cm(-1) peaks. The tetragonal-to-cubic phase transition in the Ba0.8Sr0.2TiO3 thin films is broadened, and suppressed at about 35 degreesC, with a maximum dielectric constant of 948 (100 kHz). Electrical measurements for the prepared Ba0.8Sr0.2TiO3 thin films showed a remnant polarization (P-r) of 6.5 muC/cm(2), a coercive field (E-c) of 41 kV/cm, and good insulating properties. The dispersion of the refractive index is interpreted in terms of a single electronic oscillator at 6.97 eV. The direct band gap energy (E-g) and the refractive index (n) are estimated to be 3.3 eV and n = 2.27-2.10, respectively. (C) 2002 American Institute of Physics.

Photoluminescence of nanostructured PbTiO3 processed by high-energy mechanical milling

This letter reports on a process to prepare nanostructured PbTiO3 (PT) at room temperature with photoluminescence (PL) emission in the visible range. This process is based on the high-energy mechanical milling of ultrafine PbTiO3 powder. The results suggest that high-energy mechanical milling modifies the particle's structure, resulting in localized states in an interfacial region between the crystalline PT and the amorphous PT. These localized states are believed to be responsible for the PL obtained with short milling times. When long milling times are employed, the amorphous phase that is formed causes PL behavior. An alternative method to process nanostructured wide-band-gap semiconductors with active optical properties such as PL is described in this letter. (C) 2001 American Institute of Physics.

Dipole relaxation current in n-type AlxGa1-xAs

We report for the first time the thermally stimulated depolarization current (TSDC) spectrum for a direct band-gap AlGaAs sample, where the presence of DX centers is clearly observed by photoconductivity measurements. A TSDC band is obtained, revealing the presence of dipoles, which could be attributed to DX--d+ pairs as indeed predicted by O'Reilly [Appl. Phys. Lett. 55, 1409 (1989)]. The data are fitted by relaxation time distribution approach yielding an average activation energy of 0.108 eV. This is the most striking feature of our data, since this energy has approximately the same value of the DX center binding energy.

The role of network modifiers in the creation of photoluminescence in CaTiO3

We discuss the nature of visible photoluminescence (PL) at room temperature in amorphous calcium titanate in the light of the results of recent experimental and quantum mechanical theoretical studies. Our investigation of the electronic structure involved the use of first-principle molecular calculations to simulate the variation of the electronic structure in the calcium titanate crystalline phase, which is known to have a direct band gap, and we also made an in-depth examination of amorphous calcium titanate. The results of our theoretical calculations of amorphous calcium titanate indicate that the formation of fivefold coordination in the amorphous system may introduce delocalized electronic levels in the highest occupied and the lowest unoccupied molecular orbitals. These delocalized electronic levels are related to the formation of a tail in the absorbance spectrum curve. The results indicate that amorphous calcium titanate has the conduction band near the band gap dominated by Ca states contribution. Experimental optical absorption measurements showed the presence of a tail. These results are interpreted by the nature of these exponential optical edges and tails, associated with defects promoted by the disordered structure of the amorphous material. We associate them with delocalized states in the band gap. (C) 2002 Elsevier B.V. B.V. All rights reserved.

First-principles simulation of elastic constants and electronic properties of GaN

The electronic and structural properties and elastic constants of the wurtzite phase of GaN, was investigated by computer simulation at Density Functional Theory level, with B3LYP and B3PW hybrid functional. The electronic properties were investigated through the analysis of the band structures and density of states, and the mechanical properties were studied through the calculus of the elastic constants: C11, C33, C44, C12, and C13. The results show that the maximum of the valence band and the minimum of the conduction band are both located at the Γ point, indicating that GaN is a direct band gap semiconductor. The following constants were obtained for B3LYP and B3PW (in brackets): C11 = 366.9 [372.4], C33 = 390.9 [393.4], C44 = 99.1 [96.9], C12 = 143.6 [155.2], and C13 = 107.6 [121.4].

Synthesis, optical and ferroelectric properties of PZT thin films: experimental and theoretical investigation