Surface morphology and structural modification induced by femtosecond pulses in hydrogenated amorphous silicon films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of argon ion bombardment on amorphous silicon carbonitride films

Amorphous silicon carbonitride (a-SiCN:H) films were synthesized by radiofrequency (RF) Plasma Enhanced Vapor Chemical Deposition (PECVD) using hexamethyldisilazane (HMDSN) as precursor compound. Then, the films were post-treated by Plasma Immersion Ion Implantation (PIII) in argon atmosphere from 15 to 60 min The hardness of the film enhanced after ion implantation, and the sample treated at 45 min process showed hardness greater than sixfold that of the untreated sample. This result is explained by the crosslinking and densification of the structure Films were exposed to oxygen plasma for determining of the etching rate. It decreased monotonically from 33 angstrom/min to 19 angstrom/min for the range of process time, confirming structural alterations. Hydrophobic character of the a-SiCN:H films were modified immediately after ion bombardment, due to incorporation of polar groups. However, the high wettability of the films acquired by the ion implantation was diminished after aging in air. Therefore, argon PIII made a-SiCN.H films mechanically more resistant and altered their hydrophobic character.

Amorphous silicon carbonitride films modified by plasma immersion ion implantation

Amorphous silicon carbonitride (a-SiCN:H) films were deposited from hexamethyldisilazane (HMDSN) organic compounds via radio-frequency (RF) glow discharges. Afterwards the films were bombarded, from 15 to 60 min, with nitrogen ions using Plasma Immersion Ion Implantation (PIII) technique. X-ray photoelectron spectroscopy (XPS) showed that O-containing groups increased, while C-C and/or C-H groups decreased with treatment time. This result indicates chemical alterations of the polymeric films with the introduction of polar groups on the surface, which changes the surface wettability. In fact, the hydrophobic nature of a-SiCN:H films (contact angle of 100 degrees) was changed by nitrogen ion implantation and, and after aging in atmosphere air, all samples preserved the hydrophilic character (contact angle <80 degrees) independently of treatment time. The exposure of the films to oxygen plasma was performed to evaluate the etching rate, which dropped from 24% to 6% while the implantation time increased from 15 to 60 min. This data suggests that Pill increased the film structure strength, probably due to crosslinking enhancement of polymeric chains. Therefore, the treatment with nitrogen ions via Pill process was effective to modify the wettability and oxidation resistance of a-SiCN:H films. (C) 2014 Elsevier Ltd. All rights reserved.

Properties of hydrogenated amorphous carbon films deposited by PECVD and modified by SF6 plasma

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Crystallization process of amorphous GaSb films studied by Raman spectroscopy

Thermal annealings of amorphous gallium antimonide films were accompanied using Raman spectroscopy, both for stoichiometric and nonstoichiometric compositions. The films were prepared by flash evaporation on silicon substrates. Structural changes were induced by the heat treatments: an increasing degree of crystallization as a function of the annealing temperature is observed. Sb clusters are found to crystallize before GaSb does, and the dependence of the corresponding Raman peak intensity with the annealing temperature (occurring in two regimes) is explained. A mechanism for the crystallization of the amorphous GaSb is proposed, based on the prior migration of the Sb excess outside the GaSb region to be crystallized. © 1995 American Institute of Physics.

Crystallization of amorphous GaAs films prepared onto different substrates

This work reports changes in structural properties produced by thermal annealing of flash evaporated amorphous GaAs films using the micro-Raman scattering and the X-ray diffraction (XRD) techniques. Films of about 1 μm were grown on c-Si and glass substrates. The crystallization process is less effective for samples deposited on c-Si. This could be due to the ordering in the first layers of the film imposed by the oriented Si substrates. We propose that this ordering makes the growth of crystallites in these films more restrained than the growth occurring in the completely amorphous films on glass substrates. © 2002 Elsevier Science B.V. All rights reserved.

Optical, mechanical and surface properties of amorphous carbonaceous thin films obtained by plasma enhanced chemical vapor deposition and plasma immersion ion implantation and deposition

Diverse amorphous hydrogenated carbon-based films (a-C:H, a-C:H:F, a-C:H:N, a-C:H:Cl and a-C:H:Si:O) were obtained by radiofrequency plasma enhanced chemical vapor deposition (PECVD) and plasma immersion ion implantation and deposition (PIIID). The same precursors were used in the production of each pair of each type of film, such as a-C:H, using both PECVD and PIIID. Optical properties, namely the refractive index, n, absorption coefficient, α, and optical gap, ETauc, of these films were obtained via transmission spectra in the ultraviolet-visible near-infrared range (wavelengths from 300 to 3300 nm). Film hardness, elastic modulus and stiffness were obtained as a function of depth using nano-indentation. Surface energy values were calculated from liquid drop contact angle data. Film roughness and morphology were assessed using atomic force microscopy (AFM). The PIIID films were usually thinner and possessed higher refractive indices than the PECVD films. Determined refractive indices are consistent with literature values for similar types of films. Values of ETauc were increased in the PIIID films compared to the PECVD films. An exception was the a-C:H:Si:O films, for which that obtained by PIIID was thicker and exhibited a decreased ETauc. The mechanical properties - hardness, elastic modulus and stiffness - of films produced by PECVD and PIIID generally present small differences. An interesting effect is the increase in the hardness of a-C:H:Cl films from 1.0 to 3.0 GPa when ion implantation is employed. Surface energy correlates well with surface roughness. The implanted films are usually smoother than those obtained by PECVD. ©2013 Elsevier B.V. All rights reserved.

Photoluminescence at room temperature in amorphous SrTiO3 thin films obtained by chemical solution deposition

Intense photoluminescence in highly disordered strontium titanate amorphous thin films prepared by the polymeric precursor method was observed at room temperature (300 K). The luminescence spectra of SrTiO3 amorphous thin films at room temperature revealed an intense single-emission band in the visible region. X-ray absorption near edge structure was used to probe the local atomic structure of SrTiO3 amorphous and crystalline thin films. Photoluminescence intensity in the 535 nm range was found to be correlated with the presence of non-bridging oxygen defects. A discussion is presented of the nature of this photoluminescence, which may be related to the disordered structure in SrTiO3 amorphous thin films. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Correlation between the surface morphology and structure and the photoluminescence of amorphous PbTiO3 thin films obtained by the chemical route

A polymeric precursor method was used to synthesis PbTiO3 amorphous thin film processed at low temperature. The luminescence spectra of PbTiO3 amorphous thin films at room temperature revealed an intense single-emission band in the visible region, the visible emission band was found to be dependent on the thermal treatment history, Photoluminescence properties Versus different annealing temperatures were investigated. The experimental results (XRD, AFM, FL) indicate that the nature of photoluminescence (PL) must be related to the disordered structure of PbTiO3 amorphous thin films, Copyright (C) 2000 John Wiley & Sons, Ltd.

Development of amorphous carbon protective coatings on poly(vinyl)chloride

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Relationship between the optical gap and the optical-absorption tail breadth in amorphous GaAs

We study the relationship between the optical gap and the optical-absorption tail breadth for the case of amorphous gallium arsenide (a-GaAs). In particular, we analyze the optical-absorption spectra corresponding to some recently prepared a-GaAs samples. The optical gap and the optical-absorption tail breadth corresponding to each sample is determined. Plotting the optical gap as a function of the corresponding optical-absorption tail breadth, we note that a trend, similar to that found for the cases of the hydrogenated amorphous silicon and hydrogenated amorphous germanium, is also found for the case of a-GaAs. The impact of alloying on the optical-absorption spectrum associated with a-GaAs is also briefly examined. (C) 2004 American Institute of Physics.

Photoluminescence in amorphous TiO2-PbO systems

Photoluminescence (PL) at room temperature has been achieved in amorphous thin films and powders of the TiO2-PbO system. They were prepared by the polymeric precursor method with [PbO]/[TiO2] molar ratios ranging from 0.0 to 1.0. The energy position of maximum PL emission and the PL intensity showed dependence on Pb concentration. The Pb addition suggests an increase in the number of nonbridging oxygens (NBO) in the amorphous TiO2 network. These results support the relationship between photoluminescence and structure in TiO2-based amorphous materials.

Ferroelectric materials with photoluminescent properties

Amorphous LiNbO3 thin films processed by polymeric precursor method exhibited efficient luminescence at room temperature. The films were deposited on silicon substrates and treated at 200degreesC for different times. The photoluminescence emission yield decreases with the increase of the treatment time and disappears for crystalline films. A theoretical-experimental study was performed on amorphous and crystalline materials to understand the influence of the defects on the photoluminescence properties. The theoretical band gap obtained by the difference of energy between the HOMO and LUMO levels is larger for crystalline structure when compared with amorphous material. This result, which is in agreement with experimental band gaps obtained from optical measurements, revealed the emergence of new electronic levels for the amorphous material, which are localized in the wide band gap of the crystalline structure. These new electronic levels may explain the photoluminescence observed at room temperature for LiNbO3 amorphous films.

Thin films prepared from tungstate glass matrix

Vitreous samples containing high concentrations of WO3 (above 40% M) have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. These films were characterized by X-ray diffraction (XRD), perfilometry, X-ray energy dispersion spectroscopy (EDS), M-Lines and UV-vis absorption spectroscopy. In this work, experimental parameters were established to obtain stable thin films showing a chemical composition close to the glass precursor composition and with a high concentration of WO3. These amorphous thin films of about 4 mu m in thickness exhibit a deep blue coloration but they can be bleached by thermal treatment near the glass transition temperature. Such bleached films show several guided modes in the visible region and have a high refractive index. Controlled crystallization was realized and thus it was possible to obtain WO3 microcrystals in the amorphous phase. (C) 2007 Elsevier B.V. All rights reserved.

Caracterização de filmes finos obtidos por deposição de vapor químico assistido a plasma (PECVD) e deposição e implantação iônica por imersão em plasma (PIIID)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)