Comprovação da real comunicação entre o endodonto e o periodonto através do canal cavo inter-radicular e sua prevalência em molares inferiores humanos

The neurovascular system of the pulp and of the periodontium is interconnected and among the possible intercommunications between these two tissues, there is the cavo inter-radicular canal. It is a small canal that goes through any inter-radicular dentine and arises in the furca region of the multi-radicular teeth. Its predominance has been studied in the literature, by several methodologies, with divergent results. The objective of this work was to establish, in vitro, the predominance of the cavo inter-radicular canal, in human lower molars, through the diaphanization technique and dye leakage. For this research, 140 teeth (100 first and second 40 lower molars) were selected, extracted due to different reasons, belonging to a teeth bank of the Endodontics discipline of the Dentistry College at Federal University of Rio Grande do Norte. The teeth were preserved in formol until the moment of use and immersed in physiological solution. Had the endodontic access fulfilled and the whole external surface, except for the furcation, sealed with two layers of nail enamel. The cleaning of the pulpar chamber floor was carried out with sodium hypochlorite solution 5%, being this solution renewed every 5 minutes, during 1 hour. The teeth were immersed in Indian dye and, after drying of the dye, they had their crowns split up in the amelo-cemental junction. Then, they were examined in a stereomicroscope, where marks of the coloring were observed in the furcation and on the pulpar floor. After this recording, the sample was diaphanized and with the transparent teeth, it was possible to observe in the stereomicroscope, the true inter-radicular canals. As a result of this experiment, the presence of these canals was observed in 13 % of the first and 7, 5 % of the second evaluated molars. The study showed that both the presence of the cavo inter-radicular canal is real and the diaphanization and dye leakage is an efficient method for this type of research

Otimização de parâmetros mecânicos e microestruturais dos moldes em areia de sílica ligados quimicamente pelo processo de cura a frio em fundição de aço

Surface defects on steel parts borne costs of smelting industries due to the need of rework. Sand molds are frequently used in foundry industries and largely responsible for providing surface defects. This study aims to optimize the levels of the molding process variables to minimize the occurrence of surface defects in steel castings in silica sand molds chemically linked by cold cure process. The methodology used the experimental design with split plot, being considered in the study the resin percentage factors in the mold formulation, addition of iron oxide, type of paint, the paint application method, amount of ink layers, use of hot air along the lines and waiting time of the mold before casting. They were analyzed as response variables erosion defects, sand inclusion, penetration, porosity and surface finish. Tensile strength tests were performed to evaluate the influence of factors on mechanical parameters and the microstructural parameters were carried out the analysis of X-ray diffraction, scanning electron microscopy (SEM) and thermal analysis (TG / DSC / dilatometry). The results elucidate that for the faulty erosion, the only significant factor with a 95% confidence level was the type of ink and the ink alumina-based superior results obtained. For the sand inclusion of defect, there were three significant factors, with best results obtained with alumina-based paint and spray applied using hot air in the mold before casting the metal. For the defect penetration, there were four significant factors, the best results being achieved with 0.8% of resin and addition of iron oxide in the molding formulation, the paint being applied by brush and standby time of 24 hours before leak. For the defect porosity with a 95% confidence level, no significant factors. For the defect surface finish, the best results were achieved with the 0.8% formulation of the resin in the mold and application of the paint brush. To obtain the levels of the factors that optimize all defects simultaneously, we performed a weighted average of the results of each type of fault, concluding that the best levels of the factors were: 0.8% resin and addition of iron oxide in the formulation of the template, application of two coats of paint applied with a brush or spray, using hot air in the mold before casting and 24 hours of waiting ready the mold before casting. These levels of the optimized factors were used in an experiment to confirm that ratified the results, helping to reduce rework and consequently reducing costs of cast steel parts.

Modificação do eletrodo AWS E7018 com adição de filmes finos externos de PVC e Al, para soldagem de aço C-Mn

This paper suggests modifications in coating of electrodes providing an alternative for execution of welding with low hydrogen electrode AWS E7018 without having to dry it, reducing thus the cost and time of manufacturing of high resistance welds. The welds in this research were developed with basic coated electrodes (hygroscopic) – SMAW process – externally painted with aluminum spray paint for high temperatures or wrapped with thin plastic films (PVC) and aluminum foil films used commonly for food protection. The basic premise is that establishing a barrier between the atmosphere and the electrode coating could reduce the effects of high hygroscopicity presented by coatings of low hydrogen, minimizing this way the main source of supply of hydrogen to the fusion pool during welding. It is also expected that the addition of new materials from the electrode coating to the fusion pool would induce metallurgical changes in the deposited metal and, as a consequence, modifications in its mechanical properties. This research dealt with measuring the dissolved hydrogen in the deposited metal after welding with modified electrodes, evaluating the influence of these changes in the produced microstructures and in the mechanical properties of the resulting weld, and comparing the obtained results with the standard welding procedures and with the recently developed waterproof electrodes. The results obtained in most samples welded with modified electrodes showed increased mechanical resistance and increased tenacity due to the increased percentage of acicular ferrite in metal deposited without significant elevation of hardness, when compared with the traditional welding with AWS E7018 electrode and with ELBRÁS BRH4R waterproof electrode. The diffusing hydrogen measured in the modified electrodes was kept inside the parameters defined by international codes.

Modificação do eletrodo AWS E7018 com adição de filmes finos externos de PVC e Al, para soldagem de aço C-Mn

This paper suggests modifications in coating of electrodes providing an alternative for execution of welding with low hydrogen electrode AWS E7018 without having to dry it, reducing thus the cost and time of manufacturing of high resistance welds. The welds in this research were developed with basic coated electrodes (hygroscopic) – SMAW process – externally painted with aluminum spray paint for high temperatures or wrapped with thin plastic films (PVC) and aluminum foil films used commonly for food protection. The basic premise is that establishing a barrier between the atmosphere and the electrode coating could reduce the effects of high hygroscopicity presented by coatings of low hydrogen, minimizing this way the main source of supply of hydrogen to the fusion pool during welding. It is also expected that the addition of new materials from the electrode coating to the fusion pool would induce metallurgical changes in the deposited metal and, as a consequence, modifications in its mechanical properties. This research dealt with measuring the dissolved hydrogen in the deposited metal after welding with modified electrodes, evaluating the influence of these changes in the produced microstructures and in the mechanical properties of the resulting weld, and comparing the obtained results with the standard welding procedures and with the recently developed waterproof electrodes. The results obtained in most samples welded with modified electrodes showed increased mechanical resistance and increased tenacity due to the increased percentage of acicular ferrite in metal deposited without significant elevation of hardness, when compared with the traditional welding with AWS E7018 electrode and with ELBRÁS BRH4R waterproof electrode. The diffusing hydrogen measured in the modified electrodes was kept inside the parameters defined by international codes.