Efeito da adição de fibras da palma do licuri (syagrus coronata) no comportamento físico e mecânico de compósitos de matriz cimentícia

This research was motivated by the requirement of asbestos s replacement in building systems and the need to generate jobs and income in the country side of the state of Bahia, Brazil. The project aimed at using fibers from licuri leaves (syagrus coronata), an abundant palm in the region, to produce composites appropriate for the sustainable production of cement fibre reinforced products in small plants. The composites were produced in laboratory using Portland cement CP-II-F32, sand, water, licuri palm fiber contents of 1.0, 1.5 and 2.0% by weight of binder (two different fiber length) and metakaolin. The latter was chosen as an additional binder for its efficiency to reduce the alkalinity of cementitious matrixes therefore preventing the degradation of vegetable fibers. The characterization of the composite components was carried out by sieving and laser particle size analyses, thermal analysis, fluorescence and X-ray diffraction. The composites performance was evaluated by 3- point-bending tests, compressive strength, ultrasound module of elasticity, free and restrained shrinkage, water capillarity absorption and apparent specific gravity. It has been found that the addition of fibers increased the time to onset of cracking over 200.00% and a 25% reduction in cracks opening in the restrained shrinkage test. The capillary absorption reduced about 25% when compared to fiber-free composites. It was also observed with regard to flexural strength, compressive strength and specific gravity, that the addiction of fibers did not affect the composite performance presenting similar results for compounds with and without fibers. In general it can be stated that the reinforced composite fibers of palm licuri presents physical and mechanical characteristics which enable them to be used in the intended proposals of this research

Estudo do perfil térmico de fornos do tipo "caipira" utilizados pelo setor de cerâmica vermelha em parelhas na região Seridó-RN

The present study aimed to characterize the thermal profile of wood fired oven used by the red ceramic industry in Parelhas, in the Seridó region/RN, aiming to propose structural interventions that can contribute to increasing productivity and product quality, optimize wood consumption and mitigate existing losses during the burning process. The study was conducted at Cerâmica Esperança in the city of Parelhas -RN, Brazil, during the period from August 2012 to September 2013. Four treatments were performed with three replicates, ie, with, a total of 12 experimental units (burnings). In the first stage 4 treatments were performed with three replicates, totaling 12 experimental units (firings). In the second stage 2 treatments were performed with three replications, totaling 6 experimental units (firings). The physical characteristics of the wood were analyzed using standard NBR 11941 and NBR 7190 for basic density and moisture, respectively. The clay was used as a reference parameter for distinguishing treatments. For both the analysis and characterization was carried out using techniques of fluorescence X (XRF) rays, X-ray diffraction (XRD) analysis, particle size analysis (FA). In the first and second stages were monitored: the time during the firing process, the amount of wood used at each firing, the number of parts enfornadas for subsequent determination of the percentages of losses, but also product quality. To characterize the thermal profile of the oven, we measured the temperature at 15 points scored in the surface charge put into the oven. Measurements were taken every 30 minutes from preheat until the end of burning, using a pyrometer laser sight sighting from preheating until the end of burning. In the second step 12 metal cylinders distributed on the oven walls, and the cylinder end walls 8 of the furnace 2 and rollers on each side walls are installed equidistant to 17 cm from the soil and the surface 30 of the wall are installed. The cylinders distributed on the front were placed 50 cm above the furnace, and the base of the oven 20 cm distant from the ground. 10 also thermocouples were installed, and five thermocouples distributed 1.77 cm above the combustion chambers, and one thermocouple on each side, and three thermocouples in front of the oven. We carried out the measurements of the temperatures every 1 hour during the burning two hours in cooling the cylinders with a pyrometer and thermocouples for dattaloger. These were fixed with depth of 30 cm from the wall. After statistical analysis it was found that: the thermal profile of the furnace surface and at different heights was heterogeneous; and the ranges of density and moisture content of wood are within recommended for use as an energy source standards. We conclude that even at low temperatures reached during firing there was a significant production of good quality products, this is due to high concentrations of iron oxide and potassium oxide found in clay, which lowers the melting point of the piece. The average burn time for each step varied 650-2100 minutes wood consumption was on average 20 m3, product quality was on average 16% of first quality, 70% second, third and 5% to 10% loss . The distance between the wire and the surface of the oven was a significant parameter for all treatments, but with different variations, meaning that the wire should not be so generic and unique form, used as a criterion for completion of the burn process. The central part of the furnace was the area that reached higher temperature, and in a unified manner, with the highest concentration of top quality products. The ideal temperature curve, which provided the highest quality of ceramic products was achieved in the central part of the furnace

Estudo do potencial de utilização do resíduo da extração de esmeraldas na fabricação de cerâmica de revestimento

Companies involved in emerald mining and treatment represent an important area of industrial development in Brazil, with significative contribution to the worldwide production of such mineral. As a result, large volumes of emerald waste are constantly generated and abandoned in the environment, negatively contributing to its preservation. By the other side the interest of the use of mining waste as additive in ceramic products has been growing from researchers in recent years. The ceramic industry is constantly seeking to the marked amplification for the sector and perfecting the quality of the products and to increase the variety of applications. The technology of obtaining of ceramic tiles that uses mining residues assists market niches little explored. In this scenario, the objective of the present study was to characterize the residue generated from emerald mining as well as to assess its potential use as raw material for the production of ceramic tiles. Ceramic mixtures were prepared from raw materials characterized by X-ray fluorescence, X-ray diffraction, particle size analysis and thermal analysis. Five compositions were prepared using emerald residue contents of 0%, 10%, 20%, 30% and 40%. Samples were uniaxially pressed, fired at 1000, 1100 and 1200ºC and characterized aiming at establishing their mineralogical composition, water absorption, apparent porosity, specific mass, linear retraction and modulus of rupture. The results shows that the emerald residue, basically consisted of 73% of (SiO2 + Al2O3) and 17,77% of (MgO + Na2O+ K2O) (that facilitates sintering), can be added to the ceramic tile materials with no detrimental effect on the properties of the sintered products