Estudo da viabilidade da utilização de cinza de lodo de esgoto como adição em argamassa de cimento Portland

The use of sewage sludge as a raw material falls within the waste recycling key in the current process model environmental sustainability .Waste recycling has been consolidated as a sustainable environmentally sound technical solution, and. Despite showing very variable composition and characteristics, sewage sludge, can be considered as a residue with a high recycling potential in the building sector. In this paper the feasibility of using sewage sludge ash was studied in addition to Portland cement mortar in 1:3 mass considered the standard dash. This gray additions were studied in proportions of 5%, 10 %, 15 %, 20 %, 25% and 30% by mass of cement. The methodology was focused on the characterization of materials by physical, chemical , mechanical , environmental and morphological followed by the production of mortar tests ,and finalized by the characterization tests of mortar in the fresh state, through the consistency index, content of entrained air, bulk density and water retention, and in the hardened state by bulk density, water absorption by capillarity capillarity coefficient, compressive strength, tensile strength in bending ,tensile bond strength and microstructural analysis for percentages of 0 to 20%. After comparing with the standard mortar mortars with addition of ash, it is concluded that the ash of sewage sludge did not impair the integrity and properties of mortars with addition, including increasing resistance to compression and tension, being 20% more indicated percentage. Thus, it becomes feasible the addition of sewage sludge ash in Portland cement mortar for the trait studied

Uso da cinza do bagaço da cana-de-açúcar como matéria-prima na substituição dos fundentes para aplicações em porcelanato

The present study aims to evaluate the potential use of bagasse ash from sugar cane (CBC) as a flux, replacing phyllite and/or feldspar in standard industrial mass production of enameled porcelain, verifying the possibility of the CBC contribute to the overall reduction of the coefficient of thermal expansion of the ceramic mass. To this end, as a result of the research, we characterized the raw material components of the standard mass (clay, phyllite, kaolin, feldspar, quartz and talc) and the residue of BCC, by testing by XRF, XRD, AG, DTA and ATG. Specimens (CDP) were manufactured in the dimensions of 100 mm x 50 mm x 8 mm in uniaxial matrix under compaction pressure of 33 MPa, assembled in batches of 3 units subsequently sintered at temperatures of 1150°C to 1210°C by varying the Rating Scale at 10°C, heating and cooling ramp of 50°C/min and 25°C/min, with levels of 1 min, 3 min, 5 min, 8 min, 10 min, 15 min, 30 min and 60 min. analyzing the results of the physical properties of water absorption (WA), linear firing shrinkage (LFS), dilatometric analysis (DTA), flexural strain (SFT) and SEM of the sintered bodies in order to verify the adequacy of CDP to ISO 13006, ISO 10545, NBR 13816 standards; NBR 13817 and NBR 13818. The study showed that the formulations that best suit the requirements of the standards are:. G4 - which was applied in 10% of replacing the CBC phyllite, sintering temperature 1210 ° C for 10 min and porch, and F3 - with application of 7.5% of CBC to replace the feldspar in the sintering temperatures of 1190°C, 1200°C and 1210°C for 10 min and porch. These formulations showed better performance regarding the formation of primary and secondary mullite, with considerable reduction of cracks and pores, meeting the prerequisites of standards for glazed porcelain. The results shows that the use of the CBC as a flux in the preparation of porcelain mass meets standard parameters for the manufacture of the product, and thereby can reduce environmental impact and the cost of production. Therefore, it is recommended to use this residue in the ceramics industry, due to its industrial, commercial and collaborative viability for sustainability.