Desenvolvimento de bionanocompósitos: nano e microcristais de celulose com poli (álcool vinílico) e poli (ácido lático)

This work has the main objective to obtain nano and microcrystals of cellulose, extracted from the pineapple leaf fibres (PALF), as reinforcement for the manufacture of biocomposite films with polymeric matrices of Poly(vinyl alcohol) (PVA) and Poly(lactic acid) (PLA). The polymer matrices and the nano and microcrystals of cellulose were characterised by means of TGA, FTIR and DSC. The analysis was performed on the pineapple leaves to identify the macro and micronutrients. The fibers of the leaves of the pineapple were extracted in a desfibradeira mechanical. The PALF extracted were washed to remove washable impurities and subsequently treated with sodium hydroxide (NaOH) and sodium hypochlorite (NaClO) in the removal of impurities, such as fat, grease, pectates, pectin and lignin. The processed PALF fibers were hydrolysed in sulfuric acid (H2SO4) at a concentration of 13.5 %, to obtain nano and microcrystals of cellulose. In the manufacture of biocomposite films, concentrations of cellulose, 0 %, 1 %, 3 %, 6 %, 9% and 12% were used as reinforcement to the matrices of PVA and PLA. The PVA was dissolved in distilled water at 80 ± 5 oC and the PLA was dissolved in dichloromethane at room temperature. The manufacture of biocompósitos in the form of films was carried out by "casting". Tests were carried out to study the water absorption by the films and mechanical test of resistance to traction according to ASTM D638-10 with a velocity of 50 mm/min.. Chi-square statistical test was used to check for the existence of significant differences in the level of 0.05: the lengths of the PALF, lengths of the nano and microcrystals of cellulose and the procedures used for the filtration using filter syringe of 0.2 μm or filtration and centrifugation. The hydrophilicity of biocompósitos was analysed by measuring the contact angle and the thickness of biocompósitos were compared as well as the results of tests of traction. Statistical T test - Student was also applied with the significance level (0.05). In biodegradation, Sturm test of standard D5209 was used. Nano and microcrystals of cellulose with lengths ranging from 7.33 nm to 186.17 nm were found. The PVA films showed average thicknesses of 0.153 μm and PLA 0.210 μm. There is a strong linear correlation directly proportional between the traction of the films of PVA and the concentration of cellulose in the films (composite) (0,7336), while the thickness of the film was correlated in 0.1404. Nano and microcrystals of cellulose and thickness together, correlated to 0.8740. While the correlation between the cellulose content and tensile strength was weak and inversely proportional (- 0,0057) and thickness in -0.2602, totaling -0,2659 in PLA films. This can be attributed to the nano and microcrystals of cellulose not fully adsorbed to the PLA matrix. In the comparison of the results of the traction of the two polymer matrices, the nano and microcrystals have helped in reducing the traction of the films (composite) of PLA. There was still the degradation of the film of PVA, within a period of 20 days, which was not seen in the PLA film, on the other hand, the observations made in the literature, the average time to start the degradation is above 60 days. What can be said that the films are biodegradable composites, with hydrophilicity and the nano and microcrystals of cellulose, contribute positively in the improvement of the results of polymer matrices used.

Síntese hidrotérmica assistida por micro-ondas de tiO2, e aplicação em nanocompósito

In recent decades have seen a sharp growth in the study area of nanoscience and nanotechnology and is included in this area, the study of nanocomposites with self-cleaning properties. Since titanium dioxide (TiO2) has high photocatalytic activity and also antimicrobial, self-cleaning surfaces in your application has been explored. In this study a comparison was made between two synthesis routes to obtain TiO2 nanoparticles by hydrothermal method assisted by microwave. And after analysis of XRD and SEM was considered the best material for use in nanocomposites. It was deposited nanocomposite film of poly (dimethyl siloxane) (PDMS) with 0.5, 1, 1.5 and 2% by weight of nanoparticles of titanium dioxide (TiO2) by the spraying method. The nanocomposite was diluted with hexane and the suspension was deposited onto glass substrate, followed by curing in an oven with forced air circulation. The photocatalytic activity of the nanocomposite impregnated with methylene blue was evaluated by UV- vis spectroscopy from the intensity variation of absorption main peak at 660nm with time of exposure to the UV chamber. Changes in the contact angle and microhardness were analyzed before and after UV aging test. The effect of ultraviolet radiation on the chemical structure of the PDMS matrix was evaluated by spectrophotometry Fourier transform infrared (FTIR).The results indicated that the addition of TiO2 nanoparticles in the coating PDMS gave high photocatalytic activity in the decomposition of methylene blue, an important characteristic for the development of self-cleaning coatings

Síntese hidrotérmica assistida por micro-ondas de tiO2, e aplicação em nanocompósito

In recent decades have seen a sharp growth in the study area of nanoscience and nanotechnology and is included in this area, the study of nanocomposites with self-cleaning properties. Since titanium dioxide (TiO2) has high photocatalytic activity and also antimicrobial, self-cleaning surfaces in your application has been explored. In this study a comparison was made between two synthesis routes to obtain TiO2 nanoparticles by hydrothermal method assisted by microwave. And after analysis of XRD and SEM was considered the best material for use in nanocomposites. It was deposited nanocomposite film of poly (dimethyl siloxane) (PDMS) with 0.5, 1, 1.5 and 2% by weight of nanoparticles of titanium dioxide (TiO2) by the spraying method. The nanocomposite was diluted with hexane and the suspension was deposited onto glass substrate, followed by curing in an oven with forced air circulation. The photocatalytic activity of the nanocomposite impregnated with methylene blue was evaluated by UV- vis spectroscopy from the intensity variation of absorption main peak at 660nm with time of exposure to the UV chamber. Changes in the contact angle and microhardness were analyzed before and after UV aging test. The effect of ultraviolet radiation on the chemical structure of the PDMS matrix was evaluated by spectrophotometry Fourier transform infrared (FTIR).The results indicated that the addition of TiO2 nanoparticles in the coating PDMS gave high photocatalytic activity in the decomposition of methylene blue, an important characteristic for the development of self-cleaning coatings

Modulação da expressão da proteína XPA em resposta ao tratamento com azul de metileno fotossensibilizado

Reactive oxygen species (ROS) are produced by aerobic metabolism and react with biomolecules, such as lipids, proteins and DNA. In high concentration, they lead to oxidative stress. Among ROS, singlet oxygen (1O2) is one of the main ROS involved in oxidative stress and is one of the most reactive forms of molecular oxygen. The exposure of some dyes, such as methylene blue (MB) to light (MB+VL), is able to generate 1O2 and it is the principle involved in photodynamic therapy (PDT). 1O2 e other ROS have caused toxic and carcinogenic effects and have been associated with ageing, neurodegenerative diseases and cancer. Oxidative DNA damage is mainly repaired by base excision repair (BER) pathway. However, recent studies have observed the involvement of nucleotide excision repair (NER) factors in the repair of this type of injury. One of these factors is the Xeroderma Pigmentosum Complementation Group A (XPA) protein, which acts with other proteins in DNA damage recognition and in the recruitment of other repair factors. Moreover, oxidative agents such as 1O2 can induce gene expression. In this context, this study aimed at evaluating the response of XPA-deficient cells after treatment with photosensitized MB. For this purpose, we analyzed the cell viability and occurrence of oxidative DNA damage in cells lines proficient and deficient in XPA after treatment with MB+VL, and evaluated the expression of this enzyme in proficient and complemented cells. Our results indicate an increased resistance to treatment of complemented cells and a higher level of oxidative damage in the deficient cell lines. Furthermore, the treatment was able to modulate the XPA expression up to 24 hours later. These results indicate a direct evidence for the involvement of NER enzymes in the repair of oxidative damage. Besides, a better understanding of the effects of PDT on the induction of gene expression could be provided

Análise tribológica de um sistema de acionamento alternativo de pigs para a indústria do petróleo

It is analyzed through the concepts of tribology and mechanical contact and damage the suggestion of implementing a backup system for traction and passage of Pipeline Inspection Gauge (Pig) from the inside of pipelines. In order to verify the integrity of the pipelines, it is suggested the possibility of displacement of such equipment by pulling wires with steel wires. The physical and mechanical characteristics of this method were verified by accelerated tests in the laboratory in a tribological pair, wire versus a curve 90. It also considered the main mechanisms of wear of a sliding system with and without lubricant, in the absence and presence of contaminants. To try this, It was constructed a test bench able to reproduce a slip system, work on mode back-and-forth ("reciprocation"). It was used two kinds of wires, a galvanized steel and other stainless steel and the results achieved using the two kinds of steel cables were compared. For result comparative means, it was used steel cables with and without coating of Poly Vinyl Chloride (PVC). The wires and the curves of the products were characterized using metallographic analysis, microhardness Vickers tests, X-ray diffraction (XRD), X-Ray Refraction (XRF) and tensile tests. After the experiments were analyzed some parameters that have been measurable, it demonstrates to the impracticality of this proposed method, since the friction force and the concept of alternating request at the contact between the strands of wire and the inner curves that are part ducts caused severe wear. These types of wear are likely to cause possible failures in future products and cause fluid leaks

Efeito in vitro da terapia fotodinâmica sobre bactérias orais em suspensão e na formação de biofilme : ensaio com azul de metileno e toluidina ativados por luz halógena

Photodynamic therapy (PDT) has been proposed as an alternative method for the treatment of biofilm-dependent oral diseases like dental caries. This therapy consists of simultaneous action of a visible light (L) and a photosensitizer (FS) in the presence of oxygen, which leads to production of different reactive oxygen species that can interact with the bacterial cell components, and promote cell death. This study aims to evaluate the antimicrobial action of PDT on oral bacteria in suspension, as well as the formation of mono and multi-species biofilms, in vitro, from a standard strain of Streptococcus mutans (ATCC 25175) and saliva samples, respectively. The dye methylene blue (MB) and toluidine blue (TB) were used at a concentration of 100 mg/ L and activated by halogen light (600 to 750 nm) from a modified hand held photopolymerizer (Ultralux ®, Dabi Atlante, Ribeirão Preto , São Paulo, Brazil.). Planktonic cultures were prepared and submitted to different experimental conditions: 1. PDT using TB 2. PDT using MB, 3. L+ FS- , 4. TB + L - ; 5. MB+ L-; 6. L- FS- (negative control) and 7. administration of 0.12% chlorhexidine digluconate (positive control) (Periogard ®, Colgate-Palmolive Company, New York, USA). The immediate and mediated action of PDT on bacterial suspensions, as well as its effect on biofilm formation were observed from the number of colony-forming units per milliliter (CFU/mL) and measures optical density (OD). The data were statistically analyzed using the Kruskal-Wallis and Mann-Whitney test for the significance level of 5%. According to the results, the PDT showed no antibacterial action on suspensions of S. mutans, regardless of the dye used. PDT with MB activated by halogen light was able to reduce 86.6% CFU/mL multi-species planktonic cultures, however, this reduction was not significant (p > 0.05). PDT showed antibacterial effect, mediate on multi-species planktonic cultures with TB (p < 0.001) and MB (p < 0.001), activated by halogen light. PDT was able to prevent the formation of multispecies biofilm, through the activation of TB by halogen light (p = 0.01). We conclude that activation of the dye toluidine blue and methylene blue, by halogen light (PDT) showed antimicrobial activity, compared to multi-species planktonic cultures prepared from saliva samples

Matrizes poliméricas puras e modificadas para adsorção do gás sulfeto de hidrogênio

The underground natural gas found associated or not with oil is characterized by a mixture of hydrocarbons and residual components such as carbon dioxide (CO2), nitrogen gas (N2) and hydrogen sulfide (H2S), called contaminants. The H2S especially promotes itself as a contaminant of natural gas to be associated with corrosion of pipelines, to human toxicity and final applications of Natural Gas (NG). The sulfur present in the GN must be fully or partially removed in order to meet the market specifications, security, transport or further processing. There are distinct and varied methods of desulfurization of natural gas processing units used in Natural Gas (UPGN). In order to solve these problems have for example the caustic washing, absorption, the use of membranes and adsorption processes is costly and great expenditure of energy. Arises on such findings, the need for research to active processes of economic feasibility and efficiency. This work promoted the study of the adsorption of sulfide gas in polymer matrices hydrogen pure and modified. The substrates of Poly(vinyl chloride) (PVC), poly(methyl methacrylate) (PMMA) and sodium alginate (NaALG) were coated with vanadyl phosphate compounds (VOPO4.2H2O), vanadium pentoxide (V2O5), rhodamine B (C28H31N2O3Cl) and ions Co2+ and Cu2+, aiming to the adsorption of hydrogen sulfide gas (H2S). The adsorption tests were through a continuous flow of H2S in a column system (fixed bed reactor) adsorption on a laboratory scale. The techniques used to characterize the adsorbents were Infrared spectroscopy (FTIR), thermogravimetry analysis (TGA), X-ray fluorescence (XRF), the X-ray diffraction (XRD) electron microscopy (SEM). Such work indicates, the results obtained, the adsorbents modified PMMA, PVC and NaALG have a significant adsorptive capacity. The matrix that stood out and had the best adsorption capacity, was to ALG modified Co2+ with a score of 12.79 mg H2S / g matrix

Caracterização e aplicação de vermicultura natural e quimicamente modificada na adsorção de azul de metileno

Chemical modification of clays has been extremely studied in the search for improvements of their properties for use in various areas, such as in combating pollution by industrial effluents and dyes. In this work, the vermiculite was chemically modified in two ways, characterized and evaluated the adsorption of methylene blue dye. First was changed with the addition of a surfactant (hexadecyltrimethylammonium bromide, BHTA) making it an organophilic clay and then by adding an acid (HCl) by acid activation. Some analyzes were performed as X-ray fluorescence (FRX), X-ray diffraction (DRX), adsorption isotherms of methylene blue dye, infrared (FTIR) , scanning electron microscopy (SEM), thermal gravimetric analysis and spectroscopy energy dispersive (EDS). Analysis by FRX of natural vermiculite indicates that addition of silicon and aluminum, clay presents in its structure the magnesium, calcium and potassium with 16 % organic matter cations. The DRX analyzes indicated that the organic vermiculite was an insertion of the surfactant in the space between the lamellae, vermiculite and acid partial destruction of the structure with loss of crystallinity. The adsorption isotherms of methylene blue showed that there was a significant improvement in the removal of dye to the vermiculite with the addition of cationic surfactant hexadecyltrimethylammonium bromide and treatment with acid using HCl 2 mol/L. In acid vermiculites subsequently treated with surfactant, the adsorption capacity increased with respect to natural vermiculite, however was much lower compared vermiculite modified with acid and surfactant separately. Only the acidic vermiculite treated with surfactant adjusted to the Langmuir model. As in the infrared spectrometry proved the characteristics of natural vermiculite. In the organic vermiculite was observed the appearance of characteristic bands of CH3, CH2, and (CH3)4N. Already on acid vermiculite, it was realized a partial destruction with decreasing intensity of the characteristic band of vermiculite that is between 1074 and 952 cm-1. In the SEM analysis, it was observed that there was partial destruction to the acid treatment and a cluster is noted between the blades caused by the presence of the surfactant. The TG shows that the higher mass loss occurs at the beginning of the heating caused by the elimination of water absorbed on the surface between layers. In the organic vermiculite also observed a loss of mass between 150 and 300 °C caused decomposition of the alkylammonium molecules (surfactants)

Avaliação da eficiência da técnica de obturação pela compressão hidrùlica vertical após instrumentação automatizada

The purpose of this study was to evaluate through radiographic and microscopic analysis the efficiency of the filling techniques by vertical hidraulic compression after the root canal mechanical instrumentation in vitro as well to evaluate the marginal apical leakage through macroscopic and microscopic analysis. Thirty human mandibular molars were used , they were divided on three groups, these were subdivided on six subgroups with five specimens each, come down to 106 root canals filled. Initially, the teeth were instrumented with Profile system series 29 and filled with two ways: single accessory cone or single cone associated with gutta-percha secundary cone, with Fill Canal sealer or Sealer 26. Completed the filling, the teeth were coated with araldit and finger -nail polish except for the apical 2 mm and dried for 3 hours, thep radiographs were taken of the teeth in orto and disto-radiai directions. Next, the coronal seal was carried out with composite resin photopolymerized and with their process of making impermeable. Teeth of positive controls were used without araldit and finger-nail polish whereas the negative controls were used with total coat of araldit and finger-nail polish. The specimens were placed in 2% Methylene Blue dye for 24 hours and thermocycled for 7 days. Afterwards, sections were made of each tooth at mesial and distal roat, after this the teeth were radiographed at buccolíngual direction for a macroscopic analysis and at buccolingual and mesiodistal directions for assessment of the marginal apical leakage. Cross sections were made 3 mm to 3mm since the tooth apice. The sections obtained for each group were observed with a stereomicroscope to evaluate the quality of the root canal filling and the marginal apical leakage. The results showed that: In the four techniques the marginal dye leakage was present in the apical third; in all groups the quality of the root canal filling in the radiography was better at mesial root canal and the single cone technique showed inefficient when only a single distal root canal was present. In the radiographic evaluation the best quality of the root canal filling was observed in the 1A group (single accessory cone + FiIl Canal), as in the mesial root as in the distal root wich Shcwed twe root canals: when the distaI root had only one canal. the best result was showed by 28 group (single accessory cone associated with secundary cone + Fill Canal) In the macroscopic analysis of longitudinal !eaKage (outside surface). less leakage was showed as In the mesial root as in the distal root in the negative control group (3) followed 2A group (single accessory cone + Sealer 26). When the microscopic analysis of tranversal leakage of both roots (inside surface) was carried out. the groups that showed less dye leakage were the negative control (38) followed the 28 group (single acessory cone associated with secundary cone + Sealer 26). The homogeneity o filling was best noted in the 1 A group (.single accessoty cone + Fill Canal). The groups that showed less dye penetration in the tranversal leakage (total area) were negative control (3B) and 2B

Características estruturais e fotocatalíticas do compósito oxihidróxido de nióbio/vermiculita

The preparation of nanostructured materials using natural clays as support, has been studied in literature under the same are found in nature and consequently, have a low price. Generally, clays serve as supports for metal oxides by increasing the number of active sites present on the surface and can be applied for various purposes such as adsorption, catalysis and photocatalysis. Some of the materials that are currently highlighted are niobium compounds, in particular, its oxides, by its characteristics such as high acidity, rigidity, water insolubility, oxidative and photocatalytic properties. In this scenario, the study aimed preparing a composite material oxyhydroxide niobium (NbO2OH) / sodium vermiculite clay and evaluate its effectiveness with respect to the natural clay (V0) and NbO2OH. The composite was prepared by precipitation-deposition method and then characterized by X-ray diffraction, infrared spectroscopy (XRD), energy dispersive X-ray (EDS), thermal analysis (TG/DTG), scanning electron microscopy (SEM), N2 adsorption-desorption and investigation of distribution of load. The application of the material NbO2OH/V0 was divided in two steps: first through oxidation and adsorption methods, and second through photocatalytic activity using solar irradiation. Studies of adsorption, oxidation and photocatalytic oxidation monitored the percentage of color removal from the dye methylene blue (MB) by UV-Vis spectroscopy. The XRD showed a decrease in reflection d (001) clay after modification; the FTIR indicated the presence of both the clay when the oxyhydroxide niobium to present bands in 1003 cm-1 related to Si-O stretching bands and 800 cm-1 to the Nb-O stretching. The presence of niobium was also confirmed by EDS indicated that 17 % by mass amount of the metal. Thermal analysis showed thermal stability of the composite at 217 °C and micrographs showed that there was a decrease in particle size. The investigation of the surface charge of NbO2OH/V0 found that the material exhibits a heterogeneous surface with average low and high negative charges. Adsorption tests showed that the composite NbO2OH/V0 higher adsorption capacity to remove 56 % of AM, while the material removed from V0 only 13 % showed no NbO2OH and adsorptive capacity due to the formation of H-aggregates. The percent removal of dye color for the oxidation tests showed little difference from the adsorption, being 18 and 66 % removal of dye color for V0 and NbO2OH/V0 respectively. The NbO2OH/V0 material shows excellent photocatalytic activity managing to remove just 95,5 % in 180 minutes of the color of MB compared to 41,4 % and 82,2 % of V0 the NbO2OH, proving the formation of a new composite with distinct properties of its precursors.

Síntese e caracterização de catalisadores baseados em vermiculita modificada com ferro: aplicação em processos do tipo foto-fenton

Clays are materials with specific properties that make them promising for various studies. In this work we used the vermiculite clay as support for iron compounds, in order to obtain promising materials for application in the heterogeneous type photo-Fenton process. In all, the study included six solid, starting from the vermiculite (V0) was obtained calcined vermiculite (V0-C), the mixed material (V0/β-FeOOH) formed by vermiculite more akaganeite, exchanged vermiculite (v0t-C), vermiculite impregnated Wet (V0u-C) and V0u-CL that is the solid obtained by impregnating with a back washing. The solids of the study had their physical and chemical characteristics investigated by the following characterization techniques: X-Ray Diffraction (XRD), Infrared Spectroscopy (IR), Energy Dispersive Spectroscopy (EDS), X-Ray Fluorescence Spectroscopy (XRF), UV-Vis by Diffuse Reflectance (DR UV-Vis), Thermogravimetric Analysis (TGA) and Scanning Electron Microscopy (SEM). The V0 material showed three distinct phases, which are the very vermiculite, hidrobiotite and biotite, the last two phases are part of the geological of formation process vermiculite. The solids obtained after the modification showed an increase in the amount of iron present in the clay, these being quantities important for application in photocatalysis. The micrographs and EDS data, show that after treatment of addition of the metal , the iron was intercalary in structure of vermiculite for solid V0t-C and V0u-C, however, this did not occur with mixed material. In the photoFenton process, was observed a maximum removal of 88.8% of the dye methylene blue coloring for the catalyst V0/β-FeOOH, while for the other solids was obtained values between 76.8 and 62.6%, compared to 37.8% of discoloration without the presence of catalyst. Therefore, it is concluded that the vermiculite clay presents as a good catalyst and iron support for the, beyond of presenting a low cost because of its high abundance.

Avaliação do tratamento eletroquímico (direto e indireto) como alternativa de degradação do corante azul de metileno

Textile industry has been a cause of environmental pollution, mainly due to the generation of large volumes of waste containing high organic loading and intense color. In this context, this study evaluated the electrochemical degradation of synthetic effluents from textile industry containing Methylene Blue (AM) dye, using Ti/IrO2-Ta2O5 and Ti/Pt anodes, by direct and indirect (active chlorine) electrooxidation. We evaluated the influence of applied current density (20, 40 and 60 mA/cm2 ), and the presence of different concentrations of electrolyte (NaCl and Na2SO4), as well as the neutral and alkaline pH media. The electrochemical treatment was conducted in a continuous flow reactor, in which the electrolysis time of the AM 100 ppm was 6 hours. The performance of electrochemical process was evaluated by UV-vis spectrophotometry, chemical oxygen demand (COD) and total organic carbon (TOC). The results showed that with increasing current density, it was possible to obtain 100 % of color removal at Ti/IrO2-Ta2O5 and Ti/Pt electrodes. Regarding the color removal efficiency, increasing the concentration of electrolyte promotes a higher percentage of removal using 0,02 M Na2SO4 and 0,017 M NaCl. Concerning to the aqueous medium, the best color removal results were obtained in alkaline medium using Ti/Pt. In terms of organic matter, 86 % was achieved in neutral pH medium for Ti/Pt; while a 30 % in an alkaline medium. To understand the electrochemical behavior due to the oxygen evolution reaction, polarization curves were registered, determining that the presence of NaCl in the solution favored the production of active chlorine species. The best results in energy consumption and cost were obtained by applying lower current density (20 mA/cm2 ) in 6 hours of electrolysis.

Modulação da expressão da proteína XPA em resposta ao tratamento com azul de metileno fotossensibilizado

Reactive oxygen species (ROS) are produced by aerobic metabolism and react with biomolecules, such as lipids, proteins and DNA. In high concentration, they lead to oxidative stress. Among ROS, singlet oxygen (1O2) is one of the main ROS involved in oxidative stress and is one of the most reactive forms of molecular oxygen. The exposure of some dyes, such as methylene blue (MB) to light (MB+VL), is able to generate 1O2 and it is the principle involved in photodynamic therapy (PDT). 1O2 e other ROS have caused toxic and carcinogenic effects and have been associated with ageing, neurodegenerative diseases and cancer. Oxidative DNA damage is mainly repaired by base excision repair (BER) pathway. However, recent studies have observed the involvement of nucleotide excision repair (NER) factors in the repair of this type of injury. One of these factors is the Xeroderma Pigmentosum Complementation Group A (XPA) protein, which acts with other proteins in DNA damage recognition and in the recruitment of other repair factors. Moreover, oxidative agents such as 1O2 can induce gene expression. In this context, this study aimed at evaluating the response of XPA-deficient cells after treatment with photosensitized MB. For this purpose, we analyzed the cell viability and occurrence of oxidative DNA damage in cells lines proficient and deficient in XPA after treatment with MB+VL, and evaluated the expression of this enzyme in proficient and complemented cells. Our results indicate an increased resistance to treatment of complemented cells and a higher level of oxidative damage in the deficient cell lines. Furthermore, the treatment was able to modulate the XPA expression up to 24 hours later. These results indicate a direct evidence for the involvement of NER enzymes in the repair of oxidative damage. Besides, a better understanding of the effects of PDT on the induction of gene expression could be provided