Estudo da síntese e sinterização de pós compósitos do sistema Ta-Cu

Ta-Cu bulk composites combine high mechanical resistance of the Ta with high electrical and thermal conductivity of the Cu. These are important characteristics to electrical contacts, microwave absorber and heat skinks. However, the low wettability of Ta under Cu liquid and insolubility mutual these elements come hard sintering this composite. High-energy milling (HEM) produces composite powders with high homogeneity and refines the grain size. This work focus to study Ta-20wt%Cu composite powders prepared by mechanical mixture and HEM with two different conditions of milling in a planetary ball mill and then their sintering using hydrogen plasma furnace and a resistive vacuum furnace. After milling, the powders were pressed in a steel dye at a pressure of 200 MPa. The cylindrical samples pressed were sintered by resistive vacuum furnace at 10-4torr with a sintering temperature at 1100ºC / 60 minutes and with heat rate at 10ºC/min and were sintered by plasma furnace with sintering temperatures at 550, 660 and 800ºC without isotherm under hydrogen atmosphere with heat rate at 80ºC/min. The characterizations of the powders produced were analyzed by scanning electron microscopy (SEM), x-ray diffraction (XRD) and laser granulometry. After the sintering the samples were analyzed by SEM, XRD and density and mass loss tests. The results had shown that to high intense milling condition produced composite particles with shorter milling time and amorphization of both phases after 50 hours of milling. The composite particles can produce denser structure than mixed powders, if heated above the Cu melting point. After the Cu to arrive in the melting point, liquid copper leaves the composite particles and fills the pores

Estudo e desenvolvimento de um capacitor eletrolítico de nióbio

It seeks to find an alternative to the current tantalum electrolytic capacitors in the market due to its high cost. Niobium is a potential substitute, since both belong to the same group of the periodic table and because of this have many similar physical and chemical properties. Niobium has several technologically important applications, and Brazil has the largest reserves, around 96%. There are including niobium in reserves of tantalite and columbite in Rio Grande do Norte. These electrolytic capacitors have high capacitance specifies, ie they can store high energy in small volumes compared to other types of capacitors. This is the main attraction of this type of capacitor because is growing demand in the production of capacitors with capacitance specifies increasingly high, this because of the miniaturization of various devices such as GPS devices, televisions, computers, phones and many others. The production route of the capacitor was made by powder metallurgy. The initial niobium powder supplied by EEL-USP was first characterized by XRD, SEM, XRF and laser particle size, to then be sieved into three particle size, 200, 400 e 635mesh. The powders were then compacted and sintered at 1350, 1450 and 1550°C using two sintering time 30 and 60min. Sintering is one of the most important parts of the process as it affects properties as porosity and surface cleaning of the samples, which greatly affected the quality of the capacitor. The sintered samples then underwent a process of anodic oxidation, which created a thin film of niobium pentóxido over the whole porous surface of the sample, this film is the dielectric capacitor. The oxidation process variables influence the performance of the film and therefore the capacitor. The samples were characterized by electrical measurements of capacitance, loss factor, ESR, relative density, porosity and surface area. After the characterizations was made an annealing in air ate 260ºC for 60min. After this treatment were made again the electrical measurements. The particle size of powders and sintering affected the porosity and in turn the specific area of the samples. The larger de area of the capacitor, greater is the capacitance. The powder showed the highest capacitance was with the smallest particle size. Higher temperatures and times of sintering caused samples with smaller surface area, but on the other hand the cleaning surface impurities was higher for this cases. So a balance must be made between the gain that is achieved with the cleaning of impurities and the loss with the decreased in specific area. The best results were obtained for the temperature of 1450ºC/60min. The influence of annealing on the loss factor and ESR did not follow a well-defined pattern, because their values increased in some cases and decreased in others. The most interesting results due to heat treatment were with respect to capacitance, which showed an increase for all samples after treatment

Efeito da adição de fibras da palma do licuri (syagrus coronata) no comportamento físico e mecânico de compósitos de matriz cimentícia

This research was motivated by the requirement of asbestos s replacement in building systems and the need to generate jobs and income in the country side of the state of Bahia, Brazil. The project aimed at using fibers from licuri leaves (syagrus coronata), an abundant palm in the region, to produce composites appropriate for the sustainable production of cement fibre reinforced products in small plants. The composites were produced in laboratory using Portland cement CP-II-F32, sand, water, licuri palm fiber contents of 1.0, 1.5 and 2.0% by weight of binder (two different fiber length) and metakaolin. The latter was chosen as an additional binder for its efficiency to reduce the alkalinity of cementitious matrixes therefore preventing the degradation of vegetable fibers. The characterization of the composite components was carried out by sieving and laser particle size analyses, thermal analysis, fluorescence and X-ray diffraction. The composites performance was evaluated by 3- point-bending tests, compressive strength, ultrasound module of elasticity, free and restrained shrinkage, water capillarity absorption and apparent specific gravity. It has been found that the addition of fibers increased the time to onset of cracking over 200.00% and a 25% reduction in cracks opening in the restrained shrinkage test. The capillary absorption reduced about 25% when compared to fiber-free composites. It was also observed with regard to flexural strength, compressive strength and specific gravity, that the addiction of fibers did not affect the composite performance presenting similar results for compounds with and without fibers. In general it can be stated that the reinforced composite fibers of palm licuri presents physical and mechanical characteristics which enable them to be used in the intended proposals of this research

Efeitos da laserterapia de baixa potência sobre a fadiga do músculo quadríceps de indivíduos jovens

The objective of this study was to evaluate the effect of low laser power on the performance of anaerobic endurance of the quadriceps muscle in young subjects. Low-level laser therapy (LLLT) appears to decrease some indices of muscle fatigue. Most of these effects may be due to the influence of the laser on the muscles predominantly aerobic. Animal studies and clinical trials have already shown that the laser can improve the efficiency of mitochondrial metabolism for the resynthesis of adenosine triphosphate and thus slow down - or minimize, the deleterious effects of muscle fatigue. This research was characterized as an experimental study of the controlled clinical trial, randomized, blinded, attended by 93 volunteers, military, with ages between 18 and 19 years. The subjects were randomly allocated into three groups: Control (G1), Placebo (G2) and Laser (G3). All volunteers underwent an anthropometric assessment and a protocol Fatigue. This protocol was applied to an initial assessment (AV-1) for the collection of baseline data, and a final evaluation (AV-2). As the study variables, we used the blood lactate concentrations and indices of muscle power, as average power and peak velocity. The fatigue protocol consisted of a test of speed with twenty repetitions, performed on an exercise machine leg press 45º . In conclusion, it was found that, in this study, LLLT caused a significant increase in the Average of the Averages Powers, phase eccentric exercise in leg press 45º performed by young individuals

Efeito da crioterapia e da laserterapia na resposta ao dano muscular induzido pelo exercício excêntrico: ensaio clínico e randomizado

Exercise-induced muscle damage mainly affects individuals who returned to physical activity after a time without practicing it or had some kind of exhaustive exercise, particularly eccentric exercise. To evaluate the effect of cryotherapy and laser therapy in response to muscle damage induced by eccentric exercise on the biceps muscle. This was a randomized clinical trial consisting of 60 female subjects. All subjects initially underwent an evaluation consisting of perimetry, measurement of pain sensation (via algometry and visual analogue scale), electromyography and dynamometry. Then the subjects performed an exercise protocol on the isokinetic dynamometer consisting of 2 sets of 10 eccentric elbow flexors contraction at 60 °/s. Completed this protocol, an intervention was held according to a previously random group distribution: control group (no intervention), cryotherapy group and laser therapy group. Finally, subjects were re-evaluated immediately and 48 hours after the intervention protocol, except for Visual Analogue Scale (VAS), which was also evaluated 24 hours after exercise. The circumference of the limb, the pain sensation (VAS and algometry), the muscle activation amplitude (via Root Mean Square - RMS), median frequency, peak torque normalized per body weight, average peak torque, power and work were analyzed. The median frequency immediately after the intervention protocol on the cryotherapy group was the only variable that showed inter and intra-group differences; the remaining variables showed only intragroup differences. The perimetry values did not change immediately after the protocol on the groups which underwent cryotherapy and laser therapy, however, there was an increase after 48 hours; algometry values decreased in all groups for 48 hours and the VAS values increased 24 and 48 hours also for all groups. Regarding RMS no significant change was observed. For dynamometry, peak torque normalized per body weight and average peak torque had a similar behavior, with a reduction in the post protocol that has remained after 48 hours. For the power and work, a decrease was observed immediately after the protocol with a further reduction after 48 hours. Cryotherapy and laser therapy does not alter the muscle damage response, except for the perimetry values immediately after exercise.

Eficácia do cimento de ionômero de vidro como selante oclusal sobre a paralisação de lesões cariosas em dentina

Dental caries consists in a multifactorial and dynamic process. The knowledge of the ionic interactions among dental tissues and dental biofilm make possible its understanding as a process that can be stopped. Recently, the use of sealants have lost its function as preventive agent and passed to be argued as a possible therapeutical agent. This happens by hindering the substratum flow to the lesion inner and, therefore, controls the advance of the process. This study aimed to evaluate glass ionomer cement as a not invasive technique of treatment in occlusal caries without clinical cavitation, but with dentinal involvement. The research was accomplished using a controlled clinical trial with two groups (experimental and control) in 38 subjects (8-18 years) with 51 molars. The teeth of the experimental group were sealed with glass ionomer cement (Vidrion-R, S.S.White, Juiz de Fora, Brazil) and the molars control did not suffer intervention. The experimental group was followed by a year and the control by 8 months due the progression of the carious injury. Both groups were reevaluated to each 4 months with the use of clinical, radiographic and laser fluorescence (DIAGNOdent®) examination. The analysis of the clinical evaluation did not observe a significant difference between experimental and control groups. However, analysis with radiographic and laser fluorescence (DIAGNOdent®) examination observed a significant difference (p> 0,05) between groups, demonstrating a wors condition to the group without intervention. The results suggest that glass ionomer cement as sealant can be efficient to paralyze dentinal caries without clinical cavitation