Conversão do metano via oxicloração em reator de leito fixo utilizando catalisador do tipo CuCl2/SiO2

Supported catalysts of CuCl2 on sílica were used in the methane oxychlorination reaction. The materials were synthesized by the ion exchange technique in a basic solution, using a copper-ammonia complex with 3 and 6 % of nominal copper loading. The materials where characterized by thermogravimetry (TG), X-ray Fluorescence Spectroscopy (XRF), Temperature Programmed Reduction (TPR), Scanning Electron Microscopy with X-ray microanalysis (SEM/EDS), BET specific area and pore distribution. The characterization confirms the presence of copper on the support surface, concluding that the ion exchange technique was adequate in the catalyst synthesis. For the reaction test, an oxychlorination bench scale unit was employed. The tests were carried at 673 and 773 K. The results showed the influence of temperature and catalyst copper content on the oxychlorination of methane reaction

Síntese, caracterizaçao e propriedades catalicas da peneira molecular nanoestruturada modificada com lantanio

The nanostructured molecular sieve SBA-15 was synthesized by the hydrothermal method, and modified with lanthanum with Si/La molar ratios of 25, 50, 75 and 100. The materials were evaluated as catalysts for the cracking of n-hexane model reaction. Type SBA- 15 and LaSBA-15 mesoporous materials were synthesized using tetraetilortosilicato as a source of silica, hydrochloric acid, heptahydrate lanthanum chloride and distilled water. Pluronic P123 triblock. polymer was used as structure template. The syntheses were carried out by 72 hours. The obtained SBA-15 samples were previously analyzed by thermogravimetry, in order to check the conditions of calcination for removal of organic template. Then, the calcined materials were characterized by X-ray diffraction, infrared spectroscopy, adsorption and desorption of nitrogen, scanning electron microscopy and X-ray microanalysis by dispersive energy. The acidity of the samples was determined using adsorption of n-bulinamina and desorption followed by thermogravimetry. It was found that the hydrothermal synthesis method was suitable for the synthesis of the SBA-15 mesoporous materials, with an excellent degree of hexagonal ordering. The reactions of catalytic cracking of n-hexane were carried out using a fixed bed continuous flow microreactor, coupled on-line to a gas chromatograph. From the catalytic evaluation, it was observed that the mesoporous materials containing lanthanum showed different results for the reaction of cracking of nhexane compared to the unmodified mesoporous material SBA-15. As a result of cracking was obtained as main products hydrocarbons in the range of C1 to C5. The catalyst that showed better properties in relation to the acidity and catalytic activity was LaSBA-15 with the ratio Si/La = 50