This work deals with the application of X-Ray Absorption Spectroscopy on the study of the behavior of Cu2+ ions in inverse micelles. The formation of copper nanoparticles in water-in-oil microemulsions in pseudo-ternary systems of cetyl trimethylammonium Bromide (CTAB) surfactant, butanol co-surfactant, heptane as oil phase and aqueous solutions of CuSO4.5H2O, and NaBH4. The microemulsions were prepared with a fixed percentage (60 %) of oil phase and a variable water to tensoative proportion. It was observed an increase on Cu2+ reduction by the sodium borohydride in microemulsions with 13 % of aqueous phase, independent of the reaction time. For the microemulsions in which the aqueous phase is composed only by the CuSO4 solution, it was observed that the color of the solution depends on the water to surfactant ratio. These changes in color were attributed to a competition for the hidratation water between the polar head of the tensoative and Cu2+ ions with the eventual substitution of oxygen by bromine atoms in the first coordination shell of Cu2+ ions

Caracterização estrutural de Perovskitas Lax-1AxCoO3 (x=0 e 0,2) ,dopadas com cálcio e bario, por espectroscopia de absorção de raios X (XAS).

In this work, the structures of LaCoO3, La0,8Ba0,2CoO3 and La0,8Ca0,2CoO3 perovskites were characterized as a function of temperature (LaCoO3 structure being analyzed only at room temperature). The characterization of these materials were made by X-Ray Absorption Spectroscopy (XAS), in the cobalt K-edge, taking into account the correlated Einstein model X-ray absorption fine structure (EXAFS). The first part of the absorption spectrum corresponded the X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS). These materials were prepared by the combustion method. The combustion products were calcinated at 900 0C, for 6 hours in air. Noted that the sample LaCoO3 at room temperature and samples doped with Calcium and Barium in the temperature range of 50 K to 298 K showed greater distortion to monoclinic symmetry with space group I2/a. However, the sample doped with barium at the temperatures 50 K, 220 K, and 260 K showed a slight distortion to rhombohedral symmetry with space group R-3c. The La0,8Ca0, 2CoO3 structure was few sensitive to temperature variation, showing a higher local distortion in the octahedron and a higher local thermal disorder. These interpretations were in agreement with the information electronic structural on the XANES region and geometric in the EXAFS region