Aplicação de argila branca comercial pura e modificada para adsorção de sulfeto de hidrogênio

In this work were synthesized matrix-based commercial white clay in its composition having large amounts of kaolinite and quartz, with a certain percentage of iron oxide for use as an adsorbent for hydrogen sulfide (H2S). To characterize the effect of initial matrix techniques were used to characterize XRD, FTIR, XRF and TG. The initial clay mineral matrix was placed in contact with 0.1 molar solutions of the salts of Co2+, Ni2+, Cr3+ and a solution 0.1 g / 100ml rhodamine B. During the synthesis process, the solutions were placed in contact with the initial matrix for a period of 48 hours in order to have ion exchange with the clay mineral. To check the amount of exchanged metals, we used the technique of X-ray Fluorescence (XRF). After synthesis was initiated the process of adsorption of H2S, where the arrays were placed in the reactor, then by passing a stream of hydrogen sulfide. The matrix along with the reactor was weighed before and after to measure the amount of gas adsorbed. Based on the gravimetric data the matrix which had the highest performance of the adsorption matrix was exchanged with Ni2+ ions, obtaining a result of 11.13 mg H2S / g matrix, then the matrix coated with rhodamine B which was reached 10.13 mg H2S / g matrix

Matrizes poliméricas puras e modificadas para adsorção do gás sulfeto de hidrogênio

The underground natural gas found associated or not with oil is characterized by a mixture of hydrocarbons and residual components such as carbon dioxide (CO2), nitrogen gas (N2) and hydrogen sulfide (H2S), called contaminants. The H2S especially promotes itself as a contaminant of natural gas to be associated with corrosion of pipelines, to human toxicity and final applications of Natural Gas (NG). The sulfur present in the GN must be fully or partially removed in order to meet the market specifications, security, transport or further processing. There are distinct and varied methods of desulfurization of natural gas processing units used in Natural Gas (UPGN). In order to solve these problems have for example the caustic washing, absorption, the use of membranes and adsorption processes is costly and great expenditure of energy. Arises on such findings, the need for research to active processes of economic feasibility and efficiency. This work promoted the study of the adsorption of sulfide gas in polymer matrices hydrogen pure and modified. The substrates of Poly(vinyl chloride) (PVC), poly(methyl methacrylate) (PMMA) and sodium alginate (NaALG) were coated with vanadyl phosphate compounds (VOPO4.2H2O), vanadium pentoxide (V2O5), rhodamine B (C28H31N2O3Cl) and ions Co2+ and Cu2+, aiming to the adsorption of hydrogen sulfide gas (H2S). The adsorption tests were through a continuous flow of H2S in a column system (fixed bed reactor) adsorption on a laboratory scale. The techniques used to characterize the adsorbents were Infrared spectroscopy (FTIR), thermogravimetry analysis (TGA), X-ray fluorescence (XRF), the X-ray diffraction (XRD) electron microscopy (SEM). Such work indicates, the results obtained, the adsorbents modified PMMA, PVC and NaALG have a significant adsorptive capacity. The matrix that stood out and had the best adsorption capacity, was to ALG modified Co2+ with a score of 12.79 mg H2S / g matrix

Estudo da participação das espécies fortemente oxidantes produzidas durante a oxidação eletroquímica de corantes usando eletrodo de diamante dopado com boro: função das propriedades eletroquímicas do eletrodo e condições experimentais

The textile industry is one of the most polluting in the world (AHMEDCHEKKAT et al. 2011), generating wastewater with high organic loading. Among the pollutants present in these effluents are dyes, substances with complex structures, toxic and carcinogenic characteristics, besides having a strong staining. Improper disposal of these substances to the environment, without performing a pre-treatment can cause major environmental impacts. The objective this thesis to use a technique of electrochemical oxidation of boron doped diamond anode, BDD, for the treatment of a synthetic dye and a textile real effluent. In addition to studying the behavior of different electrolytes (HClO4, H3PO4, NaCl and Na2SO4) and current densities (15, 60, 90 and 120 mA.cm-2 ), and compare the methods with Rhodamine B (RhB) photolysis, electrolysis and photoelectrocatalytic using H3PO4 and Na2SO4. Electrochemical oxidation studies were performed in different ratio sp3 /sp2 of BDD with solution of RhB. To achieve these objectives, analysis of pH, conductivity, UV-visible, TOC, HPLC and GC-MS were developed. Based on the results with the Rhodamine B, it was observed that in all cases occurred at mineralization, independent of electrolyte and current density, but these parameters affect the speed and efficiency of mineralization. The radiation of light was favorable during the electrolysis of RhB with phosphate and sulfate. Regarding the oxidation in BDD anode with different ratio sp3 /sp2 (165, 176, 206, 220, 262 e 329), with lower carbon-sp3 had a longer favoring the electrochemical conversion of RhB, instead of combustion. The greater the carbon content on the anodes BDD took the biggest favor of direct electrochemical oxidation