Nitriding in cathodic cage of stainless steel AISI 316: influence of sample position

R.R.M. de Sousa et al. Nitriding in cathodic cage of stainless steel AISI 316: Influence of sample position. Vacuum, [s.l.], n.83, 2009. Disponivel em: . Acesso em: 04 out.2010.

Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.

Avaliação da espécie vegetal Croton cajucara Benth como inibidor de biocorrosão em aço carbono Aisi 1020

Actually in the oil industry biotechnological approaches represent a challenge. In that, attention to metal structures affected by electrochemical corrosive processes, as well as by the interference of microorganisms (biocorrosion) which affect the kinetics of the environment / metal interface. Regarding to economical and environmental impacts reduction let to the use of natural products as an alternative to toxic synthetic inhibitors. This study aims the employment of green chemistry by evaluating the stem bark extracts (EHC, hydroalcoholic extract) and leaves (ECF, chloroform extract) of plant species Croton cajucara Benth as a corrosion inhibitor. In addition the effectiveness of corrosion inhibition of bioactive trans-clerodane dehydrocrotonin (DCTN) isolated from the stem bark of this Croton was also evaluated. For this purpose, carbon steel AISI 1020 was immersed in saline media (3,5 % NaCl) in the presence and absence of a microorganism recovered from a pipeline oil sample. Corrosion inhibition efficiency and its mechanisms were investigated by linear sweep voltammetry and electrochemical impedance. Culture-dependent and molecular biology techniques were used to characterize and identify bacterial species present in oil samples. The tested natural products EHC, ECF and DCTN (DMSO as solvent) in abiotic environment presented respectively, corrosion inhibition efficiencies of 57.6% (500 ppm), 86.1% (500 ppm) and 54.5% (62.5 ppm). Adsorption phenomena showed that EHC best fit Frumkin isotherm and ECF to Temkin isotherm. EHC extract (250 ppm) dissolved in a polar microemulsion system (MES-EHC) showed significant maximum inhibition efficiency (93.8%) fitting Langmuir isotherm. In the presence of the isolated Pseudomonas sp, EHC and ECF were able to form eco-compatible organic films with anti-corrosive properties

Avaliação por pig de perfilagem de danos superfciais nos materiais das paredes de dutos de petróleo

The modern technology of materials and structural integrity of pipelines requests the use of inspection tools named inspection pigs to detect, localize and measure the length, width and depth dimensions of the thickness losses of walls of buried and underwater pipelines in service. These tools run them internally, performing and recording measurements, with performance that varies according to the pig s technology. It has been developed recently an instrumented pig technology, called feller pig. This work aims to indicate factors that influence the feller pig technology performance in the detection and in the accuracy of measurement of the length, width and depth dimensions of the thickness losses on the internal surface of an oil pipeline wall under normal conditions of oil pipe inspection with pig. In this work, is made a collection of factors and an analyses of the technology based on the available literature, as well as an experiment to observe the technology and the factors operating. In the experiment, a feeler pig is used in a pipeline built in carbon steel and in operation that flows petroleum, in witch are observed areas with internal thickness losses occurred naturally. Some of these areas and their dimensions taken by automated ultra-sound scanner are compared with the ones indicated by the feller pig. Based on the data collection, on the analysis and on the experiment, the influence of factors object of this research is discussed. It is concluded that, among these, there are factors related to pipe fabrication tolerances, to wear of pig components, to internal adhesive wear of pipeline, to other pipeline damages and to technology characteristics. Finally, actions are suggested to know better, improve and define the applicability of this technology

Análise tribológica de um sistema de acionamento alternativo de pigs para a indústria do petróleo

It is analyzed through the concepts of tribology and mechanical contact and damage the suggestion of implementing a backup system for traction and passage of Pipeline Inspection Gauge (Pig) from the inside of pipelines. In order to verify the integrity of the pipelines, it is suggested the possibility of displacement of such equipment by pulling wires with steel wires. The physical and mechanical characteristics of this method were verified by accelerated tests in the laboratory in a tribological pair, wire versus a curve 90. It also considered the main mechanisms of wear of a sliding system with and without lubricant, in the absence and presence of contaminants. To try this, It was constructed a test bench able to reproduce a slip system, work on mode back-and-forth ("reciprocation"). It was used two kinds of wires, a galvanized steel and other stainless steel and the results achieved using the two kinds of steel cables were compared. For result comparative means, it was used steel cables with and without coating of Poly Vinyl Chloride (PVC). The wires and the curves of the products were characterized using metallographic analysis, microhardness Vickers tests, X-ray diffraction (XRD), X-Ray Refraction (XRF) and tensile tests. After the experiments were analyzed some parameters that have been measurable, it demonstrates to the impracticality of this proposed method, since the friction force and the concept of alternating request at the contact between the strands of wire and the inner curves that are part ducts caused severe wear. These types of wear are likely to cause possible failures in future products and cause fluid leaks

Análise topológica experimental por perfilometria cíclica indutiva de superficies de paredes estruturais

To enhance the maintenance practices, Oil and Gas Pipelines are inspected from the inside by automated systems called PIG (Pipeline Inspection Gauge). The inspection and mapping of defects, as dents and holes, in the internal wall of these pipelines are increasingly put into service toward an overall Structural Integrity Policy. The residual life of these structures must be determined such that minimize its probability of failure. For this reason, the investigation on the detection limits of some basic topological features constituted by peaks or valleys disposed along a smooth surface is of great value for determining the sensitivity of the measurements of defects from some combinations of circumferential, axial and radial extent. In this investigation, it was analyzed an inductive profilometric sensor to scan three races, radius r1, r2, r3, in a circular surface of low carbon steel, equipped with eight consecutive defects simulated by bulges and holes by orbit, equally spaced at p/4 rad. A test rig and a methodology for testing in laboratory were developed to evaluate the sensor response and identify their dead zones and jumps due to fluctuations as a function of topological features and scanning velocity, four speeds different. The results are presented, analyzed and suggestions are made toward a new conception of sensor topologies, more sensible to detect these type of damage morphologies