Síntese de zeólitas e argilas ácidas pilarizadas a partir de matérias primas naturais

Structural changes in waste for zeolites synthesis are subject of many studies carried out in the synthesis of molecular sieves. These materials are named molecular sieves because they have well defined pore sizes and they have the capacity of select molecules by its size. In this work, it was studied the synthesis processes of two types of molecular sieves: pillared acid clays using as starting material one natural montmorillonite clay and the synthesis of zeolites from a silico-aluminous residue. This residue is a byproduct of the extraction of lithium -spodumene. The preparation of pillared acid clays was performed in two steps: 1° acid treatment of clay samples (time and temperature studies) and 2°pilarization of them with Al13 (Keggin ion). The temperature and acid concentration affect the removal of cations in the structure and porosity of the material obtained. The analysis of X-ray diffraction (XRD) and infrared spectroscopy (IR), showed that increasing the severity of the acid treatment compromises the structural material. Also the pore size distribution is approximately uniform. Despite presenting a structural disorganization, the samples were pillared. As evidenced by XRD increasing the basal spacing, specific area and uniform porosity by adsorption of N2. Regarding the microporous molecular sieves were synthesized zeolites A and NaP1 from a silico-aluminous residue, a byproduct of extracting lithium. The temperature and time of agitation during the synthesis were the most important factors for obtaining zeolite A. The aging of the gel and the highest crystallization time promoted the formation of zeolite NaP1 using a Si / Al ratio = 3.2

Síntese e caracterização de argilas pilarizadas com pilares mistos Al/Co

Two pillaring methods were tested to synthesize pillared clays containing mixed Al/Co pillars. Using the first method, based on the traditional procedure, were obtained materials containing different Co concentrations: 10, 25, 50, 75 and 100 % of Co in the pillaring solution. Just the experiments with low concentrations (10 and 25 % of Co) has formed pillared clays, whereas the sample with 25 % of cobalt showed best results compared with the one obtained just using Al as pillaring agent (basal spacing higher than 18 Å and surface area bigger than 300 m²/g). The 27Al NMR results pointed out the formation of mixed Al/Co pillars due to decreased between the intensities of AlVI/AlIV signals, indicating that the AlIV content decreased while Co content increased, suggesting the isomorphic substitution of Al atoms for Co in the Keggin ion structure (pillaring agent). For the samples containing 75 and 100 % of cobalt, it was verified the formation of others materials, which could be identified as hydrotalcite like compounds. The second pillarization method was named mixed layers, because the objective was to intercalate clay layers with hydrotalcite layers. Thus, after calcination, the hydrotalcite layers would dehydroxylate, resulting just in the metals oxides, intercalated between the clay sheets, thus generating, a pillared clay. For this purpose, were tested 4 synthesis procedures: physical mixture, mixture in water, ionic exchange under reflux and in situ synthesis. Of these, the method which showed the best results was the in situ synthesis, in which basal spacings of 14 Å (after calcination) were obtained, indicating that the samples are intercalated with metal oxides (Mg and Al). This procedure was reproduced with a Co-Al LDH (layered double hydroxide) and similar results were obtained, testifying the method reproducibility